采用沉淀法-水热法合成了电催化Bi_(2)O_(3)-CuO复合材料.利用X-射线衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X-射线光电子能谱(XPS)等方法对样品的结构和形貌进行了研究.用电化学测试方法对材料电催化性能进行研究,用...采用沉淀法-水热法合成了电催化Bi_(2)O_(3)-CuO复合材料.利用X-射线衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X-射线光电子能谱(XPS)等方法对样品的结构和形貌进行了研究.用电化学测试方法对材料电催化性能进行研究,用气相色谱和核磁共振氢谱对产物进行分析.电催化实验结果表明,Bi_(2)O_(3)-CuO复合材料的电催化性能及对甲酸盐的选择性远高于Bi_(2)O_(3)和CuO.其中比例为1∶1的Bi_(2)O_(3)-CuO复合材料性能最好,在-1.2 V vs.RHE的电位下,甲酸盐的法拉第效率为90.3%,电流密度为20 mA/cm^(2),测试10 h保持稳定.展开更多
TiO_(2) nanobelts and Co_(3)O_(4)/TiO_(2) catalytic materials were prepared using the hydrothermal method.The cat-alyst was characterized by X-ray diffraction,scanning electron microscopy,transmission electron microsc...TiO_(2) nanobelts and Co_(3)O_(4)/TiO_(2) catalytic materials were prepared using the hydrothermal method.The cat-alyst was characterized by X-ray diffraction,scanning electron microscopy,transmission electron microscopy,X-ray electron spectroscopy,and fluorescence spectroscopy.At room temperature,with a relative humidity of 50.0%,the total gas flow rate of 1.0 L·min-1,the space velocity of 1.05×10^(4) h^(-1),and toluene volume concentration of 25.0µL·L^(-1),two 6 W vacuum ultraviolet lamps were used as light sources to catalyze,degrade,and mineralize toluene.The results show that the prepared catalyst is in the shape of nano-ribbons.The loading of Co_(3)O_(4) inhibits the recombina-tion of photogenerated electrons and holes and can effectively improve the catalytic performance.The Co_(3)O_(4)/TiO_(2) with a load of 6.0%Co_(3)O_(4) has the best catalytic effect.When N2 was used as a carrier gas,the degradation rate of tol-uene was only 34.7%.The toluene degradation is mainly due to the photolysis of vacuum ultraviolet light.When air was used as a carrier gas,O_(3) was produced.The Co_(3)O_(4)/TiO_(2) with a load of 6.0%and vacuum ultraviolet synergistical-ly promote toluene degradation.The highest degradation rate of toluene was 91.7%and the mineralization rate was 74.6%.The degradation rate of toluene was 2.6 times that of nitrogen as a carrier gas.展开更多
High-capacity nickel-rich layered oxides are promising cathode materials for high-energy-density lithium batteries.However,the poor structural stability and severe side reactions at the electrode/electrolyte interface...High-capacity nickel-rich layered oxides are promising cathode materials for high-energy-density lithium batteries.However,the poor structural stability and severe side reactions at the electrode/electrolyte interface result in unsatisfactory cycle performance.Herein,the thin layer of two-dimensional(2D)graphitic carbon-nitride(g-C_(3)N_(4))is uniformly coated on the LiNi_(0.8)Co_(0.1)Mn_(0.1)O_(2)(denoted as NCM811@CN)using a facile chemical vaporization-assisted synthesis method.As an ideal protective layer,the g-C_(3)N_(4)layer effectively avoids direct contact between the NCM811 cathode and the electrolyte,preventing harmful side reactions and inhibiting secondary crystal cracking.Moreover,the unique nanopore structure and abundant nitrogen vacancy edges in g-C_(3)N_(4)facilitate the adsorption and diffusion of lithium ions,which enhances the lithium deintercalation/intercalation kinetics of the NCM811 cathode.As a result,the NCM811@CN-3wt%cathode exhibits 161.3 mAh g^(−1)and capacity retention of 84.6%at 0.5 C and 55°C after 400 cycles and 95.7 mAh g^(−1)at 10 C,which is greatly superior to the uncoated NCM811(i.e.129.3 mAh g^(−1)and capacity retention of 67.4%at 0.5 C and 55°C after 220 cycles and 28.8 mAh g^(−1)at 10 C).The improved cycle performance of the NCM811@CN-3wt%cathode is also applicable to solid–liquid-hybrid cells composed of PVDF:LLZTO electrolyte membranes,which show 163.8 mAh g^(−1)and the capacity retention of 88.1%at 0.1 C and 30°C after 200 cycles and 95.3 mAh g^(−1)at 1 C.展开更多
文摘采用沉淀法-水热法合成了电催化Bi_(2)O_(3)-CuO复合材料.利用X-射线衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X-射线光电子能谱(XPS)等方法对样品的结构和形貌进行了研究.用电化学测试方法对材料电催化性能进行研究,用气相色谱和核磁共振氢谱对产物进行分析.电催化实验结果表明,Bi_(2)O_(3)-CuO复合材料的电催化性能及对甲酸盐的选择性远高于Bi_(2)O_(3)和CuO.其中比例为1∶1的Bi_(2)O_(3)-CuO复合材料性能最好,在-1.2 V vs.RHE的电位下,甲酸盐的法拉第效率为90.3%,电流密度为20 mA/cm^(2),测试10 h保持稳定.
文摘TiO_(2) nanobelts and Co_(3)O_(4)/TiO_(2) catalytic materials were prepared using the hydrothermal method.The cat-alyst was characterized by X-ray diffraction,scanning electron microscopy,transmission electron microscopy,X-ray electron spectroscopy,and fluorescence spectroscopy.At room temperature,with a relative humidity of 50.0%,the total gas flow rate of 1.0 L·min-1,the space velocity of 1.05×10^(4) h^(-1),and toluene volume concentration of 25.0µL·L^(-1),two 6 W vacuum ultraviolet lamps were used as light sources to catalyze,degrade,and mineralize toluene.The results show that the prepared catalyst is in the shape of nano-ribbons.The loading of Co_(3)O_(4) inhibits the recombina-tion of photogenerated electrons and holes and can effectively improve the catalytic performance.The Co_(3)O_(4)/TiO_(2) with a load of 6.0%Co_(3)O_(4) has the best catalytic effect.When N2 was used as a carrier gas,the degradation rate of tol-uene was only 34.7%.The toluene degradation is mainly due to the photolysis of vacuum ultraviolet light.When air was used as a carrier gas,O_(3) was produced.The Co_(3)O_(4)/TiO_(2) with a load of 6.0%and vacuum ultraviolet synergistical-ly promote toluene degradation.The highest degradation rate of toluene was 91.7%and the mineralization rate was 74.6%.The degradation rate of toluene was 2.6 times that of nitrogen as a carrier gas.
基金supported by the National Key R&D Program of China(Grant No.2023YFB2503900)the National Natural Science Foundation of China(Grant No.52372203)+1 种基金the National Natural Science Foundation of China(Grant No.52202259)the Shandong Province Natural Science Foundation(ZR2022QE093).
文摘High-capacity nickel-rich layered oxides are promising cathode materials for high-energy-density lithium batteries.However,the poor structural stability and severe side reactions at the electrode/electrolyte interface result in unsatisfactory cycle performance.Herein,the thin layer of two-dimensional(2D)graphitic carbon-nitride(g-C_(3)N_(4))is uniformly coated on the LiNi_(0.8)Co_(0.1)Mn_(0.1)O_(2)(denoted as NCM811@CN)using a facile chemical vaporization-assisted synthesis method.As an ideal protective layer,the g-C_(3)N_(4)layer effectively avoids direct contact between the NCM811 cathode and the electrolyte,preventing harmful side reactions and inhibiting secondary crystal cracking.Moreover,the unique nanopore structure and abundant nitrogen vacancy edges in g-C_(3)N_(4)facilitate the adsorption and diffusion of lithium ions,which enhances the lithium deintercalation/intercalation kinetics of the NCM811 cathode.As a result,the NCM811@CN-3wt%cathode exhibits 161.3 mAh g^(−1)and capacity retention of 84.6%at 0.5 C and 55°C after 400 cycles and 95.7 mAh g^(−1)at 10 C,which is greatly superior to the uncoated NCM811(i.e.129.3 mAh g^(−1)and capacity retention of 67.4%at 0.5 C and 55°C after 220 cycles and 28.8 mAh g^(−1)at 10 C).The improved cycle performance of the NCM811@CN-3wt%cathode is also applicable to solid–liquid-hybrid cells composed of PVDF:LLZTO electrolyte membranes,which show 163.8 mAh g^(−1)and the capacity retention of 88.1%at 0.1 C and 30°C after 200 cycles and 95.3 mAh g^(−1)at 1 C.