A simple solvothermal approach employing oleic acid has been developed to prepare anatase TiO2 nanocrystals with different shapes, which were tuned from nanorods to nano-ellipsoids by increasing the amount of NaF from...A simple solvothermal approach employing oleic acid has been developed to prepare anatase TiO2 nanocrystals with different shapes, which were tuned from nanorods to nano-ellipsoids by increasing the amount of NaF from 0 to 0.5 retool, and the optical band gap decreased from 3.47 eV to 3.29 eV accordingly. However, when the fluoride was changed to NH4F, the resultant TiO2 nanocrystals possessed an anatase phase but were made up of smaller-sized nanocrystals and nanorods, and the band gap was increased to 3.53 eV. The X-ray photoelectron spectroscopy （XPS） results illustrated an increase of fluorine content with an increasing amount of NaF could account for the variation of the shape and optical band gap of TiO2 nanocrystals. Moreover, the absence of fluorine content brought about less change of shape and increase of optical band gap of the product synthesized in the presence of NH4F. This result may offer another way to alter the shape and band gap of metal oxide nanocrystals with the assistance of fluoride.展开更多
基金supported by the Fundamental Research Fund of the Central Universities (Beijing Jiao Tong University) (No.2014JBZ010)the support from the ‘‘Excellent One Hundred’’ project of Beijing Jiao Tong Universitythe National Undergraduates Training Programs for Innovation and Enterpreneuship
文摘A simple solvothermal approach employing oleic acid has been developed to prepare anatase TiO2 nanocrystals with different shapes, which were tuned from nanorods to nano-ellipsoids by increasing the amount of NaF from 0 to 0.5 retool, and the optical band gap decreased from 3.47 eV to 3.29 eV accordingly. However, when the fluoride was changed to NH4F, the resultant TiO2 nanocrystals possessed an anatase phase but were made up of smaller-sized nanocrystals and nanorods, and the band gap was increased to 3.53 eV. The X-ray photoelectron spectroscopy （XPS） results illustrated an increase of fluorine content with an increasing amount of NaF could account for the variation of the shape and optical band gap of TiO2 nanocrystals. Moreover, the absence of fluorine content brought about less change of shape and increase of optical band gap of the product synthesized in the presence of NH4F. This result may offer another way to alter the shape and band gap of metal oxide nanocrystals with the assistance of fluoride.