(Nd_(0.5)Ta_(0.5))^(4+)复合离子对BNT-BKT陶瓷微结构及电学性能的影响

采用固相烧结法制备了(Nd_(0.5)Ta_(0.5))^(4+)复合离子调控的Bi_(0.5)(Na_(0.82)K_(0.18))_(0.5)Ti_(1-x)(Nd_(0.5)Ta_(0.5))_xO_3(BNKT-xNT)无铅陶瓷。研究了(Nd_(0.5)Ta_(0.5))^(4+)复合离子掺杂量对BNKT陶瓷的表面形貌、微观结构,以及铁电、介电、储能、阻抗等电学性能的影响。研究结果表明:(Nd_(0.5)Ta_(0.5))^(4+)复合离子进入了BNKT陶瓷的B位并形成了单一的钙钛矿结构;晶粒分布均匀、致密,晶界清晰;(Nd_(0.5)Ta_(0.5))^(4+)复合离子的引入显著降低了BNKT陶瓷的剩余极化强度、饱和极化强度以及矫顽场,电滞回线变得瘦小、细长,储能效率随之升高,并在x=0.08和60×10~3 V/cm电场下达到了70%;储能密度先减小、后增大、再减小,在x=0.04时达到最大值0.36 J/cm^3;电致应变在x=0.03时最大为0.183%;随着掺杂含量的增加,BNKT-xNT陶瓷从铁电相与弛豫铁电相共存转变为弛豫铁电相,其介电常数峰T_m逐渐降低且平坦化;交流阻抗谱表明BNKT-xNT陶瓷在低温下具有良好的绝缘性。