The centrifugal casting of compound HSS/nodular cast iron roll collar was studied,and the factors affecting transition zone quality were analyzed.The pouring temperature and interval in pouring are the main factors af...The centrifugal casting of compound HSS/nodular cast iron roll collar was studied,and the factors affecting transition zone quality were analyzed.The pouring temperature and interval in pouring are the main factors affecting transition zone quality.By controlling process parameter and flux adding during casting,high quality roll collar was obtained.The cause,why in the casting of HSS part,segregation appears easily,was analyzed and the countermeasure eliminating segregation was put forward,the measure eliminating heat treatment crackling was also put forward.展开更多
High speed steel (HSS) rolls can replace traditional rolls such as alloyed cast iron rolls and powder metallurgical (PM) hard alloy rolls. The main reasons for the replacement are that the wear resistance of low-cost ...High speed steel (HSS) rolls can replace traditional rolls such as alloyed cast iron rolls and powder metallurgical (PM) hard alloy rolls. The main reasons for the replacement are that the wear resistance of low-cost alloyed cast iron rolls is poor and the cost of high-quality PM hard alloy rolls is very high. By means of centrifugal casting, HSS rolls having excellent wear resistance have been manufactured. The hardness of the HSS roll is 6.5~67 HRC, the range of variation is smaller than 2 HRC and its impact toughness is 15 J/cm^2. The wear rate of HSS rolls used in the pre-finishing stands of high-speed hot wire-rod rolling mill reaches 2.5×10^(-4)mm per ton steel. Furthermore, the manufacturing cost of HSS rolls is significantly lower than that of PM hard alloy rolls; it is only 30 percent of that of PM hard alloy rolls.展开更多
The present study aims at developing the high speed steel (HSS) as rollmaterials to replace the traditional roll materials such as the alloy cast iron and powdermetallurgical (PM) hard alloy. The HSS roll billet was f...The present study aims at developing the high speed steel (HSS) as rollmaterials to replace the traditional roll materials such as the alloy cast iron and powdermetallurgical (PM) hard alloy. The HSS roll billet was formed by centrifugal casting, and the billetwas rough machined alter soften annealing heat treatment, then it was quenched and tempered to getsuitable hardness and toughness. After that the HSS roll was finish machined to the final dimensionof phi 285 mm in the outer diameter, phi 160 mm in the inner diameter and 120 mm in width and itssurface hardness was tested. Finally the HSS roll was used in high speed wire rod mill. The testresults show that a high and homogeneous hardness can obtain on the work surface of HSS rolls, thesurface hardness is 63-65HRC and its variation is smaller than 2HRC. The impact toughness of thiskind of HSS is about 16 J/cm^2. The results of on-line service investigation in high speed wire rodmill indicate that the HSS rolls have excellent wear resistance, the steel rolling quantity per mmof HSS rolls is 3120 t, the service life-span of HSS rolls is 4 times longer than that of highchromium cast iron rolls and it is close to that of the PM hard alloy rolls. The manufacturingburden of HSS rolls is obviously lower than that of the PM hard alloy rolls, it is only 25 percentof that of the PM hard alloy rolls.展开更多
The present study aims at developing high speed steel (HSS) as roll materialsto replace traditional roll materials such as the alloy cast iron and powder metallurgical (PM)hard alloy, because low-cost alloy cast iron ...The present study aims at developing high speed steel (HSS) as roll materialsto replace traditional roll materials such as the alloy cast iron and powder metallurgical (PM)hard alloy, because low-cost alloy cast iron rolls have poor wear resistance and the cost ofhigh-quality PM hard alloy rolls is too high to be accepted by some users. By means of a centrifugalcasting method, HSS rolls with excellent wear resistance have been developed. Its hardness is 65-67 HRC, and its variation is smaller than 2HRC; its impact toughness excels 15J/cm^2. Usingpre-finishing stands of a high-speed hot wire-rod rolling mill, the wear rate of HSS rolls per onethousand ton of steel is 0. 25mm. However, the manufacturing burden of HSS rolls is obviously lowerthan that of PM hard alloy rolls; it is only 30% of that of PM hard alloy rolls.展开更多
The centrifugal casting of compound HSS/nodular cast iron roll collar was studied, and the factors affecting transition zone quality were analyzed. The pouring temperature and interval in pouring are the main factors ...The centrifugal casting of compound HSS/nodular cast iron roll collar was studied, and the factors affecting transition zone quality were analyzed. The pouring temperature and interval in pouring are the main factors affecting transition zone quality. By controlling process parameter and flux adding during casting, high quality roll collar was obtained. The cause, why in the casting of HSS part, segregation appears easily, was analyzed and the countermeasure eliminating segregation was put forward, the measure eliminating heat treatment crackling was also put forward.展开更多
文摘The centrifugal casting of compound HSS/nodular cast iron roll collar was studied,and the factors affecting transition zone quality were analyzed.The pouring temperature and interval in pouring are the main factors affecting transition zone quality.By controlling process parameter and flux adding during casting,high quality roll collar was obtained.The cause,why in the casting of HSS part,segregation appears easily,was analyzed and the countermeasure eliminating segregation was put forward,the measure eliminating heat treatment crackling was also put forward.
文摘High speed steel (HSS) rolls can replace traditional rolls such as alloyed cast iron rolls and powder metallurgical (PM) hard alloy rolls. The main reasons for the replacement are that the wear resistance of low-cost alloyed cast iron rolls is poor and the cost of high-quality PM hard alloy rolls is very high. By means of centrifugal casting, HSS rolls having excellent wear resistance have been manufactured. The hardness of the HSS roll is 6.5~67 HRC, the range of variation is smaller than 2 HRC and its impact toughness is 15 J/cm^2. The wear rate of HSS rolls used in the pre-finishing stands of high-speed hot wire-rod rolling mill reaches 2.5×10^(-4)mm per ton steel. Furthermore, the manufacturing cost of HSS rolls is significantly lower than that of PM hard alloy rolls; it is only 30 percent of that of PM hard alloy rolls.
文摘The present study aims at developing the high speed steel (HSS) as rollmaterials to replace the traditional roll materials such as the alloy cast iron and powdermetallurgical (PM) hard alloy. The HSS roll billet was formed by centrifugal casting, and the billetwas rough machined alter soften annealing heat treatment, then it was quenched and tempered to getsuitable hardness and toughness. After that the HSS roll was finish machined to the final dimensionof phi 285 mm in the outer diameter, phi 160 mm in the inner diameter and 120 mm in width and itssurface hardness was tested. Finally the HSS roll was used in high speed wire rod mill. The testresults show that a high and homogeneous hardness can obtain on the work surface of HSS rolls, thesurface hardness is 63-65HRC and its variation is smaller than 2HRC. The impact toughness of thiskind of HSS is about 16 J/cm^2. The results of on-line service investigation in high speed wire rodmill indicate that the HSS rolls have excellent wear resistance, the steel rolling quantity per mmof HSS rolls is 3120 t, the service life-span of HSS rolls is 4 times longer than that of highchromium cast iron rolls and it is close to that of the PM hard alloy rolls. The manufacturingburden of HSS rolls is obviously lower than that of the PM hard alloy rolls, it is only 25 percentof that of the PM hard alloy rolls.
文摘The present study aims at developing high speed steel (HSS) as roll materialsto replace traditional roll materials such as the alloy cast iron and powder metallurgical (PM)hard alloy, because low-cost alloy cast iron rolls have poor wear resistance and the cost ofhigh-quality PM hard alloy rolls is too high to be accepted by some users. By means of a centrifugalcasting method, HSS rolls with excellent wear resistance have been developed. Its hardness is 65-67 HRC, and its variation is smaller than 2HRC; its impact toughness excels 15J/cm^2. Usingpre-finishing stands of a high-speed hot wire-rod rolling mill, the wear rate of HSS rolls per onethousand ton of steel is 0. 25mm. However, the manufacturing burden of HSS rolls is obviously lowerthan that of PM hard alloy rolls; it is only 30% of that of PM hard alloy rolls.
基金Sponsored by National Natural Science Foundation(59874024)
文摘The centrifugal casting of compound HSS/nodular cast iron roll collar was studied, and the factors affecting transition zone quality were analyzed. The pouring temperature and interval in pouring are the main factors affecting transition zone quality. By controlling process parameter and flux adding during casting, high quality roll collar was obtained. The cause, why in the casting of HSS part, segregation appears easily, was analyzed and the countermeasure eliminating segregation was put forward, the measure eliminating heat treatment crackling was also put forward.