The liquid citrate method was used to synthesize perovskite-type SrCe0.9 Y0.1O3-α powder. SrCe09Y01O3-α membranes were prepared from the powder by sintering at 1450℃ for 10 h. The reactions in the process of the he...The liquid citrate method was used to synthesize perovskite-type SrCe0.9 Y0.1O3-α powder. SrCe09Y01O3-α membranes were prepared from the powder by sintering at 1450℃ for 10 h. The reactions in the process of the heat treatment were studied by XRD and DSC/TG. The microstructure of the powder and the membrane was observed by SEM. The results indicate that the perovskite-type SrCe0.9Y0.1 O3-α can be synthesized at 1100℃. The particle size of the synthesized SrCe0.9Y0.1O3-α powder is less than 1μm. The powder can be densified at 1450℃.展开更多
SrCe0.92 Nb 0.03 Tm0.05 O 3-δ powders were synthesized by a modified sol-gel method using citrate as a chelating agent.X-ray diffraction（XRD） analysis verified SrCe 0.92 Nb 0.03 Tm 0.05 O 3-δ powders and membranes...SrCe0.92 Nb 0.03 Tm0.05 O 3-δ powders were synthesized by a modified sol-gel method using citrate as a chelating agent.X-ray diffraction（XRD） analysis verified SrCe 0.92 Nb 0.03 Tm 0.05 O 3-δ powders and membranes consisting of a single perovskite phase.The morphologies of the sintered membranes were investigated by using scanning electron microscopy（SEM） technique.Stability tests demonstrated that the Nb introduction into doped strontium cerate greatly enhanced the chemical stability.Electrical conductivities of SrCe 0.92 Nb 0.03 Tm 0.05 O 3-δ and SrCe 0.95 Tm 0.05 O 3-δ were measured by the four-point DC method under 10% H 2 /He atmosphere and temperatures（700-900℃）.With a maximum conductivity of 0.0067 S cm^-1 at 900℃,the total electrical conductivity of SrCe 0.92 Nb 0.03 Tm 0.05 O 3-δ increases with increasing temperature.The H 2 permeation flux of SrCe 0.92 Nb 0.03 Tm 0.05 O 3-δ is 0.035 mL cm-2 min-1 when 40% H 2 /He and Ar were used respectively as the feed and sweeping gases at 900℃.展开更多
文摘The liquid citrate method was used to synthesize perovskite-type SrCe0.9 Y0.1O3-α powder. SrCe09Y01O3-α membranes were prepared from the powder by sintering at 1450℃ for 10 h. The reactions in the process of the heat treatment were studied by XRD and DSC/TG. The microstructure of the powder and the membrane was observed by SEM. The results indicate that the perovskite-type SrCe0.9Y0.1 O3-α can be synthesized at 1100℃. The particle size of the synthesized SrCe0.9Y0.1O3-α powder is less than 1μm. The powder can be densified at 1450℃.
基金supported by Joint Funds of NSFC-Guangdong (No. U0834004)NSFC (No. 20976057)Guangdong Provincial Natural Science Funding (No. 06025657)
文摘SrCe0.92 Nb 0.03 Tm0.05 O 3-δ powders were synthesized by a modified sol-gel method using citrate as a chelating agent.X-ray diffraction（XRD） analysis verified SrCe 0.92 Nb 0.03 Tm 0.05 O 3-δ powders and membranes consisting of a single perovskite phase.The morphologies of the sintered membranes were investigated by using scanning electron microscopy（SEM） technique.Stability tests demonstrated that the Nb introduction into doped strontium cerate greatly enhanced the chemical stability.Electrical conductivities of SrCe 0.92 Nb 0.03 Tm 0.05 O 3-δ and SrCe 0.95 Tm 0.05 O 3-δ were measured by the four-point DC method under 10% H 2 /He atmosphere and temperatures（700-900℃）.With a maximum conductivity of 0.0067 S cm^-1 at 900℃,the total electrical conductivity of SrCe 0.92 Nb 0.03 Tm 0.05 O 3-δ increases with increasing temperature.The H 2 permeation flux of SrCe 0.92 Nb 0.03 Tm 0.05 O 3-δ is 0.035 mL cm-2 min-1 when 40% H 2 /He and Ar were used respectively as the feed and sweeping gases at 900℃.