In order to improve the red luminescent properties,Sr_(2)MgSi_(2)O_(7):Eu^(2+),Dy^(3+)was selected as a blue persistent luminescent donor phosphor,while light conversion agent was utilized to tune the persistent lumin...In order to improve the red luminescent properties,Sr_(2)MgSi_(2)O_(7):Eu^(2+),Dy^(3+)was selected as a blue persistent luminescent donor phosphor,while light conversion agent was utilized to tune the persistent luminescent spectra from blue to red.Composite red luminescent material Sr_(2)MgSi_(2)O_(7):Eu^(2+),Dy^(3+)/light conversion agent(SMED/LCA)was fabricated with light conversion agent and Sr_(2)MgSi_(2)O_(7):Eu^(2+),Dy^(3+)at a certain mass ratio.SiO_(2)(Al2 O_(3) or MgF2)were coated on the surface of SMED/LCA through heterogeneous deposition method.The structural and optical characteristics of the resulting samples were launched in terms of X-ray diffraction and emission spectrum as well as afterglow brightness.The results demonstrate that the emission spectrum exhibits two emission bands,and the peaks are located at around 470 and 615 nm.SiO_(2),Al_(2)O_(3) and MgF_(2) are coated on the surface of SMED/LCA like a protective shell to maintain its stability and luminescent properties,the afterglow initial brightness is still up to 0.37 cd/m^(2) and the afterglow color purity calculated from CIE color coordinates is basically unchanged.展开更多
基金Project supported by Natural Science Foundation of Jiangsu Province(BK20171140,BK20180629)National Natural Science Foundation of China(51803076)。
文摘In order to improve the red luminescent properties,Sr_(2)MgSi_(2)O_(7):Eu^(2+),Dy^(3+)was selected as a blue persistent luminescent donor phosphor,while light conversion agent was utilized to tune the persistent luminescent spectra from blue to red.Composite red luminescent material Sr_(2)MgSi_(2)O_(7):Eu^(2+),Dy^(3+)/light conversion agent(SMED/LCA)was fabricated with light conversion agent and Sr_(2)MgSi_(2)O_(7):Eu^(2+),Dy^(3+)at a certain mass ratio.SiO_(2)(Al2 O_(3) or MgF2)were coated on the surface of SMED/LCA through heterogeneous deposition method.The structural and optical characteristics of the resulting samples were launched in terms of X-ray diffraction and emission spectrum as well as afterglow brightness.The results demonstrate that the emission spectrum exhibits two emission bands,and the peaks are located at around 470 and 615 nm.SiO_(2),Al_(2)O_(3) and MgF_(2) are coated on the surface of SMED/LCA like a protective shell to maintain its stability and luminescent properties,the afterglow initial brightness is still up to 0.37 cd/m^(2) and the afterglow color purity calculated from CIE color coordinates is basically unchanged.