Mesoporous titania （meso-TiO2） has received extensive attention owing to its versatile potential applications. This paper reports a low-temperature templating approach for the fabrication of meso-TiO2 using the pero...Mesoporous titania （meso-TiO2） has received extensive attention owing to its versatile potential applications. This paper reports a low-temperature templating approach for the fabrication of meso-TiO2 using the peroxo titanic acid （PTA） sol as precursor and Pluronic P123 as nonionic template. The TGA, XRD, N2 sorption, FE-SEM and HRTEM were used to characterize the obtained samples. The results showed that meso-TiO2 with high surface area up to 163 m2.g^-1 and large pore volume of 0.65 cm3.^-1 can be obtained. The mesopore sizes can be varied between 13 and 20 nm via this synthesis approach. The amount of P123 and the calcination conditions were found to have great influence on the mesoporous and crystalline structures of meso-TiO2. The photocatalytic activity testing clearly shows that the high surface area and bi-crystallinity phases of meso-TiO2 play important roles in enhancing photocatalytic properties of meso-TiO2 in photo-decomposing Rhodamine B in water.展开更多
In this study, novel molecularly imprinted open porous membranes（MIOPMs） were prepared using the Pickering HIPEs template method and molecular imprinting technology for selective adsorption and separation of methyl ...In this study, novel molecularly imprinted open porous membranes（MIOPMs） were prepared using the Pickering HIPEs template method and molecular imprinting technology for selective adsorption and separation of methyl 4-hydroxybenzoate（M4HB）. The template M4 HB, functional monomers,crosslinker and plastifier 2-ethylhexyl acrylate（2-EHA） were contained in the oil phase. Hydrophobic silica nanoparticles（HNP-SiO2） were employed as a stabilizer to establish stable W/O Pickering HIPEs with nonionic surfactant sorbitantrioleate（Span 85）. The results of SEM and FTIR indicated that the optimal MIOPMs were prepared successfully and possessed open and interconnecting pores. Then, the MIOPMs were used as sorbents for M4 HB. The correlation coefficient（R^2） values for the Langmuir–Freundlich isotherm model and pseudo-second-order kinetic model fitting to the adsorption equilibrium and kinetic data respectively were all higher than 0.95. The maximum adsorption capacity and the time of rapid adsorption for MIOPM4 were 4.146 mg g^-1 and 100 min, respectively. In addition, the permeability separation factor of MIOPMs for M4 HB compared to a structurally related analog methyl2-hydroxybenzoate（M2HB） could reach 3.122.展开更多
基金Acknowledgements This work was supported by the National Natural Science Foundation of China （Grant Nos. 21201030, 21471026 and 51272039）, the Fundamental Research Funds for the Central Universities （N141005001, L1502020 and N130810003） and the Liaoning Province Innovation Funds （Grant No. 2014020030）.
文摘Mesoporous titania （meso-TiO2） has received extensive attention owing to its versatile potential applications. This paper reports a low-temperature templating approach for the fabrication of meso-TiO2 using the peroxo titanic acid （PTA） sol as precursor and Pluronic P123 as nonionic template. The TGA, XRD, N2 sorption, FE-SEM and HRTEM were used to characterize the obtained samples. The results showed that meso-TiO2 with high surface area up to 163 m2.g^-1 and large pore volume of 0.65 cm3.^-1 can be obtained. The mesopore sizes can be varied between 13 and 20 nm via this synthesis approach. The amount of P123 and the calcination conditions were found to have great influence on the mesoporous and crystalline structures of meso-TiO2. The photocatalytic activity testing clearly shows that the high surface area and bi-crystallinity phases of meso-TiO2 play important roles in enhancing photocatalytic properties of meso-TiO2 in photo-decomposing Rhodamine B in water.
基金financially supported by the National Natural Science Foundation of China(Nos.21406085,21207051)
文摘In this study, novel molecularly imprinted open porous membranes（MIOPMs） were prepared using the Pickering HIPEs template method and molecular imprinting technology for selective adsorption and separation of methyl 4-hydroxybenzoate（M4HB）. The template M4 HB, functional monomers,crosslinker and plastifier 2-ethylhexyl acrylate（2-EHA） were contained in the oil phase. Hydrophobic silica nanoparticles（HNP-SiO2） were employed as a stabilizer to establish stable W/O Pickering HIPEs with nonionic surfactant sorbitantrioleate（Span 85）. The results of SEM and FTIR indicated that the optimal MIOPMs were prepared successfully and possessed open and interconnecting pores. Then, the MIOPMs were used as sorbents for M4 HB. The correlation coefficient（R^2） values for the Langmuir–Freundlich isotherm model and pseudo-second-order kinetic model fitting to the adsorption equilibrium and kinetic data respectively were all higher than 0.95. The maximum adsorption capacity and the time of rapid adsorption for MIOPM4 were 4.146 mg g^-1 and 100 min, respectively. In addition, the permeability separation factor of MIOPMs for M4 HB compared to a structurally related analog methyl2-hydroxybenzoate（M2HB） could reach 3.122.