The amino-functionalization of TS-1 zeolite followed by immobilization of phosphotungstic acid(HPW)was presented to prepare a strong solid acid catalyst for the synthesis of bio-based tributyl citrate from the esterif...The amino-functionalization of TS-1 zeolite followed by immobilization of phosphotungstic acid(HPW)was presented to prepare a strong solid acid catalyst for the synthesis of bio-based tributyl citrate from the esterification of citric acid and n-butanol.γ-Aminopropyltriethoxysilane(APTES)was first grafted on the TS-1 zeolite via the condensation reactions with surface hydroxyl groups,and subsequently the HPW was immobilized via the reaction between the amino groups and the protons from HPW-forming strong ionic bonding.The Keggin structure of HPW and MFI topology of TS-1 zeolite were well maintained after the modifications.The amino-functionalization generated abundant uniformly distributed active sites on TS-1 for HPW immobilization,which promoted the dispersity,abundance,as well as the stability of the acid sites.The tetrahedrally coordinated framework titanium and non-framework titania behaved as weak Lewis acid sites,and the protons from the immobilized HPW acted as the moderate or strong Brønsted acid sites.An optimized TBC yield of 96.2%(mol)with a conversion of-COOH of 98.1%(mol)was achieved at 150℃for 6 h over the HPW immobilized on amino-functionalized TS-1.The catalyst exhibited good stability after four consecutive reaction runs,where the activity leveled off at still a relatively high level after somewhat deactivation possibly caused by the leaching of a small portion of weakly anchored APTES or HPW.展开更多
The exploration of highly efficient catalysts based on nano-sized Ti-rich titanosilicate zeolites with controllable active titanium species is of great importance in zeolite catalytic reactions.Herein,we reported an e...The exploration of highly efficient catalysts based on nano-sized Ti-rich titanosilicate zeolites with controllable active titanium species is of great importance in zeolite catalytic reactions.Herein,we reported an efficient and facile synthesis of nano-sized Ti-rich TS-1(MFI)zeolites by replacing tetrabutyl orthotitanate(TBOT)with tetrabutyl orthotitanate tetramer(TBOT-tetramer)as the titanium source.The introduced TBOT-tetramer slowed down the zeolite crystallization process,and accordingly balanced the rate of incorporating Ti and the crystal growth and inhibited the massive formation of anatase species.Notably,the prepared Ti-rich TS-1 zeolite sample had a Si/Ti as low as 27.6 in contrast to conventional one with a molar ratio of 40.The TBOT-tetramer endowed the titanosilicate zeolites with enriched active titanium species and enlarged external surface area.It also impeded the formation of anatase species,resulting in superior catalytic behavior toward the oxidative desulfurization of dibenzothiophene compared with the conventional TS-1 zeolite counterpart prepared with TBOT.展开更多
A novel composite material(TD)composed of TS-1 microcrystalline and dendritic mesoporous silica nanospheres(DMSNs)was successfully prepared.The TD composite material had open pore structure and large specific surface ...A novel composite material(TD)composed of TS-1 microcrystalline and dendritic mesoporous silica nanospheres(DMSNs)was successfully prepared.The TD composite material had open pore structure and large specific surface area,which was conducive to the mass transfer of reactants and products.The Ti element in TS-1 could be used as an electron assistant,and the spillover d-electrons were conducive to the improvement of the sulfidation and dispersion of MoS_(2),thereby forming more type II MoS_(2) active phases.The incorporation of Ti could bring more Brønsted(B)and Lewis(L)acid,which was conducive to the hydrogenation pathway(HYD)selectivity(41.2%)of dibenzothiophene(DBT)hydrodesulfurization(HDS)and isomerization(ISO)route selectivity(21.9%)of 4,6-dimethyldibenzothiophene(4,6-DMDBT)HDS,thus improve the HDS activity of DBT and 4,6-DMDBT.NiMo/TD-70(Aging temperature=70℃)had the best HDS activities of DBT(99.0%)and 4,6-DMDBT(93.7%)due to its large open pore structure,good acidity,suitable metal-support interaction(MSI)and perfect dispersion of the metallic active sites.展开更多
基金supported by the National Natural Science Foundation of China(21978089)the Program of Shanghai Academic/Technology Research Leader(21XD1433000)and Key Research and Development Program of Xinjiang Uygur Autonomous Region(2022B01032-1).
文摘The amino-functionalization of TS-1 zeolite followed by immobilization of phosphotungstic acid(HPW)was presented to prepare a strong solid acid catalyst for the synthesis of bio-based tributyl citrate from the esterification of citric acid and n-butanol.γ-Aminopropyltriethoxysilane(APTES)was first grafted on the TS-1 zeolite via the condensation reactions with surface hydroxyl groups,and subsequently the HPW was immobilized via the reaction between the amino groups and the protons from HPW-forming strong ionic bonding.The Keggin structure of HPW and MFI topology of TS-1 zeolite were well maintained after the modifications.The amino-functionalization generated abundant uniformly distributed active sites on TS-1 for HPW immobilization,which promoted the dispersity,abundance,as well as the stability of the acid sites.The tetrahedrally coordinated framework titanium and non-framework titania behaved as weak Lewis acid sites,and the protons from the immobilized HPW acted as the moderate or strong Brønsted acid sites.An optimized TBC yield of 96.2%(mol)with a conversion of-COOH of 98.1%(mol)was achieved at 150℃for 6 h over the HPW immobilized on amino-functionalized TS-1.The catalyst exhibited good stability after four consecutive reaction runs,where the activity leveled off at still a relatively high level after somewhat deactivation possibly caused by the leaching of a small portion of weakly anchored APTES or HPW.
基金the National Natural Science Foundation of China, China (Grant 21920102005, 22288101, and 21835002)the 111 Project, China (B17020)+2 种基金the European Union through the European Research Council, European Union (grant ERC-AdG-2014-671093, SynCatMatch)the Spanish Government through “Severo Ochoa”, Spain (SEV2016-0683, MINECO) for supporting this workthe financial support from China Scholarship Council, China
文摘The exploration of highly efficient catalysts based on nano-sized Ti-rich titanosilicate zeolites with controllable active titanium species is of great importance in zeolite catalytic reactions.Herein,we reported an efficient and facile synthesis of nano-sized Ti-rich TS-1(MFI)zeolites by replacing tetrabutyl orthotitanate(TBOT)with tetrabutyl orthotitanate tetramer(TBOT-tetramer)as the titanium source.The introduced TBOT-tetramer slowed down the zeolite crystallization process,and accordingly balanced the rate of incorporating Ti and the crystal growth and inhibited the massive formation of anatase species.Notably,the prepared Ti-rich TS-1 zeolite sample had a Si/Ti as low as 27.6 in contrast to conventional one with a molar ratio of 40.The TBOT-tetramer endowed the titanosilicate zeolites with enriched active titanium species and enlarged external surface area.It also impeded the formation of anatase species,resulting in superior catalytic behavior toward the oxidative desulfurization of dibenzothiophene compared with the conventional TS-1 zeolite counterpart prepared with TBOT.
基金This research was supported by the Science Foundation of China University of Petroleum-Beijing(No.2462023QNXZ002)the National Key R&D Program of China(2021YFA1501201)+2 种基金the National Natural Science Foundation of China(No.22278174)Independent research project of State Key Laboratory of heavy oil(2021–01)Shandong Excellent Young Scientists Fund Program(Overseas,2022HWYQ-082).
文摘A novel composite material(TD)composed of TS-1 microcrystalline and dendritic mesoporous silica nanospheres(DMSNs)was successfully prepared.The TD composite material had open pore structure and large specific surface area,which was conducive to the mass transfer of reactants and products.The Ti element in TS-1 could be used as an electron assistant,and the spillover d-electrons were conducive to the improvement of the sulfidation and dispersion of MoS_(2),thereby forming more type II MoS_(2) active phases.The incorporation of Ti could bring more Brønsted(B)and Lewis(L)acid,which was conducive to the hydrogenation pathway(HYD)selectivity(41.2%)of dibenzothiophene(DBT)hydrodesulfurization(HDS)and isomerization(ISO)route selectivity(21.9%)of 4,6-dimethyldibenzothiophene(4,6-DMDBT)HDS,thus improve the HDS activity of DBT and 4,6-DMDBT.NiMo/TD-70(Aging temperature=70℃)had the best HDS activities of DBT(99.0%)and 4,6-DMDBT(93.7%)due to its large open pore structure,good acidity,suitable metal-support interaction(MSI)and perfect dispersion of the metallic active sites.
基金supported by the National Natural Science Foundation of China(21403070 and 21373088)Innovation Program of Shanghai Municipal Education Commission(13zz038)+2 种基金Key Project of the Shanghai Committee of Science and Technology(12JC1403600)National Key Technology R&D Program(2012BAE05B02)Shanghai Leading Academic Discipline Project(B409)~~