The two series of as-deposited and annealed Ti/Co/Ti thin films were deposited by magnetron sputtering onto glass substrates at room temperature. The structural and magnetic properties of the films at room temperature...The two series of as-deposited and annealed Ti/Co/Ti thin films were deposited by magnetron sputtering onto glass substrates at room temperature. The structural and magnetic properties of the films at room temperature were investigated as function of Co layer thickness. X-ray diffraction (XRD) profiles show Co nanograins are formed as the hexagonal-close-packed (hcp) structure. The perpendicular coercivity of the Ti(15 nm)/Co(30 nm)/Ti(15 nm) film annealed at 450 ℃ for 30 min is about 288 kA·m-1.展开更多
基金This work was financially supported by the National Natural Science Foundation of China (No.10274018) and the Foundation of Hebei Provincial Education Department (No.2002116).
文摘The two series of as-deposited and annealed Ti/Co/Ti thin films were deposited by magnetron sputtering onto glass substrates at room temperature. The structural and magnetic properties of the films at room temperature were investigated as function of Co layer thickness. X-ray diffraction (XRD) profiles show Co nanograins are formed as the hexagonal-close-packed (hcp) structure. The perpendicular coercivity of the Ti(15 nm)/Co(30 nm)/Ti(15 nm) film annealed at 450 ℃ for 30 min is about 288 kA·m-1.