Fe-based layer with Ti（CxN1-x） particulates on Adamite roller surface was obtained by a 5 kW traverse-flowing CO2 laser cladding technology. The microstructures of the layer were detected by optical microscopy （OM...Fe-based layer with Ti（CxN1-x） particulates on Adamite roller surface was obtained by a 5 kW traverse-flowing CO2 laser cladding technology. The microstructures of the layer were detected by optical microscopy （OM）,X-ray diffraction （XRD）,scanning electron microscopy （SEM）,and electron probe microscopy analysis （EMPA）. The tests of wear resistance was carried out on the test machine. It was seen that a good metallurgical bonding between the coating and the substrate was achieved. The microstructure contains bulky dendritic crystal and small size Ti（CxN1-x） grains that are uniformly distributed in the solid solution matrix. The wear tests showed that the laser coating provided an excellent wear resistance property at room temperature.展开更多
基金Sponsored by Shandong Natural Science Foundation of China (Z2006F07)
文摘Fe-based layer with Ti（CxN1-x） particulates on Adamite roller surface was obtained by a 5 kW traverse-flowing CO2 laser cladding technology. The microstructures of the layer were detected by optical microscopy （OM）,X-ray diffraction （XRD）,scanning electron microscopy （SEM）,and electron probe microscopy analysis （EMPA）. The tests of wear resistance was carried out on the test machine. It was seen that a good metallurgical bonding between the coating and the substrate was achieved. The microstructure contains bulky dendritic crystal and small size Ti（CxN1-x） grains that are uniformly distributed in the solid solution matrix. The wear tests showed that the laser coating provided an excellent wear resistance property at room temperature.