Polydiacetylene(PDA)is one kind of the conjugated polymer with layered structure,which can serve as a host to accommodate the guest components through intercalation.In these intercalated PDAs,some of them were reporte...Polydiacetylene(PDA)is one kind of the conjugated polymer with layered structure,which can serve as a host to accommodate the guest components through intercalation.In these intercalated PDAs,some of them were reported to have a nearly perfect organized structure and perform completely reversible thermochromism.Till now,these reported intercalated PDAs were made by only introducing a single component for intercalation.Here,we chose 10,12-pentacosadiynoic acid(PCDA)as the monomer,of which the carboxyl-terminal groups can interact with either Tb^3+ ions or melamines(MAs).When the feeding molar ratio of PCDA,MA,and Tb^3+ ion was 3:267:1,only Tb^3+ ions were intercalated though excess MAs existed.Such Tb^3+- intercalated poly-PCDA exhibited completely reversible thermochromism,where almost all the carboxyl groups interacted with Tb^3+ ions to form the nearly perfect structure.When the feeding molar ratio of PCDA,MA,and Tb^3+ ion was 3:267:0.6,both Tb^3+ ions and MAs were intercalated.There existed some defects in the imperfect MA-intercalated domains and at the domain boundaries.The MA/Tb^3+- intercalated poly-PCDA exhibits partially reversible thermochromism,where the backbones near the defects are hard to return the initial conformation,while the rest,those at nearly perfect organized domains,are still able to restore the initial conformation.展开更多
To obtain high efficiency luminescent materials, the system Al2O3-B2O3 containing Ce3+ andTb3+ ions with variation of B2O3-content, has been prepared by Al2O3, H3BO3, CeO2 and Tb4O7 underreducing atmosphere at 1250i ....To obtain high efficiency luminescent materials, the system Al2O3-B2O3 containing Ce3+ andTb3+ ions with variation of B2O3-content, has been prepared by Al2O3, H3BO3, CeO2 and Tb4O7 underreducing atmosphere at 1250i . It is notable that the brightness of the sample with appropriatecomposition is similar to that of commercial phosphorous containing Ce3+ and Tb3+, indicating that a newhigh efficency green luminescent material was obtained with appropriate B2O3-content.展开更多
基金supported by the Programs of the Shanghai Pujiang Program(No.18PJ1401500)the National Natural Science Foundation of China(No.21801046,No.51721002,No.21574025 and No.21871057)the Ministry of Science and Technology(2016YFA0203302)。
文摘Polydiacetylene(PDA)is one kind of the conjugated polymer with layered structure,which can serve as a host to accommodate the guest components through intercalation.In these intercalated PDAs,some of them were reported to have a nearly perfect organized structure and perform completely reversible thermochromism.Till now,these reported intercalated PDAs were made by only introducing a single component for intercalation.Here,we chose 10,12-pentacosadiynoic acid(PCDA)as the monomer,of which the carboxyl-terminal groups can interact with either Tb^3+ ions or melamines(MAs).When the feeding molar ratio of PCDA,MA,and Tb^3+ ion was 3:267:1,only Tb^3+ ions were intercalated though excess MAs existed.Such Tb^3+- intercalated poly-PCDA exhibited completely reversible thermochromism,where almost all the carboxyl groups interacted with Tb^3+ ions to form the nearly perfect structure.When the feeding molar ratio of PCDA,MA,and Tb^3+ ion was 3:267:0.6,both Tb^3+ ions and MAs were intercalated.There existed some defects in the imperfect MA-intercalated domains and at the domain boundaries.The MA/Tb^3+- intercalated poly-PCDA exhibits partially reversible thermochromism,where the backbones near the defects are hard to return the initial conformation,while the rest,those at nearly perfect organized domains,are still able to restore the initial conformation.
文摘To obtain high efficiency luminescent materials, the system Al2O3-B2O3 containing Ce3+ andTb3+ ions with variation of B2O3-content, has been prepared by Al2O3, H3BO3, CeO2 and Tb4O7 underreducing atmosphere at 1250i . It is notable that the brightness of the sample with appropriatecomposition is similar to that of commercial phosphorous containing Ce3+ and Tb3+, indicating that a newhigh efficency green luminescent material was obtained with appropriate B2O3-content.