It is evident that matrix metalloproteinases (MMPs) are involved in the pathophysiology of different inflammatory skin diseases. In this pilot study, we investigated the ability of very high frequency ultrasound—frequencies of approximately 10 MHz—to modulate the activity of MMPs in the skin in inflammatory skin diseases such as acne and rosacea. It was shown that such waves can significantly improve the skin appearance in these diseases;however, the results are dependent on applied treatment schedule. The best results were obtained through the application of a super-fractionation strategy in the form of home treatments carried out twice daily.

表面加工状态对Super 304H钢抗蒸汽氧化性能的影响

对6种不同表面加工状态(磨床粗磨、砂轮磨削、320号砂纸研磨、600号砂纸研磨、1200号砂纸研磨和抛光)的Super 304H钢在650℃/25MPa超临界水蒸气中的氧化行为进行了研究,采用增重法对氧化1 200h后的试样单位表面上的质量变化进行了测量,采用扫描电镜(SEM)和能谱仪(EDS)对氧化膜表面和截面形貌、微观结构和元素分布进行了分析,并利用X射线衍射仪(XRD)对氧化膜物相进行了表征.结果表明:Super 304H钢的抗蒸汽氧化性能对材料的表面加工状态比较敏感;不同表面加工状态的Super 304H钢经氧化后,试样单位表面上的质量变化、表面氧化物形态以及横截面氧化物形态差异明显;形成的典型氧化膜分内、外2层,外层氧化膜主要为Fe3O4,内层氧化膜主要为含Cr量较高的(Fe,Cr)3O4以及少量的Cr2O3;随着材料表面粗糙度的增加和比表面应变层的形成,越容易形成具有保护性的富铬氧化膜,Super 304H钢的抗蒸汽氧化性能越好.

时效温度对Super 304H钢焊缝金属组织和韧性影响

采用光学显微镜、扫描电子显微镜、能谱仪、X射线衍射分析等方法并通过冲击试验,研究了时效温度600~700℃,500 h时效条件下Super 304H钢焊缝金属的组织和冲击韧性变化.结果表明,焊缝金属组织均为γ＋析出相,焊态焊缝组织中主要析出相种类为Nb（C,N）和富铜相,时效组织中析出相种类又新增加了M23C6;随时效温度升高,析出相数量不断增加,但Nb（C,N）的数量呈缓慢增加趋势,而M23C6的数量先快速析出后处于稳定;时效后焊缝金属的冲击功出现了显著降低,造成时效脆化的主要原因是时效过程中M23C6沿晶析出,而且析出量是决定因素.

基于Super-SBM模型的污水厂投资效率实证分析

随着我国对污水处理行业投资的不断增长,污水厂建设也得到了迅速的发展。由于污水厂建设具有投资规模大、投资周期长等特点,研究污水厂投资效率具有重要意义。本文针对传统的CCR模型没有考虑投入要素"松弛"和无法解决有效单元排序问题,运用Super-SBM模型对河南省新建13座污水厂投资效率进行了评价。结果表明:污水厂平均投资效率较高,但在建设单位管理费、征地移民、人员培训、勘察设计方面仍存在浪费资金现象。

时效处理Super304H不锈钢的晶间腐蚀敏感性

利用电化学动电位再活化法,研究了经650℃时效处理Super304H不锈钢晶间腐蚀敏感性的变化。结果表明,时效处理Super304H晶间腐蚀的主要原因是M_(23)C_6沿晶析出;M_(23)C_6在晶界的析出速度和析出量均随时间而变化,时效初期M_(23)C_6析出最快,晶间腐蚀敏感性快速增大,随时效时间延长M_(23)C_6析出数量增加,晶间腐蚀敏感性不断增大,增大速度与M_(23)C_6相对析出量增速有关。此外,M_(23)C_6不仅沿晶析出引发贫Cr型晶间腐蚀,在晶内析出也会导致周围贫Cr,促进腐蚀发生。

超微血流成像(SMI)及能量多普勒超声(PDUS)在类风湿关节炎达标治疗中的应用价值

目的 在类风湿关节炎(RA)达标治疗中比较分析SMI与PDUS两种成像模式的应用价值。方法 选取2022年1月至2024年1月于河南科技大学第一附属医院就诊的经临床治疗满足达标治疗标准的50例RA患者,对其双侧腕关节、双侧掌指关节及双侧近端指间关节共1 100个关节进行超声检查,分别启动SMI模式和PDUS模式,检测并比较50例RA患者关节缓解情况;记录并比较PDUS模式和SMI模式对关节滑膜内血流的显示率;结合Szkudlarek半定量评分,记录并比较PDUS模式和SMI模式对关节滑膜内血流的分级情况,并对两种检测模式进行一致性分析。结果 50例RA经治疗后满足达标治疗标准的患者中,PDUS模式缓解率58.00%(29/50),高于SMI模式缓解率46.00%(23/50),差异具有统计学意义(χ2=5.769,P=0.016)。对50例RA 1 100手腕关节,SMI模式滑膜血流显示率13.45%(148/1 100),高于PDUS模式7.73%(85/1 100),差异具有统计学意义(χ2=9.648,P=0.002)。Kappa滑膜血流分级一致性检验显示,PDUS模式与SMI模式具有较好的一致性(Kappa=0.727,P=0.032),但SMI模式血流分级显著高于PDUS模式,差异具有统计学意义(Z=-3.348,P=0.001)。结论 在RA达标治疗中,SMI模式和PDUS模式均就有一定临床应用价值,SMI较PDUS更能敏感地发现亚临床滑膜炎,并对滑膜血流强度进行评估,临床应用价值较高,为临床医生判断RA患者是否达到真正影像学缓解提供重要的参考信息。

MORA—Super生物共振诊断治疗仪治疗慢性过敏性疾病的临床研究

目的评价生物共振治疗仪治疗慢性过敏性疾病的疗效和安全性。方法治疗组采用德国MORA—Super生物共振诊断治疗仪对慢性过敏性疾病患者进行综合脱敏治疗，每周1次；对照组采用组织胺皮下注射脱敏治疗（常规脱敏治疗），每周2次。结果治疗组和对照组总有效率和痊愈率分别为76．8％、45．1％和48．5％、17．2％，治疗效果差异显著（P〈0．05）。结论生物共振诊．断治疗仪在诊治慢性过敏性疾病方面与传统的针刺法优势明显，治疗效果明显优于针刺法，而且治疗过程无痛苦、无创伤、不良反应少，值得在临床中推广使用。

超(超)临界锅炉用Super304H钢管研究试制

对Super304H的冶炼、冷加工、固溶热处理工艺进行了研究;观察了钢坯和钢管的显微组织。通过在EF和LF炉中深度脱硫,钢中硫的质量分数可达0.005%以下;钢坯中具有极少量的δ铁素体,钢管具有单相奥氏体组织;钢的冷加工硬化与其他18Cr-8Ni型不锈钢相当,冷加工性能优异,可采用类似的冷加工工艺;固溶热处理对钢管晶粒度有明显影响。试制钢管的化学成分及各项室温性能完全符合技术条件要求。

超(超)临界锅炉用Super304H钢管试制研究

Super304H是超(超)临界锅炉管用材,在我公司属首次试制。根据Super304H钢及钢管技术条件要求,对试制工艺进行了研究,着重对冶炼工艺和冷加工工艺进行了深入分析和研究。结果表明,通过在EF和LF炉中深度脱S,钢中S含量可以达到0.005%以下;观察了钢坯和钢管的显微组织,表明钢管具有单相奥氏体组织;钢的冷加工硬化试验也表明Super304H的冷加工性能优异,与其它18Cr-8Ni型不锈钢相当,采用类似的冷加工工艺完全可行;同时还研究了固溶热处理制度对钢管晶粒度的影响。试制结果表明,钢管的化学成分及各项室温性能,完全符合技术条件要求。

Electro-physical Properties of Super-thin Basalt Fiber Chemically Modified by Hydrochloric or Sulphuric Acid

The influence of hydrochloric or sulphuric acid treatment on the electro-physical properties of superthin basalt fiber (STBF) made from Armenian basalt rocks was studied. Specific electric resistance for direct and alternating currents, dielectric parameters of ε, and ε,, were measured. It is shown that specific resistance and dielectric parameters of super-thin basalt fiber change essentially after hydrochloric or sulphuric acid treatment. The temperature dependences of these parameters were studied, too, and their non–monotonic behavior was observed. The probable variation of mentioned STBF parameters is explained by different water absorption capacity of pores as a result of acid treatment.

某超高层建筑混凝土梁开裂原因分析与处理

现浇钢筋混凝土结构在我国的超高层建筑中大量应用。混凝土开裂是目前许多现浇混凝土结构中较易发生的质量问题。混凝土开裂不仅影响美观,也易引起内部钢筋锈蚀,降低结构的耐久性,甚至会影响结构安全。本文基于某新建超高层建筑中混凝土梁普遍开裂的实例,通过现场调查、检测,以及对设计和施工资料的分析,分析混凝土梁的开裂原因,并结合现场实际情况提出相应的处理意见,以期对类似的工程质量问题的检测、鉴定和处理提供参考。

超级铁精矿深度提纯试验研究

为探索化学法获取超纯铁精矿的可能性,以国内某铁矿选厂的超级铁精矿为原料,分别以硫酸—氟化钠和硫酸—氢氧化钠为浸出剂开展提纯试验。结果表明:①经过硫酸—氟化钠联合处理,在硫酸浓度10%、矿浆浓度15%、氟化钠用量14 g/L,30℃恒温反应1 h的条件下,可以得到铁品位为72.12%、铁回收率为94.23%的超纯铁精矿。②经过硫酸—氢氧化钠联合处理,在一阶段硫酸浓度10%、矿浆浓度15%、30℃恒温反应1 h,二阶段氢氧化钠用量160 g/L、液固比6 mL/g、80℃恒温反应2 h的条件下,可以得到铁品位为72.14%、铁回收率为99.67%的超纯铁精矿。硫酸—氟化钠联合处理法比硫酸—氢氧化钠联合处理法简洁,但铁回收率较低,含氟废水需处理后才能排放;硫酸—氢氧化钠联合处理法铁回收率较高,生产成本也较高。与常规选矿工艺提升铁品位的方式相比,化学处理法能更深度地纯化铁精矿。

固溶处理对电弧增材制造超级双相不锈钢微观组织及摩擦磨损性能的影响

采用直径为1.2 mm的ER2594-超级双相不锈钢焊丝进行了多层单道墙体电弧增材试验,对增材件分别进行1050、1150和1250℃的固溶处理,并在固溶处理后对各试样进行了往复式摩擦磨损试验.试验结果表明:随着固溶温度的升高,双相比中的铁素体含量增加,其显微硬度也相应提高.此外,固溶处理可降低增材件的内应力,最终基于较高硬度和较低内应力的协同作用,在1250℃时获得耐磨性能较优的试样,有效地提升了热处理后增材件试样的摩擦磨损性能.

超大型污水厂超水量负荷高效能运行研究

以上海某超大型污水厂作为研究对象,开展了1.4倍超水量负荷高效能运行试验,考察了污水厂在夏季汛期超水量负荷条件下的过流能力和生物处理系统效能。试验时长为37 h,污水厂进水水力平均负荷为设计处理量的1.418倍,最高瞬时水力负荷达1.803倍,进水COD、NH_(4)^(+)-N、TN和TP浓度分别维持在250、20、25、4.5 mg/L以下,出水COD、NH_(4)^(+)-N、TN和TP浓度分别在25、0.2、8、0.2 mg/L以下,出水水质满足一级A排放标准。1.4倍超水量负荷对污水厂预处理、生物处理、二沉池等工艺段过流能力影响不大,对中间提升泵房前池液位有一定影响,污水厂设施设备运行情况整体稳定。结果表明,在夏季汛期,污水厂可实现短期内在1.4倍超水量负荷下安全稳定运行,能够初步应对汛期进水流量突增情况,最大程度的减少汛期污水溢流。

超大型大水冶金矿山水处理工艺创新优化

随着井下施工与开采技术的进步,井下排水中含有的杂质越来越难以处理,大水金属矿山面临着排水量大、排出水水质较差、政府环保管控严格等难题,国内外尚无技术可借鉴,因此大水冶金矿山水处理工艺优化势在必行。当前常规冶金矿山水处理工艺处理成本高且难以适应当前矿山井下排水水质,导致施工、采矿成本高,经济效益差。因此创新优化大水冶金矿山水处理工艺,是创建绿色矿山和清洁生产的关键研究课题。为此,河钢矿业作为国内超大型矿山的生产建设基地之一,水处理项目组开展超大型大水冶金矿山基建期井下排水处理工艺优化技术攻关,并实现工业化应用,不仅能够获得显著的经济效益和环保效益,而且为矿山排水处理探索出一条途径。

基于数据包络分析的中国污染地块治理绩效评价研究

中国高速的城市化进程产生了大量工业企业搬迁,造成众多污染地块需要治理。中国为治理污染地块耗资巨大,但缺乏相关的绩效评价。筛选了40个典型污染地块治理工程(涉及全国33个区县)进行绩效评价并探究了污染地块治理绩效的影响因素。结果表明:(1)山东省、河北省及湖南省中南部地区的污染地块治理绩效较高,重庆市、湖南省等华中地区及东南沿海地区零星有一些污染地块治理绩效相对较低。(2)地块尺度,资金投入不足、时间投入过短、人员投入过少是影响污染地块治理绩效的重要因素,期望产出方面也仍有很大提升空间,非期望产出方面需要进一步控制污染排放。(3)区县尺度,污染地块治理绩效主要与工业增加值占国内生产总值比例和年末总人口呈显著(p<0.05)正相关,说明经济和人口是主要影响因素。

旋转超重力场净化沥青烟颗粒物的研究

沥青在加热使用过程中产生大量沥青烟颗粒物,为了克服传统的过滤法容易堵塞滤料、喷淋塔水洗法净化率不高、静电捕集法存在着火隐患等不足。本文研究了旋转超重力机转子外腔体进气,内腔体喷水条件下,转子转速、喷水量、气体流量等参数对沥青烟颗粒物去除率的影响规律。研究发现:沥青烟颗粒物去除率随转速增加而增大,在低转速阶段转速对去除率的影响较大,高转速阶段转速对去除率影响增幅减缓。在不喷水条件下去除率较低,喷水可以有效提高去除率。随入口气体流量增加去除率降低,缩短了停留时间。在本研究最优化条件下最高去除率为99.2%。研究表明超重力机能够有效净化沥青烟颗粒物,为沥青烟颗粒物净化提供一种新技术,具有环保意义和应用价值。

超选择性肾动脉栓塞治疗不同病因肾出血的疗效评估

目的评估超选择性肾动脉栓塞治疗不同病因肾出血的疗效及安全性。方法收集2018年7月至2023年6月安徽医科大学第三附属医院/合肥市第一人民医院收治的18例不同病因导致肾出血患者的临床资料,所有患者均在内科保守治疗效果不佳或要求介入治疗后采用了超选择性肾动脉栓塞治疗。观察所有患者的术中造影表现、介入栓塞治疗效果及介入术后并发症发生情况。结果18例患者术中造影表现均为阳性,其中,11例患者表现为单纯造影剂聚集或外溢;2例患者表现为造影剂外溢合并动静脉畸形;1例患者表现为造影剂外溢合并假性动脉瘤;4例患者表现为靶血管增粗,分支杂乱,部分可见瘤样扩张。18例患者术后活动性出血停止,肉眼血尿逐渐好转至消失,肾周血肿逐渐吸收,术后血红蛋白水平高于术前(P﹤0.05),治疗有效率为100%。2例患者术后发生轻度栓塞后综合征。所有患者均未出现严重并发症。除了2例透析患者外,其余16例患者术后肾功能均正常。结论超选择性肾动脉栓塞治疗肾出血的疗效显著,创伤性小,对肾功能无明显损伤,安全性高,可作为内科保守治疗效果不佳的各种病因所致肾出血患者的首选治疗方法。

滨海回填区深基坑支护技术分析

滨海回填区具有地质环境复杂、软弱层较厚、地下水位高等带来的基坑开挖难度大的特点,寻找一种既安全又经济的基坑支护方式为滨海回填区基坑支护设计的一大难题。文章以深圳机场站前综合配套保障用房项目基坑支护工程为例,根据不同区域的地质情况以及后续施工工艺要求,分别采用“锚桩+三轴搅拌桩”、“双排灌注桩+三轴搅拌桩”、“复合土钉墙”3种支护方式,开挖过程中采用现场监测以及数值模型分析坑支护结构的水平与竖向位移值均小于预警值。研究结果表明:滨海回填区有针对性的按区域分段选择支护技术,可以将支护结构的变形控制在限值范围内,满足支护结构安全,且具有较好的经济性,可为滨海回填区深大基坑的开挖提供一定的指导和借鉴。

基于SBM-DEA和云模型的农村生活污水治理效率评价——来自中国27个省份2011—2020年面板数据的分析

农村生活污水治理问题一直是农村人居环境领域备受关注的重要难题之一。尽管针对这一问题的投资逐年增加,但治理效果并不尽如人意。为此,有必要对农村生活污水治理效率进行科学测算,以推动实现宜居宜业和美乡村的目标。通过构建三阶段超效率SBM-DEA模型结合云模型,以2011—2020年全国27个省份的面板数据为基础,对我国农村生活污水治理效率进行评价,并分析不同区域间的差异。研究发现:(1)随机误差和外部环境因素对农村生活污水治理效率产生显著影响;(2)排除随机误差和外部环境因素的影响后,我国农村生活污水治理效率得到改善,仍存在较大提升空间;(3)27个省份的农村生活污水治理效率呈现“两头小、中间大”的态势,同时东部地区的治理效率较高,中部地区的效率相对较低,而东北和西部地区的治理效率波动明显。各省份之间的农村生活污水治理效率存在显著差异。