The deformation behavior and formability of gradient nano-grained（GNG） AISI 304 stainless steel in uniaxial and biaxial states were investigated by means of tensile test and small punch test（SPT）. The GNG top laye...The deformation behavior and formability of gradient nano-grained（GNG） AISI 304 stainless steel in uniaxial and biaxial states were investigated by means of tensile test and small punch test（SPT）. The GNG top layer was fabricated on coarse grains（CG） AISI 304 by ultrasonic impact treatment. The results showed that the CG substrate could effectively suppress the strain localization of NC in GNG layer, and an approximate linear relationship existed between the thickness of substrate（h） and uniform true strain before necking（ε_（unif））. Grain growth of NC was observed at the stress state with high Stress triaxiality T, which led to better ductility of GNG/CG 304 in SPT, as well as similar true strain after the onset of necking（ε_（neck）） compared with coarse 304 in tensile test. Ei-values of GNG/CG 304 with different structures were nearly the same at different punch speeds, and good formability of GNG/CG 304 was demonstrated. However, punch speed and microstructure needed to be optimized to avoid much lost of membrane strain region in biaxial stress state.展开更多
In this work,the influence of heat treatment on Polyamide-1010 structure of aggregation state was studied by using WAXD and SAXS techniques.The results showed that the best crystallinity was obtained nearby T=175℃ fo...In this work,the influence of heat treatment on Polyamide-1010 structure of aggregation state was studied by using WAXD and SAXS techniques.The results showed that the best crystallinity was obtained nearby T=175℃ for Polyamide-1010 samples with various annealing treatment.Through extrapolating method,the Tg obtained was approximately 58℃.Based on the one-dimensional electron density correlation function of partially crystalline polymers,some structural parameters of Polyamide-1010 were determined by SAXS.展开更多
The microstructure of 40Cr steel sample and its surface is ultra-fined through salt-bath cyclic quenching and high frequency hardening, then the superplasticity is studied under isothermal superplastic compressive def...The microstructure of 40Cr steel sample and its surface is ultra-fined through salt-bath cyclic quenching and high frequency hardening, then the superplasticity is studied under isothermal superplastic compressive deformation condition. The experimental results indicate that the stress-strain curves are shown to take place obvious superplastic flow characteristic at the temperature of 750-770℃ and at the initial strain rate of (1.7-5.0)×10-4 s-1. Its strain rate sensitivity is 0.30-0.38, the steady superplastic flow stress is 60-70MPa, the superplastic flow activation energy is 198-217kJ/mol, and it is close to α-Fe grain boundary self-diffusion activation energy. The super-plastic compressive constitute equations of this steel are correspondingly set up. Due to the finer microstructure of high frequency hardening, it appears bigger strain rate sensitivity value, smaller the steady superplastic flow stress and the superplastic flow activation energy, so it has better superplastic deformation capability.展开更多
基金Funded by the National National Natural Science Foundation of China(No.51505189)Open Project of Jiangsu Key Laboratory of Advanced Food Manufacturing Equipment&Technology(No.FM-2015-5)
文摘The deformation behavior and formability of gradient nano-grained（GNG） AISI 304 stainless steel in uniaxial and biaxial states were investigated by means of tensile test and small punch test（SPT）. The GNG top layer was fabricated on coarse grains（CG） AISI 304 by ultrasonic impact treatment. The results showed that the CG substrate could effectively suppress the strain localization of NC in GNG layer, and an approximate linear relationship existed between the thickness of substrate（h） and uniform true strain before necking（ε_（unif））. Grain growth of NC was observed at the stress state with high Stress triaxiality T, which led to better ductility of GNG/CG 304 in SPT, as well as similar true strain after the onset of necking（ε_（neck）） compared with coarse 304 in tensile test. Ei-values of GNG/CG 304 with different structures were nearly the same at different punch speeds, and good formability of GNG/CG 304 was demonstrated. However, punch speed and microstructure needed to be optimized to avoid much lost of membrane strain region in biaxial stress state.
文摘In this work,the influence of heat treatment on Polyamide-1010 structure of aggregation state was studied by using WAXD and SAXS techniques.The results showed that the best crystallinity was obtained nearby T=175℃ for Polyamide-1010 samples with various annealing treatment.Through extrapolating method,the Tg obtained was approximately 58℃.Based on the one-dimensional electron density correlation function of partially crystalline polymers,some structural parameters of Polyamide-1010 were determined by SAXS.
基金supported by State Key Laboratory of New Nonferrous Metal Materials Natural Science Foundation of He'nan Province,China(No.984040900)Natural Science Foundation of the Education Department of He'nan Province,China(No.2003430211).
文摘The microstructure of 40Cr steel sample and its surface is ultra-fined through salt-bath cyclic quenching and high frequency hardening, then the superplasticity is studied under isothermal superplastic compressive deformation condition. The experimental results indicate that the stress-strain curves are shown to take place obvious superplastic flow characteristic at the temperature of 750-770℃ and at the initial strain rate of (1.7-5.0)×10-4 s-1. Its strain rate sensitivity is 0.30-0.38, the steady superplastic flow stress is 60-70MPa, the superplastic flow activation energy is 198-217kJ/mol, and it is close to α-Fe grain boundary self-diffusion activation energy. The super-plastic compressive constitute equations of this steel are correspondingly set up. Due to the finer microstructure of high frequency hardening, it appears bigger strain rate sensitivity value, smaller the steady superplastic flow stress and the superplastic flow activation energy, so it has better superplastic deformation capability.