Sr2Bi4Ti5O18(SBTi) single layered and Sr2Bi4Ti5O18 /Pb(Zr0.53Ti0.47)O3(SBTi/PZT) bilayered thin films have been prepared on Pt/TiO2/SiO2/Si substrates by pulsed-laser deposition(PLD).The related structural characteriz...Sr2Bi4Ti5O18(SBTi) single layered and Sr2Bi4Ti5O18 /Pb(Zr0.53Ti0.47)O3(SBTi/PZT) bilayered thin films have been prepared on Pt/TiO2/SiO2/Si substrates by pulsed-laser deposition(PLD).The related structural characterizations and electrical properties have been comparatively investigated.X-ray diffraction reveals that both films have crystallized into perovskite phases and scanning electron microscopy shows the sharp interfaces.Both films show well-saturated ferroelectric hysteresis loops,however,compared with the single layered SBTi films,the SBTi/PZT bilayered films have significantly increased remnant polarization(Pr) and decreased coercive field(Ec),with the applied field of 260 kV/cm.The measured Pr and Ec of SBTi and SBTi/PZT films were 7.9 C/cm 2,88.1 kV/cm and 13.0 C/cm 2,51.2 kV/cm,respectively.In addition,both films showed good fatigue-free characteristics,the switchable polarization decreased by 9% and 11% of the initial values after 2.2 10 9 switching cycles for the SBTi single layered films and the SBTi/PZT bilayered films,respectively.Our results may provide some guidelines for further optimization of multilayered ferroelectric thin films.展开更多
基金2013年国家级大学生创新创业训练计划项目(201313256001)湖北师范学院硕士研究生创新科研基金项目(1051320130216)+1 种基金National Undergraduate Training Programs for Innovation and Entrepreneurship(201313256001)Postgraduate Innovation Scientific Research Foundation of Hubei Normal University(1051320130216)
基金supported by the National Natural Science Foundation(Grant Nos. 50805076 and 51275237)the National Natural Science Key Corporation Foundations (Grant No. 61161120323)Science Research Foundation at NUAA (Grant No. NS2012014)
文摘Sr2Bi4Ti5O18(SBTi) single layered and Sr2Bi4Ti5O18 /Pb(Zr0.53Ti0.47)O3(SBTi/PZT) bilayered thin films have been prepared on Pt/TiO2/SiO2/Si substrates by pulsed-laser deposition(PLD).The related structural characterizations and electrical properties have been comparatively investigated.X-ray diffraction reveals that both films have crystallized into perovskite phases and scanning electron microscopy shows the sharp interfaces.Both films show well-saturated ferroelectric hysteresis loops,however,compared with the single layered SBTi films,the SBTi/PZT bilayered films have significantly increased remnant polarization(Pr) and decreased coercive field(Ec),with the applied field of 260 kV/cm.The measured Pr and Ec of SBTi and SBTi/PZT films were 7.9 C/cm 2,88.1 kV/cm and 13.0 C/cm 2,51.2 kV/cm,respectively.In addition,both films showed good fatigue-free characteristics,the switchable polarization decreased by 9% and 11% of the initial values after 2.2 10 9 switching cycles for the SBTi single layered films and the SBTi/PZT bilayered films,respectively.Our results may provide some guidelines for further optimization of multilayered ferroelectric thin films.