A stacked Si/SiO_(x)/C composite anode material with carbon-coated structure was prepared by sol-gel method combined with carbothermal reduction using organic silicon.The results of X-ray diffractometry, scanning elec...A stacked Si/SiO_(x)/C composite anode material with carbon-coated structure was prepared by sol-gel method combined with carbothermal reduction using organic silicon.The results of X-ray diffractometry, scanning electron microscopy, and elemental analysis show that the Si/SiO_(x)/C material is a secondary particle with a porous micronanostructure, and the presence of nanometer silicon does not affect the carbothermal reduction and carbon coating.Electrochemical test results indicate that the specific capacity and first coulombic efficiency of SiO_(x)/C composite with nanometer silicon can be increased to 1 946.05 mAh/g and 76.49%,respectively.The reversible specific capacity of Si/SiO_(x)/C material blended with graphite is 749.69 mAh/g after 100 cycles at a current density of 0.1 C,and the capacity retention rate is up to 89.03%.Therefore, the composite has excellent electrochemical cycle stability.展开更多
This paper concentrates on the development of glasses with self-cleaning surfaces exhibiting high water contact angles. In this study, we prepared super-hydrophobic nano-ceramic coated glass based on titania & sil...This paper concentrates on the development of glasses with self-cleaning surfaces exhibiting high water contact angles. In this study, we prepared super-hydrophobic nano-ceramic coated glass based on titania & silica using simple sol-gel & dip coating methods and studied the best composition of the coatings by altering ratios of titanium tetraisopropoxide (TTIP)/tetraethyl orthosilicate (TEOS) with different homogenizing agents. We characterized the coatings by surface roughness measurement, percentage of optical transmission, static contact angle, near-infrared (NIR) transmission, and diffuse reflectance. The fabrication of coatings on glass substrates played an important role in increasing the water contact angle of about 95° and visible & NIR transmission of about 90%. We compared our modified glass substrate with commercial low emissivity (Low E) glass using X-ray diffraction (XRD) analysis, which showed pure amorphous surface claiming excellent wettability and thus the prepared glass substrate could have a variety of applications in different fields.展开更多
The purpose of this study was to prepare iron-based catalysts supported on silica by autocombustion method for directly using for Fischer-Tropsch synthesis（FTS） without a reduction step. The effect of different citr...The purpose of this study was to prepare iron-based catalysts supported on silica by autocombustion method for directly using for Fischer-Tropsch synthesis（FTS） without a reduction step. The effect of different citric acid（CA）：iron nitrate（N） molar ratios and acid types on the FTS performance of catalysts were investigated. The CA：N molar ratios had an important influence on the formation of iron active phases and FTS activity. The iron carbide（FexC）, which is known to be one of the iron active phases, was demonstrated by the X-ray diffraction and X-ray photoelectron spectroscopy. Increasing the CA：N molar ratios up to 0.1 increased CO conversion of catalyst to 86.5%, which was then decreased markedly at higher CA：N molar ratios. An excess of CA resulted in carbon residues covering the catalyst surface and declined FTS activity. The optimal catalyst（CA：N molar ratio = 0.1） achieved the highest CO conversion when compared with other autocombustion catalysts as well as reference catalyst prepared by impregnation method, followed by a reduction step. The autocombustion method had the advantage to synthesize more efficient catalysts without a reduction step. More interestingly, iron-based FTS catalysts need induction duration at the initial stage of FTS reaction even after reduction, because metallic iron species need time to be transformed to FexC. But here, even if without reduction, FexC was formed directly by autocombustion and induction period was eliminated during FTS reaction.展开更多
Dual-band electrochromic smart windows(DESWs)with independent control of the transmittance of near-infrared and visible light show great potential in the application of smart and energy-saving buildings.The current st...Dual-band electrochromic smart windows(DESWs)with independent control of the transmittance of near-infrared and visible light show great potential in the application of smart and energy-saving buildings.The current strategy for building DESWs is to screen materials for composite or prepare plasmonic nanocrystal films.These rigorous preparation processes seriously limit the further development of DESWs.Herein,we report a facile and effective sol-gel strategy using a foaming agent to achieve porous Ti-doped tungsten oxide film for the high performance of DESWs.The introduction of foaming agent polyvinylpyrrolidone during the film preparation can increase the specific surface area and free carrier concentration of the films and enhance their independent regulation ability of near-infrared electrochromism.As a result,the optimal film shows excellent dual-band electrochromic properties,including high optical modulation(84.9%at 633 nm and 90.3%at 1200 nm),high coloration efficiency(114.9 cm^(2) C^(-1) at 633 nm and 420.3 cm^(2) C^(-1) at 1200 nm),quick switching time,excellent bistability,and good cycle stability(the transmittance modulation losses at 633 and 1200 nm were 11%and 3.5%respectively after 1000 cycles).A demonstrated DESW fabricated by the sol-gel film showed effective management of heat and light of sunlight.This study represents a significant advance in the preparation of dual-band electrochromic films,which will shed new light on advancing electrochromic technology for future energy-saving smart buildings.展开更多
The effect of Na-excess content in the precursor on the structural and electrochemical performances of sodium nickel manganese oxide(NNMO)prepared by sol-gel and electrospinning methods is investigated in this paper.X...The effect of Na-excess content in the precursor on the structural and electrochemical performances of sodium nickel manganese oxide(NNMO)prepared by sol-gel and electrospinning methods is investigated in this paper.X-ray diffraction results of the prepared NNMO without adding Na-excess content indicate sodium loss,while the mixed phase of P2/O′3-type layered NNMO presented after adding Na-excess content.Compared with the sol-gel method,the secondary phase of NiO is more suppressed by using the electrospinning method,which is further confirmed by field emission scanning electron microscope images.N_(2) adsorption-desorption isotherms show no remarkably difference in specific surface areas between different preparation methods and Na-excess contents.The analysis of X-ray absorption near edge structure indicates that the oxidation states of Ni and Mn are+2 and+4,respectively.For the electrochemical properties,superior electrochemical performance is observed in the NNMO electrode with a low Na-excess content of 5wt%.The highest specific capacitance is 36.07 F·g^(-1)at0.1 A·g^(-1)in the NNMO electrode prepared by using the sol-gel method.By contrast,the NNMO electrode prepared using the electrospinning method with decreased Na-excess content shows excellent cycling stability of 100%after charge-discharge measurements for 300 cycles.Therefore,controlling the Na excess in the precursor together with the preparation method is important for improving the electrochemical performance of Na-based electrode materials in supercapacitors.展开更多
Transparent conducting aluminum doped tin oxide thin films were prepared by sol-gel dip coating method with differ-ent Al concentrations and characterized by X-ray diffraction (XRD), atomic force microscopy (AFM), UV-...Transparent conducting aluminum doped tin oxide thin films were prepared by sol-gel dip coating method with differ-ent Al concentrations and characterized by X-ray diffraction (XRD), atomic force microscopy (AFM), UV-Vis spectrophotometry and photoconductivity study. The variation observed in the properties of the measured films agrees with a difference in the film's thickness, which decreases when Al concentration augments. X-ray diffraction analysis reveals that all films are polycrystal-line with tetragonal structure, (110) plane being the strongest diffraction peak. The crystallite size calculated by the Debye Scher-rer’s formula decreases from 11.92 to 8.54 nm when Al concentration increases from 0 to 5 wt.%. AFM images showed grains uni-formly distributed in the deposited films. An average transmittance greater than 80% was measured for the films and an en-ergy gap value of about 3.9 eV was deduced from the optical analysis. Finally, the photosensitivity properties like current-voltage characteristics, ION/IOFF ratio, growth and decay time are studied and reported. Also, we have calculated the trap depth energy using the decay portion of the rise and decay curve photocurrent.展开更多
Multiferroic(BFO)nanoparticles doped with strontium with the general formula Bi1-xSrx FeO3(x=0,0.3,0.5,0.7)were synthesized using a modified sol-gel auto-combustion process.The structural,electrical,optical,and magnet...Multiferroic(BFO)nanoparticles doped with strontium with the general formula Bi1-xSrx FeO3(x=0,0.3,0.5,0.7)were synthesized using a modified sol-gel auto-combustion process.The structural,electrical,optical,and magnetic properties of the samples are discussed.The structural analysis,carried out using the x-ray powder diffraction technique,shows a structural transition from rhombohedral(R-3c)to cubic(Pm-3m)for the doping amount of strontium(Sr)equal to x=0.3.Morphological analysis of the prepared samples were carried out using scanning electron microscopy(SEM).Frequency-dependent dielectric constant and ac conductivity were studied.The doped samples,with improved dielectric properties,can be used to fabricate different optoelectronic devices.Strong dielectric dispersion and broad relaxation were exhibited by all the samples.Cole–Cole plots were employed as an effective tool to study the dispersion parameters,namely,the optical dielectric constant,static dielectric constant,relaxation time,and spreading factor.The activation energy was calculated from the relaxation peaks and Cole–Cole plots,which were found to be compatible with each other.The bandgap of the samples was calculated using diffuse reflectance spectral(DRS)analysis.Sharp and strong photoluminescence in the IR region was observed in the samples,similar to ZnO,which was reported for the first time.Room-temperature and low-temperature magnetization studies point towards the superparamagnetic nature of the samples,with an improvement in magnetic properties with doping.The antiferromagnetic behavior of bulk bismuth ferrite transforms to superparamagnetic in nature for both pure and Sr-substituted bismuth ferrite nanoparticles due to the close dimensions of crystallite size with magnetic domains leading to the break-down of the frustrated spin cycloidal moment.展开更多
To protect the AM60B magnesium alloy from corrosion,a sol-gel coating containing hydroxylated g-C_(3)N_(4)nanoplates was applied.The chemical composition of the hydroxylated g-C_(3)N_(4)nanoplates was investigated usi...To protect the AM60B magnesium alloy from corrosion,a sol-gel coating containing hydroxylated g-C_(3)N_(4)nanoplates was applied.The chemical composition of the hydroxylated g-C_(3)N_(4)nanoplates was investigated using X-ray photoelectron spectroscopy(XPS).The hydroxylation process did not affect the crystal size,specific surface area,pore volume,average pore diameter,and thermal stability of the g-C_(3)N_(4)nanoplates.After incorporating pristine and hydroxylated g-C_(3)N_(4)nanoplates,dense sol-gel coatings were obtained.Transmission electron microscopy(TEM)revealed the uniform distribution of the modified g-C_(3)N_(4)in the coating.The average roughness of the coating was also reduced after adding the modified nanoplates due to the decreased aggregation tendency.Electrochemical impedance spectroscopy(EIS)examinations in simulated acid rain revealed a significant improvement in the anticorrosion properties of the sol-gel film after the addition of the modified g-C_(3)N_(4)due to the chemical bonding of the coating to the nanoplates.展开更多
Titania films with nano-sized pores were prepared on the NaOH？HCl pretreated NiTi alloy substrate by sol？gel method.A crack-free film is obtained for the sample with a dense inner layer and a porous outside layer（s...Titania films with nano-sized pores were prepared on the NaOH？HCl pretreated NiTi alloy substrate by sol？gel method.A crack-free film is obtained for the sample with a dense inner layer and a porous outside layer（sample TC1＋1）.The X-ray diffraction shows that the titania films are composed of anatase,and a little Ni4Ti3 phase in the heat treated substrate is also detected.The X-ray photoelectron spectroscopy results indicate that the titania film completely covered the NiTi substrate for sample TC1＋1.The sample TC1＋1 is hydrophilic with a contact angle about 20°,and UV illumination treatment for 15 min further decreases the contact angle to（9.2±3.2）°.The potentiodynamic polarization test in 0.9% NaCl solution reveals a better corrosion resistance of sample TC1＋1 than the polished NiTi sample.展开更多
文摘A stacked Si/SiO_(x)/C composite anode material with carbon-coated structure was prepared by sol-gel method combined with carbothermal reduction using organic silicon.The results of X-ray diffractometry, scanning electron microscopy, and elemental analysis show that the Si/SiO_(x)/C material is a secondary particle with a porous micronanostructure, and the presence of nanometer silicon does not affect the carbothermal reduction and carbon coating.Electrochemical test results indicate that the specific capacity and first coulombic efficiency of SiO_(x)/C composite with nanometer silicon can be increased to 1 946.05 mAh/g and 76.49%,respectively.The reversible specific capacity of Si/SiO_(x)/C material blended with graphite is 749.69 mAh/g after 100 cycles at a current density of 0.1 C,and the capacity retention rate is up to 89.03%.Therefore, the composite has excellent electrochemical cycle stability.
文摘This paper concentrates on the development of glasses with self-cleaning surfaces exhibiting high water contact angles. In this study, we prepared super-hydrophobic nano-ceramic coated glass based on titania & silica using simple sol-gel & dip coating methods and studied the best composition of the coatings by altering ratios of titanium tetraisopropoxide (TTIP)/tetraethyl orthosilicate (TEOS) with different homogenizing agents. We characterized the coatings by surface roughness measurement, percentage of optical transmission, static contact angle, near-infrared (NIR) transmission, and diffuse reflectance. The fabrication of coatings on glass substrates played an important role in increasing the water contact angle of about 95° and visible & NIR transmission of about 90%. We compared our modified glass substrate with commercial low emissivity (Low E) glass using X-ray diffraction (XRD) analysis, which showed pure amorphous surface claiming excellent wettability and thus the prepared glass substrate could have a variety of applications in different fields.
基金financial support to the Overseas Academic Presentation Scholarship for Graduate Students, Graduate School, Chulalongkorn University
文摘The purpose of this study was to prepare iron-based catalysts supported on silica by autocombustion method for directly using for Fischer-Tropsch synthesis（FTS） without a reduction step. The effect of different citric acid（CA）：iron nitrate（N） molar ratios and acid types on the FTS performance of catalysts were investigated. The CA：N molar ratios had an important influence on the formation of iron active phases and FTS activity. The iron carbide（FexC）, which is known to be one of the iron active phases, was demonstrated by the X-ray diffraction and X-ray photoelectron spectroscopy. Increasing the CA：N molar ratios up to 0.1 increased CO conversion of catalyst to 86.5%, which was then decreased markedly at higher CA：N molar ratios. An excess of CA resulted in carbon residues covering the catalyst surface and declined FTS activity. The optimal catalyst（CA：N molar ratio = 0.1） achieved the highest CO conversion when compared with other autocombustion catalysts as well as reference catalyst prepared by impregnation method, followed by a reduction step. The autocombustion method had the advantage to synthesize more efficient catalysts without a reduction step. More interestingly, iron-based FTS catalysts need induction duration at the initial stage of FTS reaction even after reduction, because metallic iron species need time to be transformed to FexC. But here, even if without reduction, FexC was formed directly by autocombustion and induction period was eliminated during FTS reaction.
基金supported by the National Natural Science Foundation of China(51902064)the Natural Science Foundation of Guangxi(2022GXNSFFA0350325)+2 种基金the Scientific and Technological Bases and Talents of Guangxi(Guike AD20159073)the special fund for“Guangxi Bagui Scholars”the“Guangxi HundredTalent Program”。
文摘Dual-band electrochromic smart windows(DESWs)with independent control of the transmittance of near-infrared and visible light show great potential in the application of smart and energy-saving buildings.The current strategy for building DESWs is to screen materials for composite or prepare plasmonic nanocrystal films.These rigorous preparation processes seriously limit the further development of DESWs.Herein,we report a facile and effective sol-gel strategy using a foaming agent to achieve porous Ti-doped tungsten oxide film for the high performance of DESWs.The introduction of foaming agent polyvinylpyrrolidone during the film preparation can increase the specific surface area and free carrier concentration of the films and enhance their independent regulation ability of near-infrared electrochromism.As a result,the optimal film shows excellent dual-band electrochromic properties,including high optical modulation(84.9%at 633 nm and 90.3%at 1200 nm),high coloration efficiency(114.9 cm^(2) C^(-1) at 633 nm and 420.3 cm^(2) C^(-1) at 1200 nm),quick switching time,excellent bistability,and good cycle stability(the transmittance modulation losses at 633 and 1200 nm were 11%and 3.5%respectively after 1000 cycles).A demonstrated DESW fabricated by the sol-gel film showed effective management of heat and light of sunlight.This study represents a significant advance in the preparation of dual-band electrochromic films,which will shed new light on advancing electrochromic technology for future energy-saving smart buildings.
基金financially supported by (i) Suranaree University of Technology,(ii) Thailand Science Research and Innovation,and (iii) National Science,Research and Innovation Fund(project codes 90464 and 160363)。
文摘The effect of Na-excess content in the precursor on the structural and electrochemical performances of sodium nickel manganese oxide(NNMO)prepared by sol-gel and electrospinning methods is investigated in this paper.X-ray diffraction results of the prepared NNMO without adding Na-excess content indicate sodium loss,while the mixed phase of P2/O′3-type layered NNMO presented after adding Na-excess content.Compared with the sol-gel method,the secondary phase of NiO is more suppressed by using the electrospinning method,which is further confirmed by field emission scanning electron microscope images.N_(2) adsorption-desorption isotherms show no remarkably difference in specific surface areas between different preparation methods and Na-excess contents.The analysis of X-ray absorption near edge structure indicates that the oxidation states of Ni and Mn are+2 and+4,respectively.For the electrochemical properties,superior electrochemical performance is observed in the NNMO electrode with a low Na-excess content of 5wt%.The highest specific capacitance is 36.07 F·g^(-1)at0.1 A·g^(-1)in the NNMO electrode prepared by using the sol-gel method.By contrast,the NNMO electrode prepared using the electrospinning method with decreased Na-excess content shows excellent cycling stability of 100%after charge-discharge measurements for 300 cycles.Therefore,controlling the Na excess in the precursor together with the preparation method is important for improving the electrochemical performance of Na-based electrode materials in supercapacitors.
基金support of the laboratory of active components and materials,Oum El Bouaghi University.
文摘Transparent conducting aluminum doped tin oxide thin films were prepared by sol-gel dip coating method with differ-ent Al concentrations and characterized by X-ray diffraction (XRD), atomic force microscopy (AFM), UV-Vis spectrophotometry and photoconductivity study. The variation observed in the properties of the measured films agrees with a difference in the film's thickness, which decreases when Al concentration augments. X-ray diffraction analysis reveals that all films are polycrystal-line with tetragonal structure, (110) plane being the strongest diffraction peak. The crystallite size calculated by the Debye Scher-rer’s formula decreases from 11.92 to 8.54 nm when Al concentration increases from 0 to 5 wt.%. AFM images showed grains uni-formly distributed in the deposited films. An average transmittance greater than 80% was measured for the films and an en-ergy gap value of about 3.9 eV was deduced from the optical analysis. Finally, the photosensitivity properties like current-voltage characteristics, ION/IOFF ratio, growth and decay time are studied and reported. Also, we have calculated the trap depth energy using the decay portion of the rise and decay curve photocurrent.
基金Project supported by the Support from DST, Govt of India for the FIST grant sanctioned to Vimala College Thrissur (Grant No. SR/FST/College-046/2011)Sultan Qaboos University for the support provided during this study
文摘Multiferroic(BFO)nanoparticles doped with strontium with the general formula Bi1-xSrx FeO3(x=0,0.3,0.5,0.7)were synthesized using a modified sol-gel auto-combustion process.The structural,electrical,optical,and magnetic properties of the samples are discussed.The structural analysis,carried out using the x-ray powder diffraction technique,shows a structural transition from rhombohedral(R-3c)to cubic(Pm-3m)for the doping amount of strontium(Sr)equal to x=0.3.Morphological analysis of the prepared samples were carried out using scanning electron microscopy(SEM).Frequency-dependent dielectric constant and ac conductivity were studied.The doped samples,with improved dielectric properties,can be used to fabricate different optoelectronic devices.Strong dielectric dispersion and broad relaxation were exhibited by all the samples.Cole–Cole plots were employed as an effective tool to study the dispersion parameters,namely,the optical dielectric constant,static dielectric constant,relaxation time,and spreading factor.The activation energy was calculated from the relaxation peaks and Cole–Cole plots,which were found to be compatible with each other.The bandgap of the samples was calculated using diffuse reflectance spectral(DRS)analysis.Sharp and strong photoluminescence in the IR region was observed in the samples,similar to ZnO,which was reported for the first time.Room-temperature and low-temperature magnetization studies point towards the superparamagnetic nature of the samples,with an improvement in magnetic properties with doping.The antiferromagnetic behavior of bulk bismuth ferrite transforms to superparamagnetic in nature for both pure and Sr-substituted bismuth ferrite nanoparticles due to the close dimensions of crystallite size with magnetic domains leading to the break-down of the frustrated spin cycloidal moment.
文摘To protect the AM60B magnesium alloy from corrosion,a sol-gel coating containing hydroxylated g-C_(3)N_(4)nanoplates was applied.The chemical composition of the hydroxylated g-C_(3)N_(4)nanoplates was investigated using X-ray photoelectron spectroscopy(XPS).The hydroxylation process did not affect the crystal size,specific surface area,pore volume,average pore diameter,and thermal stability of the g-C_(3)N_(4)nanoplates.After incorporating pristine and hydroxylated g-C_(3)N_(4)nanoplates,dense sol-gel coatings were obtained.Transmission electron microscopy(TEM)revealed the uniform distribution of the modified g-C_(3)N_(4)in the coating.The average roughness of the coating was also reduced after adding the modified nanoplates due to the decreased aggregation tendency.Electrochemical impedance spectroscopy(EIS)examinations in simulated acid rain revealed a significant improvement in the anticorrosion properties of the sol-gel film after the addition of the modified g-C_(3)N_(4)due to the chemical bonding of the coating to the nanoplates.
基金Project(xjj2011096)supported by the Fundamental Research Fund for the Central Universities,ChinaProject(201107)supported by the Open Project Program of State Key Laboratory of Metastable Materials Science and Technology,ChinaProject(50901058)supported by the National Natural Science Foundation of China
文摘Titania films with nano-sized pores were prepared on the NaOH？HCl pretreated NiTi alloy substrate by sol？gel method.A crack-free film is obtained for the sample with a dense inner layer and a porous outside layer（sample TC1＋1）.The X-ray diffraction shows that the titania films are composed of anatase,and a little Ni4Ti3 phase in the heat treated substrate is also detected.The X-ray photoelectron spectroscopy results indicate that the titania film completely covered the NiTi substrate for sample TC1＋1.The sample TC1＋1 is hydrophilic with a contact angle about 20°,and UV illumination treatment for 15 min further decreases the contact angle to（9.2±3.2）°.The potentiodynamic polarization test in 0.9% NaCl solution reveals a better corrosion resistance of sample TC1＋1 than the polished NiTi sample.