Vapor liquid solid three phase equilibria of ethanol water 4A molecular sieve system are studied experimentally and theoritically. It is proved that the addition of adsorbent does not chang...Vapor liquid solid three phase equilibria of ethanol water 4A molecular sieve system are studied experimentally and theoritically. It is proved that the addition of adsorbent does not change the equilibrium relation between vapor and bulk liquid phase. A calculation procedure is proposed to predict vapor liquid solid (adsorbent) three phase euquilibria.展开更多
The alloys were prepared in Mg-rich corner of Mg-Zn-Ce system. Partial phase equilibrium relationships of these alloys at 350 ℃ were identified by using scanning electron microscopy(SEM), electron probe microanalysis...The alloys were prepared in Mg-rich corner of Mg-Zn-Ce system. Partial phase equilibrium relationships of these alloys at 350 ℃ were identified by using scanning electron microscopy(SEM), electron probe microanalysis(EPMA), X-ray diffraction(XRD) analysis and selected area electron diffraction(SAED) pattern analysis of transmission electron microscopy(TEM). Partial isothermal section of Mg-Zn-Ce system in Mg-rich corner was identified. The results show that there is one ternary compound (T-phase) in Mg-Zn-Ce system. The T-phase is a linear ternary compound in which the content of Ce is about 7.7% (molar fraction); while the content of Zn is changed from 19.3% to 43.6% (molar fraction). The crystal structure of T-phase is C-centered orthorhombic. In addition, one two-phase region of Mg+T-phase and one three-phase region of Mg+T-phase+MgZn(Ce) exist in the Mg-rich corner of Mg-Zn-Ce system at 350 ℃.展开更多
文摘Vapor liquid solid three phase equilibria of ethanol water 4A molecular sieve system are studied experimentally and theoritically. It is proved that the addition of adsorbent does not change the equilibrium relation between vapor and bulk liquid phase. A calculation procedure is proposed to predict vapor liquid solid (adsorbent) three phase euquilibria.
基金Project(50471025) supported by the National Natural Science Foundation of ChinaProject(20052028) supported by the Natural Science Foundation of Liaoning Province, ChinaProject(2006BAE04B09-7) supported by the National Key Technology R&D Program during the 11th Five-Year Plan Period
文摘The alloys were prepared in Mg-rich corner of Mg-Zn-Ce system. Partial phase equilibrium relationships of these alloys at 350 ℃ were identified by using scanning electron microscopy(SEM), electron probe microanalysis(EPMA), X-ray diffraction(XRD) analysis and selected area electron diffraction(SAED) pattern analysis of transmission electron microscopy(TEM). Partial isothermal section of Mg-Zn-Ce system in Mg-rich corner was identified. The results show that there is one ternary compound (T-phase) in Mg-Zn-Ce system. The T-phase is a linear ternary compound in which the content of Ce is about 7.7% (molar fraction); while the content of Zn is changed from 19.3% to 43.6% (molar fraction). The crystal structure of T-phase is C-centered orthorhombic. In addition, one two-phase region of Mg+T-phase and one three-phase region of Mg+T-phase+MgZn(Ce) exist in the Mg-rich corner of Mg-Zn-Ce system at 350 ℃.