STUDY ON PREPARATION OF SUPPORTED ALUMINA MEMBRANE USING SOL- GEL METHOD

A stable colloidal boehmite sol was made with the aluminium iso propoxide made in China and used to prepare the supported γ alumina membrane using sol gel method. The γ alumina thin layer was characterized by SEM, N 2 sorption method and permeation measurement. The γ alumina membrane was prepared with uniform surface, thickness of 3 μm and average diameter of about 5 nm. The permeabilities of the single gases of H 2, N 2, Ar and their separation factors were measured. The experimental data explained a behavior of Knudsen diffusion for the gas transport through the thin membrane.

微波辅助sol-gel法合成Bi_(0.5)Na_(0.5)TiO_(3)粉体及其压电性能研究

采用微波辅助溶胶-凝胶(sol-gel)法制备Bi_(0.5)Na_(0.5)TiO_(3)(BNT)粉体,通过DSC/TG,XRD,SEM,FT-IR等表征方法,分析BNT的反应历程,煅烧温度对BNT成分、晶粒尺寸和压电性能的影响.结果表明,当微波煅烧温度为650℃时,可合成出高纯度BNT粉体(30~120 nm),其居里温度为394℃,d_(33)=7.5 pC/N,ε_(r)=535.58,tanδ=0.29.对比传统马弗炉煅烧sol-gel法,微波辅助sol-gel法有利于提高BNT的介电性能和居里温度,降低介质损耗.

Photocatalytic Activity of Nanosized ZnWO_4 Prepared by the Sol-gel Method

Nanosized ZnWO4 photocatalysts were successfully synthesized via the sol-gel process in a temperature range of 450-800℃. The grain size, crystal size, and crystallinity of ZnWO4 particles increased with the increase of calcina- tion temperature and prolonging calcination time. The photocatalytic activity was measured for the degradation of an aqueous Rhodamine-B（RhB） solution and gaseous formaldehyde（FAD）. With the increase of calcination temperature and time, the activities increased to a maximum and then decreased. ZnWO4 photocatalyst prepared at 550℃ for I0 h showed the highest activity, which is similar to the photocatalytic activity of P25TiO2 for the degradation of gase-ous FAD. High crystallinity, large surface area, and good dispersion are responsible for the high photocatalytic per- formance of the prepared ZnWO4.

Direct Synthesis of Diphenyl Carbonate with Heterogeneous Catalyst and Optimal Synthesis Conditions of the Support Prepared by Sol-gel Method

为由异构的催化反应的 diphenyl (DPC ) 的直接合成的催化剂的支持被大音阶的第五音胶化方法准备。与激活的炭相比，分子筛，多孔的陶艺，一氧化碳消灭剂，大音阶的第五音胶化方法准备的支持举办更高的活动。由 X 射线衍射(XRD ) 和传播电子显微镜(TEM ) 的支持的描述主要水晶阶段是 Co2MnO4 和平均粒子直径的表演是大约 40 nm。为支持的合成的最佳条件被直角的实验决定，它显示 Cu， Mn，和公司的比例是影响 DPC 的收益和选择的第一个重要因素。锻烧的温度是第二。最佳条件是：Cu， Mn，和公司的臼齿的比例是 1:1:1，锻烧 700 ° C 的温度，在 100 ° C 弄干，水洗澡 85 ° C 的温度。在这个过程的 DPC 的收益和选择能分别地在批操作到达 38% 和 99% 。选择为支持的混合氧化物比大音阶的第五音胶化方法更贡献到高催化活的铜钴锰。

Grain Size and Photocatalytic Activity of Nanometer TiO_2 Thin Films Prepared by the Sol-gel Method

Transparent anatase TiO2 nanometer thin films with photocatalytic activity were prepared via the sol-gel method on soda-lime glass. The thickness , crystalline phase, grain size, surface hydroxyl amount and so on were characterized by scanning electron microscopy (SEM) , X-ray diffraction (XRD), transmission electron microscopy ( TEM), X-ray photoelectron spectroscopy (XPS) and UV-visible spectrophotometer ( UV-VIS). The photocatalytic activity of TiO2 thin films was evaluated for the photocatalytic decolorization of aqueous methyl orange . The effects of film thickness on the crystalline phase, grain size, transmittance and photocatalytic activity of nanometer Ti02 thin films were discussed.

Barium titanate ceramic inks for continuous ink-jet printing synthesized by mechanical mixing and sol-gel methods

Ink-jet printing of ceramic thick films is one of low cost on-site ceramic pattern fabrication methods.It is necessary to investigate the rheological behaviour of ceramic inks and drying behaviour of droplets.Two kinds of BaTiO3 ceramic inks were prepared by mechanical mixing and sol-gel methods,respectively.The effect of preparation parameters,such as quantity of polyacrylic acid(PAA)and solid content,on physicochemical and rheologic properties of the ceramic inks was investigated.The results show that they satisfy the requirements of continuous ink-jet printing.The appearances of printed dots and single printed layers were observed by SEM.The SEM images indicate that dots printed with mixing method ink are in ring shape,and dots printed with sol-gel method ink are in pancake shape,so the printed layer surface with the latter ink is smoother.The causes of these phenomena were discussed.

Influence of dopant content on morphology and optical constants of ZnO:Na films by sol-gel method

Undoped and Na-doped ZnO films were deposited by sol-gel method.The effects of sodium incorporation on structure,surface morphology and optical constants of the films were investigated.X-ray diffraction patterns show the hexagonal wurtzite polycrystalline structure and that the sodium incorporation leads to the change in the structural characteristics of ZnO films.The SEM observations show that the surface morphology of the films is affected by the sodium incorporation.The transmission spectra show that the average transmittance of the films is above 85% in the visible range.The absorption edge initially blue-shifts and then red-shifts with the increase of Na doping content.The optical constants of these films were calculated using transmission spectra.Refractive indices of the films in the visible range decrease at first and then increase with increasing Na doping content.

Surface and Texture Properties of Tb-Doped Ceria-Zirconia Solid Solution Prepared by Sol-Gel Method

The three-way catalysts （TWCs） promoters Ce0.6Zr0.4- x TbxO2-y were prepared by sol-gel method. BET surface areas analysis indicated that an increase of the dopant Tb content from x = 0.05 to x = 0.15 favors an increase of surface area from 66.8 to 80.4 m^2· g^-1 compared with the undoped sample Ce0 .6oZr0.40O2 65.1 m^2·g^- 1 after calcination at 650℃. Transmission electron microscopy （TEM） observation indicated that the doped samples have a higher thermal stability. The XRD and Raman spectra confirmed that the Ce0.6Zr0.4-xTbxO2-y cubic solid solution is formed. XPS analysis revealed that Ce and Tb mainly existed in the form of Ce^4＋ and Tb^3 ＋ , and Zr existed in the form of Zr^4＋ on the surface of the samples. The doped samples were homogenous in composition ; the introduction of Tb into the CeO2-ZrO2 promoters resuited in the formation of a solid solution, and the concentration of surface lattice oxygen was increased.

Preparation and properties of nanocrystal SmBO_3 by nitrate-citrate sol-gel combustion method

Nanocrystal SmBO3 powders were synthesized by nitrate-citrate sol-gel combustion method. The phase evolution, morphologies and absorbency of the synthesized powders were characterized by X-ray diffraction （XRD）, Field emission scanning electronic microscope （FESEM）, Fourier transform infrared spectroscopy （FFIR） and UV-3101PC spectrophotometer （UVPC）, respectively. XRD and FESEM results showed that pure SmBO3 phase was obtained at 750 ℃, with an average original particle size of about 100 nm. FTIR showed that there were apparently concentrated absorbent peaks between 500 and 1400 cm^-1. Moreover, the reflectivity of the powders apparently decreased at the wavelength between 1.05 and 1.15 μm. Therefore, SmBO3 might be a kind of absorbent material for infrared laser.

Luminescence properties of red-emitting Ca_2Al_2SiO_7:Eu^(3+) nanoparticles prepared by sol-gel method

A series of red-emitting Ca2_xA12SiOT：xEu^3＋ （x = 1 mol.%-10 tool.%） phosphors were synthesized by the sol-gel method. The effects of annealing temperature and doping concentration on the crystal structure and luminescence properties of Ca2A12SiO7：Eu^3＋ phosphors were investigated. X-ray diffraction （XRD） profiles showed that all peaks could be attributed to the tetragonal Ca2A12SiO7 phase when the sample was annealed at 1000℃. Scanning electron microscopy （SEM） micrographs indicate that the phosphors have an irregularly rounded mor- phology with particles of about 200 nm. Excitation spectra showed that the strong broad band at around 258 nm and weak sharp lines in 350-490 nm were attributed to the charge transfer band of Eu^3＋-O^2- and f-f transitions within the 4f^6 configuration of Eu^3＋ ions, respectively. Emission spectra implied that the red luminescence could be attributed to the transitions from the ^5D0 excited level to the 7Fj （J = 0, 1, 2, 3, 4） levels of Eu3＋ions with the main electric dipole transition ^5D0→^7F2 （618 and 620 nm）, and Eu^3＋ ions prefer to occupy a lower symmetry site in the crystal lattice. Moreover, the photoluminescence （PL） intensity was strongly dependent on both the sintering temperature and doping concentration, and the highest PL intensity was observed at an Eu^3＋ concentration x = 7 mol.% after annealing at ll00℃. The obtained Ca2A12SiO7：Eu^＋3＋ phosphor may have potential application for the red lamp phosphor.

Synthesis of Long Afterglow Photoluminescent Materials Sr_2MgSi_2O_7∶Eu^(2+), Dy^(3+) by Sol-Gel Method

Long afterglow photoluminescent materials Sr2MgSi2O7 doped with Eu2+, Dy3+ were prepared by sol-gel method. The synthesized samples were characterized by X-ray diffraction. The excitation spectrum, emission spectrum and long decay curve were measured and analyzed. XRD pattern indicates that phosphor is with Sr2MgSi2O7 crystal structure. The wide range of excitation wavelength indicates that luminescent material can be excited by light from ultraviolet ray to visible light. The main peak of emission spectrum is located at 466 nm. Sample excited by visible light can emit bright blue light, and the afterglow time lasts more than 8 h.

Effects of sol-gel method and lanthanum addition on catalytic performances of nickel-based catalysts for methane reforming with carbon dioxide

The nickel-based catalysts were prepared by the sol-gel method and used for the CH4 reforming with CO2. The effects of the sol-gel method on the specific surface area, catalytic activity, desorption, and reduction performances of catalysts were investigated with BET, TPR, and TPD. Compared with the catalyst prepared by the impregnation method, the results indicated that the catalysts prepared by the sol-gel method had larger specific surface area, showing higher catalytic activities and exhibiting perfect desorption and reduction performances. In addition, the modification effects of adding La were studied, and it was found that the 0.75NLBT catalyst constituted of 5wt.%Ni-0.75wt.%La was optimal.

Synthesis and Characterization of Nanocrystalline SrAl_2O_4∶Eu, Dy Long Afterglow Phosphors by Sol-Gel Method

Eu 2+, Dy 3+ co-doped nanocrystalline strontium aluminate phosphor powders with brightness and long afterglow were synthesized by the sol-gel method at 1200 ℃ for 2 h. The samples were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results of XRD show that the single crystalline phase is α-SrAl_2O_4. According to the observation of SEM, the particles of the samples are needle-like. Compared with the samples synthesized by solid state reaction, the grain size of the sol-gel method is to nanometer grade. A clear blue shift occurs in the excitation and emission spectra. The blue shift in nanocrystalline SrAl_2O_4∶Eu, Dy phosphor can be attributed to the quantum-size-effect of the luminescent particles.

Fabrication and characterization of highly ordered Ni_(0.5)Zn_(0.5)Fe_2O_4 nanowire/tube arrays by sol-gel template method

Highly ordered nanowire/tube arrays of Ni0.5Zn0.5Fe2O4were fabricated by the sol-gel method in the pores of anodic alumina membrane （AAM）. Whether nanowires or nanotubes were fabricated depends on immersion time. The immersion time was 15- 40 s for nanotubes and over 60 s for nanowires. The topography and crystalline structure of the nanowire arrays were characterized by scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, and X-ray diffraction （XRD）. It was found that the length and diameter of the Ni0.5Zn0.5Fe2O4 nanowires are related to the thickness of the AAM and the diameter of the pores. The results indicated that the Ni0.5Zn0.5Fe2O4 nanowires are uniform and parallel to each other.

Preparation of Perovskite-Type Oxides La_(1-x)Sr_xFe_(1-y)Co_yO_3 Using EDTA Sol-Gel Method

Two series of perovskite-type oxides with composition (La_(1-x))Sr_xFeO_3(x≤0.8)and La_(1-x)Sr_xFe_(1-y)Co_yO_3(x=0.2; y=0.2, 0.4)powder productions were synthesized by EDTA complexing sol-gel method. The products were characterized by XRD, TEM, SEM, BET method(N_2 adsorption)and laser granularity analysis for different synthesis conditions to obtain the optimum conditions for the preparation process. Single-phased, uniform perovskite-type oxides with small particle size were obtained by EDTA sol-gel process with high stability and repeatability, and the process temperature is much lower than that of solid state reaction method.

Synthesis of CaCu_3Ti_4O_(12)powders and ceramics by sol-gel method using decanedioic acid and its dielectric properties

The CaCu3Ti4O12 xerogels,powders and ceramics were prepared through the sol-gel method using two kinds of organic acid(decanoic acid and decanedioic acid).The xerogels,powders and ceramics were characterized by the methods of TG-DTG,FT-IR,XRD,SEM and TEM.The dielectric properties of the ceramics were also measured.The results indicated that the powders calcined at 850°C for 2h are both nanometer scale particles.After sintering,the ceramics mainly consist of the CaCu3Ti4O12 phase.Compared with the powders prepared using monoacid,the particle size of the powders prepared using diacid obviously increases,and the grain size,the relative density and the whole permittivity of the ceramics increase as well.Specially,the ceramic prepared using decanedioic acid has higher relative density(97.3%),dielectric constant(316 808)and lower dielectric loss(0.242 5)at 30°C(10kHz)

Progress in Research on Nanometer Al_2O_3 Fabricated by Sol-Gel Method

Nanometer Al_2O_3 is one of new types of functional materials with broad application and development prospects in the future. The basic principle and ways of nanometer Al_2O_3 fabricated using sol-gel technique were introduced, and the factors affecting nanometer Al_2O_3 fabricated using sol-gel method were analyzed. The progress in research on nanometer Al_2O_3 and the application fields of nanometer Al_2O_3 were reviewed. The existing problems and the problems prospect for nanometer Al_2O_3 were pointed out.

Electrochemical performance of Al-substituted Li_3V_2(PO_4)_3 cathode materials synthesized by sol-gel method

The effect of Al-substitution on the electrochemical performances of Li3V2(PO4)3 cathode materials was studied.Samples with stoichiometric proportion of Li3AlxV2-x(PO4)3(x=0,0.05,0.10)were prepared by adding Al(NO3)3 in the raw materials of Li3V2(PO4)3.The XRD analysis shows that the Al-substituted Li3V2(PO4)3 has the same monoclinic structure as the un-substituted Li3V2(PO4)3.The SEM images show that Al-substituted Li3V2(PO4)3 has regular and uniform particles.The electrochemical measurements show that Al-substitution can improve the rate capability of cathode materials.The Li3Al0.05V1.95(PO4)3 sample shows the best high-rate performance.The discharge capacity at 1C rate is 119 mA·h/g with 30th capacity retention rate about 92.97%.The electrode reaction reversibility and electronic conductivity are enhanced,and the charge transfer resistance decreases through Al-substitution.The improved electrochemical performances of Al-substituted Li3V2(PO4)3 cathode materials offer some favorable properties for their commercial application.

Preparation and optical characteristics of ZnO films by chelating sol-gel method

The effect of different annealing temperatures on the structure, morphology,and optical properties of ZnO thin films prepared by the chelating sol-gel method was investigated.Zinc-oxide thin films were coated on quartz glass substrates by dip coating. Zinc nitrate, absoluteethanol, and citric acid were used as precursor, solvent, and chelating agent, respectively. Theresults show that ZnO films derived from zinc-citrate have lower crystallization temperature (below400℃), and that the crystal structure is wurtzite. The films, treated over 500℃, consist ofnano-particles and show to be porous at 600℃. The particle size of the film increases with theincrease of the annealing temperature. The largest particle size is 60 nm at 600℃. The opticaltransmittances related to the annealing temperatures become 90% higher in the visible range. Thefilm shows a starting absorption at 380 nm, and the optical band-gap of the thin film (fired at500℃) is 3.25 eV and close to the intrinsic band-gap of ZnO (3.2 eV).

Synthesis of hexagonal barium ferrite nanoparticle by sol-gel method

M-type Ba hexaferrites were successfully synthesized by sol-gel method. Several synthesizing factors, such as pH value, citric acid/metal ion ratio, and dispersion agent were mainly discussed. Fine and pure powders of BaFe12O19 were optimally synthesized under the conditions of the pH value is 7 and citric acid/metal ion ratio is 3. The X-ray diffraction analysis demonstrates that no impurity is observed in the synthesized powders after presintered at 450 ℃ and calcinated at 1100 ℃. SEM observations indicate that the size of the synthesized BaFe12O19 powders is small and uniform distribution. It can also be learned from SEM that the co-synthesizing sol-gel method can be in favor of the formation of finer particles.