The effects of sulfide stress cracking on the mechanical properties and intergranular cracking of P110 casing steel in sour environments

Variation and degradation of P-110 casing steel mechanical properties, due to sulfide stress cracking （SSC） in sour environments, was investigated using tensile and impact tests. These tests were carried out on specimens, which were pretreated under the following conditions for 168 hours： temperature, 60 ℃; pressure, 10 MPa; H2S partial pressure, 1 MPa and CO2 partial pressure, 1 MPa; preload stress, 80% of the yield strength （os）; medium, simulated formation water. The reduction in tensile and impact strengths for P-110 casing specimens in corrosive environments were 28% and 54%, respectively. The surface morphology analysis indicated that surface damage and uniform plastic deformation occurred as a result of strain aging. Impact toughness of the casing decreased significantly and intergranular cracking occurred when specimens were maintained at a high stress level of 85% %.

Sulfide Stress Cracking Assessment of Carbon Steel Welding with High Content of H<SUB>2</SUB>S and CO<SUB>2</SUB>at High Temperature: A Case Study

In the oil and gas industry, it has been established that for pipelines fabricated with carbon steels, their limitation is related to H2S and CO2 environments, which is 7 to 10 psia of partial pressure of CO2. Therefore, in carbon steel cracking is shown, after 7 or 10 psia of partial pressure of CO2. The experimental work was performed under static conditions in autoclaves within a pH of 3 to 3.8;partial pressures of 16 - 96 psi for H2S and 15 - 53 psi for CO2, in the temperature range of 25°C - 150°C. It was observed that the average yielding stress used in Sulfide Stress Cracking (SSC) tests decreases with temperature increment. Hydrogen Induced Cracking (HIC) evaluations showed that X52 steel, under conditions, was not susceptible to HIC. Results of SSC did not show indications of cracking after exposure to sour solutions, except for the specimen exposed to high H2S and CO2 content (96 psi of H2S and 53 psi of CO2 of the partial pressure) and high temperature (150°C). Microcracks located between the upper and lower weld beads were also observed. However, the highest average corrosion rate was 0.27 mm/year (10.6 mpy), which occurred in samples exposed to 96 psi of H2S and 53 psi of CO2 at 150°C. Likewise, the highest localized corrosion (severe pitting attack) was obtained at the same environment with a corrosion rate of 4.2 mm/year (167 mpy). The oil and gas industry could use carbon steels pipelines in partial pressure higher than 10 psia.

Stress corrosion cracking behavior of buried oil and gas pipeline steel under the coexistence of magnetic field and sulfate-reducing bacteria

Magnetic field and microorganisms are important factors influencing the stress corrosion cracking(SCC)of buried oil and gas pipelines. Once SCC occurs in buried pipelines, it will cause serious hazards to the soil environment. The SCC behavior of X80 pipeline steel under the magnetic field and sulfate-reducing bacteria(SRB) environment was investigated by immersion tests, electrochemical tests, and slow strain rate tensile(SSRT) tests. The results showed that the corrosion and SCC sensitivity of X80 steel decreased with increasing the magnetic field strength in the sterile environment. The SCC sensitivity was higher in the biotic environment inoculated with SRB, but it also decreased with increasing magnetic field strength, which was due to the magnetic field reduces microbial activity and promotes the formation of dense film layer. This work provided theoretical guidance on the prevention of SCC in pipeline steel under magnetic field and SRB coexistence.

Effect of icosahedral phase formation on the stress corrosion cracking(SCC)behaviors of the as-cast Mg-8%Li(in wt.%)based alloys

Through exploring the stress corrosion cracking(SCC)behaviors of the as-cast Mg-8%Li and Mg-8%Li-6%Zn-1.2%Y alloys in a 0.1 M NaCl solution,it revealed that the SCC susceptibility index(I_(SCC))of the Mg-8%Li alloy was 47%,whilst the I_(SCC)of the Mg-8%Li-6%Zn-1.2%Y alloy was 68%.Surface,cross-sectional and fractography observations indicated that for the Mg-8%Li alloy,theα-Mg/β-Li interfaces acted as the preferential crack initiation sites and propagation paths during the SCC process.With regard to the Mg-8%Li-6%Zn-1.2%Y alloy,the crack initiation sites included the I-phase and the interfaces of I-phase/β-Li andα-Mg/β-Li,and the preferential propagation paths were the I-phase/β-Li andα-Mg/β-Li interfaces.Moreover,the SCC of the two alloys was concerned with hydrogen embrittlement(HE)mechanism.

Stress corrosion cracking of magnesium alloys:A review

Magnesium(Mg)alloys have been widely used in automobile,aviation,computer,and other fields due to their lightweight,high specific strength and stiffness,low pollution,and good electromagnetic shielding performance.However,the chemical stability of Mg alloys is poor,especially in the corrosive medium environment with high stress corrosion sensitivity,which causes sudden damage to structural components and restricts their application field.In recent years,owing to the increasing failure rate of engineering structures caused by stress corrosion of Mg alloys,it has become necessary to understand and pay more attention to the stress corrosion cracking(SCC)behavior of Mg alloys.In this paper,the SCC mechanisms and test methods of Mg alloys have been summarized.The recent research progress on SCC of Mg alloys has been reviewed from the aspects of alloying,preparation process,surface modification,corrosive medium,and strain rate.More importantly,future research trends in the field of SCC of Mg alloys have also been proposed.

Effect of heat treatment on stress corrosion cracking, fracture toughness and strength of 7085 aluminum alloy

The influences of heat treatment on stress corrosion cracking （SCC）, fracture toughness and strength of 7085 aluminum alloy were investigated by slow strain rate testing, Kahn tear testing combined with scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. The results show that the fracture toughness of T74 overaging is increased by 22.9% at the expense of 13.6% strength, and retrogression and reaging （RRA） enhances fracture toughness 14.2% without reducing the strength compared with T6 temper. The fracture toughness of dual-retrogression and reaging （DRRA） is equivalent to that of T74 with an increased strength of 14.6%. The SCC resistance increases in the order： T6〈RRA〈DRRA≈T74. The differences of fracture toughness and SCC were explained on the basis of the role of matrix precipitates and grain boundary orecioitates.

Effects of silicon content on microstructure and stress corrosion cracking resistance of 7050 aluminum alloy

Evolution of microstructure and stress corrosion cracking （SCC） susceptibility of 7050 aluminum alloy with 0.094%, 0.134% and 0.261% Si （mass fraction） in T7651 condition have been investigated. The results show that the area fraction of Mg2Si increases from 0.16% to 1,48% and the size becomes coarser, while the area fraction of the other coarse phases including Al2CuMg, Mg（Al,Cu,Zn）2 and A17Cu2Fe decreases from 2.42% to 0.78% with Si content increasing from 0.094% to 0.261%. The tensile strength and elongation of 7050-T7651 alloys is decreased with the increase of Si content by slow strain rate test （SSRT） in ambient air. However, electrical conductivity is improved and SCC susceptibility is reduced with the increase of Si content by SSRT in corrosion environment with 3.5% NaCl solution.

Effect of hydrogen on the stress corrosion cracking behavior of X80 pipeline steel in Ku'erle soil simulated solution

Hydrogen was a key factor resulting in stress corrosion cracking （SCC） of X80 pipeline steel in Ku＇erle soil simulated solution. In this article, the effect of hydrogen on the SCC susceptibility of X80 steel was investigated further by slow strain rate tensile test, the surface fractures were observed using scanning electron microscopy （SEM）, and the fracture mechanism of SCC was discussed. The results indicate that hydrogen increases the SCC susceptibility. The SEM micrographs of hydrogen precharged samples presents a brittle quasi-cleavage feature, and pits facilitate the transgranular crack initiation. In the electrochemical impedance spectroscopy （EIS） measurement, the decreased polarization resistance and the pitting resistance of samples with hydrogen indicate that hydrogen increases the dissolution rate and deteriorates the pitting corrosion resistance. The potentiodynamic polarization curves present that hydrogen also accelerates the dissolution rate of the crack tip.

Effect of quenching rate on microstructure and stress corrosion cracking of 7085 aluminum alloy

The influence of quenching rate on microstructure and stress corrosion cracking （SCC） of 7085 aluminum alloy was investigated by tensile test, slow strain rate test （SSRT）, combined with scanning electron microscopy （SEM）, transmission electron microscopy （TEM） and electrochemical test. The results show that with decreasing the quenching rate, the size and inter-particle distance of the grain boundary precipitates as well as precipitation free zone width increase, but the copper content of grain boundary precipitates decreases. The SCC resistance of the samples increases first and then decreases, which is attributed to the copper content, size and distribution of grain boundary precipitates.

Stress corrosion cracking behaviour of 7xxx aluminum alloys: A literature review

Stress corrosion cracking （SCC） is degradation of mechanical properties under the combined action of stress and corrosive environment of the susceptible material. Out of eight series of aluminium alloys, 2xxx, 5xxx and 7xxx aluminium alloys are susceptible to SCC. Among them, 7xxx series aluminium alloys have specific application in aerospace, military and structural industries due to superior mechanical properties. In these high strength 7xxx aluminium alloys, SCC plays a vital factor of consideration, as these failures are catastrophic during the service. The understanding of SCC behaviour possesses critical challenge for this alloy. The main aim of this review paper is to understand the effect of constituent alloying elements on the response of microstructural variation in various heat-treated conditions on SCC behavior. Further, review was made for improving the SCC resistance using thermomechanical treatments and by surface modifications of 7xxx alloys. Apart from a brief review on SCC of 7xxx alloys, this paper presents the effect of stress and pre-strain, effect of constituent alloying elements in the alloy, and the effect of environments on SCC behaviour. In addition, the SCC behaviours of weldments, 7xxx metal matrix composites and also laser surface modifications were also reviewed.

Effect of pre-deformation on the stress corrosion cracking susceptibility of aluminum alloy 2519

The effects of pre-deformation and strain rate on the stress corrosion cracking （SCC） behavior of aluminum alloy 2519 in air and in 3.5% NaCI water solution were investigated by means of slow strain rate tension （SSRT）, scanning electron microscopy （SEM）, and transmission electron microscopy （TEM）. The results indicate that the alloy is susceptible to SCC in 3.5% NaCI water solution and not in air. At the same pre-deformation, the alloy is more susceptible to SCC at 1.33 × 10^-5 s^-1 than at 6.66 × 10^-5 s^-1. Moreover, it is more susceptible to SCC at free pre-deformation than at 10% pre-deformation at the same strain rate. The number of 0 precipitated along the grain boundaries is reduced and distributed discontinuously, at the same time, the precipitate-free zones （PFZ） become narrow and the susceptibility to stress corrosion cracking is reduced after 10% pre-deformation.

Diversity of intergranular corrosion and stress corrosion cracking for 5083 Al alloy with different grain sizes

5083 Al alloy sheets with different grain sizes(8.7-79.2 μm) were obtained by cold rolling and annealing. Their microstructures, intergranular corrosion(IGC), stress corrosion cracking(SCC), and crack propagation behaviors were investigated. The results showed that samples with coarse grains exhibit better IGC resistance with a corrosion depth of 15 μm. The slow strain rate test results revealed that fine-grained samples exhibit better SCC resistance with a susceptibility index(ISSRT) of 11.2%. Furthermore, based on the crack propagation mechanism, grain refinement can improve the SCC resistance by increasing the number of grain boundaries to induce the corrosion crack propagation along a tortuous path. The grains with {011} orientation could hinder crack propagation by orientating it toward the low-angle grain boundary region. The crack in the fine-grained material slowly propagates due to the tortuous path, and low H;and Cl;concentrations.

Stress Corrosion Cracking of Nitrogen-containing Stainless Steel 316LN in High Temperature Water Environments

Stress corrosion cracking （SCC） of stainless steels and Ni-based alloys in high temperature water coolant is one of the key problems affecting the safe operation of nuclear power plants （NPPs）. The nitrogen-added stainless steel is a kind of possible candidate materials for mitigating SCC since reducing the carbon content and adding nitrogen to offset the loss in strength caused by the decrease in carbon content can mitigate the problem of sensitization. However, the reports of SCC of nitrogen-added stainless steels in high temperature water are few available. The effects of applied potential and sensitization treatment on the SCC of a newly developed nitrogen-containing stainless steel （SS） 316LN in high temperature water doped with chloride at 250 ℃ were studied by using slow strain rate tests （SSRTs）. The SSRT results are compared with our data previously published for 316 SS without nitrogen and 304NG SS with nitrogen, and the possible mechanism affecting the SCC behaviors of the studied steels is also discussed based on SSRT and microstucture analysis results. The susceptibility to cracking of 316LN SS normally increases with increasing potential. The susceptibility to SCC of 316LN SS was less than that of 316 SS and 304NG SS. Sensitization treatment at 700℃ for 30 h showed little effect on the S CC of 316LN S S and significant effect on the S CC of 316 S S. The predominant cracking mode for the 316LN S S in both annealed state and the state after the sensitization treatment was transgranular. The presented conditions of mitigating stress corrosion cracking are some useful information for the safe use of 316LN SS in NPPs.

Correlations among stress corrosion cracking,grain-boundary microchemistry,and Zn content in high Zn-containing Al-Zn-Mg-Cu alloys

The correlations among the corrosion behaviour,grain-boundary microchemistry,and Zn content in Al-Zn-Mg-Cu alloys were studied using stress corrosion cracking(SCC)and intergranular corrosion(IGC)tests,combined with scanning electron microscopy(SEM)and high-angle angular dark field scanning transmission electron microscopy(HAADF-STEM)microstructural examinations.The results showed that the tensile strength enhancement of high Zn-containing Al-Zn-Mg-Cu alloys was mainly attributed to the high density nano-scale matrix precipitates.The SCC plateau velocity for the alloy with 11.0 wt.%Zn was about an order of magnitude greater than that of the alloy with 7.9 wt.%Zn,which was mainly associated with Zn enrichment in grain boundary precipitates and wide precipitates-free zones.The SCC mechanisms of different Zn-containing alloys were discussed based on fracture features,grain-boundary microchemistry,and electrochemical properties.

Stress corrosion cracking of X80 pipeline steel exposed to high pH solutions with different concentrations of bicarbonate

Susceptibilities to stress corrosion cracking （SCC） of X80 pipeline steel in high pH solutions with various concentrations of HC03 at a passive potential of-0.2 V vs. SCE were investigated by slow strain rate tensile （SSRT） test. The SCC mechanism and the effect of HC03 were discussed with the aid of electrochemical techniques. It is indicated that X80 steel shows enhunced susceptibility to SCC with the concentration of HCO3 increasing from 0.15 to 1.00 mol/L, and the susceptibility can be evaluated in terms of current density at -0.2 V vs. SCE. The SCC behavior is controlled by the dissolution-based mechanism in these circumstances. Increasing the concentration of HCO3 not only increases the risk of rupture of passive films but also promotes the anodic dissolution of crack tips. Besides, little susceptibility to SCC is found in dilute solution containing 0.05 mol/L HCO3 for X80 steel. This can be attributed to the inhibited repassivation of passive films, manifesting as a more intensive dissolution in the non-crack tip areas than at the crack tips.

Influence of aging on microstructure,mechanical properties and stress corrosion cracking of 7136 aluminum alloy

The microstructure,mechanical properties and stress corrosion cracking(SCC)of 7136 aluminum alloy under T 6,T 79 and T 74 aging treatments were studied and the effects of microstructure on the mechanical properties and SCC were discussed.The results show that the ultimate tensile strength and yield strength of the aging 7136 alloys follow this sequence from high to low:T 6>T 79>pre-aging>T 74.For 7136 Al alloy after T 6 aging,the average diameter of the precipitates was(5.7±1.7)nm,and the diameter of 60.7%(number fraction)precipitates was 2−6 nm,leading to a good precipitation strengthening.The K_(IC)of T 74-aging alloy is 38.2 MPa·m^(1/2),which is 26.1%more than that of T 6-aging alloy and 17.5%more than that of T 79-aging alloy.The improved fracture toughness in T 74-aging alloy is mainly due to the reduction of the strength difference between intragranular and grain boundary.The SCC resistance of the aging 7136 alloys follows this sequence from high to low:T 79>T 74>T 6.After T 79 aging,the discontinuous grain boundary precipitates and narrow precipitate free zones were obtained in 7136 alloy,which was beneficial to SCC resistance.

Electrochemical investigation on the hydrogen permeation behavior of 7075-T6 Al alloy and its influence on stress corrosion cracking

The hydrogen permeation behavior and stress corrosion cracking （SCC） susceptibility of precharged 7075-T6 A1 alloy were inves- tigated in this paper. Devanthan-Stachurski （D-S） cell tests were used to measure the apparent hydrogen diffusivity and hydrogen permeation current density of specimens immersed in 3.5wt% NaCl solution. Electrochemical experiment results show that the SCC susceptibility is low during anodic polarization. Both corrosion pits and hydrogen-induced cracking are evident in scanning electron microscope images after the specimens have been charging for 24 h.

Effect of deteriorated microstructures on stress corrosion cracking of X70 pipeline steel in acidic soil environment

In order to investigate stress corrosion cracking （SCC） of X70 pipeline steel and its weld joint area in acidic soil environ- ment in China, two simulating methods were used： one was to obtain bad microstructures in heat affected zone by annealing at 1300 ℃ for 10 min and then, quenching in water; the other was to get different simulating solutions of acidic soil in Yingtan in south- east China. The SCC susceptibilities of X70 pipeline steel before and after quenching in the simulating solutions were analyzed using slow stain rate test （SSRT） and potentiodynamic polarization technique to investigate the SCC electrochemical mechanism of different microstructures further. The results show that SCC appears in the original microstructure and the quenched microstructure as the polarization potential decreases. Hydrogen revolution accelerates SCC of the two tested materials within the range of-850 mV to -1200 mV vs. SCE. Microstructural hardening and grain coarsening also increase SCC. The SCC mechanisms are different, anodic dissolution is the key of causing SCC as the polarization potential is higher than the null current potential, and hydrogen embrittlement will play a more important role to SCC as the polarization potential lower than the null current potential.

Mechanical properties and stress corrosion cracking behaviour of AZ31 magnesium alloy laser weldments

An AZ31 HP magnesium alloy was laser beam welded in autogenous mode with AZ61 filler using Nd-YAG laser system.Microstructural examination revealed that the laser beam weld metals obtained with or without filler material had an average grain size of about 12 μm.The microhardness and the tensile strength of the weldments were similar to those of the parent alloy.However,the stress corrosion cracking （SCC） behaviour of both the weldments assessed by slow strain rate tensile （SSRT） tests in ASTM D1384 solution was found to be slightly inferior to that of the parent alloy.It was observed that the stress corrosion cracks originated in the weld metal and propagated through the weld metal-HAZ regions in the autogenous weldment.On the other hand,in the weldment obtained with AZ61 filler material,the crack initiation and propagation was in the HAZ region.The localized damage of the magnesium hydroxide/oxide film formed on the surface of the specimens due to the exposure to the corrosive environment during the SSRT tests was found to be responsible for the SCC.

Stress corrosion cracking susceptibility of a high strength Mg-7%Gd-5%Y-1%Nd-0.5%Zr alloy

Through performing the tensile tests with different strain rates in 3.5 wt.%NaCl solution,the stress corrosion cracking(SCC)behavior and the effect of strain rate on the SCC susceptibility of an extruded Mg-7%Gd-5%Y-1%Nd-0.5%Zr(EW75)alloy have been investigated.Results demonstrate that the alloy is susceptible to SCC when the strain rate is lower than 5×10^(−6) s^(−1).At the strain rate of 1×10^(−6) s^(−1),the SCC susceptibility index(I_(SCC))is 0.96 and the elongation-to-failure(ε_(f))is only 0.11%.Fractography indicates that the brittle quasi-cleavage feature is very obvious and become more pronounced with decreasing the strain rate.Further analysis confirms that the cracking mode is predominantly transgranular,but the partial intergranular cracking at some localized area can also occur.Meanwhile,it seems that the crack propagation path is unrelated to the existing phase particles.