The interfacial reaction behavior of Al and Ti_3AlC_(2)at different pouring temperatures and its effect on the microstructure and mechanical properties of the composites were investigated.The results show that the add...The interfacial reaction behavior of Al and Ti_3AlC_(2)at different pouring temperatures and its effect on the microstructure and mechanical properties of the composites were investigated.The results show that the addition of3.0 wt.%Ti_3AlC_(2)refines the average grain size ofα(Al)in the composite by 50.1%compared to Al6061 alloy.Morphological analyses indicate that an in-situ Al_(3Ti)transition layer of-180 nm in thickness is generated around the edge of Ti_3AlC_(2)at 720℃,forming a well-bonded Al-Al_(3Ti)interface.At this processing temperature,the ultimate tensile strength of A16061-3.0 wt.%Ti_3AlC_(2)composite is 199.2 MPa,an improvement of 41.5%over the Al6061 matrix.Mechanism analyses further elucidate that 720℃is favourable for forming the nano-sized transition layer at the Ti_3AlC_(2)edges.And,the thermal mismatch strengthening plays a dominant role in this state,with a strengthening contribution of about 74.8%.展开更多
Cold-rolled Ti/Al laminated composites were annealed at 525−625℃for 0−128 h,and the interfacial microstructure evolution was investigated.The results indicate that only the TiAl_(3) phase was formed at the Ti/Al inte...Cold-rolled Ti/Al laminated composites were annealed at 525−625℃for 0−128 h,and the interfacial microstructure evolution was investigated.The results indicate that only the TiAl_(3) phase was formed at the Ti/Al interface;most of TiAl_(3) grains were fine equiaxed with average sizes ranging from hundreds of nanometers to several microns and the TiAl_(3) grain size increased with increasing annealing time and/or temperature,but the effect of annealing temperature on the TiAl_(3) grain size was far greater than that of annealing time.The growth of the TiAl_(3) phase consisted of two stages.The initial stage was governed by chemical reaction with a reaction activation energy of 195.75 kJ/mol,and the reaction rate constant of the TiAl_(3) phase was larger as the Ti/Al interface was bonded with fresh surfaces.At the second stage,the growth was governed by diffusion,the diffusion activation energy was 33.69 kJ/mol,and the diffusion growth rate constant of the TiAl_(3) phase was mainly determined by the grain boundary diffusion owing to the smaller TiAl_(3) grain size.展开更多
Al-Al3Ti composites were prepared by a direct reaction method, in which Al3Ti was formed by the reaction of Ti and Al in aluminum alloy melt. The morphology of Al3Ti changes apparently from the fine particle, needle-l...Al-Al3Ti composites were prepared by a direct reaction method, in which Al3Ti was formed by the reaction of Ti and Al in aluminum alloy melt. The morphology of Al3Ti changes apparently from the fine particle, needle-like to large block with the increase of Al3Ti content. The addition of magnesium can markedly change the morphology of Al3Ti and reduce their size. Short rod-like Al3Ti was formed and homogeneous distribution was obtained with the addition of 3 wt.% Mg. The effect of Al3Ti and Mg on the microstructure of Al-Al3Ti composites and the mechanism were also discussed.展开更多
Ti/Cu/Ti laminated composites were fabricated by corrugated rolling(CR) and flat rolling(FR) method.Microstructure and mechanical properties of CR and FR laminated composites were investigated by scanning electron mic...Ti/Cu/Ti laminated composites were fabricated by corrugated rolling(CR) and flat rolling(FR) method.Microstructure and mechanical properties of CR and FR laminated composites were investigated by scanning electron microscopy, numerical simulation methods, peel and tensile examinations. The effect of CR and FR was comparatively analyzed. The results showed that the CR and FR laminated composites exhibited different effective plastic strain distributions of the Ti layer and Cu layer at the interface. The recrystallization texture, prismatic texture and pyramidal texture were developed in the Ti layer by CR, while the R-Goss texture and shear texture were developed in the Cu layer by CR. The typical deformation texture components were developed in the Ti layer and Cu layer of FR laminated composites. The CR laminated composites had higher bond strength, tensile strength and ductility.展开更多
A novel technique for fabricating TiB_2/Al composites in molten aluminum was introduced. The formation mechanism of brittleAl,Ti particulates up to 30 m in size produced in the composites was studied and a method of e...A novel technique for fabricating TiB_2/Al composites in molten aluminum was introduced. The formation mechanism of brittleAl,Ti particulates up to 30 m in size produced in the composites was studied and a method of eliminating them was proposed. The resultsshow that (l) the brittle Al,Ti particulates are always present in the composites when the molar ratio of Ti to B 'T,:nB is l:2; and (2) theformation of the brittle Al,Ti phase can be avoided entirely from the final product by using a proper 'T,:nB of l:4 in the Ti-B-Al preforms.In the former case, the tensile elongation of the composite is only 4%, much lower than the value of pure aluminum (20%). In the latercase, the tensile elongation of this composite is 10%, higher than the value of the composite with a lot ofAl,Ti (4%), whereas the ultimatetensile stfength of the former is nearly that of the later.展开更多
Ceramic composites Al_2O_3/(W, Ti)C/Cr_3C_2 with different contents of Cr_3C_2 and (W, Ti)C particles, and with the additive Y_2O_3, were fabricated with hot-pressing technique at 1700 ℃ under 28 MPa pressure for 30 ...Ceramic composites Al_2O_3/(W, Ti)C/Cr_3C_2 with different contents of Cr_3C_2 and (W, Ti)C particles, and with the additive Y_2O_3, were fabricated with hot-pressing technique at 1700 ℃ under 28 MPa pressure for 30 min in N_2 atmosphere. The mechanical properties were tested, and the microstructure was investigated by environment scanning electron microscope (ESEM), transmission electron microscope (TEM), energy dispersive analysis using X-ray (EDAX) and optical microscope (OM). Results indicate that the incorporation of Cr_3C_2 and (W,Ti)C particles can suppress the grain growth of the others, and the toughening and strengthening effects mainly originate from nano-particles, dispersion toughening and solidification strengthening. The multiphase composite ceramic material Al_2O_3/10%Cr_3C_2/20%(W,Ti)C shows good mechanical properties, especially the fracture toughness increases from 4.0 MPa·m 1/2 (Monolithic Al_2O_3 ceramic) to 8.92 MPa·m 1/2, the flexural strength from 260～340 MPa (Monolithic Al_2O_3 ceramic) to 496 MPa, due to incorporation of the suitable contents of Cr_3C_2 and (W,Ti)C particles.展开更多
A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer...A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.展开更多
Ti/Al 2O 3 composite with improved mechanical properties was synthesized by th e spark plasma sintering. The effect of Nb on the microstructure of the composit e was analyzed by TEM, SEM and so on. The experimental ...Ti/Al 2O 3 composite with improved mechanical properties was synthesized by th e spark plasma sintering. The effect of Nb on the microstructure of the composit e was analyzed by TEM, SEM and so on. The experimental results indicate that the bending strength, fracture toughness, micro-hardness and relative density of t he composite are 897.29MPa, 17.38MPa·m 1/2, 17.13GPa and 99.24% respec tively when adding 1.5vol%Nb. The bending strength is improved by reason of form ing dislocation ring and transfering fracture mode from intergranular to mixture fracture of intergranular and transgranular. The crack propagating is mainly th e deflection bridging. It indicates a reduction of crack driving force and an in crease in crack growth resistance,which results in toughness enhanced.展开更多
基金financially supported by the National Natural Science Foundation of China(No.51965040)Science and Technology Project of Jiangxi Provincial Department of Transportation,China(No.2022H0048)。
文摘The interfacial reaction behavior of Al and Ti_3AlC_(2)at different pouring temperatures and its effect on the microstructure and mechanical properties of the composites were investigated.The results show that the addition of3.0 wt.%Ti_3AlC_(2)refines the average grain size ofα(Al)in the composite by 50.1%compared to Al6061 alloy.Morphological analyses indicate that an in-situ Al_(3Ti)transition layer of-180 nm in thickness is generated around the edge of Ti_3AlC_(2)at 720℃,forming a well-bonded Al-Al_(3Ti)interface.At this processing temperature,the ultimate tensile strength of A16061-3.0 wt.%Ti_3AlC_(2)composite is 199.2 MPa,an improvement of 41.5%over the Al6061 matrix.Mechanism analyses further elucidate that 720℃is favourable for forming the nano-sized transition layer at the Ti_3AlC_(2)edges.And,the thermal mismatch strengthening plays a dominant role in this state,with a strengthening contribution of about 74.8%.
基金the financial supports from the S&T Program of Hebei Province,China(No.20373901D)the National Natural Science Foundation of China(Nos.51807047,51804095)+2 种基金the National Science Foundation of Hebei Province,China(No.E2019402433)the Youth Top Talents Science and Technology Research Project of Hebei Province University,China(No.BJ2019003)the Research and Development Project of Science and Technology of Handan City,China(No.19422111008-19).
文摘Cold-rolled Ti/Al laminated composites were annealed at 525−625℃for 0−128 h,and the interfacial microstructure evolution was investigated.The results indicate that only the TiAl_(3) phase was formed at the Ti/Al interface;most of TiAl_(3) grains were fine equiaxed with average sizes ranging from hundreds of nanometers to several microns and the TiAl_(3) grain size increased with increasing annealing time and/or temperature,but the effect of annealing temperature on the TiAl_(3) grain size was far greater than that of annealing time.The growth of the TiAl_(3) phase consisted of two stages.The initial stage was governed by chemical reaction with a reaction activation energy of 195.75 kJ/mol,and the reaction rate constant of the TiAl_(3) phase was larger as the Ti/Al interface was bonded with fresh surfaces.At the second stage,the growth was governed by diffusion,the diffusion activation energy was 33.69 kJ/mol,and the diffusion growth rate constant of the TiAl_(3) phase was mainly determined by the grain boundary diffusion owing to the smaller TiAl_(3) grain size.
文摘Al-Al3Ti composites were prepared by a direct reaction method, in which Al3Ti was formed by the reaction of Ti and Al in aluminum alloy melt. The morphology of Al3Ti changes apparently from the fine particle, needle-like to large block with the increase of Al3Ti content. The addition of magnesium can markedly change the morphology of Al3Ti and reduce their size. Short rod-like Al3Ti was formed and homogeneous distribution was obtained with the addition of 3 wt.% Mg. The effect of Al3Ti and Mg on the microstructure of Al-Al3Ti composites and the mechanism were also discussed.
基金financially supported by the National Key R&D Program of China (No.2018YFA0707300)the Natural Science Foundation of Shanxi Province,China (No.201801D221131)+2 种基金the National Natural Science Foundation of China (Nos.51905372,51904206,51805359,52075359)Shanxi Province Science and Technology Major Project,China (No.20181102011)China Postdoctoral Science Foundation (No.2020M670705)。
文摘Ti/Cu/Ti laminated composites were fabricated by corrugated rolling(CR) and flat rolling(FR) method.Microstructure and mechanical properties of CR and FR laminated composites were investigated by scanning electron microscopy, numerical simulation methods, peel and tensile examinations. The effect of CR and FR was comparatively analyzed. The results showed that the CR and FR laminated composites exhibited different effective plastic strain distributions of the Ti layer and Cu layer at the interface. The recrystallization texture, prismatic texture and pyramidal texture were developed in the Ti layer by CR, while the R-Goss texture and shear texture were developed in the Cu layer by CR. The typical deformation texture components were developed in the Ti layer and Cu layer of FR laminated composites. The CR laminated composites had higher bond strength, tensile strength and ductility.
文摘A novel technique for fabricating TiB_2/Al composites in molten aluminum was introduced. The formation mechanism of brittleAl,Ti particulates up to 30 m in size produced in the composites was studied and a method of eliminating them was proposed. The resultsshow that (l) the brittle Al,Ti particulates are always present in the composites when the molar ratio of Ti to B 'T,:nB is l:2; and (2) theformation of the brittle Al,Ti phase can be avoided entirely from the final product by using a proper 'T,:nB of l:4 in the Ti-B-Al preforms.In the former case, the tensile elongation of the composite is only 4%, much lower than the value of pure aluminum (20%). In the latercase, the tensile elongation of this composite is 10%, higher than the value of the composite with a lot ofAl,Ti (4%), whereas the ultimatetensile stfength of the former is nearly that of the later.
文摘Ceramic composites Al_2O_3/(W, Ti)C/Cr_3C_2 with different contents of Cr_3C_2 and (W, Ti)C particles, and with the additive Y_2O_3, were fabricated with hot-pressing technique at 1700 ℃ under 28 MPa pressure for 30 min in N_2 atmosphere. The mechanical properties were tested, and the microstructure was investigated by environment scanning electron microscope (ESEM), transmission electron microscope (TEM), energy dispersive analysis using X-ray (EDAX) and optical microscope (OM). Results indicate that the incorporation of Cr_3C_2 and (W,Ti)C particles can suppress the grain growth of the others, and the toughening and strengthening effects mainly originate from nano-particles, dispersion toughening and solidification strengthening. The multiphase composite ceramic material Al_2O_3/10%Cr_3C_2/20%(W,Ti)C shows good mechanical properties, especially the fracture toughness increases from 4.0 MPa·m 1/2 (Monolithic Al_2O_3 ceramic) to 8.92 MPa·m 1/2, the flexural strength from 260～340 MPa (Monolithic Al_2O_3 ceramic) to 496 MPa, due to incorporation of the suitable contents of Cr_3C_2 and (W,Ti)C particles.
基金Projects (51101096, 51002093) supported by the National Natural Science Foundation of ChinaProject (1052nm05000) supported by Special Foundation of the Shanghai Science and Technology Commission for Nano-Materials ResearchProject (J51042) supported by Leading Academic Discipline Project of the Shanghai Education Commission, China
文摘A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.
基金Funded by the National Natural Science Foundation of China (No. 50232020) and the Natural Science Foundation of Shandong Province(No.2002F21)
文摘Ti/Al 2O 3 composite with improved mechanical properties was synthesized by th e spark plasma sintering. The effect of Nb on the microstructure of the composit e was analyzed by TEM, SEM and so on. The experimental results indicate that the bending strength, fracture toughness, micro-hardness and relative density of t he composite are 897.29MPa, 17.38MPa·m 1/2, 17.13GPa and 99.24% respec tively when adding 1.5vol%Nb. The bending strength is improved by reason of form ing dislocation ring and transfering fracture mode from intergranular to mixture fracture of intergranular and transgranular. The crack propagating is mainly th e deflection bridging. It indicates a reduction of crack driving force and an in crease in crack growth resistance,which results in toughness enhanced.