The residual stresses on the surface of the d ifferently ground and polished silicon nitride ceramics were measured using X-r ay diffraction and identified by SEM.The effect of the residual stress on the be nding str...The residual stresses on the surface of the d ifferently ground and polished silicon nitride ceramics were measured using X-r ay diffraction and identified by SEM.The effect of the residual stress on the be nding strength was investigated.The investigations show that the grinding proces s can introduce subatantial tensile residual stresses up to 290MPa on the surfac e of silicon nitride ceramics,which has a significant effect on reducing the ben ding strength of the ceramics after grinding.Thus,in comparison with the ceramic s with a rough surface,the ceramics with a mirror image surface may have a lower strength.Polishing can smooth the residual stresses.When we evaluate the qualit y of the ceramic components after grinding,we must take residual stress into con sideration. The grinding methods and grinding conditions must be carefully selec ted in order to get the favorite residual stress as well as the surface smoothne ss.展开更多
Films were developed from the modified wheat glutens by microbial transglutamina se(MTGase, [E/S]=10u/g,15u/g and 20u/g) in order to improve physical and barri er properties of the films.Glycerol was used as a plastic...Films were developed from the modified wheat glutens by microbial transglutamina se(MTGase, [E/S]=10u/g,15u/g and 20u/g) in order to improve physical and barri er properties of the films.Glycerol was used as a plasticizer.The films prepared from the modified-glutens by MTGase show a lower elongation at break(E) and a water vapor permeability(WVP), and a higher tensile strength(TS) than the nati ve gluten films.When the modified gluten films by different concentrations of MT Gase are immersed in water at 25℃,their weight losses decreased significantly, and their water resistance increases obviously as expected, compared with the c ontrol gluten films. Moreover, an addition of glycerol as plasticizer greatly mo dified water vapor barrier and mechanical properties of the films.展开更多
基金Funded by the Key Research Foundation of China Education Ad ministration (No.02049)
文摘The residual stresses on the surface of the d ifferently ground and polished silicon nitride ceramics were measured using X-r ay diffraction and identified by SEM.The effect of the residual stress on the be nding strength was investigated.The investigations show that the grinding proces s can introduce subatantial tensile residual stresses up to 290MPa on the surfac e of silicon nitride ceramics,which has a significant effect on reducing the ben ding strength of the ceramics after grinding.Thus,in comparison with the ceramic s with a rough surface,the ceramics with a mirror image surface may have a lower strength.Polishing can smooth the residual stresses.When we evaluate the qualit y of the ceramic components after grinding,we must take residual stress into con sideration. The grinding methods and grinding conditions must be carefully selec ted in order to get the favorite residual stress as well as the surface smoothne ss.
基金Funded by the Science Technology Project of the National"TenthFive year plan"of China(No.2001BA501A04)
文摘Films were developed from the modified wheat glutens by microbial transglutamina se(MTGase, [E/S]=10u/g,15u/g and 20u/g) in order to improve physical and barri er properties of the films.Glycerol was used as a plasticizer.The films prepared from the modified-glutens by MTGase show a lower elongation at break(E) and a water vapor permeability(WVP), and a higher tensile strength(TS) than the nati ve gluten films.When the modified gluten films by different concentrations of MT Gase are immersed in water at 25℃,their weight losses decreased significantly, and their water resistance increases obviously as expected, compared with the c ontrol gluten films. Moreover, an addition of glycerol as plasticizer greatly mo dified water vapor barrier and mechanical properties of the films.