The controllable synthesis of tantalate K1.9Na0.1Ta2O6·2H2O has been successfully achieved by a two-step technique,namely,the molten salt and hydrothermal methods,at a low temperature. By simply varying the KOH c...The controllable synthesis of tantalate K1.9Na0.1Ta2O6·2H2O has been successfully achieved by a two-step technique,namely,the molten salt and hydrothermal methods,at a low temperature. By simply varying the KOH concentration in the hydrothermal process,K1.9Na0.1Ta2O6·2H2O particles with spherical,cuboctahedral,and durian-like morphologies were synthesized. The photocatalytic activity of the obtained samples for the degradation of rhodamine B was studied under ultraviolet light,which indicates that the photocatalytic properties of the samples are highly dependent on their morphologies. The K1.9Na0.1Ta2O6·2H2O nanospheres,with rough surfaces and the highest specific surface area,exhibit the best performance. The present work provides a unique approach for the controlled synthesis of tantalate photocatalysts,which are difficult to achieve through other synthetic approaches.展开更多
基金supported by the National Natural Science Foundation of China(U140319321473261+3 种基金41305112)the Excellent Youth Foundation of Xinjiang Uygur Autonomous Region(2013711004)the CAS "Light of West China" Program(YB201303)the CAS/SAFEA International Partnership Program for Creative Research Teams~~
文摘The controllable synthesis of tantalate K1.9Na0.1Ta2O6·2H2O has been successfully achieved by a two-step technique,namely,the molten salt and hydrothermal methods,at a low temperature. By simply varying the KOH concentration in the hydrothermal process,K1.9Na0.1Ta2O6·2H2O particles with spherical,cuboctahedral,and durian-like morphologies were synthesized. The photocatalytic activity of the obtained samples for the degradation of rhodamine B was studied under ultraviolet light,which indicates that the photocatalytic properties of the samples are highly dependent on their morphologies. The K1.9Na0.1Ta2O6·2H2O nanospheres,with rough surfaces and the highest specific surface area,exhibit the best performance. The present work provides a unique approach for the controlled synthesis of tantalate photocatalysts,which are difficult to achieve through other synthetic approaches.