Spark Plasma Sintering of Undoped SnO_2 Ceramics

Various parameters in spark plasma sintering（SPS）,such as sintering temperature,holding time,heating rate,and pressure,were adopted to investigate their effects on the densification of pure SnO2 power.The obtained experimental data show that the SPS process enhances densification.The high-density undoped SnO2 ceramics （96.6% of theoretical） was obtained at much lower temperature （1000℃）,within a much shorter time,compared to the conventional sintering process.The high-density undoped SnO2 ceramics （96.6% of theoretical） were obtained by SPS,under the condition of temperature：1000℃,pressure：40MPa,heating-rate：200℃/min,and holding time：3min

掺杂Sb的SnO_2基陶瓷导电薄膜的研制

对 Sn O2 陶瓷导电薄膜的特性、导电机理、制备、应用进行了叙述 ,并且利用喷涂热解工艺制备了 Sn O2 陶瓷导电薄膜 ,探讨了掺杂剂Sb的掺杂量、喷涂溶液的浓度对 Sn O2

SnO_2-ZnO二元系半导体陶瓷材料特性

报道了ＳｎＯ２－ＺｎＯ二元系半导体陶瓷体及其薄膜的制备方法，材料的电学、光学、热敏、气敏和湿敏特性，以及掺杂和热处理对材料特性的影响．ＳｎＯ２－ＺｎＯ半导体陶瓷材料有很好的稳定性，是一种多功能复合半导体材料，在光伏技术。

玻璃熔液测温用热电偶保护管的研制

研究了氧化物添加剂对氧化锡陶瓷性能的影响。选出一种适于高温玻璃熔池测温用的热电偶保护套管材料 ,并用冷等静压法制造出该种热电偶保护套管。

一种高抗湿的二氧化锡室温氢敏陶瓷的制备与研究

湿度的影响是金属氧化物半导体室温气敏材料应用中面临的主要挑战之一。本文通过传统的陶瓷制备工艺,将二氧化锡纳米粉与铂粉混合制备成块状的纳米复合陶瓷。这种块体陶瓷材料在室温50%相对湿度环境下对于较高浓度的氢气具有显著的响应,其对于体积分数1%的氢气响应很好,灵敏度可以达到150。然而它在50%相对湿度的环境下对低浓度氢气的响应仍然会受到很大的抑制。另外,二氧化锡团聚体颗粒也被作为原料用来制备Pt-SnO_2复合纳米陶瓷。在室温以及50%相对湿度环境下,它对体积分数1%的氢气灵敏度高达850,而当相对湿度上升到70%的时候,灵敏度依然能达到450。对于很低浓度的氢气,它也保留着显著的氢敏性能,在50%和70%的相对湿度下,对体积分数为0.04%的氢气灵敏度分别为5和4.1。显然,这种块体陶瓷材料在具备更强的抗湿性能的同时具有更高的灵敏度。微观结构显示这种块体陶瓷材料存在许多团聚体,这种不均匀的微观结构对于抗湿性能的调控具有非常重要的意义。