The objective of this paper was to study low temperature crack resistance mechanism of steel slag asphalt mixture(SAM).Thermal stress restrained specimen test(TSRST)and three-point bending test were carried out to eva...The objective of this paper was to study low temperature crack resistance mechanism of steel slag asphalt mixture(SAM).Thermal stress restrained specimen test(TSRST)and three-point bending test were carried out to evaluate the low-temperature crack resistance of SAM and basalt asphalt mixture(BAM).Based on the digital image correlation technique(DIC),the strain field distribution and crack propagation of SAM were analyzed from the microscopic point of view,and a new index,crack length factor(C),was proposed to evaluate the crack resistance of the asphalt mixture.The crystal phase composition and microstructure of steel slag aggregate(SA)and basalt aggregate(BA)were studied by X-ray diffraction(XRD)and scanning electron microscopy(SEM)to explore the low-temperature crack resistance mechanism of SAM.Results show that the low-temperature crack resistance of SAM is better than that of BAM;SAM has good integrity and persistent elastic deformation,and its bending failure mode is a hysteretic quasi-brittle failure;The SA surface is evenly distributed with pores and has surface roughness.SA has the composition phase of alkaline aggregate-calcite(CaCO3),so it has good adhesion to asphalt,which reveals the mechanism of excellent low-temperature crack resistance of SAM.展开更多
Chromium plays a vital role in stainless steel due to its ability to improve the corrosion resistance of the latter.However,the re-lease of chromium from stainless steel slag(SSS)during SSS stockpiling causes detrimen...Chromium plays a vital role in stainless steel due to its ability to improve the corrosion resistance of the latter.However,the re-lease of chromium from stainless steel slag(SSS)during SSS stockpiling causes detrimental environmental issues.To prevent chromium pollution,the effects of iron oxide on crystallization behavior and spatial distribution of spinel were investigated in this work.The results revealed that FeO was more conducive to the growth of spinels compared with Fe2O3 and Fe3O4.Spinels were found to be mainly distrib-uted at the top and bottom of slag.The amount of spinel phase at the bottom decreased with the increasing FeO content,while that at the top increased.The average particle size of spinel in the slag with 18wt%FeO content was 12.8μm.Meanwhile,no notable structural changes were observed with a further increase in FeO content.In other words,the spatial distribution of spinel changed when the content of iron oxide varied in the range of 8wt%to 18wt%.Finally,less spinel was found at the bottom of slag with a FeO content of 23wt%.展开更多
The slag samples taken from landfill, which originated from different metallurgical processes, have been characterized in this study. The slags were categor- ized as electric arc furnace (EAF) slag, argon oxygen dec...The slag samples taken from landfill, which originated from different metallurgical processes, have been characterized in this study. The slags were categor- ized as electric arc furnace (EAF) slag, argon oxygen decarburization/metal refining process slag and vacuum oxygen decarburization slag based on chromium content and basicity. EAF slags have higher potential in metal recovery than the other two slags due to its higher iron and chromium contents. The size of the iron-chromium-nickel alloy particles varies from a few ~tm up to several cm. The recoveries of large metal particles and metal-spinel aggregates have potential to make the metal recovery from landfilled slags economically viable.展开更多
Cement,phosphorous slag(PS),and steel slag(SS)were used to prepare low-carbon cementitious materials,and triisopropanolamine(TIPA)was used to improve the mechanical properties by controlling the hydration process.The ...Cement,phosphorous slag(PS),and steel slag(SS)were used to prepare low-carbon cementitious materials,and triisopropanolamine(TIPA)was used to improve the mechanical properties by controlling the hydration process.The experimental results show that,by using 0.06%TIPA,the compressive strength of cement containing 60%PS or 60%SS could be enhanced by 12%or 18%at 28 d.The presence of TIPA significantly affected the hydration process of PS and SS in cement.In the early stage,TIPA accelerated the dissolution of Al in PS,and the formation of carboaluminate hydrate was facilitated,which could induce the hydration;TIPA promoted the dissolution of Fe in SS,and the formation of Fe-monocarbonate,which was precipitated on the surface of SS,resulting in the postponement of hydration,especially for the high SS content.In the later stage,under the continuous solubilization effect of TIPA,the hydration of PS and SS could refine the pore structure.It was noted that compared with portland cement,the carbon emissions of cement-PS-TIPA and cement-SS-TIPA was reduced by 52%and 49%,respectively.展开更多
We investigated the effects of calcination temperature(950-1450℃),steel slag content,and the total chromium content of steel slag on the Cr^(6+)contents of clinker samples produced using steel slags with different ch...We investigated the effects of calcination temperature(950-1450℃),steel slag content,and the total chromium content of steel slag on the Cr^(6+)contents of clinker samples produced using steel slags with different chromium contents.Additionally,the reactions of chromium in clinker(produced using steel slag)during calcination were studied.It is found that Cr^(6+)conversion increases with increasing calcination temperature to 1250℃,reaching a maximum of 43%-79%,before decreasing to 18%-42%at 1450℃.Cr^(6+)is mainly formed by the oxidation of trivalent chromium(Cr^(3+))during the solid-phase reaction stage of clinker calcination.Furthermore,the Cr^(6+)content of a clinker sample is proportional to the chromium content of its raw meal precursor and is mainly in the form of water-insoluble calcium chromate(CaCrO_(4)).The chromium in clinker is mainly distributed in tricalcium aluminate and tetracalcium aluminoferrite,however,some is present in silicate minerals.We expect to inform the monitoring and control of the Cr^(6+)content of clinker(produced using steel slag)and resulting cement.展开更多
In order to evaluate the feasibility of steel slag powder as filler,the coating properties of steel slag and limestone aggregate were compared by water boiling test,the micro morphology difierences between steel slag ...In order to evaluate the feasibility of steel slag powder as filler,the coating properties of steel slag and limestone aggregate were compared by water boiling test,the micro morphology difierences between steel slag powder and mineral powder(limestone powder)were compared by scanning electron microscope(SEM),and the high-temperature rheological properties of asphalt mortar with difierent ratio of filler quality to asphalt quality(F/A)and difierent substitution rates of mineral powder(S/F)were studied by dynamic shear rheological test.The results show that the surface microstructure of steel slag powder is more abundant than that of mineral powder,and the adhesion of steel slag to asphalt is better than that of limestone.At the same temperature,the lower the ratio of S/F is,the greater the rutting factor and complex modulus will be.In addition,the complex modulus and rutting factor of the asphalt mortar increase with the increase of F/A,and the filler type and F/A have a negligible efiect on the phase angle.展开更多
Steel slag is characterized by high strength,good wear resistance and micro-expansion.This study aims at exploring the potential of steel slag in cement stabilized aggregates,mainly including mechanical properties,shr...Steel slag is characterized by high strength,good wear resistance and micro-expansion.This study aims at exploring the potential of steel slag in cement stabilized aggregates,mainly including mechanical properties,shrinkage and compensation mechanisms.For this purpose,the compressive strength and compressive resilient modulus of cement stabilized aggregates with different steel slag contents(CSMS)were initially investigated.Subsequently,the effects of steel slag and cement on dry shrinkage,temperature shrinkage,and total shrinkage were analyzed through a series of shrinkage test designs.Additionally,in combination with X-ray diffraction(XRD)and Scanning electron microscope(SEM),the characteristic peaks and microscopic images of cement,steel slag and cement-steel slag at different hydration ages were analyzed to identify the chemical substances causing the expansion volume of steel slag and reveal the compensation mechanism of CSMS.The results show that the introduction of 20%steel slag improved the mechanical properties of CSMS by 16.7%,reduced dry shrinkage by 21%,increased temperature shrinkage by 5.8%and reduced its total shrinkage by 19.2%.Compared with the hydration reaction of cement alone,the composite hydration reaction of steel slag with cement does not produce new hydrates.Furthermore,it is noteworthy that the volume expansion of the f-CaO hydration reaction in steel slag can compensate for the volume shrinkage of cement-stabilized macadam.This research can provide a solid theoretical basis for the application and promotion of steel slag in cement-stabilized macadam and reduce the possibility of shrinkage cracking.展开更多
Waste heat recovery from hot steel slag was determined in a granular bed through the combination of numerical simulation and an industrial test method.First,the effective thermal conductivity of the granular bed was c...Waste heat recovery from hot steel slag was determined in a granular bed through the combination of numerical simulation and an industrial test method.First,the effective thermal conductivity of the granular bed was calculated.Then,the unsteady-state model was used to simulate the heat recovery under three different flow fields(O-type,S-type,and nonshielding type(Nontype)).Second,the simulation results were validated by in-situ industrial experiments.The two methods confirmed that the heat recovery efficiencies of the flow fields from high to low followed the order of Nontype,S-type,and O-type.Finally,heat recovery was carried out under the Nontype flow field in an industrial test.The heat recovery efficiency increased from~76%and~78%to~81%when the steel slag thickness decreased from 400 and 300 to 200 mm,corresponding to reductions in the steel slag mass from 3.96 and 2.97 to 1.98 t with a blower air volume of 14687 m^(3)/h.Therefore,the research results showed that numerical simulation can not only guide experiments on waste heat recovery but also optimize the flow field.Most importantly,the method proposed in this paper has achieved higher waste heat recovery from hot steel slag in industrial scale.展开更多
The problem of low disposal and utilization rate of bulk industrial solid waste needs to be solved.In this paper,a high-activity admixture composed of steel slag-phosphate slag-limestone powder was proposed for most o...The problem of low disposal and utilization rate of bulk industrial solid waste needs to be solved.In this paper,a high-activity admixture composed of steel slag-phosphate slag-limestone powder was proposed for most of the solid waste with low activity and a negative impact on concrete workability,combining the characteristics of each solid waste.The paper demonstrates the feasibility and explains the principle of the composite system in terms of water requirement of standard consistency,setting time,workability,and mechanical properties,combined with the composition of the phases,hydration temperature,and microscopic morphology.The results showed that the steel slag:phosphate slag:limestone=5:2:3 gave the highest activity of the composite system,over 92%.Besides,the composite system had no significant effect on water demand and setting time compared to cement,and it could significantly increase the 7 and 28 d activity of the system.The composite system delayed the exothermic hydration of the cement and reduced the exothermic heat but had no effect on the hydration products.Therefore,the research in this paper dramatically improved the solid waste dissipation in concrete,reduced the amount of cement in concrete and positively responded to the national slogan of carbon neutral and peaking.展开更多
Energy shortage and the emission of greenhouse gases have become a global problem of urgent concern.Therefore,there is an urgent need to develop a low carbon building material.Geopolymers have become a hot topic due t...Energy shortage and the emission of greenhouse gases have become a global problem of urgent concern.Therefore,there is an urgent need to develop a low carbon building material.Geopolymers have become a hot topic due to their environmental sustainability and the feasibility of immobilizing industrial waste.In this paper,steel slag(SS)fines were investigated as auxiliary materials of blast furnace slag(BFS)based geopolymer.The hydration heat properties,flowability,compressive strength,sorptivity coefficient,X-ray diffraction(XRD),and scanning electron microscopy(SEM)of the geopolymer pastes were determined.The results showed that the incorporation of SS weakened the reactivity of the BFS-based geopolymer paste and improved the flow values of the paste.The compressive strength of the geopolymer with 20%SS content reached 117 MPa at 28 d.The geopolymer specimens with high compressive strength showed a low sorptivity coefficient.The microscopic results showed that the addition of the appropriate amount of SS reduced the cracks,improved the density of the geopolymer,and produced a geopolymer composite with excellent mechanical properties.展开更多
This study focuses on the workability and compressive strength of ceramsite self-compacting concrete with fine aggregate partially substituted by steel slag sand(CSLSCC)to prevent the pollution of steel slag in the en...This study focuses on the workability and compressive strength of ceramsite self-compacting concrete with fine aggregate partially substituted by steel slag sand(CSLSCC)to prevent the pollution of steel slag in the environment.The SF,J-ring,visual stability index,and sieve analysis tests are primarily employed in this research to investigate the workability of freshly mixed self-compacting concrete containing steel slag at various steel slag sand replacement rates.The experiment results indicate that CSLSCC with the 20%volume percentage of steel slag(VPS)performs better workability,higher strength,and higher specific strength.The 7-day compressive strength of CSLSCC with the 0.4 of the water-binder ratio(W/B),decreases with the increase of steel slag content,while the 28-day compressive strength increases significantly.The ceramsite self-compacting concrete with good comprehensive performance can be obtained when the substitution rate of steel slag sand for fine aggregate is less than 20%(volume percentage).展开更多
Two carbonation approaches are considered for studying the effects on the hardening mechanisms of slurries made of 100 wt%electric arc furnace steel slag (EAF) slag or 80 wt%EAF slag incorporating 20 wt% of Portland c...Two carbonation approaches are considered for studying the effects on the hardening mechanisms of slurries made of 100 wt%electric arc furnace steel slag (EAF) slag or 80 wt%EAF slag incorporating 20 wt% of Portland cement,which are applied during the hot-stage pretreatment with simulated gas for raw steel slag or the accelerated carbonation curing of slurry.The mechanical strengths,carbonate products,microstructures and CO_(2) uptakes were quantitatively investigated.Results manifest that accelerated carbonation curing increases the compressive strengths of steel slag slurry,from 17.1 MPa (binder of 80 wt% EAF and 20 wt%cement under standard moisture curing) to 36.0 MPa (binder of 80 wt%EAF and 20 wt%cement under accelerated carbonation curing),with a CO_(2) uptake of 52%.In contrast,hot-stage carbonation applied during the pretreatment of steel slag increases the compressive strengths to 43.7 MPa (binder of 80 wt%carbonated EAF and 20 wt%cement under accelerated carbonation curing),with a CO_(2) uptake of 67%.Hotstage carbonation of steel slag is found for particle agglomeration,minerals remodeling and calcite formed,thus causing an activated steel slag with a dense structure and more active components.Accelerated carbonation curing of steel slag slurry paste results in the newly formed amorphous CaCO_(3),calcite crystalline and silica gels that covered the pores of the matrix,facilitating microstructure densification and strength improvement.Adopting the combinative methods of the hot-stage CO_(2) pretreatment and accelerated carbonation curing creates a promising high-volume steel slag-based binder with high strengths and CO_(2) storage.展开更多
In this work,an alternative alkali-activated cement(AAC)made of ladle slag precursor mixed with sodium hydroxide and sodium silicate has been developed to enhance the bearing capacity of estuarine soils in coastal con...In this work,an alternative alkali-activated cement(AAC)made of ladle slag precursor mixed with sodium hydroxide and sodium silicate has been developed to enhance the bearing capacity of estuarine soils in coastal conditions via deep soil mixing(DSM).The AAC was optimized to use a low reactivity precursor(ladle slag)and to deal with a contaminated high-water content natural sediment cured under water.The material performance was analysed by comparison to a mixture made with Portland cement and cured in the same conditions.Flexural and unconfined compressive strength tests as well as seismic waves measurements after 3-,7-,14-and 28-d curing were performed to obtain a relationship between elastic stiffness and strength with curing time for both mixtures.Remarkably,the AAC mix demonstrated superior strength results,exhibiting almost double flexural and compressive strengths after 28 d compared to the Portland cement mix.The AAC mix also showed a higher rate of stiffness increase than the Portland cement mix,which has a higher initial stiffness at young ages but lower stiffness evolution.Leachate analysis confirmed that the proposed AAC could effectively immobilise any contaminants from soil or precursors.The effect of curing under stress was analysed in triaxial compression tests and found to be insignificant,indicating that laboratory data obtained without stress curing can represent the material's behaviour in a DSM column,which will cure under the weight of the column.展开更多
The study investigates use of dolomite sand waste as filler or/and sand material plus BOF steel slag as fine and coarse aggregate for design of high performance asphalt concrete.Both environmental and economic factors...The study investigates use of dolomite sand waste as filler or/and sand material plus BOF steel slag as fine and coarse aggregate for design of high performance asphalt concrete.Both environmental and economic factors contribute to the growing need for the use of these materials in asphalt concrete pavements.This is particularly important for Latvia,where local crushed dolomite and sandstone does not fulfill the requirements for mineral aggregate in high and medium intensity asphalt pavements roads.Annually 100 to 200 thousand tons of steel slag aggregates are produced in Latvia.However,it has not been used extensively in asphalt pavement despite its high performance characteristics.Dolomite sand waste,which is byproduct of crushed dolomite production,is another widely available polydisperse by-product in Latvia.Its quantity has reached a million of tons and is rapidly increasing.This huge quantity of technological waste needs to be recycled with maximum efficiency.Various combinations of steel slag,dolomite sand waste and conventional aggregates were used to develop AC 11 asphalt concrete mixtures.The mix properties tests include resistance to permanent deformations(wheel tracking test,dynamic creep test)and fatigue resistance.Laboratory test results showed that asphalt concrete mixtures containing steel slag and local limestone in coarse portion and dolomite sand waste in sand and filler portions had high resistance to plastic deformations and good resistance to fatigue failure.展开更多
Suitable methods for enhancing the volume stability of steel slag utilized as fine aggregate were determined. The effects of steam treatment at 100 ℃ and autoclave treatment under 2.0 MPa on the soundness of steel sl...Suitable methods for enhancing the volume stability of steel slag utilized as fine aggregate were determined. The effects of steam treatment at 100 ℃ and autoclave treatment under 2.0 MPa on the soundness of steel slag sand were investigated by means of powder ratio, linear expansion, compressive and flexural strength. DTA, EDX, XRD and ethylene glycol methods were employed to analyze both the treated slags and susceptible expansion grains. Experimental results indicate that powder ratio, content of free lime and rate of linear expansion can express the improvement in volume stability of different treated methods. Steam treatment process cannot ultimately prevent specimens from cracking and decrease of strength, but mortar made from autoclave treated slag keeps integration subjected to hot water of 80℃ until 28 d and its strength do not show significant decrement. The hydration of over-burn free lime and periclase phase are the main cause for the disintegration or crack of untreated and steam treated steel slag's specimens. Autoclave treatment process is more effective than steam treatment process on enhancement of volume stability of steel slag.展开更多
Using steel slag as a main raw material of ceramics is considered as a high value-added way. However, the relationship among the initial composition, ceramic microstructure, and macroscopic properties requires further...Using steel slag as a main raw material of ceramics is considered as a high value-added way. However, the relationship among the initial composition, ceramic microstructure, and macroscopic properties requires further study. In this paper, a series of ceramics with different slag ratios (0-70wt%) were designed, and the software FACTsage was introduced to simulate the formation of crystalline phases. The simulation results indicate that mullite is generated but drastically reduced at the slag ratios of 0-25wt%, and anorthite is the dominant crystalline phase in the slag content of 25wt%-45wt%. When the slag ratio is above 45wt%, pyroxene is generated more than anorthite. This is because increasing magnesium can promote the formation of pyroxene. Then, the formula with a slag content of 40wt% was selected and optimized. X-ray diffraction results were good consistent with the simulation results. Finally, the water absorption and bending strength of optimized samples were measured.展开更多
Hydration heat evolution, non-evaporative water, setting time and SEM tests were peorormed to investigate the effect of fine steel slag powder on the hydration process of Portland cement and its mechanism. The results...Hydration heat evolution, non-evaporative water, setting time and SEM tests were peorormed to investigate the effect of fine steel slag powder on the hydration process of Portland cement and its mechanism. The results show that the effect of fine steel slag powder on the hydration process of Portland cement is closely related to its chemical composition, mineral phases, fineness, etc. Fine steel slag powder retards the hydration of portland cement at early age. The major reason for this phenomenon is the relative high content of MgO , MnO2, P2O5 in steel slag, and MgO solid solved in C3 S contained in steel slag.展开更多
This paper studied the hydration and strength influence factors ofSteel Slag Cement (SSC), such as the quantity of steel slag and slagand the dosage of additive. The results show that: (a) In the processof hydration o...This paper studied the hydration and strength influence factors ofSteel Slag Cement (SSC), such as the quantity of steel slag and slagand the dosage of additive. The results show that: (a) In the processof hydration of SSC, steel slag and slag activate each other; (b)Waterglass's structure forms the preliminary skeleton of SSC, and thehydration products of SSC link or fill in the skeleton; (c) Sodium inWaterglass is the catalytic and its concentration does not change inthe process of hydration. (d) Structure of activation is asignificant factor to the property of SSC.展开更多
Steel slag is a byproduct produced in large amounts in the steel-making process. It is an important resource that can be effectively utilized. An experiment was described in which steel slag was tested as an adsorbent...Steel slag is a byproduct produced in large amounts in the steel-making process. It is an important resource that can be effectively utilized. An experiment was described in which steel slag was tested as an adsorbent for the removal of phosphorus from waste water. Phosphorus removal depended on the amount of steel slag added, the pH value, the contact time, and the initial concentration. Under laboratory conditions when the added slag was 7.5g/L, the contact time 2h, and the pH value was equivalent to 6.5, over 99% of the phosphorus was removed; the experimental data on steel slag adsorption of phosphorus in the water fitted the Freundlich isotherm model. Steel slag was found to be very effective in adsorbing phosphorus.展开更多
To enhance the understanding about the utilization of steel slags as a cementitious material, we comparatively studied the chemical, mineralogical and morphological properties of two types of steel slag; basicoxygen-f...To enhance the understanding about the utilization of steel slags as a cementitious material, we comparatively studied the chemical, mineralogical and morphological properties of two types of steel slag; basicoxygen-furnace carbon slag(BOF C) and electric-arc-furnace stainless steel slag(EAF S). Moreover, we studied the standard consistency, setting time and the effect of the slag replacement ratios on the fluidity and compressive strength of blended cement mortar. The experimental results showed that BOF C had higher alkalinity, higher pH value and more hydraulic phases than EAF S. Both types of slag showed water reduction effect due to its high fineness. Neat BOF C paste showed flash set and acceleration in the initial setting time of blended cement especially at high slag proportions. However, EAF S prolonged the setting time of blended cement even at low slag proportions. The pH values for blended cement contained 50% BOF C or EAF S were lower than those of pure cement paste. Despite of slag type, compressive strength gradually decreased with increasing slags content. The strength of BOF C mortar was higher than that of EAF S mortar with the same replacement ratio for the same age. Slag activity index demonstrated that BOF C and EAF S conformed to the Chinese National Standard(GB/T 20491-2006) requirements for steel slag as grade one and grade two, respectively.展开更多
基金Funded by the National Natural Science Foundation of China(No.11962024)Key Technology Project of Inner Mongolia Autonomous Region(No.2019GG031)。
文摘The objective of this paper was to study low temperature crack resistance mechanism of steel slag asphalt mixture(SAM).Thermal stress restrained specimen test(TSRST)and three-point bending test were carried out to evaluate the low-temperature crack resistance of SAM and basalt asphalt mixture(BAM).Based on the digital image correlation technique(DIC),the strain field distribution and crack propagation of SAM were analyzed from the microscopic point of view,and a new index,crack length factor(C),was proposed to evaluate the crack resistance of the asphalt mixture.The crystal phase composition and microstructure of steel slag aggregate(SA)and basalt aggregate(BA)were studied by X-ray diffraction(XRD)and scanning electron microscopy(SEM)to explore the low-temperature crack resistance mechanism of SAM.Results show that the low-temperature crack resistance of SAM is better than that of BAM;SAM has good integrity and persistent elastic deformation,and its bending failure mode is a hysteretic quasi-brittle failure;The SA surface is evenly distributed with pores and has surface roughness.SA has the composition phase of alkaline aggregate-calcite(CaCO3),so it has good adhesion to asphalt,which reveals the mechanism of excellent low-temperature crack resistance of SAM.
基金the National Natural Science Foundation of China(Nos.52074078 and 52374327)the Applied Fundamental Research Program of Liaoning Province(No.2023JH2/101600002)+2 种基金the Shenyang Young Middle-Aged Scientific and Technological Innovation Talent Support Program(No.RC220491)the Liaoning Province Steel Industry-University-Research Innovation Alliance Cooperation Project of Bensteel Group(No.KJBLM202202)the Fundamental Research Funds for the Central Universities(Nos.N2201023 and N2325009).
文摘Chromium plays a vital role in stainless steel due to its ability to improve the corrosion resistance of the latter.However,the re-lease of chromium from stainless steel slag(SSS)during SSS stockpiling causes detrimental environmental issues.To prevent chromium pollution,the effects of iron oxide on crystallization behavior and spatial distribution of spinel were investigated in this work.The results revealed that FeO was more conducive to the growth of spinels compared with Fe2O3 and Fe3O4.Spinels were found to be mainly distrib-uted at the top and bottom of slag.The amount of spinel phase at the bottom decreased with the increasing FeO content,while that at the top increased.The average particle size of spinel in the slag with 18wt%FeO content was 12.8μm.Meanwhile,no notable structural changes were observed with a further increase in FeO content.In other words,the spatial distribution of spinel changed when the content of iron oxide varied in the range of 8wt%to 18wt%.Finally,less spinel was found at the bottom of slag with a FeO content of 23wt%.
文摘The slag samples taken from landfill, which originated from different metallurgical processes, have been characterized in this study. The slags were categor- ized as electric arc furnace (EAF) slag, argon oxygen decarburization/metal refining process slag and vacuum oxygen decarburization slag based on chromium content and basicity. EAF slags have higher potential in metal recovery than the other two slags due to its higher iron and chromium contents. The size of the iron-chromium-nickel alloy particles varies from a few ~tm up to several cm. The recoveries of large metal particles and metal-spinel aggregates have potential to make the metal recovery from landfilled slags economically viable.
基金Funded by the Key Public Welfare Special Project of Henan Province(No.201300311000)the Major Technical Innovation Project in Hubei Province of China(No.2020BED025)。
文摘Cement,phosphorous slag(PS),and steel slag(SS)were used to prepare low-carbon cementitious materials,and triisopropanolamine(TIPA)was used to improve the mechanical properties by controlling the hydration process.The experimental results show that,by using 0.06%TIPA,the compressive strength of cement containing 60%PS or 60%SS could be enhanced by 12%or 18%at 28 d.The presence of TIPA significantly affected the hydration process of PS and SS in cement.In the early stage,TIPA accelerated the dissolution of Al in PS,and the formation of carboaluminate hydrate was facilitated,which could induce the hydration;TIPA promoted the dissolution of Fe in SS,and the formation of Fe-monocarbonate,which was precipitated on the surface of SS,resulting in the postponement of hydration,especially for the high SS content.In the later stage,under the continuous solubilization effect of TIPA,the hydration of PS and SS could refine the pore structure.It was noted that compared with portland cement,the carbon emissions of cement-PS-TIPA and cement-SS-TIPA was reduced by 52%and 49%,respectively.
文摘We investigated the effects of calcination temperature(950-1450℃),steel slag content,and the total chromium content of steel slag on the Cr^(6+)contents of clinker samples produced using steel slags with different chromium contents.Additionally,the reactions of chromium in clinker(produced using steel slag)during calcination were studied.It is found that Cr^(6+)conversion increases with increasing calcination temperature to 1250℃,reaching a maximum of 43%-79%,before decreasing to 18%-42%at 1450℃.Cr^(6+)is mainly formed by the oxidation of trivalent chromium(Cr^(3+))during the solid-phase reaction stage of clinker calcination.Furthermore,the Cr^(6+)content of a clinker sample is proportional to the chromium content of its raw meal precursor and is mainly in the form of water-insoluble calcium chromate(CaCrO_(4)).The chromium in clinker is mainly distributed in tricalcium aluminate and tetracalcium aluminoferrite,however,some is present in silicate minerals.We expect to inform the monitoring and control of the Cr^(6+)content of clinker(produced using steel slag)and resulting cement.
基金Funded by National Natural Science Foundation of China(No.52278446)。
文摘In order to evaluate the feasibility of steel slag powder as filler,the coating properties of steel slag and limestone aggregate were compared by water boiling test,the micro morphology difierences between steel slag powder and mineral powder(limestone powder)were compared by scanning electron microscope(SEM),and the high-temperature rheological properties of asphalt mortar with difierent ratio of filler quality to asphalt quality(F/A)and difierent substitution rates of mineral powder(S/F)were studied by dynamic shear rheological test.The results show that the surface microstructure of steel slag powder is more abundant than that of mineral powder,and the adhesion of steel slag to asphalt is better than that of limestone.At the same temperature,the lower the ratio of S/F is,the greater the rutting factor and complex modulus will be.In addition,the complex modulus and rutting factor of the asphalt mortar increase with the increase of F/A,and the filler type and F/A have a negligible efiect on the phase angle.
基金National Natural Science Foundation of China(Grant No.52078051)Fundamental Research Funds for the Central Universities(Grant No.310821163502)+1 种基金Technology Innovation Project of Shandong Department of Industry and Information(Grant No.Lugongxinji 2020-8)the Transportation Department of Shandong Province(Grant No.Lujiaokeji 2017-28).
文摘Steel slag is characterized by high strength,good wear resistance and micro-expansion.This study aims at exploring the potential of steel slag in cement stabilized aggregates,mainly including mechanical properties,shrinkage and compensation mechanisms.For this purpose,the compressive strength and compressive resilient modulus of cement stabilized aggregates with different steel slag contents(CSMS)were initially investigated.Subsequently,the effects of steel slag and cement on dry shrinkage,temperature shrinkage,and total shrinkage were analyzed through a series of shrinkage test designs.Additionally,in combination with X-ray diffraction(XRD)and Scanning electron microscope(SEM),the characteristic peaks and microscopic images of cement,steel slag and cement-steel slag at different hydration ages were analyzed to identify the chemical substances causing the expansion volume of steel slag and reveal the compensation mechanism of CSMS.The results show that the introduction of 20%steel slag improved the mechanical properties of CSMS by 16.7%,reduced dry shrinkage by 21%,increased temperature shrinkage by 5.8%and reduced its total shrinkage by 19.2%.Compared with the hydration reaction of cement alone,the composite hydration reaction of steel slag with cement does not produce new hydrates.Furthermore,it is noteworthy that the volume expansion of the f-CaO hydration reaction in steel slag can compensate for the volume shrinkage of cement-stabilized macadam.This research can provide a solid theoretical basis for the application and promotion of steel slag in cement-stabilized macadam and reduce the possibility of shrinkage cracking.
基金financially supported by the National Natural Science Foundation of China(No.51972019)the National Key Research and Development Program of China(No.2019YFC1905702)。
文摘Waste heat recovery from hot steel slag was determined in a granular bed through the combination of numerical simulation and an industrial test method.First,the effective thermal conductivity of the granular bed was calculated.Then,the unsteady-state model was used to simulate the heat recovery under three different flow fields(O-type,S-type,and nonshielding type(Nontype)).Second,the simulation results were validated by in-situ industrial experiments.The two methods confirmed that the heat recovery efficiencies of the flow fields from high to low followed the order of Nontype,S-type,and O-type.Finally,heat recovery was carried out under the Nontype flow field in an industrial test.The heat recovery efficiency increased from~76%and~78%to~81%when the steel slag thickness decreased from 400 and 300 to 200 mm,corresponding to reductions in the steel slag mass from 3.96 and 2.97 to 1.98 t with a blower air volume of 14687 m^(3)/h.Therefore,the research results showed that numerical simulation can not only guide experiments on waste heat recovery but also optimize the flow field.Most importantly,the method proposed in this paper has achieved higher waste heat recovery from hot steel slag in industrial scale.
基金Key Research and Development Plan of Shaanxi Province(2019TSLGY05-04).
文摘The problem of low disposal and utilization rate of bulk industrial solid waste needs to be solved.In this paper,a high-activity admixture composed of steel slag-phosphate slag-limestone powder was proposed for most of the solid waste with low activity and a negative impact on concrete workability,combining the characteristics of each solid waste.The paper demonstrates the feasibility and explains the principle of the composite system in terms of water requirement of standard consistency,setting time,workability,and mechanical properties,combined with the composition of the phases,hydration temperature,and microscopic morphology.The results showed that the steel slag:phosphate slag:limestone=5:2:3 gave the highest activity of the composite system,over 92%.Besides,the composite system had no significant effect on water demand and setting time compared to cement,and it could significantly increase the 7 and 28 d activity of the system.The composite system delayed the exothermic hydration of the cement and reduced the exothermic heat but had no effect on the hydration products.Therefore,the research in this paper dramatically improved the solid waste dissipation in concrete,reduced the amount of cement in concrete and positively responded to the national slogan of carbon neutral and peaking.
基金Funding Statement:This work was supported by the Priority Academic Program Development of Jiangsu Higher Education Institutions(PAPD).
文摘Energy shortage and the emission of greenhouse gases have become a global problem of urgent concern.Therefore,there is an urgent need to develop a low carbon building material.Geopolymers have become a hot topic due to their environmental sustainability and the feasibility of immobilizing industrial waste.In this paper,steel slag(SS)fines were investigated as auxiliary materials of blast furnace slag(BFS)based geopolymer.The hydration heat properties,flowability,compressive strength,sorptivity coefficient,X-ray diffraction(XRD),and scanning electron microscopy(SEM)of the geopolymer pastes were determined.The results showed that the incorporation of SS weakened the reactivity of the BFS-based geopolymer paste and improved the flow values of the paste.The compressive strength of the geopolymer with 20%SS content reached 117 MPa at 28 d.The geopolymer specimens with high compressive strength showed a low sorptivity coefficient.The microscopic results showed that the addition of the appropriate amount of SS reduced the cracks,improved the density of the geopolymer,and produced a geopolymer composite with excellent mechanical properties.
基金supported by the National Key Research and Development Program of China(No.2021YFB3802005)the National Natural Science Foundation of China(Grant No.51978002)+1 种基金the Natural Science Foundation for the Higher Education Institutions in Anhui Province of China(Grant No.KJ2020A0845)the Housing and Urban-Rural Construction Science and Technology Plan in Anhui Province of China(Grant No.2021-YF69).
文摘This study focuses on the workability and compressive strength of ceramsite self-compacting concrete with fine aggregate partially substituted by steel slag sand(CSLSCC)to prevent the pollution of steel slag in the environment.The SF,J-ring,visual stability index,and sieve analysis tests are primarily employed in this research to investigate the workability of freshly mixed self-compacting concrete containing steel slag at various steel slag sand replacement rates.The experiment results indicate that CSLSCC with the 20%volume percentage of steel slag(VPS)performs better workability,higher strength,and higher specific strength.The 7-day compressive strength of CSLSCC with the 0.4 of the water-binder ratio(W/B),decreases with the increase of steel slag content,while the 28-day compressive strength increases significantly.The ceramsite self-compacting concrete with good comprehensive performance can be obtained when the substitution rate of steel slag sand for fine aggregate is less than 20%(volume percentage).
基金Funded by the National Key Research and Development Program of China-Intergovernmental International Cooperation in Scientific and Technological Innovation MOST,China (No.2018YFE0107300)。
文摘Two carbonation approaches are considered for studying the effects on the hardening mechanisms of slurries made of 100 wt%electric arc furnace steel slag (EAF) slag or 80 wt%EAF slag incorporating 20 wt% of Portland cement,which are applied during the hot-stage pretreatment with simulated gas for raw steel slag or the accelerated carbonation curing of slurry.The mechanical strengths,carbonate products,microstructures and CO_(2) uptakes were quantitatively investigated.Results manifest that accelerated carbonation curing increases the compressive strengths of steel slag slurry,from 17.1 MPa (binder of 80 wt% EAF and 20 wt%cement under standard moisture curing) to 36.0 MPa (binder of 80 wt%EAF and 20 wt%cement under accelerated carbonation curing),with a CO_(2) uptake of 52%.In contrast,hot-stage carbonation applied during the pretreatment of steel slag increases the compressive strengths to 43.7 MPa (binder of 80 wt%carbonated EAF and 20 wt%cement under accelerated carbonation curing),with a CO_(2) uptake of 67%.Hotstage carbonation of steel slag is found for particle agglomeration,minerals remodeling and calcite formed,thus causing an activated steel slag with a dense structure and more active components.Accelerated carbonation curing of steel slag slurry paste results in the newly formed amorphous CaCO_(3),calcite crystalline and silica gels that covered the pores of the matrix,facilitating microstructure densification and strength improvement.Adopting the combinative methods of the hot-stage CO_(2) pretreatment and accelerated carbonation curing creates a promising high-volume steel slag-based binder with high strengths and CO_(2) storage.
基金funding from CNPq(Brazilian council for scientific and technological development)through 201465/2015-9 scholarship of the“Science without borders”programsupport of MCTES/FCT(Portuguese Science and Technology Foundation of Portuguese Ministry of Science and Technology)through CEECIND/04583/2017 grant+1 种基金financially supported by:Base Funding-UIDB/04708/2020 of the CONSTRUCT-Instituto de I&D em Estruturas e Construções-funded by national funds through FCT/MCTES(PIDDAC)A special acknowledgment is also due to the Portuguese National Steel Industry of Maia,part of MEGASA group,for the steel slag supply and to Professor Joaquim Faria for his support in understanding the basic notions of chemistry.
文摘In this work,an alternative alkali-activated cement(AAC)made of ladle slag precursor mixed with sodium hydroxide and sodium silicate has been developed to enhance the bearing capacity of estuarine soils in coastal conditions via deep soil mixing(DSM).The AAC was optimized to use a low reactivity precursor(ladle slag)and to deal with a contaminated high-water content natural sediment cured under water.The material performance was analysed by comparison to a mixture made with Portland cement and cured in the same conditions.Flexural and unconfined compressive strength tests as well as seismic waves measurements after 3-,7-,14-and 28-d curing were performed to obtain a relationship between elastic stiffness and strength with curing time for both mixtures.Remarkably,the AAC mix demonstrated superior strength results,exhibiting almost double flexural and compressive strengths after 28 d compared to the Portland cement mix.The AAC mix also showed a higher rate of stiffness increase than the Portland cement mix,which has a higher initial stiffness at young ages but lower stiffness evolution.Leachate analysis confirmed that the proposed AAC could effectively immobilise any contaminants from soil or precursors.The effect of curing under stress was analysed in triaxial compression tests and found to be insignificant,indicating that laboratory data obtained without stress curing can represent the material's behaviour in a DSM column,which will cure under the weight of the column.
基金supported by the ERDF(European Regional Development Fund)activity No.2.1.1.1.“Atbalsts zinātnei un pētniecībai”(support for the science and research)within the project:No.2010/0254/2DP/2.1.1.1.0/10/APIA/VIAA/015.
文摘The study investigates use of dolomite sand waste as filler or/and sand material plus BOF steel slag as fine and coarse aggregate for design of high performance asphalt concrete.Both environmental and economic factors contribute to the growing need for the use of these materials in asphalt concrete pavements.This is particularly important for Latvia,where local crushed dolomite and sandstone does not fulfill the requirements for mineral aggregate in high and medium intensity asphalt pavements roads.Annually 100 to 200 thousand tons of steel slag aggregates are produced in Latvia.However,it has not been used extensively in asphalt pavement despite its high performance characteristics.Dolomite sand waste,which is byproduct of crushed dolomite production,is another widely available polydisperse by-product in Latvia.Its quantity has reached a million of tons and is rapidly increasing.This huge quantity of technological waste needs to be recycled with maximum efficiency.Various combinations of steel slag,dolomite sand waste and conventional aggregates were used to develop AC 11 asphalt concrete mixtures.The mix properties tests include resistance to permanent deformations(wheel tracking test,dynamic creep test)and fatigue resistance.Laboratory test results showed that asphalt concrete mixtures containing steel slag and local limestone in coarse portion and dolomite sand waste in sand and filler portions had high resistance to plastic deformations and good resistance to fatigue failure.
基金the National Natural Science Foundation of China (No.50678139)
文摘Suitable methods for enhancing the volume stability of steel slag utilized as fine aggregate were determined. The effects of steam treatment at 100 ℃ and autoclave treatment under 2.0 MPa on the soundness of steel slag sand were investigated by means of powder ratio, linear expansion, compressive and flexural strength. DTA, EDX, XRD and ethylene glycol methods were employed to analyze both the treated slags and susceptible expansion grains. Experimental results indicate that powder ratio, content of free lime and rate of linear expansion can express the improvement in volume stability of different treated methods. Steam treatment process cannot ultimately prevent specimens from cracking and decrease of strength, but mortar made from autoclave treated slag keeps integration subjected to hot water of 80℃ until 28 d and its strength do not show significant decrement. The hydration of over-burn free lime and periclase phase are the main cause for the disintegration or crack of untreated and steam treated steel slag's specimens. Autoclave treatment process is more effective than steam treatment process on enhancement of volume stability of steel slag.
基金financially supported by the National Natural Science Foundation of China (Nos. 51034008 and 51004012)the National High Technology Research and Development Program of China (No. 2011AA06A105)
文摘Using steel slag as a main raw material of ceramics is considered as a high value-added way. However, the relationship among the initial composition, ceramic microstructure, and macroscopic properties requires further study. In this paper, a series of ceramics with different slag ratios (0-70wt%) were designed, and the software FACTsage was introduced to simulate the formation of crystalline phases. The simulation results indicate that mullite is generated but drastically reduced at the slag ratios of 0-25wt%, and anorthite is the dominant crystalline phase in the slag content of 25wt%-45wt%. When the slag ratio is above 45wt%, pyroxene is generated more than anorthite. This is because increasing magnesium can promote the formation of pyroxene. Then, the formula with a slag content of 40wt% was selected and optimized. X-ray diffraction results were good consistent with the simulation results. Finally, the water absorption and bending strength of optimized samples were measured.
基金Funded by National 973 Project (No.2001CB610704-2)
文摘Hydration heat evolution, non-evaporative water, setting time and SEM tests were peorormed to investigate the effect of fine steel slag powder on the hydration process of Portland cement and its mechanism. The results show that the effect of fine steel slag powder on the hydration process of Portland cement is closely related to its chemical composition, mineral phases, fineness, etc. Fine steel slag powder retards the hydration of portland cement at early age. The major reason for this phenomenon is the relative high content of MgO , MnO2, P2O5 in steel slag, and MgO solid solved in C3 S contained in steel slag.
文摘This paper studied the hydration and strength influence factors ofSteel Slag Cement (SSC), such as the quantity of steel slag and slagand the dosage of additive. The results show that: (a) In the processof hydration of SSC, steel slag and slag activate each other; (b)Waterglass's structure forms the preliminary skeleton of SSC, and thehydration products of SSC link or fill in the skeleton; (c) Sodium inWaterglass is the catalytic and its concentration does not change inthe process of hydration. (d) Structure of activation is asignificant factor to the property of SSC.
文摘Steel slag is a byproduct produced in large amounts in the steel-making process. It is an important resource that can be effectively utilized. An experiment was described in which steel slag was tested as an adsorbent for the removal of phosphorus from waste water. Phosphorus removal depended on the amount of steel slag added, the pH value, the contact time, and the initial concentration. Under laboratory conditions when the added slag was 7.5g/L, the contact time 2h, and the pH value was equivalent to 6.5, over 99% of the phosphorus was removed; the experimental data on steel slag adsorption of phosphorus in the water fitted the Freundlich isotherm model. Steel slag was found to be very effective in adsorbing phosphorus.
基金Funded by the National Natural Science Foundations of China(Nos.51378113 and 51438003)the Plan of Six Peak Talents in Jiangsu Province(No.JZ-004)Partly Supported by the National Basic Research Program of China(973 Program,No.2015CB655102)
文摘To enhance the understanding about the utilization of steel slags as a cementitious material, we comparatively studied the chemical, mineralogical and morphological properties of two types of steel slag; basicoxygen-furnace carbon slag(BOF C) and electric-arc-furnace stainless steel slag(EAF S). Moreover, we studied the standard consistency, setting time and the effect of the slag replacement ratios on the fluidity and compressive strength of blended cement mortar. The experimental results showed that BOF C had higher alkalinity, higher pH value and more hydraulic phases than EAF S. Both types of slag showed water reduction effect due to its high fineness. Neat BOF C paste showed flash set and acceleration in the initial setting time of blended cement especially at high slag proportions. However, EAF S prolonged the setting time of blended cement even at low slag proportions. The pH values for blended cement contained 50% BOF C or EAF S were lower than those of pure cement paste. Despite of slag type, compressive strength gradually decreased with increasing slags content. The strength of BOF C mortar was higher than that of EAF S mortar with the same replacement ratio for the same age. Slag activity index demonstrated that BOF C and EAF S conformed to the Chinese National Standard(GB/T 20491-2006) requirements for steel slag as grade one and grade two, respectively.