Thermal fatigue behaviors of SiC power module by Ag sinter joining under harsh thermal shock test

The excellent properties of SiC bring new challenges for the device packaging.In this study,the bonding strength,fracture behaviors and microstructural evolution of micron-porous Ag joint were elevated during thermal cycling(–50 ℃–250 ℃) in SiC/DBC(direct bonding copper) die attachment structure for different time.During harsh thermal shock test,the strength of sintered joint deceased gradually with the increase of cycling number,and the value just was half of the value of as-sintered after 1 000 cycles.Coarsening of Ag grains was observed in micron-porous joint with the structure inhomogeneity and defects increasing,which were the reasons of the strength decease.In addition,it was also found that the fracture behavior of sintered joints was changed from ductile deformation of Ag grain to brittle fracture of crack propagation after 1 000 cycles.This study will add the understanding in the mechanical properties of Ag sinter joining and its applications at high temperature.

Characterization of Failure Mechanisms of Duplex and Graded Thermal Barrier Coatings Exposed to Thermal Shock Test

The beginning of failure of a (ZrO2-7%Y2O3)/(Ni-22%Co-17%Cr-12.5%Al-0.6%Y) duplex andgraded coating systems on lnconel 617 and IN738LC in burner rig tests has been characterized.The test conditions are 40 s heating up to 75O℃ substrate temperature followed by 80 s aircooling. Failure is considered at the appearance of the first bright spot during heating period.Stresses due to thermal expansion mismatch strains on cooling are the probable cause of life-limiting in this conditions of testing.

High-Temperature Corrosion of Protective Coatings for Boiler Tubes in Thermal Power Plants

High-temperature corrosion is a serious problem for the water-wall tubes of boilers used in thermal power plants. Oxidation, sulfidation and molten salt corrosion are main corrosion ways.Thereinto, the most severe corrosion occurs in molten salt corrosion environment. Materials rich in oxides formers, such as chromium and aluminum, are needed to resist corrosion in high-temperature and corrosive environment, but processability of such bulk alloys is very limited. High velocity electric arc spraying (HVAS) technology is adopted to produce coatings with high corrosion resistance. By comparison, NiCr (Ni-45Cr-4Ti) is recommended as a promising alloy coating for the water-wall tubes, which can even resist molten salt corrosion attack. In the study of corrosion mechanism, the modern material analysis methods, such as scanning electron microscopy (SEM), X-ray diffractometry (XRD) and energy dispersive spectrometry (EDS), are used. It is found that the corrosion resistances of NiCr and FeCrAI coatings are much better than that of 20g steel, that the NiCr coatings have the best anti-corrosion properties, and that the NiCr coatings have slightly lower pores than FeCrAI coatings.It is testified that corrosion resistance of coatings is mainly determined by chromium content, and the microstructure of a coating is as important as the chemical composition of the material. In addition, the fracture mechanisms of coatings in the cycle of heating and cooling are put forward. The difference of the thermal physical properties between coatings and base metals results in the thermal stress inside the coatings. Consequently, the coatings spall from the base metal.