The self-assembly of 5-bromoisophthalic acid (H2BIPA) with Tb(NO3)3·6H2O under hydrothermal conditions gives rise to a 3D coordination polymer, [Tb2(BIPA)3(CH3CH2OH)]n (1), which was characterized by el...The self-assembly of 5-bromoisophthalic acid (H2BIPA) with Tb(NO3)3·6H2O under hydrothermal conditions gives rise to a 3D coordination polymer, [Tb2(BIPA)3(CH3CH2OH)]n (1), which was characterized by elemental analysis, IR and single-crystal X-ray diffraction. The crystal is of monoclinic system, space group P21/c with a = 19.2591(17), b = 8.2537(7), c = 18.5663(17), β = 104.4720(10)°, V = 2857.6(4)3, C26H15Br3O13Tb2, Mr = 1092.95, Dc = 2.540 g/cm3, F(000) = 2040, μ = 9.173 mm-1 and Z = 4. The final R = 0.0324 and wR = 0.0767 for 5299 observed reflections (I 〉 2σ(I)). Complex 1 displays an unusual three-dimensional (4,6)-connected network with (48.66.8)2(44.62)2(42.84) topology, which is different from [Tb(HBDC)(BDC)(H2O)4]·3.3H2O (BDC = isophthalate) because the -Br substituent of isophthalate results in different electronic effect and steric hindrance to change the coordination modes of carboxylate groups in the assembly process. Moreover, luminescent properties of 1 have also been investigated in the solid state.展开更多
A novel coordination polymer,[Pr2(BIPA)3(H2O)2].2H2O(1)(H2BIPA=5-bromoisophthalic acid),was prepared by hydrothermal synthesis and characterized by IR spectroscopy,elemental analysis and single-crystal X-ray d...A novel coordination polymer,[Pr2(BIPA)3(H2O)2].2H2O(1)(H2BIPA=5-bromoisophthalic acid),was prepared by hydrothermal synthesis and characterized by IR spectroscopy,elemental analysis and single-crystal X-ray diffraction.The crystal was of monoclinic system,space group C2/c,with a=1.98037(14),b=1.44189(14),c=2.15281(18) nm,β=95.220(2)°,V=6.1218(9) nm3,C24H17Br3O16Pr2,Mr=1082.93,Dc= 2.350 g/cm3,F(000)=4096,μ=7.136 mm-1 and Z=8.The final R1=0.0608 and wR2=0.1371 for 5624 observed reflections(I2σ(I)).Complex 1 featured an interesting 2D layer containing {Pr2(CO2)3}n right-handed and left-handed helical chains.Furthermore,hydrogen bonds linked the adjacent 2D layers to form a 3D supramolecular framework.Moreover,the near-infrared luminescent properties of 1 were also investigated in the solid state.展开更多
The self-assembly of 5-bromoisophthalic acid (H2BIPA) with Eu(NO3)3·6H2O under the hydrothermal conditions gave a 3D coordination polymer, Eu2(BIPA)3(CH3CH2OH) (1), which was characterized by elemental ...The self-assembly of 5-bromoisophthalic acid (H2BIPA) with Eu(NO3)3·6H2O under the hydrothermal conditions gave a 3D coordination polymer, Eu2(BIPA)3(CH3CH2OH) (1), which was characterized by elemental analysis, IR and single-crystal X-ray diffraction. Complex 1 displayed an unusual three-dimensional network of a rare (4,6)-connected (48.66.8)2(44.62)2(42.84) topology, which was different from Eu2(BDC)3(H2O)2 (BDC=isophthalate), because the -Br substituent of the isophthalate resulted in the different electronic effects and the steric hindrance to change the coordination modes of carboxylate groups in the assembled process. Moreover, the luminescent properties of 1 were also investigated in the solid state.展开更多
基金Supported by the National Natural Science Foundation of China (No. 20971004)the Key Project of Chinese Ministry of Education (No. 210102)
文摘The self-assembly of 5-bromoisophthalic acid (H2BIPA) with Tb(NO3)3·6H2O under hydrothermal conditions gives rise to a 3D coordination polymer, [Tb2(BIPA)3(CH3CH2OH)]n (1), which was characterized by elemental analysis, IR and single-crystal X-ray diffraction. The crystal is of monoclinic system, space group P21/c with a = 19.2591(17), b = 8.2537(7), c = 18.5663(17), β = 104.4720(10)°, V = 2857.6(4)3, C26H15Br3O13Tb2, Mr = 1092.95, Dc = 2.540 g/cm3, F(000) = 2040, μ = 9.173 mm-1 and Z = 4. The final R = 0.0324 and wR = 0.0767 for 5299 observed reflections (I 〉 2σ(I)). Complex 1 displays an unusual three-dimensional (4,6)-connected network with (48.66.8)2(44.62)2(42.84) topology, which is different from [Tb(HBDC)(BDC)(H2O)4]·3.3H2O (BDC = isophthalate) because the -Br substituent of isophthalate results in different electronic effect and steric hindrance to change the coordination modes of carboxylate groups in the assembly process. Moreover, luminescent properties of 1 have also been investigated in the solid state.
基金Project supported by the National Natural Science Foundation of China (20971004)the Key Project of Chinese Ministry of Education (210102)
文摘A novel coordination polymer,[Pr2(BIPA)3(H2O)2].2H2O(1)(H2BIPA=5-bromoisophthalic acid),was prepared by hydrothermal synthesis and characterized by IR spectroscopy,elemental analysis and single-crystal X-ray diffraction.The crystal was of monoclinic system,space group C2/c,with a=1.98037(14),b=1.44189(14),c=2.15281(18) nm,β=95.220(2)°,V=6.1218(9) nm3,C24H17Br3O16Pr2,Mr=1082.93,Dc= 2.350 g/cm3,F(000)=4096,μ=7.136 mm-1 and Z=8.The final R1=0.0608 and wR2=0.1371 for 5624 observed reflections(I2σ(I)).Complex 1 featured an interesting 2D layer containing {Pr2(CO2)3}n right-handed and left-handed helical chains.Furthermore,hydrogen bonds linked the adjacent 2D layers to form a 3D supramolecular framework.Moreover,the near-infrared luminescent properties of 1 were also investigated in the solid state.
基金Project supported by the National Natural Science Foundation of China (20971004)the Key Project of Chinese Ministry of Education (210102)
文摘The self-assembly of 5-bromoisophthalic acid (H2BIPA) with Eu(NO3)3·6H2O under the hydrothermal conditions gave a 3D coordination polymer, Eu2(BIPA)3(CH3CH2OH) (1), which was characterized by elemental analysis, IR and single-crystal X-ray diffraction. Complex 1 displayed an unusual three-dimensional network of a rare (4,6)-connected (48.66.8)2(44.62)2(42.84) topology, which was different from Eu2(BDC)3(H2O)2 (BDC=isophthalate), because the -Br substituent of the isophthalate resulted in the different electronic effects and the steric hindrance to change the coordination modes of carboxylate groups in the assembled process. Moreover, the luminescent properties of 1 were also investigated in the solid state.