Wet-etch etchants and the TaN film method for dual-metal-gate integration are investigated. Both HF/HN O3/H2O and NH4OH/H2O2 solutions can etch TaN effectively, but poor selectivity to the gate dielectric for the HF/H...Wet-etch etchants and the TaN film method for dual-metal-gate integration are investigated. Both HF/HN O3/H2O and NH4OH/H2O2 solutions can etch TaN effectively, but poor selectivity to the gate dielectric for the HF/HNO3/H2O solution due to HF being included in HF/HNO3/H2O, and the fact that TaN is difficult to etch in the NH4OH/H2O2 solution at the first stage due to the thin TaOxNy layer on the TaN surface, mean that they are difficult to individually apply to dual-metal-gate integration. A two-step wet etching strategy using the HF/HNO3/H2O solution first and the NH4OH/H2O2 solution later can fully remove thin TaN film with a photo-resist mask and has high selectivity to the HfSiON dielectric film underneath. High-k dielectric film surfaces are smooth after wet etching of the TaN metal gate and MOSCAPs show well-behaved C-V and Jg-Vg characteristics, which all prove that the wet etching of TaN has little impact on electrical performance and can be applied to dual-metal-gate integration technology for removing the first TaN metal gate in the PMOS region.展开更多
The appropriate wet etch process for the selective removal of TaN on the HfSiON dielectric with an amorphous-silicon(a-Si) hardmask is presented.SCI(NH4OH:H2O2:H2O),which can achieve reasonable etch rates for me...The appropriate wet etch process for the selective removal of TaN on the HfSiON dielectric with an amorphous-silicon(a-Si) hardmask is presented.SCI(NH4OH:H2O2:H2O),which can achieve reasonable etch rates for metal gates and very high selectivity to high-k dielectrics and hardmask materials,is chosen as the TaN etchant. Compared with the photoresist mask and the tetraethyl orthosilicate(TEOS) hardmask,the a-Si hardmask is a better choice to achieve selective removal of TaN on the HfSiON dielectric because it is impervious to the SC1 etchant and can be readily etched with NH4OH solution without attacking the TaN and the HfSiON film.In addition,the surface of the HfSiON dielectric is smooth after the wet etching of the TaN metal gate and a-Si hardmask removal,which could prevent device performance degradation.Therefore,the wet etching of TaN with the a-Si hardmask can be applied to dual metal gate integration for the selective removal of the first TaN metal gate deposition.展开更多
基金supported by the Special Funds for Major State Basic Research Projects(No.2006CB302704)the National Natural Science Foundation of China(No.60776030)
文摘Wet-etch etchants and the TaN film method for dual-metal-gate integration are investigated. Both HF/HN O3/H2O and NH4OH/H2O2 solutions can etch TaN effectively, but poor selectivity to the gate dielectric for the HF/HNO3/H2O solution due to HF being included in HF/HNO3/H2O, and the fact that TaN is difficult to etch in the NH4OH/H2O2 solution at the first stage due to the thin TaOxNy layer on the TaN surface, mean that they are difficult to individually apply to dual-metal-gate integration. A two-step wet etching strategy using the HF/HNO3/H2O solution first and the NH4OH/H2O2 solution later can fully remove thin TaN film with a photo-resist mask and has high selectivity to the HfSiON dielectric film underneath. High-k dielectric film surfaces are smooth after wet etching of the TaN metal gate and MOSCAPs show well-behaved C-V and Jg-Vg characteristics, which all prove that the wet etching of TaN has little impact on electrical performance and can be applied to dual-metal-gate integration technology for removing the first TaN metal gate in the PMOS region.
基金Project supported by the Special Funds for Major State Basic Research Project of China(No.2006CB302704)the National Natural Science Foundation of China(No.60776030)
文摘The appropriate wet etch process for the selective removal of TaN on the HfSiON dielectric with an amorphous-silicon(a-Si) hardmask is presented.SCI(NH4OH:H2O2:H2O),which can achieve reasonable etch rates for metal gates and very high selectivity to high-k dielectrics and hardmask materials,is chosen as the TaN etchant. Compared with the photoresist mask and the tetraethyl orthosilicate(TEOS) hardmask,the a-Si hardmask is a better choice to achieve selective removal of TaN on the HfSiON dielectric because it is impervious to the SC1 etchant and can be readily etched with NH4OH solution without attacking the TaN and the HfSiON film.In addition,the surface of the HfSiON dielectric is smooth after the wet etching of the TaN metal gate and a-Si hardmask removal,which could prevent device performance degradation.Therefore,the wet etching of TaN with the a-Si hardmask can be applied to dual metal gate integration for the selective removal of the first TaN metal gate deposition.