Welding voltage and current in arc signals are directly related to arc stability and welding quality.Process experiments with different parameters were organized according to the orthogonal experimental design method ...Welding voltage and current in arc signals are directly related to arc stability and welding quality.Process experiments with different parameters were organized according to the orthogonal experimental design method by constructing an aluminum alloy double-pulse metal inert gas(MIG)welding arc electric signal test platform.The data acquisition system of the aluminum alloy MIG welding process was established to obtain real-time arc signal information reflecting the welding process.The aluminum alloy’s collected double-pulse arc current signals are decomposed adaptively by broadband mode decomposition(BMD).The direct current(DC)signal,pulse signal,distortion signal,ripple signal,and noise signal are separated and extracted,and the composite multiscale fuzzy entropy(CMFE)is calculated for the component set of the electrical signal.The experimental results show that the current waveform obtained by the double-pulse MIG welding current signal is consistent with the corresponding weld forming diagram.Simultaneously,the composite multiscale fuzzy entropy is calculated for the arc characteristic parameters.The rationality of matching process parameters and arc stability of aluminum alloy’s double-pulse MIG welding were evaluated.展开更多
The effects of vanadium(V)on the microstructures and mechanical properties of the TiC cermet fusion welding interface were studied by adjusting the content of V in the self-developed flux-cored wires using metal inert...The effects of vanadium(V)on the microstructures and mechanical properties of the TiC cermet fusion welding interface were studied by adjusting the content of V in the self-developed flux-cored wires using metal inert gas arc(MIG)welding for surfacing on the TiC cermet.The results show that the increase in V content promotes the element diffusion between TiC cermet and weld metal.There are no de-fects observed in the interface,and the diffusion of elements refers to excellent metallurgical bonding.The shear strength of the fusion zone initially decreases and then increases with the increase in V content.The maximum shear strength of the TiC cermet/weld interface,reaching 552 MPa,occurred when the V content reached 0.65%.Meanwhile,the average hardness in the transition zone reached 488.2 HV0.2.展开更多
Repair welding of AA 6082-T6 joints was carried out using ER 4043 filler through the TIG welding process with or without pulsed current.Microstructure and mechanical characteristics of the joints before and after repa...Repair welding of AA 6082-T6 joints was carried out using ER 4043 filler through the TIG welding process with or without pulsed current.Microstructure and mechanical characteristics of the joints before and after repairing were investigated by examining macrostructure,microstructure,and distributions of porosity in the weld metal(WM),and by hardness,tensile,and bending tests.We observed that the welding current,phase transformations in heat-affected zone(HAZ)and porosity introduced in the WM during welding influence on its mechanical properties in sequence.The experimental results showed that the bead width and penetration as well as size of pores in the joints were mainly influenced by the welding currents.The sound joints were obtained at a welding current of 140 A with or without pulsed current when welding speed and gas flow rate were set at 20 cm·min-1 and 15 L·min-1,respectively.Among them,the decrease in mechanical properties of repair weld(RW)was directly related to the phase transformations in the over-ageing zone due to the double welding thermal cycles and elevated distribution of porosity in the WM.In addition,it was observed that the comparatively smaller grain size and lower porosity in WM of the RW produced by pulsed TIG welding gave a positive effect on its mechanical properties.展开更多
The effect of current on the morphology of Al alloy T-joint in double-pulsed metal inert gas(DP-MIG) welding process was investigated by simulation and experiment.A three-dimensional finite element model and the DP-...The effect of current on the morphology of Al alloy T-joint in double-pulsed metal inert gas(DP-MIG) welding process was investigated by simulation and experiment.A three-dimensional finite element model and the DP-MIG heat source of double-ellipsoidal volumetric model were developed to simulate the temperature and stress fields under different welding conditions.The macro-morphology and microstructure of welding joints at the corresponding currents were observed in the experiment.The results show that the best condition is at an average current of 90 A and current difference of 40 A,when the maximum temperature is 200 °C higher than the fusion points,with the temperature difference of about 100 °C and stress change of 10 MPa between thermal pulse and thermal base.Under these conditions,Al alloy T-joint with proper fusion condition has smooth fish-scale welding appearance and finer microstructure.Furthermore,the thermal curves and stress distribution in the experiment are consistent with those in the simulation,verifying the precision of the welding simulation.展开更多
A device for superimposing vibration on workpiece in both horizontal and vertical directions during tungsten-arc inert gas (TIG) welding was developed, with maximum power output of 2 kW at frequency of 15 kHz. AZ31 ...A device for superimposing vibration on workpiece in both horizontal and vertical directions during tungsten-arc inert gas (TIG) welding was developed, with maximum power output of 2 kW at frequency of 15 kHz. AZ31 sheets with thickness of I and 3 mm were used in the vibratory welding. Microstructures along with the mechanical properties of the weld joints under different vibrating conditions (vibration direction, vibration amplitude and groove angle) were examined. It is observed that the grain size in welding zone decreases remarkably with the application of vibration, while the amount of second phase β-Mg_17Al_12 within the zone decreases slightly; meanwhile, microhardness of the weld joints, macroscopic tensile strength and elongation of the weldment increase. Vibration, especially the one along vertical direction, has more impact on the performance of the thick weldments. Influence of vibration on mierostructure and mechanical properties of weldments is affected by wave energy transferring in the melt and depends on the processing and geometric parameters including amplitude and direction of vibration, thickness, and groove angles.展开更多
采用TIG(Tungsten inert gas welding,TIG)焊对FeCrAl合金管同质材料进行焊接,通过扫描电子显微镜、透射电子显微镜及能谱仪等手段研究了焊后接头的显微组织特征、焊后接头不同区域氧化物颗粒的分布情况及焊接接头的力学性能。FeCrAl合...采用TIG(Tungsten inert gas welding,TIG)焊对FeCrAl合金管同质材料进行焊接,通过扫描电子显微镜、透射电子显微镜及能谱仪等手段研究了焊后接头的显微组织特征、焊后接头不同区域氧化物颗粒的分布情况及焊接接头的力学性能。FeCrAl合金TIG焊通过填充等成分的FeCrAl合金丝材进行焊接,焊后焊接接头主要由焊缝区、热影响区及母材组成。其中焊缝区为粗大的铁素体组织,热影响区为细小的等轴晶组织。焊缝区的Y_(2)O_(3)氧化物颗粒发生了明显粗化并与基体反应生成复合氧化物Y_(3)Al_(5)O_(12)。TIG焊焊接FeCrAl合金管热处理后,焊接接头最大抗拉强度值为530 MPa,约为母材强度的80.8%,可以实现大口径、大壁厚的FeCrAl合金管材的对接接头的力学性能要求。展开更多
Tungsten inert gas weld was carried out on super-light magnesium-lithium alloy plates with a thickness of 2 mm, using argon gas as a protecting atmosphere. The microstructure and mechanical properties of the welded jo...Tungsten inert gas weld was carried out on super-light magnesium-lithium alloy plates with a thickness of 2 mm, using argon gas as a protecting atmosphere. The microstructure and mechanical properties of the welded joints were investigated. The results indicate that the microstructure in the fusion zone is fine, and the microstructure in the heat-affected zone is coarser than the parent metal. The tensile strength of the welded joint is about 84% that of the parent metal. The fracture occurs in a mixed type of toughness and brittleness in the heat-affected zone. During the welding process, aluminum and cerium are enriched at grain boundaries in the fusion zone.展开更多
Welding research of A6N01S-T5 aluminum alloy profile for high-speed train was done by using laser-MIG hybrid welding and MIG welding individually. And the weld appearance,welding distortion,mechanical properties of th...Welding research of A6N01S-T5 aluminum alloy profile for high-speed train was done by using laser-MIG hybrid welding and MIG welding individually. And the weld appearance,welding distortion,mechanical properties of the joints and microstructures were analyzed. The test results demonstrated that high-efficient welding for the profile can be achieved by using laser-MIG hybrid welding,the speed of which can be over 3. 0 m/min. The processing had a good gap bridging ability,even if the gap of the butt joint was up to 2. 0 mm,a good weld appearance can also be got. While the hybrid welding speed was greater than 2. 5 m/min,the welding distortion of the laser-tandem MIG hybrid joints was just about 33% of that of the MIG joints,but the welding efficiency was over 3 times of MIG welding. And tensile strength of the hybrid joints was 85% of that of A6N01S-T5 base metal,9% higher than that of the MIG joints. Fatigue properties was tested individually with pulsed tensile fatigue method in the condition of 1 × 10~7 lifetime. The test results demonstrated that the fatigue strength of the joints was a little lower than that of base material,which could be up to 115 MPa. But the fatigue strength of hybrid welding joints was 107. 5 MPa,which was 23% higher than 87 MPa of MIG welding joints.展开更多
The ultrasonic assisted tungsten inert gas (U-TIG) welding is a newly developed arc welding method, which is aimed at improving the weld quality and efficiency. TIG welding and U-TIG welding of 2014 aluminum alloy w...The ultrasonic assisted tungsten inert gas (U-TIG) welding is a newly developed arc welding method, which is aimed at improving the weld quality and efficiency. TIG welding and U-TIG welding of 2014 aluminum alloy with 5 mm thickness were experimentally carried out in this paper. The microstructure and porosity of welded joints were analyzed. Compared with conventional TIG welding, the columnar crystals are changed into equiaxed crystals at the centre of weld zone and the grain of fusion zone in U-TIG welding is refined and equiaxed. The porosities of joint decrease after the ultrasonic was applied on the arc. The mechanism of crystal grain refinement is discussed in this paper and the reasons of porosity decrease in U-TIG welded joint may be due to the effect of acoustic streaming and cavitation, which need further research.展开更多
This paper deals with a novel dual shield TIG welding method named gas pool coupled activating TIG( GPCA-TIG)welding. The welding method divides the shielding gas into two layers. Inert gas such as Ar is adopted as th...This paper deals with a novel dual shield TIG welding method named gas pool coupled activating TIG( GPCA-TIG)welding. The welding method divides the shielding gas into two layers. Inert gas such as Ar is adopted as the inner layer gas to protect the tungsten electrode and the molten pool metal. Pure O_2,N_2 or mixture of them are used as the outer layer gas to increase the weld penetration and improve the low temperature toughness of weld metal. Through analyzing the interaction between outer gas and arc and the distributions and existing forms of oxygen and nitrogen elements,the transfer behaviors of nitrogen and oxygen from arc to pool were investigated. The results show that,the interaction between the outer gas and arc plasma makes the arc slightly constrict. The incoming oxygen enriches on the molten pool surface and exists in the form of iron oxide,chromium oxide,manganese oxide and silicon oxygen compounds. The incoming nitrogen evenly distributes in the molten pool and exists in the form of nitrogen atom.展开更多
The high-speed camera system and data acquisition system of welding parameters were created in tandem MIG welding of high strength aluminum alloy. The experiments were carried out in order to obtain the photos of drop...The high-speed camera system and data acquisition system of welding parameters were created in tandem MIG welding of high strength aluminum alloy. The experiments were carried out in order to obtain the photos of droplet transfer under different welding parameters in pulsed mode. The droplet transfer mode of “one pulse one droplet” becomes the preferred selection during welding process because of its stable procedure and sound weld form. The parameter ranges for corresponding transfer mode were experimentally achieved, among which the stable droplet transfer mode of “one pulse one droplet” can be realized. These efforts brave the way for control weld heat input and weld formation in the future.展开更多
Three-dimensional finite element model was established to simulate temperature fields of T-joint titanium sheets during TIG welding with finite element method (FEM) software. Temperature dependent material propertie...Three-dimensional finite element model was established to simulate temperature fields of T-joint titanium sheets during TIG welding with finite element method (FEM) software. Temperature dependent material properties and the effect of latent heat were considered. A technique of element birth and death was used to simulate the process of welded metal filling. Dynamic variation process of temperature fields during T1G welding was achieved. The simulated results agreed well with the measured results.展开更多
In order to realize automatic control of the width of weld pool, a visual sensor system for the width of weld pool detection is developed. By initiative arc light, the image of copper plate weld pool is taken back of ...In order to realize automatic control of the width of weld pool, a visual sensor system for the width of weld pool detection is developed. By initiative arc light, the image of copper plate weld pool is taken back of the torch through the process of weakening and filtering arc light. In order to decrease the time of processing video signals, analog circuit is applied in the processing where video signals is magnified, trimmed and processed into binary on the datum of dynamic average value, therefore the waveform of video signals of weld pool is obtained. The method that is used for detecting the width of weld pool is established. Results show that the vision sensing method for real-time detecting weld pool width to copper-clad aluminum wire TIG welding is feasible. The response cycle of this system is no more than 50 ms, and the testing precision is less than 0. 1 mm.展开更多
基金The 2024 University-level Higher Education Teaching Reform Project of Guangzhou Xinhua University,“Teaching Reform and Practice Based on OBE Concept”:A Case Study of“University Physics Experiment”(Project No.2024J044)。
文摘Welding voltage and current in arc signals are directly related to arc stability and welding quality.Process experiments with different parameters were organized according to the orthogonal experimental design method by constructing an aluminum alloy double-pulse metal inert gas(MIG)welding arc electric signal test platform.The data acquisition system of the aluminum alloy MIG welding process was established to obtain real-time arc signal information reflecting the welding process.The aluminum alloy’s collected double-pulse arc current signals are decomposed adaptively by broadband mode decomposition(BMD).The direct current(DC)signal,pulse signal,distortion signal,ripple signal,and noise signal are separated and extracted,and the composite multiscale fuzzy entropy(CMFE)is calculated for the component set of the electrical signal.The experimental results show that the current waveform obtained by the double-pulse MIG welding current signal is consistent with the corresponding weld forming diagram.Simultaneously,the composite multiscale fuzzy entropy is calculated for the arc characteristic parameters.The rationality of matching process parameters and arc stability of aluminum alloy’s double-pulse MIG welding were evaluated.
基金supported by Henan Province Key Research and Development and Promotion Project(Grant No.201ZP20220010).
文摘The effects of vanadium(V)on the microstructures and mechanical properties of the TiC cermet fusion welding interface were studied by adjusting the content of V in the self-developed flux-cored wires using metal inert gas arc(MIG)welding for surfacing on the TiC cermet.The results show that the increase in V content promotes the element diffusion between TiC cermet and weld metal.There are no de-fects observed in the interface,and the diffusion of elements refers to excellent metallurgical bonding.The shear strength of the fusion zone initially decreases and then increases with the increase in V content.The maximum shear strength of the TiC cermet/weld interface,reaching 552 MPa,occurred when the V content reached 0.65%.Meanwhile,the average hardness in the transition zone reached 488.2 HV0.2.
基金Funded by the Center of Excellence in Metals and Materials Engineering(CEMME),Faculty of Engineering,Prince of Songkla UniversitySupported by the National Science,Research and Innovation Fund(NSRF)and Prince of Songkla University(No.ENG6505079S)。
文摘Repair welding of AA 6082-T6 joints was carried out using ER 4043 filler through the TIG welding process with or without pulsed current.Microstructure and mechanical characteristics of the joints before and after repairing were investigated by examining macrostructure,microstructure,and distributions of porosity in the weld metal(WM),and by hardness,tensile,and bending tests.We observed that the welding current,phase transformations in heat-affected zone(HAZ)and porosity introduced in the WM during welding influence on its mechanical properties in sequence.The experimental results showed that the bead width and penetration as well as size of pores in the joints were mainly influenced by the welding currents.The sound joints were obtained at a welding current of 140 A with or without pulsed current when welding speed and gas flow rate were set at 20 cm·min-1 and 15 L·min-1,respectively.Among them,the decrease in mechanical properties of repair weld(RW)was directly related to the phase transformations in the over-ageing zone due to the double welding thermal cycles and elevated distribution of porosity in the WM.In addition,it was observed that the comparatively smaller grain size and lower porosity in WM of the RW produced by pulsed TIG welding gave a positive effect on its mechanical properties.
基金Project(51475156)supported by the National Natural Science Foundation of China
文摘The effect of current on the morphology of Al alloy T-joint in double-pulsed metal inert gas(DP-MIG) welding process was investigated by simulation and experiment.A three-dimensional finite element model and the DP-MIG heat source of double-ellipsoidal volumetric model were developed to simulate the temperature and stress fields under different welding conditions.The macro-morphology and microstructure of welding joints at the corresponding currents were observed in the experiment.The results show that the best condition is at an average current of 90 A and current difference of 40 A,when the maximum temperature is 200 °C higher than the fusion points,with the temperature difference of about 100 °C and stress change of 10 MPa between thermal pulse and thermal base.Under these conditions,Al alloy T-joint with proper fusion condition has smooth fish-scale welding appearance and finer microstructure.Furthermore,the thermal curves and stress distribution in the experiment are consistent with those in the simulation,verifying the precision of the welding simulation.
基金Project(2012ZX04010-081)supported by the National High-tech Research and Development Program of ChinaProject(CDJZR12110072)supported by Fundamental Research Funds for Central Universities of China
文摘A device for superimposing vibration on workpiece in both horizontal and vertical directions during tungsten-arc inert gas (TIG) welding was developed, with maximum power output of 2 kW at frequency of 15 kHz. AZ31 sheets with thickness of I and 3 mm were used in the vibratory welding. Microstructures along with the mechanical properties of the weld joints under different vibrating conditions (vibration direction, vibration amplitude and groove angle) were examined. It is observed that the grain size in welding zone decreases remarkably with the application of vibration, while the amount of second phase β-Mg_17Al_12 within the zone decreases slightly; meanwhile, microhardness of the weld joints, macroscopic tensile strength and elongation of the weldment increase. Vibration, especially the one along vertical direction, has more impact on the performance of the thick weldments. Influence of vibration on mierostructure and mechanical properties of weldments is affected by wave energy transferring in the melt and depends on the processing and geometric parameters including amplitude and direction of vibration, thickness, and groove angles.
文摘采用TIG(Tungsten inert gas welding,TIG)焊对FeCrAl合金管同质材料进行焊接,通过扫描电子显微镜、透射电子显微镜及能谱仪等手段研究了焊后接头的显微组织特征、焊后接头不同区域氧化物颗粒的分布情况及焊接接头的力学性能。FeCrAl合金TIG焊通过填充等成分的FeCrAl合金丝材进行焊接,焊后焊接接头主要由焊缝区、热影响区及母材组成。其中焊缝区为粗大的铁素体组织,热影响区为细小的等轴晶组织。焊缝区的Y_(2)O_(3)氧化物颗粒发生了明显粗化并与基体反应生成复合氧化物Y_(3)Al_(5)O_(12)。TIG焊焊接FeCrAl合金管热处理后,焊接接头最大抗拉强度值为530 MPa,约为母材强度的80.8%,可以实现大口径、大壁厚的FeCrAl合金管材的对接接头的力学性能要求。
基金Project (51001034) supported by the National Natural Science Foundation of ChinaProject (208181) supported by the Key Project of Chinese Ministry of Education+1 种基金Projects (2008AA4CH044, 2009AA1AG065, 2010AA4BE031) supported by the Key Project of Science and Technology of Harbin City, ChinaProject (HEUCF101001) supported by the Fundamental Research Funds for the Central Universities, China
文摘Tungsten inert gas weld was carried out on super-light magnesium-lithium alloy plates with a thickness of 2 mm, using argon gas as a protecting atmosphere. The microstructure and mechanical properties of the welded joints were investigated. The results indicate that the microstructure in the fusion zone is fine, and the microstructure in the heat-affected zone is coarser than the parent metal. The tensile strength of the welded joint is about 84% that of the parent metal. The fracture occurs in a mixed type of toughness and brittleness in the heat-affected zone. During the welding process, aluminum and cerium are enriched at grain boundaries in the fusion zone.
基金supported by National Natural Science Foundation of China(61640423)Additive Manufacturing&Laser Manufacturing of China(2016YFB1102100)High-end CNC Machine Tools&Basic Manufacturing Equipment of China(2016ZX04003002)
文摘Welding research of A6N01S-T5 aluminum alloy profile for high-speed train was done by using laser-MIG hybrid welding and MIG welding individually. And the weld appearance,welding distortion,mechanical properties of the joints and microstructures were analyzed. The test results demonstrated that high-efficient welding for the profile can be achieved by using laser-MIG hybrid welding,the speed of which can be over 3. 0 m/min. The processing had a good gap bridging ability,even if the gap of the butt joint was up to 2. 0 mm,a good weld appearance can also be got. While the hybrid welding speed was greater than 2. 5 m/min,the welding distortion of the laser-tandem MIG hybrid joints was just about 33% of that of the MIG joints,but the welding efficiency was over 3 times of MIG welding. And tensile strength of the hybrid joints was 85% of that of A6N01S-T5 base metal,9% higher than that of the MIG joints. Fatigue properties was tested individually with pulsed tensile fatigue method in the condition of 1 × 10~7 lifetime. The test results demonstrated that the fatigue strength of the joints was a little lower than that of base material,which could be up to 115 MPa. But the fatigue strength of hybrid welding joints was 107. 5 MPa,which was 23% higher than 87 MPa of MIG welding joints.
文摘The ultrasonic assisted tungsten inert gas (U-TIG) welding is a newly developed arc welding method, which is aimed at improving the weld quality and efficiency. TIG welding and U-TIG welding of 2014 aluminum alloy with 5 mm thickness were experimentally carried out in this paper. The microstructure and porosity of welded joints were analyzed. Compared with conventional TIG welding, the columnar crystals are changed into equiaxed crystals at the centre of weld zone and the grain of fusion zone in U-TIG welding is refined and equiaxed. The porosities of joint decrease after the ultrasonic was applied on the arc. The mechanism of crystal grain refinement is discussed in this paper and the reasons of porosity decrease in U-TIG welded joint may be due to the effect of acoustic streaming and cavitation, which need further research.
基金supported by National Natural Science Foundation of China(Grant No.51265029)
文摘This paper deals with a novel dual shield TIG welding method named gas pool coupled activating TIG( GPCA-TIG)welding. The welding method divides the shielding gas into two layers. Inert gas such as Ar is adopted as the inner layer gas to protect the tungsten electrode and the molten pool metal. Pure O_2,N_2 or mixture of them are used as the outer layer gas to increase the weld penetration and improve the low temperature toughness of weld metal. Through analyzing the interaction between outer gas and arc and the distributions and existing forms of oxygen and nitrogen elements,the transfer behaviors of nitrogen and oxygen from arc to pool were investigated. The results show that,the interaction between the outer gas and arc plasma makes the arc slightly constrict. The incoming oxygen enriches on the molten pool surface and exists in the form of iron oxide,chromium oxide,manganese oxide and silicon oxygen compounds. The incoming nitrogen evenly distributes in the molten pool and exists in the form of nitrogen atom.
文摘The high-speed camera system and data acquisition system of welding parameters were created in tandem MIG welding of high strength aluminum alloy. The experiments were carried out in order to obtain the photos of droplet transfer under different welding parameters in pulsed mode. The droplet transfer mode of “one pulse one droplet” becomes the preferred selection during welding process because of its stable procedure and sound weld form. The parameter ranges for corresponding transfer mode were experimentally achieved, among which the stable droplet transfer mode of “one pulse one droplet” can be realized. These efforts brave the way for control weld heat input and weld formation in the future.
基金China Postdoctoral Science Foundation (No 20080430129)
文摘Three-dimensional finite element model was established to simulate temperature fields of T-joint titanium sheets during TIG welding with finite element method (FEM) software. Temperature dependent material properties and the effect of latent heat were considered. A technique of element birth and death was used to simulate the process of welded metal filling. Dynamic variation process of temperature fields during T1G welding was achieved. The simulated results agreed well with the measured results.
文摘In order to realize automatic control of the width of weld pool, a visual sensor system for the width of weld pool detection is developed. By initiative arc light, the image of copper plate weld pool is taken back of the torch through the process of weakening and filtering arc light. In order to decrease the time of processing video signals, analog circuit is applied in the processing where video signals is magnified, trimmed and processed into binary on the datum of dynamic average value, therefore the waveform of video signals of weld pool is obtained. The method that is used for detecting the width of weld pool is established. Results show that the vision sensing method for real-time detecting weld pool width to copper-clad aluminum wire TIG welding is feasible. The response cycle of this system is no more than 50 ms, and the testing precision is less than 0. 1 mm.