An annealed TC4 titanium alloy sheet was treated by high density electropulsing(Jmax=(5.09-5.26)×103A/mm2,tp=110μs)under ambient conditions.The effect of electropulsing treatment(EPT)on the plastic deformation b...An annealed TC4 titanium alloy sheet was treated by high density electropulsing(Jmax=(5.09-5.26)×103A/mm2,tp=110μs)under ambient conditions.The effect of electropulsing treatment(EPT)on the plastic deformation behavior of TC4 titanium alloysheet was studied using uniaxial tension tests.The experimental results indicate that electropulsing treatment significantly changesthe mechanical properties of sheet metal:the uniform elongation is increased by 35%,the yield stress is decreased by 19.8%and theyield to tensile ratio is decreased by 17.6%.It is of significant meaning to improve the formability of TC4 titanium alloy sheet.Theoptical microscope and scanning electron microscope(SEM)were used to examine the changes of the microstructure and the fracturemorphology before and after the electropulsing treatment.It is found that recrystallization occurs in the sheet metal and dimples infracture surface are large and deep after the electropulsing treatment.The research results show that the electropulsing treatment is aneffective method to improve the formability of titanium alloy sheets.展开更多
对TC4钛合金薄板进行高真空电子束焊接,结合室温拉伸试验和硬度试验,研究了焊接接头的显微组织及性能。结果表明,焊缝和热影响区的组织内部均析出了针状的α＇马氏体,焊缝中心单位面积内析出的该相比热影响区较多。随着焊接速度的增大,...对TC4钛合金薄板进行高真空电子束焊接,结合室温拉伸试验和硬度试验,研究了焊接接头的显微组织及性能。结果表明,焊缝和热影响区的组织内部均析出了针状的α＇马氏体,焊缝中心单位面积内析出的该相比热影响区较多。随着焊接速度的增大,接头抗拉强度和断面收缩率均先增大后减小。焊接接头的显微硬度分布为距离焊缝中心越远,硬度越小。焊缝的显微硬度比热影响区硬度平均高25~30 HV,热影响区的显微硬度比母材硬度平均高20~30HV。在电子束流为17 m A、聚焦电流为498 m A、焊接速度为1000 mm/min下焊接,焊接效果较好。展开更多
文摘An annealed TC4 titanium alloy sheet was treated by high density electropulsing(Jmax=(5.09-5.26)×103A/mm2,tp=110μs)under ambient conditions.The effect of electropulsing treatment(EPT)on the plastic deformation behavior of TC4 titanium alloysheet was studied using uniaxial tension tests.The experimental results indicate that electropulsing treatment significantly changesthe mechanical properties of sheet metal:the uniform elongation is increased by 35%,the yield stress is decreased by 19.8%and theyield to tensile ratio is decreased by 17.6%.It is of significant meaning to improve the formability of TC4 titanium alloy sheet.Theoptical microscope and scanning electron microscope(SEM)were used to examine the changes of the microstructure and the fracturemorphology before and after the electropulsing treatment.It is found that recrystallization occurs in the sheet metal and dimples infracture surface are large and deep after the electropulsing treatment.The research results show that the electropulsing treatment is aneffective method to improve the formability of titanium alloy sheets.
文摘对TC4钛合金薄板进行高真空电子束焊接,结合室温拉伸试验和硬度试验,研究了焊接接头的显微组织及性能。结果表明,焊缝和热影响区的组织内部均析出了针状的α＇马氏体,焊缝中心单位面积内析出的该相比热影响区较多。随着焊接速度的增大,接头抗拉强度和断面收缩率均先增大后减小。焊接接头的显微硬度分布为距离焊缝中心越远,硬度越小。焊缝的显微硬度比热影响区硬度平均高25~30 HV,热影响区的显微硬度比母材硬度平均高20~30HV。在电子束流为17 m A、聚焦电流为498 m A、焊接速度为1000 mm/min下焊接,焊接效果较好。