Effects of iron oxide on crystallization behavior and spatial distribution of spinel in stainless steel slag

Chromium plays a vital role in stainless steel due to its ability to improve the corrosion resistance of the latter.However,the re-lease of chromium from stainless steel slag(SSS)during SSS stockpiling causes detrimental environmental issues.To prevent chromium pollution,the effects of iron oxide on crystallization behavior and spatial distribution of spinel were investigated in this work.The results revealed that FeO was more conducive to the growth of spinels compared with Fe2O3 and Fe3O4.Spinels were found to be mainly distrib-uted at the top and bottom of slag.The amount of spinel phase at the bottom decreased with the increasing FeO content,while that at the top increased.The average particle size of spinel in the slag with 18wt%FeO content was 12.8μm.Meanwhile,no notable structural changes were observed with a further increase in FeO content.In other words,the spatial distribution of spinel changed when the content of iron oxide varied in the range of 8wt%to 18wt%.Finally,less spinel was found at the bottom of slag with a FeO content of 23wt%.

Novel wood-plastic composite fabricated via modified steel slag:Preparation,mechanical and flammability properties

A novel method was developed to enhance the utilization rate of steel slag(SS).Through treatment of SS with phosphoric acid and aminopropyl triethoxysilane(KH550),we obtained modified SS(MSS),which was used to prepare MSS/wood-plastic composites(MSS/WPCs)by replacing talcum powder(TP).The composites were fabricated through melting blending and hot pressing.Their mechanical and combustion properties,which comprise heat release,smoke release,and thermal stability,were systematically investigated.MSS can improve the mechanical strength of the composites through grafting reactions between wood powder and thermoplastics.Notably,MSS/WPC#50(16wt%MSS)with an MSS-to-TP mass ratio of 1:1 exhibited optimal comprehensive performance.Compared with those of WPC#0 without MSS,the tensile,flexural,and impact strengths of MSS/WPC#50 were increased by 18.5%,12.8%,and 18.0%,respectively.Moreover,the MSS/WPC#50 sample achieved the highest limited oxygen index of 22.5%,the highest vertical burning rating at the V-1 level,and the lowest horizontal burning rate at 44.2 mm/min.The formation of a dense and stable char layer led to improved thermal stability and a considerable reduction in heat and smoke releases of MSS/WPC#50.However,the partial replacement of TP with MSS slightly compromised the mechanical and flame-retardant properties,possibly due to the weak grafting caused by SS powder agglomeration.These findings suggest the suitability of MSS/WPCs for high-value-added applications as decorative panels indoors or outdoors.

Multiscale Study on Low Temperature Crack Resistance Mechanism of Steel Slag Asphalt Mixture

The objective of this paper was to study low temperature crack resistance mechanism of steel slag asphalt mixture(SAM).Thermal stress restrained specimen test(TSRST)and three-point bending test were carried out to evaluate the low-temperature crack resistance of SAM and basalt asphalt mixture(BAM).Based on the digital image correlation technique(DIC),the strain field distribution and crack propagation of SAM were analyzed from the microscopic point of view,and a new index,crack length factor(C),was proposed to evaluate the crack resistance of the asphalt mixture.The crystal phase composition and microstructure of steel slag aggregate(SA)and basalt aggregate(BA)were studied by X-ray diffraction(XRD)and scanning electron microscopy(SEM)to explore the low-temperature crack resistance mechanism of SAM.Results show that the low-temperature crack resistance of SAM is better than that of BAM;SAM has good integrity and persistent elastic deformation,and its bending failure mode is a hysteretic quasi-brittle failure;The SA surface is evenly distributed with pores and has surface roughness.SA has the composition phase of alkaline aggregate-calcite(CaCO3),so it has good adhesion to asphalt,which reveals the mechanism of excellent low-temperature crack resistance of SAM.

Recycling of Local Qatar’s Steel Slag and Gravel Deposits in Road Construction

Every year,the State of Qatar generates about 400,000 tons of steel slag and another 500,000 tons of gravel as a result of steel manufacturing and washing sand,respectively.The two materials(by-products)are not fully utilized to their best market values.At the same time,infrastructural renewal will take place in Qatar over the next ten years,and there will be a greater demand for aggregates and other construction materials as the country suffers from the availability of good aggregates.This paper presents results obtained on the use of steel slag,gravel and gabbro(control)in HMAC(hot mix asphalt concrete)paving mixtures and road bases and sub-bases.Tests were conducted in accordance with QCS-2010(Qatar Construction Specifications)and results were compared with QCS requirements for aggregates used in these applications.Based on the data obtained in this work,steel slag and gravel aggregates have a promising potential to be used in HMAC paving mixtures on Qatar’s roads,whether in asphalt base and asphalt wearing courses or as unbound aggregates in the base and sub-base pavement structure.

Exploring the Mechanical Properties,Shrinkage and Compensation Mechanism of Cement Stabilized Macadam-Steel Slag from Multiple Perspectives

Steel slag is characterized by high strength,good wear resistance and micro-expansion.This study aims at exploring the potential of steel slag in cement stabilized aggregates,mainly including mechanical properties,shrinkage and compensation mechanisms.For this purpose,the compressive strength and compressive resilient modulus of cement stabilized aggregates with different steel slag contents(CSMS)were initially investigated.Subsequently,the effects of steel slag and cement on dry shrinkage,temperature shrinkage,and total shrinkage were analyzed through a series of shrinkage test designs.Additionally,in combination with X-ray diffraction(XRD)and Scanning electron microscope(SEM),the characteristic peaks and microscopic images of cement,steel slag and cement-steel slag at different hydration ages were analyzed to identify the chemical substances causing the expansion volume of steel slag and reveal the compensation mechanism of CSMS.The results show that the introduction of 20%steel slag improved the mechanical properties of CSMS by 16.7%,reduced dry shrinkage by 21%,increased temperature shrinkage by 5.8%and reduced its total shrinkage by 19.2%.Compared with the hydration reaction of cement alone,the composite hydration reaction of steel slag with cement does not produce new hydrates.Furthermore,it is noteworthy that the volume expansion of the f-CaO hydration reaction in steel slag can compensate for the volume shrinkage of cement-stabilized macadam.This research can provide a solid theoretical basis for the application and promotion of steel slag in cement-stabilized macadam and reduce the possibility of shrinkage cracking.

Research on the Low-carbon Cementitious Materials:Effect of Triisopropanolamine on the Hydration of Phosphorous Slag and Steel Slag

Cement,phosphorous slag(PS),and steel slag(SS)were used to prepare low-carbon cementitious materials,and triisopropanolamine(TIPA)was used to improve the mechanical properties by controlling the hydration process.The experimental results show that,by using 0.06%TIPA,the compressive strength of cement containing 60%PS or 60%SS could be enhanced by 12%or 18%at 28 d.The presence of TIPA significantly affected the hydration process of PS and SS in cement.In the early stage,TIPA accelerated the dissolution of Al in PS,and the formation of carboaluminate hydrate was facilitated,which could induce the hydration;TIPA promoted the dissolution of Fe in SS,and the formation of Fe-monocarbonate,which was precipitated on the surface of SS,resulting in the postponement of hydration,especially for the high SS content.In the later stage,under the continuous solubilization effect of TIPA,the hydration of PS and SS could refine the pore structure.It was noted that compared with portland cement,the carbon emissions of cement-PS-TIPA and cement-SS-TIPA was reduced by 52%and 49%,respectively.

Reactions of Chromium during the Calcination of Cement Clinker Produced Using Steel Slag

We investigated the effects of calcination temperature(950-1450℃),steel slag content,and the total chromium content of steel slag on the Cr^(6+)contents of clinker samples produced using steel slags with different chromium contents.Additionally,the reactions of chromium in clinker(produced using steel slag)during calcination were studied.It is found that Cr^(6+)conversion increases with increasing calcination temperature to 1250℃,reaching a maximum of 43%-79%,before decreasing to 18%-42%at 1450℃.Cr^(6+)is mainly formed by the oxidation of trivalent chromium(Cr^(3+))during the solid-phase reaction stage of clinker calcination.Furthermore,the Cr^(6+)content of a clinker sample is proportional to the chromium content of its raw meal precursor and is mainly in the form of water-insoluble calcium chromate(CaCrO_(4)).The chromium in clinker is mainly distributed in tricalcium aluminate and tetracalcium aluminoferrite,however,some is present in silicate minerals.We expect to inform the monitoring and control of the Cr^(6+)content of clinker(produced using steel slag)and resulting cement.

The Research for Surface Properties of Steel Slag Powder and High-Temperature Rheological Properties of Asphalt Mortar

In order to evaluate the feasibility of steel slag powder as filler,the coating properties of steel slag and limestone aggregate were compared by water boiling test,the micro morphology difierences between steel slag powder and mineral powder(limestone powder)were compared by scanning electron microscope(SEM),and the high-temperature rheological properties of asphalt mortar with difierent ratio of filler quality to asphalt quality(F/A)and difierent substitution rates of mineral powder(S/F)were studied by dynamic shear rheological test.The results show that the surface microstructure of steel slag powder is more abundant than that of mineral powder,and the adhesion of steel slag to asphalt is better than that of limestone.At the same temperature,the lower the ratio of S/F is,the greater the rutting factor and complex modulus will be.In addition,the complex modulus and rutting factor of the asphalt mortar increase with the increase of F/A,and the filler type and F/A have a negligible efiect on the phase angle.

Workability and Strength of Ceramsite Self-Compacting Concrete with Steel Slag Sand

This study focuses on the workability and compressive strength of ceramsite self-compacting concrete with fine aggregate partially substituted by steel slag sand(CSLSCC)to prevent the pollution of steel slag in the environment.The SF,J-ring,visual stability index,and sieve analysis tests are primarily employed in this research to investigate the workability of freshly mixed self-compacting concrete containing steel slag at various steel slag sand replacement rates.The experiment results indicate that CSLSCC with the 20%volume percentage of steel slag(VPS)performs better workability,higher strength,and higher specific strength.The 7-day compressive strength of CSLSCC with the 0.4 of the water-binder ratio(W/B),decreases with the increase of steel slag content,while the 28-day compressive strength increases significantly.The ceramsite self-compacting concrete with good comprehensive performance can be obtained when the substitution rate of steel slag sand for fine aggregate is less than 20%(volume percentage).

Waste heat recovery from hot steel slag on the production line:Numerical simulation,validation and industrial test

Waste heat recovery from hot steel slag was determined in a granular bed through the combination of numerical simulation and an industrial test method.First,the effective thermal conductivity of the granular bed was calculated.Then,the unsteady-state model was used to simulate the heat recovery under three different flow fields(O-type,S-type,and nonshielding type(Nontype)).Second,the simulation results were validated by in-situ industrial experiments.The two methods confirmed that the heat recovery efficiencies of the flow fields from high to low followed the order of Nontype,S-type,and O-type.Finally,heat recovery was carried out under the Nontype flow field in an industrial test.The heat recovery efficiency increased from~76%and~78%to~81%when the steel slag thickness decreased from 400 and 300 to 200 mm,corresponding to reductions in the steel slag mass from 3.96 and 2.97 to 1.98 t with a blower air volume of 14687 m^(3)/h.Therefore,the research results showed that numerical simulation can not only guide experiments on waste heat recovery but also optimize the flow field.Most importantly,the method proposed in this paper has achieved higher waste heat recovery from hot steel slag in industrial scale.

Synergistic Use of CO_(2) Pretreatment and Accelerated Carbonation Curing for Maximum Recycling of Steel Slag

Two carbonation approaches are considered for studying the effects on the hardening mechanisms of slurries made of 100 wt%electric arc furnace steel slag (EAF) slag or 80 wt%EAF slag incorporating 20 wt% of Portland cement,which are applied during the hot-stage pretreatment with simulated gas for raw steel slag or the accelerated carbonation curing of slurry.The mechanical strengths,carbonate products,microstructures and CO_(2) uptakes were quantitatively investigated.Results manifest that accelerated carbonation curing increases the compressive strengths of steel slag slurry,from 17.1 MPa (binder of 80 wt% EAF and 20 wt%cement under standard moisture curing) to 36.0 MPa (binder of 80 wt%EAF and 20 wt%cement under accelerated carbonation curing),with a CO_(2) uptake of 52%.In contrast,hot-stage carbonation applied during the pretreatment of steel slag increases the compressive strengths to 43.7 MPa (binder of 80 wt%carbonated EAF and 20 wt%cement under accelerated carbonation curing),with a CO_(2) uptake of 67%.Hotstage carbonation of steel slag is found for particle agglomeration,minerals remodeling and calcite formed,thus causing an activated steel slag with a dense structure and more active components.Accelerated carbonation curing of steel slag slurry paste results in the newly formed amorphous CaCO_(3),calcite crystalline and silica gels that covered the pores of the matrix,facilitating microstructure densification and strength improvement.Adopting the combinative methods of the hot-stage CO_(2) pretreatment and accelerated carbonation curing creates a promising high-volume steel slag-based binder with high strengths and CO_(2) storage.

Preparation of High Activity Admixture from Steel Slag,Phosphate Slag and Limestone Powder

The problem of low disposal and utilization rate of bulk industrial solid waste needs to be solved.In this paper,a high-activity admixture composed of steel slag-phosphate slag-limestone powder was proposed for most of the solid waste with low activity and a negative impact on concrete workability,combining the characteristics of each solid waste.The paper demonstrates the feasibility and explains the principle of the composite system in terms of water requirement of standard consistency,setting time,workability,and mechanical properties,combined with the composition of the phases,hydration temperature,and microscopic morphology.The results showed that the steel slag:phosphate slag:limestone=5:2:3 gave the highest activity of the composite system,over 92%.Besides,the composite system had no significant effect on water demand and setting time compared to cement,and it could significantly increase the 7 and 28 d activity of the system.The composite system delayed the exothermic hydration of the cement and reduced the exothermic heat but had no effect on the hydration products.Therefore,the research in this paper dramatically improved the solid waste dissipation in concrete,reduced the amount of cement in concrete and positively responded to the national slogan of carbon neutral and peaking.

Efficient Use of Steel Slag in Alkali-Activated Blast Furnace Slag Based Geopolymer

Energy shortage and the emission of greenhouse gases have become a global problem of urgent concern.Therefore,there is an urgent need to develop a low carbon building material.Geopolymers have become a hot topic due to their environmental sustainability and the feasibility of immobilizing industrial waste.In this paper,steel slag(SS)fines were investigated as auxiliary materials of blast furnace slag(BFS)based geopolymer.The hydration heat properties,flowability,compressive strength,sorptivity coefficient,X-ray diffraction(XRD),and scanning electron microscopy(SEM)of the geopolymer pastes were determined.The results showed that the incorporation of SS weakened the reactivity of the BFS-based geopolymer paste and improved the flow values of the paste.The compressive strength of the geopolymer with 20%SS content reached 117 MPa at 28 d.The geopolymer specimens with high compressive strength showed a low sorptivity coefficient.The microscopic results showed that the addition of the appropriate amount of SS reduced the cracks,improved the density of the geopolymer,and produced a geopolymer composite with excellent mechanical properties.

Sintering preparation of porous sound-absorbing materials from steel slag

Porous sound-absorbing materials were prepared from steel slag using waste expanded polystyrene（EPS） particles as pore former.The influences of the experimental conditions such as fly ash content,sintering temperature,sintering time,and pore former addition on the performance of the porous sound-absorbing materials were investigated.The results show that the porosity of the specimens can reach above 50.0%;the compressive strength and average sound-adsorption coefficient of the sintered specimens are above 3.0 MPa and 0.47,respectively.The optimum preparation conditions for the steel slag porous sound-absorbing materials are as follows：mass fraction of fly ash 50%,waste EPS particles 3.6 g,sintering temperature 1100℃,and sintering time 7.5h,which are determined by considering the properties of the sound-absorbing materials,energy consumption and cost.

Properties of Steel Slag and Stainless Steel Slag as Cement Replacement Materials:A Comparative Study

To enhance the understanding about the utilization of steel slags as a cementitious material, we comparatively studied the chemical, mineralogical and morphological properties of two types of steel slag; basicoxygen-furnace carbon slag(BOF C) and electric-arc-furnace stainless steel slag(EAF S). Moreover, we studied the standard consistency, setting time and the effect of the slag replacement ratios on the fluidity and compressive strength of blended cement mortar. The experimental results showed that BOF C had higher alkalinity, higher pH value and more hydraulic phases than EAF S. Both types of slag showed water reduction effect due to its high fineness. Neat BOF C paste showed flash set and acceleration in the initial setting time of blended cement especially at high slag proportions. However, EAF S prolonged the setting time of blended cement even at low slag proportions. The pH values for blended cement contained 50% BOF C or EAF S were lower than those of pure cement paste. Despite of slag type, compressive strength gradually decreased with increasing slags content. The strength of BOF C mortar was higher than that of EAF S mortar with the same replacement ratio for the same age. Slag activity index demonstrated that BOF C and EAF S conformed to the Chinese National Standard(GB/T 20491-2006) requirements for steel slag as grade one and grade two, respectively.

Study on the properties and application of the steel slag special fine aggregate

The physical properties, grading stability and application stability of the steel slag special fine aggregate （diameter≤0. 8mm） at Baosteel were analyzed in this study, and the mechanical and working properties were studied when the aggregate was applied to concrete. The： result shows that the aggregate has special advantages of hardness and wear-resistance, so it can be used as an excellent road surface material. The concrete mixed with the steel slag special fine aggregate exhibits good mechanical properties and working properties,which is safe and reliable.

Thermodynamic analysis and formula optimization of steel slag-based ceramic materials by FACTsage software

Using steel slag as a main raw material of ceramics is considered as a high value-added way. However, the relationship among the initial composition, ceramic microstructure, and macroscopic properties requires further study. In this paper, a series of ceramics with different slag ratios （0-70wt%） were designed, and the software FACTsage was introduced to simulate the formation of crystalline phases. The simulation results indicate that mullite is generated but drastically reduced at the slag ratios of 0-25wt%, and anorthite is the dominant crystalline phase in the slag content of 25wt%-45wt%. When the slag ratio is above 45wt%, pyroxene is generated more than anorthite. This is because increasing magnesium can promote the formation of pyroxene. Then, the formula with a slag content of 40wt% was selected and optimized. X-ray diffraction results were good consistent with the simulation results. Finally, the water absorption and bending strength of optimized samples were measured.

Methods for Improving Volume Stability of Steel Slag as Fine Aggregate

Suitable methods for enhancing the volume stability of steel slag utilized as fine aggregate were determined. The effects of steam treatment at 100 ℃ and autoclave treatment under 2.0 MPa on the soundness of steel slag sand were investigated by means of powder ratio, linear expansion, compressive and flexural strength. DTA, EDX, XRD and ethylene glycol methods were employed to analyze both the treated slags and susceptible expansion grains. Experimental results indicate that powder ratio, content of free lime and rate of linear expansion can express the improvement in volume stability of different treated methods. Steam treatment process cannot ultimately prevent specimens from cracking and decrease of strength, but mortar made from autoclave treated slag keeps integration subjected to hot water of 80℃ until 28 d and its strength do not show significant decrement. The hydration of over-burn free lime and periclase phase are the main cause for the disintegration or crack of untreated and steam treated steel slag＇s specimens. Autoclave treatment process is more effective than steam treatment process on enhancement of volume stability of steel slag.

Steel Slag as an Iron Fertilizer for Corn Growth and Soil Improvement in a Pot Experiment

The feasibility of steel slag used as an iron fertilizer was studied in a pot experiment with corn. Slag alone or acidified slag was added to two Fe-deficient calcareous soils at different rates. Results showed that moderate rates (10 and 20 g kg-1) of slag or acidified slag substantially increased corn dry matter yield and Fe uptake. Application of steel slag increased the residual concentration of ammonium bicarbonate-diethylenetriamine pentaacetic acid (AB-DTPA) extractable Fe in the soils. The increase of extractable Fe was usually proportional to the application rate, and enhanced by the acidification of slag. Steel slag appeared to be a promising and inexpensive source of Fe to alleviate crop Fe chlorosis in Fe-deficient calcareous soils.

Research on Hydration of Steel Slag Cement Activated with Waterglass

This paper studied the hydration and strength influence factors ofSteel Slag Cement (SSC), such as the quantity of steel slag and slagand the dosage of additive. The results show that: (a) In the processof hydration of SSC, steel slag and slag activate each other; (b)Waterglass's structure forms the preliminary skeleton of SSC, and thehydration products of SSC link or fill in the skeleton; (c) Sodium inWaterglass is the catalytic and its concentration does not change inthe process of hydration. (d) Structure of activation is asignificant factor to the property of SSC.