The VC_p reinforced stainless steel composite was produced by in-situ reaction casting. The composite was tested for its wear resistance under the wet abrasive condition and corrosion resistance, compared with the wea...The VC_p reinforced stainless steel composite was produced by in-situ reaction casting. The composite was tested for its wear resistance under the wet abrasive condition and corrosion resistance, compared with the wear-resistant white iron and stainless steel. The results show that the wear resistance of the composite is slightly inferior to that of the white iron, but much better than that of the stainless steel under the wet grinding abrasive condition. The corrosion resistance of the composite is much better than that of the white iron in the acid medium, and a little worse than that of the stainless steel. Thus the composite exhibits superior properties of wear resistance and corrosion resistance.展开更多
In this study,a few Fe-based amorphous matrix composite coatings reinforced with various portions(4,8 and16 vol.%) of 31 6L stainless steel powders have been successfully produced through high velocity oxy-fuel(HVOF) ...In this study,a few Fe-based amorphous matrix composite coatings reinforced with various portions(4,8 and16 vol.%) of 31 6L stainless steel powders have been successfully produced through high velocity oxy-fuel(HVOF) spraying.The microstructure of the composite coatings was systematically characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM) and transmission electron microscopy(TEM).The main structure of composite coatings remained amorphous while 31 6L stainless steel splats were distributed homogeneously in the amorphous matrix and well connected with surrounding amorphous phase.Bonding strength of coatings to the substrate was determined by 'pull-off' tensile tests.The results revealed that the31 6L stainless steel phase effectively improved the bonding strength of amorphous coatings,which is mainly contributed by the strong metallurgical bonding between stainless steel and amorphous splats.The addition of31 6L stainless steel also enhanced the ductility and fracture resistance of the coatings due to the ductile stainless steel phases,which can arrest crack propagation and increase energy dissipation.展开更多
文摘The VC_p reinforced stainless steel composite was produced by in-situ reaction casting. The composite was tested for its wear resistance under the wet abrasive condition and corrosion resistance, compared with the wear-resistant white iron and stainless steel. The results show that the wear resistance of the composite is slightly inferior to that of the white iron, but much better than that of the stainless steel under the wet grinding abrasive condition. The corrosion resistance of the composite is much better than that of the white iron in the acid medium, and a little worse than that of the stainless steel. Thus the composite exhibits superior properties of wear resistance and corrosion resistance.
基金financially supported by the National Natural Science Foundation of China (Grant Nos. 51271081 and 51301072)partially supported by the Key Fundamental Research Project from Shenzhen Research Council (No. JC201105170745A)
文摘In this study,a few Fe-based amorphous matrix composite coatings reinforced with various portions(4,8 and16 vol.%) of 31 6L stainless steel powders have been successfully produced through high velocity oxy-fuel(HVOF) spraying.The microstructure of the composite coatings was systematically characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM) and transmission electron microscopy(TEM).The main structure of composite coatings remained amorphous while 31 6L stainless steel splats were distributed homogeneously in the amorphous matrix and well connected with surrounding amorphous phase.Bonding strength of coatings to the substrate was determined by 'pull-off' tensile tests.The results revealed that the31 6L stainless steel phase effectively improved the bonding strength of amorphous coatings,which is mainly contributed by the strong metallurgical bonding between stainless steel and amorphous splats.The addition of31 6L stainless steel also enhanced the ductility and fracture resistance of the coatings due to the ductile stainless steel phases,which can arrest crack propagation and increase energy dissipation.
