A catalyst-free novel synthesis of diethyl carbonate from ethyl carbamate in supercritical ethanol

Diethyl carbonate has been synthesized via the alcoholysis of ethyl carbamate in supercritical ethanol under catalyst-free conditions.The influences of various parameters such as reaction temperature,reaction time,reaction pressure,ethanol/ethyl molar ratios and reaction loading volume on the yield of DEC were studied systematically.The experimental results indicated that the alcoholysis of ethyl carbamate was greatly improved in supercritical ethanol.The optimal reaction conditions were as follows：a reaction temperature of 573 K,a reaction time of 30 min,a reaction pressure of 13.2 MPa,an ethanol/ethyl carbamate molar ratio of 10 and a reactor loading volume of 285 μL respectively.The optimal yield of DEC was 22.9%.

碱性氧化物催化氨基甲酸乙酯与乙醇合成碳酸二乙酯

在釜式反应器中,以碱性氧化物为催化剂,对尿素与乙醇合成碳酸二乙酯(DEC)的决速步骤氨基甲酸乙酯(EC)与乙醇反应合成DEC进行了活性测试,并采用CO2-TPD方法表征了催化剂的碱性质,研究了碱性氧化物的碱性质与催化活性的关系,同时考察了反应温度、反应时间和催化剂用量对DEC合成反应的影响。实验结果表明,CaO具有最佳的催化活性,这是因为CaO表面具有最强的碱性位;以CaO为催化剂合成DEC的最佳反应条件为:EC 0.1 g、乙醇1.0 mol、反应温度190℃、反应时间9 h、催化剂用量1.0 g;在此条件下,EC转化率为40.7%,DEC收率为20.8%。表征结果显示,碱性氧化物的碱强度是影响其催化活性的重要因素,其表面碱性位可与乙醇中的羟基作用释放Hδ+,从而活化乙醇,促进DEC的合成。

氧化铅催化氨基甲酸乙酯与乙醇合成碳酸二乙酯

在间歇反应器中,对尿素醇解法合成碳酸二乙酯(DEC)的控制步骤——氨基甲酸乙酯(EC)与乙醇合成DEC的反应进行了研究。采用热分解法制备了一系列金属氧化物催化剂,对其催化EC与乙醇合成DEC的反应性能进行了评价。实验结果表明,氧化铅的催化活性最高。确定了氧化铅催化剂的适宜制备条件:以PbCO3为前体,在300℃下焙烧4h。活性评价结合X射线衍射分析结果表明,四方晶相PbO有利于EC与乙醇合成DEC。氧化铅催化剂催化合成DEC的优化反应条件为:n(乙醇):n(EC)=10、催化剂用量1%(占总物料量的质量分数)、反应温度180℃、反应时间7h。在此条件下,EC转化率为36.0%,DEC选择性为45.0%,DEC收率为16.2%。

氧化铅在氨基甲酸乙酯与乙醇合成碳酸二乙酯反应中的催化作用

研究了氧化铅在氨基甲酸乙酯(EC)与乙醇反应合成碳酸二乙酯(DEC)中的催化作用.结果表明,氧化铅具有很好的稳定性,重复使用5次,其催化活性无明显下降.回收的催化剂为立方晶相金属Pb和斜方晶相PbO2的混合物,结合反应结果可认为,该混合物为反应的活性组分.结果还发现,PbO与DEC反应是PbO被还原为Pb的主要原因.