A model for estimating the rate constant between CO_2-CO gas and molten slag containing iron oxides using optical basicity

A simple model for estimating the rate constant between CO2-CO gas and molten slag containing iron oxides was developed using optical basicity only. In this model, the temperature dependence of the rate constant can be described by the Arrhenius law, and the activation energy can be expressed with a linear function of the slag＇s optical basicity. The model was applied to some molten slag systems, such as FeO, FeO-CaO, FeO-SiO2, FeO-Na2O, FeO-CaO-SiO2, FeO-SiO2-P2O5, FeO-SiOE-Na2O, and FeO-CaO-SiOE-P2O5. A comparison between the predicted results and measured data showed that the model worked well.

Co-pyrolysis of soybean soapstock with iron slag/aluminum scrap,and characterization and analysis of their products

Soybean soapstock(SS) is one of the main solid wastes produced in the refinery of edible oil processing. In this study, the co-pyrolysis of SS with iron slag(IS) and aluminum scrap(AS) was carried out in a tubular furnace. The gas, liquid and solid products were characterized and the char yield decreased with increasing IS/AS ratio. IS and AS can improve the gas yield, and when the ratio of SS/IS was 1:0.25, the total pyrolysis gas and hydrogen contents were significantly increased. The content of oxygen compounds in pyrolysis oil decreased during co-pyrolysis, while AS promoted the content of polycyclic aromatic hydrocarbons in pyrolysis oil. The co-pyrolysis reaction can be divided into four stages, the mass loss rate reaches the maximum at the third stage(390–575 ℃). The molar ratio of H/C was lower for pyrolysis,indicating good stability of pyrolysis char owing to the high degree of carbonization and aromaticity.The possible co-pyrolysis reaction mechanism was explored.

Thermodynamic Behavior of Manganese and Phosphorus between Liquid Iron and CaO-MgO-SiO_2-Al_2O_3-Fe_tO-MnO-P_2O_5 Slags

The thermodynamic behavior of manganese and phosphorus between liquid iron and CaO-MgO-SiO2-Al2O3-FetO-MnO-P2O5 ladle slag system was addressed by investigating the thermodynamic equilibria between liquid iron containing Mn and P and the ladle slag at 1873 K. The Mn distribution ratio L-Mn increases with increasing FetO content and decreasing the basicity ((%CaO + %MgO)/(%SiO2 + %Al2O3 + %P2O5)) in slag, while the P distribution ratio Lp seems to be increased as FetO content and the basicity increases. The values of L-Mn and L-p decrease by the addition of Al2O3 into slag. The expression of the dependence of L-Mn and L-p on the basicity and FetO content in slag was obtained.

Recovery of iron from copper slag by deep reduction and magnetic beneficiation

Aiming at recovering iron from high-iron-content copper slag, this article introduced a combination technol- ogy of deep reduction and magnetic beneficiation, investigated the iron recovery efficiency and optimized the technical conditions. When coke powder with 86wt% fixed carbon was used as a reductant, iron was successfully extracted from the copper slag. Under the optimized condition of the coke powder content of 14wt%, the calcium-to-silicon mass ratio （Ca/Si） of 0.2, the roasting temperature of 1300℃, the roasting time of 3 h, the grinding time of 20 min, and the magnetic field intensity of 61 kA-m-1, the iron recovery rate of the copper slag can reach 91.82%, and the extracted iron powder has an iron grade of 96.21%. With the characteristics of high iron grade and low impurity content, the extracted iron powder can be used as high-quality raw materials of weathering steel.

Steel Slag as an Iron Fertilizer for Corn Growth and Soil Improvement in a Pot Experiment

The feasibility of steel slag used as an iron fertilizer was studied in a pot experiment with corn. Slag alone or acidified slag was added to two Fe-deficient calcareous soils at different rates. Results showed that moderate rates (10 and 20 g kg-1) of slag or acidified slag substantially increased corn dry matter yield and Fe uptake. Application of steel slag increased the residual concentration of ammonium bicarbonate-diethylenetriamine pentaacetic acid (AB-DTPA) extractable Fe in the soils. The increase of extractable Fe was usually proportional to the application rate, and enhanced by the acidification of slag. Steel slag appeared to be a promising and inexpensive source of Fe to alleviate crop Fe chlorosis in Fe-deficient calcareous soils.

Leaching of iron concentrate separated from kiln slag in zinc hydrometallurgy with hydrochloric acid and its mechanism

It is taken as a novel prospective process to treat iron concentrate from hydrometallurgical zinc kiln slag forcomprehensive utilization of valuable metals by a hydrochloric acid leaching-spray pyrolysis method.The leaching mechanism ofdifferent valuable metals was studied.The results revealed that the leaching rates of Ag,Pb,Cu,Fe,As and Zn were99.91%,99.25%,95.12%,90.15%,87.58%and58.15%,respectively with6mol/L HCl and L/S ratio of10:1at60°C for120min.The actionof SiO2in leaching solution was also studied.The results showed that the precipitation and settlement of SiO2(amorphous)adsorbedpart of metal ions in solution,which greatly inhibited the leaching of Cu,Fe,As and Zn,so it is crucial to control the precipitation ofamorphous SiO2.

Effects of sintering atmosphere on the physical and mechanical properties of modified BOF slag glass

This study proposes an efficient way to utilize all the chemical components of the basic oxygen fttrnace （BOF） slag to prepare high value-added glass-ceramics. A molten modified BOF slag was converted from the melting BOF slag by reducing it and separating out iron component in it, and the modified BOF slag was then quenched in water to form glasses with different basicities. The glasses were subsequently sintered in the temperature range of 600-1000℃ in air or nitrogen atmosphere for 1 h. The effects of different atmospheres on the physical and mechanical properties of sintered samples were studied by using differential scanning calorimetry （DSC）, X-ray diffraction （XRD） and scanning electron microscopy （SEM） and by conducting experiment on evaluating the sintering shrinkage, water absorption and bulk density. It is found that the kinetics of the sintering process is significantly affected by sintering atmosphere. In particular, compared with sintering in air atmosphere, sintering in N2 atmosphere promotes the synergistic growth of pyroxene and melilite crystalline phases, which can contribute to better mechanical properties and denser microstructure.

Iron and copper recovery from copper slags through smelting with waste cathode carbon from aluminium electrolysis

To recover metal from copper slags,a new process involving two steps of oxidative desulfurization followed by smelting reduction was proposed in which one hazardous waste(waste cathode carbon)was used to treat another(copper slags).The waste cathode carbon is used not only as a reducing agent but also as a fluxing agent to decrease slag melting point.Upon holding for 60 min in air atmosphere first and then smelting with 14.4 wt%waste cathode carbon and 25 wt%CaO for 180 min in high purity Ar atmosphere at 1450℃,the recovery rates of Cu and Fe reach 95.89%and 94.64%,respectively,and meanwhile greater than 90%of the fluoride from waste cathode carbon is transferred into the final slag as CaF_(2) and Ca_(2)Si_(2)F_(2)O_(7),which makes the content of soluble F in the slag meet the national emission standard.Besides,the sulphur content in the obtained Fe-Cu alloy is low to 0.03 wt%.

Study on Foaming Behaviour of Molten Slag during Smelting Reduction with Iron Bath

The molten slag in smelting reduction with iron bath has peculiar behaviour for its high FeO concentration. Slag foaming is effected by the concentration and reduction rate of FeO, basicity of slag and temperature. Addition of granulated coke can greatly decrease slag foaming extent in the process of smelting reduction with iron bath. The anti-foaming capacity of granulated coke is the best when the ratio of coke used for coke layer to total coke used in smelting reduction is controlled at about 20%.

Effect of Fe_2O_3 on the crystallization behavior of glass-ceramics produced from naturally cooled yellow phosphorus furnace slag

CaO–Al2O3–SiO2(CAS) glass-ceramics were prepared via a melting method using naturally cooled yellow phosphorus furnace slag as the main raw material. The effects of the addition of Fe2O3on the crystallization behavior and properties of the prepared glass-ceramics were studied by differential thermal analysis, X-ray diffraction, and scanning electron microscopy. The crystallization activation energy was calculated using the modified Johnson–Mehl–Avrami equation. The results show that the intrinsic nucleating agent in the yellow phosphorus furnace slag could effectively promote the crystallization of CAS. The crystallization activation energy first increased and then decreased with increasing amount of added Fe2O3. At 4wt% of added Fe2O3, the crystallization activation energy reached a maximum of 676.374 kJ·mol−1. The type of the main crystalline phase did not change with the amount of added Fe2O3. The primary and secondary crystalline phases were identified as wollastonite (CaSiO3) and hedenbergite (CaFe(Si2O6)), respectively. © 2017, University of Science and Technology Beijing and Springer-Verlag Berlin Heidelberg.

Iron extraction from lead slag by bath smelting

A new bath smelting process was proposed to recover iron for solid wastes reduction.99.79%of iron metallization,99.61%of iron recovery,pig iron with93.58%Fe,0.021%S,0.11%P,1.38%C,0.22%Si,0.01%Pb and0.031%Zn were achievedafter the wastes were smelted at1575°C for20min under C/Fe molar ratio of1.6and basicity of1.2.The produced pig iron could beused in steel-making.This study provides a way for recycling iron from smelting slag and hydrometallurgical residue.

Recovery of iron from lead-zinc metallurgical slags by bath smelting

The recovery of iron from iron sinking slag and lead smelter slag was investigated by desulfurization-reduction bath smelting. The effects of lead smelter slag(LSS) to iron sinking slag(ISS) mass ratio and temperature were investigated in desulfurization experiments. The X-ray diffraction(XRD) and X-ray fluorescence(XRF) analyses show that the optimum conditions are LSS:ISS of 3:7 and temperature of 1350°C. The composition of desulfurization products is mainly Zn Fe2O4, and the desulfurization rate of 99.66% is obtained under optimum conditions. The thermogravimetric(TG) and differential scanning calorimeter(DSC) analyses demonstrate that reductant is necessary for decomposition and reduction of zinc ferrite in desulfurization product. The effects of reductant, temperature and feeding modes on iron enrichment were investigated in reduction experiments. The scanning electron microscope(SEM) and energy dispersive spectrometer(EDS) determination show that the iron content of reduction product is up to 99.36% under optimum conditions of coke as reductant, reduction temperature of 1450°C and the feeding mode of premixing.

Distribution behavior of Copper and Tin between FeO-rich slag and iron solution

The distribution behavior of residual elements copper and tin between FeO rich slag and iron solution was investigated under the condition of an induction furnace. The results indicate that a part of copper and tin is incidently oxidized when oxygen is blasted into bath to react with iron element. The distribution ratio of copper and tin between slag and metal is about 0.1. Phenomena of Cu and Sn elements segregation and accumulation in slag were observed by means of EPMA analysis. The distribution ratio of copper and tin between slag and metal may descend with increasing of CaO content in slag.

Leaching of magnesium from desiliconization slag of nickel laterite ores by carbonation process

The leaching of magnesium from desiliconization slag of nickel laterite ores by carbonation process was studied.The influence of various parameters was investigated to optimize the conditions and determine the kinetics of the reaction.The results show that with increasing stirring speed,liquid-to-solid ratio and reaction time,and decreasing temperature,the leaching rate of magnesium enhances.The leaching process of the desiliconization slag in the range of 288-298 K is controlled by the surface chemical reaction model.The apparent activation energy is-20.45 kJ/mol,and the kinetics model is obtained.

KINETICS OF REDUCTION IRON OXIDE IN CaO-SiO_2-Al_2O_3-Fe_tO SLAGS WITH CARBON SATURATED IN MOLTEN IRON

The rate of reducing Fet O in CaO-SiO2-Al2O3-Fet O slags with carbon saturated in molten iron has been determined in a graphite crucible in the temperature range of 1673-1773K. The effects of temperature, slag basicity and FetO content on the reduction rate have also been discussed. Test results show that the reduction rate increases with increasing temperature or FEtO concentration in slags, and the reduction rate has a parabolic relation with the simple basicity or optical basicity of slag, the maximum reduction rate being observed at around CaO/SiO2=1.5 of molten slags. The reduction reaction order is 1. 73 or 1.80, and the reduction activation energy is 299.9 or 295.9 kJ/mol in regard to Fet O weight content or Fet O activity calculated by using regular solution model, respectively. The reduction rate of CaO-SiO2-Al2 O3-Fet O slags with carbon saturated in molten iron is in the range of 0.32-3.48 mol-O/cm2·s.

Properties of boron-rich slag separated from boron-bearing iron concentrate

In the present paper,the fundamental research on the properties of boron-rich slag melting separated from boron-bearing iron concentrate was performed.The melting and fluidity of B2O3–MgO–SiO2–FeO slag system,crystallization of separated boron-rich slag and factors on the extraction efficiency of boron-rich slag were systematically investigated.B2O3 content would heavily affect the melting and fluidity property of boron-rich slag.Generally,FeO could improve the melting and fluidity property of boron-rich slag.Boron-containing crystalline phase mainly precipitated in temperature range from 1200°C to 1100°C.Higher smelting temperature and B2O3 reduction ratio were negative for the extraction of boron.The cooling rate of 10–20°C/min was better for the crystallization of boron-containing crystalline phase.Based on the obtained experimental results,the optimum operating parameters for the development of pyrometallurgical boron and iron separation process and further boron-rich slag cooling process were proposed.

Slag Resistance of Refractories for Direct Reduction of Laterite Nickel Ores in Rotary Kilns

Aiming at prolonging the service life of refractories for direct reduction of laterite nickel ores in rotary kilns,the slag resistance of ten materials(corundum bricks,chrome corundum bricks,silicon nitride bonded silicon carbide bricks,high alumina silicon carbide bricks,high alumina bricks,magnesia chrome bricks,magnesium aluminate spinel bricks,spinel chrome corundum bricks,chrome corundum castables and magnesia alumina chrome composite spinel bricks)was evaluated by rotary slag tests,which simulate the service conditions in rotary kilns.The corroded residual bricks were analyzed by SEM and EDS.The results show that the magnesia alumina chrome composite spinel brick possesses the advantages of magnesium aluminate spinel bricks and chrome corundum bricks;MgO-rich spinel can absorb the penetrated ferric oxide,and forms a dense zeylanite layer,which prevents the penetration of the molten laterite nickel ores;therefore,it is an ideal lining of rotary kilns for direct reduction of laterite nickel ores.

Corrosion of Magnesia-chrome Brick by Smelting Reduction Slag with Iron Bath

Effects of FeO content （0, 5%, 10%, and 15% in mass, respectively ） in lab-synthesized smelting redttc- tion slag with iron bath and test temperature （1 450, 1 500, 1550, anti 1 600 ℃ ） on corrosion am,amount and microstructure of fused rebonded magnesia - chrome brick with 26.02 massqc of Cr2O3 were researched by rotary cylinder method. The results show that ： （ 1 ） the corro- sion amolult of magnesia -chrome brick by slag without FeO is higher than that by the slag with 5% FeO, and the vorrosion amount increases when FeO content increa- ses from 5% to 15% ; （2） the test temperature is one of the important factors affecting the slag corrosion resist- ance of magnesia - chrome brick, and the corrosion of smelting reduction slag to brick increases with the temperature rising.

A novel process for the recovery of iron,titanium,and vanadium from vanadium-bearing titanomagnetite:sodium modification–direct reduction coupled process

A sodium modification–direct reduction coupled process was proposed for the simultaneous extraction of V and Fe from vanadium- bearing titanomagnetite. The sodium oxidation of vanadium oxides to water-soluble sodium vanadate and the transformation of iron oxides to metallic iron were accomplished in a single-step high-temperature process. The increase in roasting temperature favors the reduction of iron oxides but disfavors the oxidation of vanadium oxides. The recoveries of vanadium, iron, and titanium reached 84.52%, 89.37%, and 95.59%, respectively. Moreover, the acid decomposition efficiency of titanium slag reached 96.45%. Compared with traditional processes, the novel process provides several advantages, including a shorter flow, a lower energy consumption, and a higher utilization efficiency of vanadium-bearing titanomagnetite resources. © 2017, University of Science and Technology Beijing and Springer-Verlag Berlin Heidelberg.