Air quenched basic oxygen furnace steel slag （BOF-SS） is processed at very high cooling rate, which is expected to have different cementitious properties from conventional slowly cooled BOF-SS. For this purpose, the...Air quenched basic oxygen furnace steel slag （BOF-SS） is processed at very high cooling rate, which is expected to have different cementitious properties from conventional slowly cooled BOF-SS. For this purpose, the strength activity indexes of air quenched and slowly cooled BOF-SS are investigated. The results reveal that, under the specific surface area （S） of 490 m^2/kg, the compressive strength activity index reaches 1.24 after 28 days with replacement of 15% air quenched BOF-SS and reaches 1.05 after 28 days with replacement of 20% air quenched BOF-SS and 30%granulated blast furnace slag （GBFS）. The cementitious activity of air quenched BOF-SS is obviously higher than that of slowly cooled BOF-SS, mainly because it contains more C3 S and glassy phases.展开更多
Reducing steel slag （RSS） was mainly acquired from five electric-arc furnace （EAF） steelmaking plants （among them, the products of two plants were carbon steel and those of other plants were stainless steel） for...Reducing steel slag （RSS） was mainly acquired from five electric-arc furnace （EAF） steelmaking plants （among them, the products of two plants were carbon steel and those of other plants were stainless steel） for research tests. The chemical properties, compound compositions, activities and contents of main expansive compounds were tested. The results showed that the field sampled RSS had a very high crystallinity and hydraulicity with main chemical compositions close to those of Portland cement. It can be known from the study that in case of C/S ratio higher than 2.0, the main compound compositions are C2S, C3S, C2F and f-CaO. However, after the RSS was stored for six months, an obvious variation occurred with potential pre-hydration in RSS, where the SO3 content was slightly reduced and the compressive activity index was obviously higher than that at the 28th day.展开更多
基金Item Sponsored by National Natural Science Foundation of China(51234003)
文摘Air quenched basic oxygen furnace steel slag （BOF-SS） is processed at very high cooling rate, which is expected to have different cementitious properties from conventional slowly cooled BOF-SS. For this purpose, the strength activity indexes of air quenched and slowly cooled BOF-SS are investigated. The results reveal that, under the specific surface area （S） of 490 m^2/kg, the compressive strength activity index reaches 1.24 after 28 days with replacement of 15% air quenched BOF-SS and reaches 1.05 after 28 days with replacement of 20% air quenched BOF-SS and 30%granulated blast furnace slag （GBFS）. The cementitious activity of air quenched BOF-SS is obviously higher than that of slowly cooled BOF-SS, mainly because it contains more C3 S and glassy phases.
文摘Reducing steel slag （RSS） was mainly acquired from five electric-arc furnace （EAF） steelmaking plants （among them, the products of two plants were carbon steel and those of other plants were stainless steel） for research tests. The chemical properties, compound compositions, activities and contents of main expansive compounds were tested. The results showed that the field sampled RSS had a very high crystallinity and hydraulicity with main chemical compositions close to those of Portland cement. It can be known from the study that in case of C/S ratio higher than 2.0, the main compound compositions are C2S, C3S, C2F and f-CaO. However, after the RSS was stored for six months, an obvious variation occurred with potential pre-hydration in RSS, where the SO3 content was slightly reduced and the compressive activity index was obviously higher than that at the 28th day.