This work focuses on fundamental understanding of microstructure evolution of nanostructured ferritic alloy(NFA) and 25 vol.% Cr3C2 coated Si C(Cr3C2@Si C)-NFA composite during spark plasma sintering at950°C and ...This work focuses on fundamental understanding of microstructure evolution of nanostructured ferritic alloy(NFA) and 25 vol.% Cr3C2 coated Si C(Cr3C2@Si C)-NFA composite during spark plasma sintering at950°C and the following thermal treatment at 1000°C. A unique bi-phase microstructure with distinct Cr-rich and Si-rich phases has been observed for the 25 vol.% Cr3C2@Si C-NFA composite, while for the NFA sample, the traditional large grain microstructure remains. Grain sizes are significantly smaller for the25 vol.% Cr3C2@Si C-NFA composite compared to those for the pure NFA, which can be attributed to the presence of grain boundary phases in the composite sample. During the thermal treatment, microstructure features can be directly correlated with the dissolution kinetics and phase diagrams calculated using Thermo-Calc/DICTRA/PRISMA~?.展开更多
以水稻温敏核不育系孟S为材料,利用海拔100,700和1 000 m 3个不同的海拔高度设立不同温度梯度的3个环境,在自然条件下种植大群体,通过对比育性检测,筛选不育起点温度比原群体更低的单株。结果表明,经过3次选择,孟S不育起点温度由24℃降...以水稻温敏核不育系孟S为材料,利用海拔100,700和1 000 m 3个不同的海拔高度设立不同温度梯度的3个环境,在自然条件下种植大群体,通过对比育性检测,筛选不育起点温度比原群体更低的单株。结果表明,经过3次选择,孟S不育起点温度由24℃降到了23℃。展开更多
基金supported financially by the Office of Nuclear Energy of Department of Energy(No.#DE-NE0008264)。
文摘This work focuses on fundamental understanding of microstructure evolution of nanostructured ferritic alloy(NFA) and 25 vol.% Cr3C2 coated Si C(Cr3C2@Si C)-NFA composite during spark plasma sintering at950°C and the following thermal treatment at 1000°C. A unique bi-phase microstructure with distinct Cr-rich and Si-rich phases has been observed for the 25 vol.% Cr3C2@Si C-NFA composite, while for the NFA sample, the traditional large grain microstructure remains. Grain sizes are significantly smaller for the25 vol.% Cr3C2@Si C-NFA composite compared to those for the pure NFA, which can be attributed to the presence of grain boundary phases in the composite sample. During the thermal treatment, microstructure features can be directly correlated with the dissolution kinetics and phase diagrams calculated using Thermo-Calc/DICTRA/PRISMA~?.