Anodic oxide films grown on titanium alloy Ti-10V-2Fe-3Al in the solution of sodium tartrate, then sealed in boiling deionised water and calcium acetate solution were observed by using field emission scanning electron...Anodic oxide films grown on titanium alloy Ti-10V-2Fe-3Al in the solution of sodium tartrate, then sealed in boiling deionised water and calcium acetate solution were observed by using field emission scanning electron microscopy （FE-SEM）, and were chemically analysed by using energy dispersive spectroscopy （EDS）. Corrosion behaviour was investigated in a 3.5% sodium chloride solution, using electrochemical impedance spectroscopy （EIS）. The morphology of the anodic oxide films was dependent on the sealing processes. The surface sealed in calcium acetate solution presented a more homogeneous and smooth structure compared with that sealed in boiling deionised water. The corrosion resistance of the oxide films sealed in calcium acetate solution was better than that sealed in boiling deionised water.展开更多
The microstructure evolution and formability of Ti-10V-2Fe-3Al alloy related to the initial microstructures and processing variables were investigated during hot forming process. The experimental results show that the...The microstructure evolution and formability of Ti-10V-2Fe-3Al alloy related to the initial microstructures and processing variables were investigated during hot forming process. The experimental results show that the α-phase growth is controlled by solute diffusion during the heat treatment processes. Four different microstructures were established by combinations of several heat treatments, and Ti-10V-2Fe-3Al alloy shows excellent formability both above and below the β transus temperature. The alloy possesses low deformation resistance and active restoration mechanism during the deformation. A constitutive equation describing the hot deformation behavior of Ti-10V-2Fe-3Al alloy was obtained. Higher fl ow stress was observed for the acicular morphology of α phase in microstructures with large aspect ratios as compared with that of small aspect ratios. Due to the dynamic recovery in soft β phase, and the dynamic recrystallization and breakage of acicular α-phase, fl ow softening occurred signifi cantly during deformation. Dynamic recrystallization also occurred especially in the severely deformed regions of forged parts.展开更多
Effect of β-flecks on properties of tensile elongation and low cycle.fatigue life at room tern. perature for Ti-10V-2Fe-3Al alloy has been investigated.The cracks along initial β-grain boundaries in the β-fleck reg...Effect of β-flecks on properties of tensile elongation and low cycle.fatigue life at room tern. perature for Ti-10V-2Fe-3Al alloy has been investigated.The cracks along initial β-grain boundaries in the β-fleck region may propagate to form intergranular brittle fracture.Under alternating load,the β-fleck often becomes a fatigue origin.While under higher strain,the cracks initiate and propagate to fracture early at the original β-grain boundaries in β-fleck region and at α-grain boundaries.展开更多
基金Supported by the National Natural Science Foundation of China(No.51271012)
文摘Anodic oxide films grown on titanium alloy Ti-10V-2Fe-3Al in the solution of sodium tartrate, then sealed in boiling deionised water and calcium acetate solution were observed by using field emission scanning electron microscopy （FE-SEM）, and were chemically analysed by using energy dispersive spectroscopy （EDS）. Corrosion behaviour was investigated in a 3.5% sodium chloride solution, using electrochemical impedance spectroscopy （EIS）. The morphology of the anodic oxide films was dependent on the sealing processes. The surface sealed in calcium acetate solution presented a more homogeneous and smooth structure compared with that sealed in boiling deionised water. The corrosion resistance of the oxide films sealed in calcium acetate solution was better than that sealed in boiling deionised water.
基金Funded by the National Natural Science Foundation of China(Nos.51222405 and 51474063)
文摘The microstructure evolution and formability of Ti-10V-2Fe-3Al alloy related to the initial microstructures and processing variables were investigated during hot forming process. The experimental results show that the α-phase growth is controlled by solute diffusion during the heat treatment processes. Four different microstructures were established by combinations of several heat treatments, and Ti-10V-2Fe-3Al alloy shows excellent formability both above and below the β transus temperature. The alloy possesses low deformation resistance and active restoration mechanism during the deformation. A constitutive equation describing the hot deformation behavior of Ti-10V-2Fe-3Al alloy was obtained. Higher fl ow stress was observed for the acicular morphology of α phase in microstructures with large aspect ratios as compared with that of small aspect ratios. Due to the dynamic recovery in soft β phase, and the dynamic recrystallization and breakage of acicular α-phase, fl ow softening occurred signifi cantly during deformation. Dynamic recrystallization also occurred especially in the severely deformed regions of forged parts.
文摘Effect of β-flecks on properties of tensile elongation and low cycle.fatigue life at room tern. perature for Ti-10V-2Fe-3Al alloy has been investigated.The cracks along initial β-grain boundaries in the β-fleck region may propagate to form intergranular brittle fracture.Under alternating load,the β-fleck often becomes a fatigue origin.While under higher strain,the cracks initiate and propagate to fracture early at the original β-grain boundaries in β-fleck region and at α-grain boundaries.