High alumina slag is widely found in pyrometallurgical extractions of ferronickel,ferrochromium,and platinum group metals.The effects of MgO,Al_(2)O_(3),and CaO/SiO_(2) on the sulfur distribution ratio between high-al...High alumina slag is widely found in pyrometallurgical extractions of ferronickel,ferrochromium,and platinum group metals.The effects of MgO,Al_(2)O_(3),and CaO/SiO_(2) on the sulfur distribution ratio between high-alumina CaO–SiO_(2)–MgO–Al_(2)O_(3) slag and carbon-saturated iron were investigated.The slag consisted of Al_(2)O_(3) content in the range of 27.61–40.00 wt.%,CaO/SiO_(2) ratio of 0.8–1.1,and MgO content of 8–16 wt.%.The theoretical liquid areas of CaO–SiO_(2)–MgO–Al_(2)O_(3) slag were analyzed through the phase diagrams.The sulfur distribution ratio was measured via the slag–metal equilibrium technique at 1500ºC.It was observed that the sulfur distribution ratio increased with higher MgO content and higher CaO/SiO_(2) ratio largely due to the increase in free O^(2-)ions and the decrease in activity coefficient of sulfur ion in slag,but slightly decreased with the increasing Al_(2)O_(3) content because of the decrease in free O^(2-).展开更多
CaO-Al2O3-SiO2-CaF2-MgO was selected as the slag system for desulfurization in LF process.The reaction between steel and slag during desulfurization has been simulated by using Factsage software to study the influence...CaO-Al2O3-SiO2-CaF2-MgO was selected as the slag system for desulfurization in LF process.The reaction between steel and slag during desulfurization has been simulated by using Factsage software to study the influence of component on the sulfur distribution ratio.In order to research the influence of CaO content,aluminum powder content and its granularity on desulfurization,laboratory experiments have been carried out in a 200 kg inductive furnace.Results showed that the optimal composition of deep desulfurizer is wCaO=64% and aluminium powder 10% with a granularity of 30 μm.Industrial trials showed that the main composition range of final slag in LF process is wCaO=53.0%-57.0%,wAl2O3=23.4%-25.1%,wSiO2=8.1%-10.0%,and wCaF2=3.2%-4.7%.The sulfur mass percent in steel is lower than 0.0008% with a desulfurization rate above 89%.According to the result of industrial production,this desulfurizer could meet the production requirement for ultra-low sulfur steel,of which sulfur mass percent is under 0.0015%展开更多
基金The authors gratefully acknowledge the support from the National Natural Science Foundation of China Project(52104345)the Major Science and Technology Special Project of Yunnan Province(202002AB080001-1).
文摘High alumina slag is widely found in pyrometallurgical extractions of ferronickel,ferrochromium,and platinum group metals.The effects of MgO,Al_(2)O_(3),and CaO/SiO_(2) on the sulfur distribution ratio between high-alumina CaO–SiO_(2)–MgO–Al_(2)O_(3) slag and carbon-saturated iron were investigated.The slag consisted of Al_(2)O_(3) content in the range of 27.61–40.00 wt.%,CaO/SiO_(2) ratio of 0.8–1.1,and MgO content of 8–16 wt.%.The theoretical liquid areas of CaO–SiO_(2)–MgO–Al_(2)O_(3) slag were analyzed through the phase diagrams.The sulfur distribution ratio was measured via the slag–metal equilibrium technique at 1500ºC.It was observed that the sulfur distribution ratio increased with higher MgO content and higher CaO/SiO_(2) ratio largely due to the increase in free O^(2-)ions and the decrease in activity coefficient of sulfur ion in slag,but slightly decreased with the increasing Al_(2)O_(3) content because of the decrease in free O^(2-).
基金Sponsored by National Key Technology Research and Development Program in 11th Five-Year Plan of China(2007BAF08B01-03)
文摘CaO-Al2O3-SiO2-CaF2-MgO was selected as the slag system for desulfurization in LF process.The reaction between steel and slag during desulfurization has been simulated by using Factsage software to study the influence of component on the sulfur distribution ratio.In order to research the influence of CaO content,aluminum powder content and its granularity on desulfurization,laboratory experiments have been carried out in a 200 kg inductive furnace.Results showed that the optimal composition of deep desulfurizer is wCaO=64% and aluminium powder 10% with a granularity of 30 μm.Industrial trials showed that the main composition range of final slag in LF process is wCaO=53.0%-57.0%,wAl2O3=23.4%-25.1%,wSiO2=8.1%-10.0%,and wCaF2=3.2%-4.7%.The sulfur mass percent in steel is lower than 0.0008% with a desulfurization rate above 89%.According to the result of industrial production,this desulfurizer could meet the production requirement for ultra-low sulfur steel,of which sulfur mass percent is under 0.0015%