Ti/Sb-SnO2 anodes were prepared by thermal decomposition to examine the influence of the amount of Sb dopant on the structure and electrocatalytic capability of the electrodes in the oxidation of 4-chlorophenol. The p...Ti/Sb-SnO2 anodes were prepared by thermal decomposition to examine the influence of the amount of Sb dopant on the structure and electrocatalytic capability of the electrodes in the oxidation of 4-chlorophenol. The physicochemical properties of the Sb-SnO2 coating were markedly influenced by different amounts of Sb dopant. The electrodes, which contained 5% Sb dopant in the coating, presented a much more homogenous surface and much smaller mud-cracks, compared with Ti/Sb-SnO2 electrodes containing 10% or 15% Sb dopant, which exibited larger mud cracks and pores on the surface. However, the main microstructure remained unchanged with the addition of the Sb dopant. No new crystal phase was observed by X-ray diffraction （XRD）. The electrochemical oxidation of 4-chlorophenol on the Ti/SnO2 electrode with 5% Sb dopant was inclined to electrochemical combustion; while for those containing more Sb dopant, intermediate species were accumulated. The electrodes with 5% Sb dopant showed the highest efficiency in the bulk electrolysis of 4-chlorophenol at a current density of 20 mA/cm^2 for 180 min; and the removal rates of 4-chlorophenol and COD were 51.0% and 48.9%, respectively.展开更多
Ti3C2Tx,a novel two-dimensional layer material,is widely used as electrode materials of supercapacitor due to its good metal conductivity,redox reaction active surface,and so on.However,there are many challenges to be...Ti3C2Tx,a novel two-dimensional layer material,is widely used as electrode materials of supercapacitor due to its good metal conductivity,redox reaction active surface,and so on.However,there are many challenges to be addressed which impede Ti3C2Tx obtaining the ideal specific capacitance,such as restacking,re-crushing,and oxidation of titanium.Recently,many advances have been proposed to enhance capacitance performance of Ti3C2Tx.In this review,recent strategies for improving specific capacitance are summarized and compared,for example,film formation,surface modification,and composite method.Furthermore,in order to comprehend the mechanism of those efforts,this review analyzes the energy storage performance in different electrolytes and influencing factors.This review is expected to predict redouble research direction of Ti3C2Tx materials in supercapacitors.展开更多
Praseodymium was selected as a promoter for SnO2/Ti electrode to improve the electrocatalytic performance by electrodeposition in pharmaceutical wastewater treatment; the micrograph and the structure were characterize...Praseodymium was selected as a promoter for SnO2/Ti electrode to improve the electrocatalytic performance by electrodeposition in pharmaceutical wastewater treatment; the micrograph and the structure were characterized by SEM and XRD. Mixture uniform design was used in the optimization of the electrolytic conditions; mathematical model was established according to the rate of wiping COD off, which revealed the relationship between the current intensity, time of electrolysis, the amount of doped Pr, and the ratio of area （SnOJTi：Al）. On the basis of the analysis of the empirical model, the optimized parameters had been obtained; the rate of wiping COD off was up to 94.9%, it decreased from 392 to 20 mg/L. Experimental results showed that the electrocatalytic performance of the electrode doped with Pr was superior for the treatment of pharmaceutical wastewater.展开更多
Regulation of the electronic structure and interface property becomes a major strategy in the preparation of electrocatalyst.This paper reports the synthesis of cerium(Ce)and sodium dodecyl benzene sulfonate(SDBS)como...Regulation of the electronic structure and interface property becomes a major strategy in the preparation of electrocatalyst.This paper reports the synthesis of cerium(Ce)and sodium dodecyl benzene sulfonate(SDBS)comodified Ti/PbO_(2)electrodes(Ti/PbO2CeSDBS).Ce and SDBS could greatly change the electronic structure and interface property of PbO2.Ti/PbO_(2)CeSDBS exhibited excellent electrocatalytic activity and stability in Rhodamine B(RhB)electrocatalytic oxidation reaction.The improved electrocatalytic activity associates with the synergistic effect of electronic and interface factors.In the electrochemical degradation of RhB,the removal efficiencies of RhB and COD are about 0.880 and 0.694 respectively after the electrolysis of 220 min with Ti/PbO_(2)Ce4SDBS40,which are higher than the contrast Ti/PbO_(2)electrodes.In the meantime,the accelerated lifetime of Ti/PbO_(2)Ce4SDBS40 is more than 6.2 times than that of Ti/PbO_(2).展开更多
The degradation of ethinylestradiol (EE, an orally bio-active estrogen) in an aqueous-methanolic solution using a Ti/TiO2 thin-film electrode and UV radiation (a photoelectrocatalytic system) was evaluated. Hence, HPL...The degradation of ethinylestradiol (EE, an orally bio-active estrogen) in an aqueous-methanolic solution using a Ti/TiO2 thin-film electrode and UV radiation (a photoelectrocatalytic system) was evaluated. Hence, HPLC/UV analysis shows that EE (at 0.34 mmol) is totally consumed after 30 minutes of exposure to the photoelectrocatalytic system in the presence of Na2SO4 (0.1 mol·L-1) and with an applied bias potential of +1.0 V versus the Ag/AgCl reference electrode. Moreover, monitoring by direct infusion electrospray ionization mass spectrometry (ESI-MS) and SPME-GC/ MS (solid phase microextraction coupled with gas chromatography-mass spectrometry) reveals that apparently no degradation products are formed under these conditions. Hence, this study demonstrates that the photoelectrocatalytic system can be efficiently used to promote the complete degradation (and likely mineralization) of this hormone under these conditions.展开更多
苯胺是一种重要的化工原料,广泛应用于印染、制药、造纸、橡胶等领域.随着化工行业的迅速发展,苯胺的需求量越来越大.然而,苯胺毒性高,大量使用势必造成水体中苯胺浓度的升高,给人类健康及生态环境造成危害.因此,急需一种高效、洁净、...苯胺是一种重要的化工原料,广泛应用于印染、制药、造纸、橡胶等领域.随着化工行业的迅速发展,苯胺的需求量越来越大.然而,苯胺毒性高,大量使用势必造成水体中苯胺浓度的升高,给人类健康及生态环境造成危害.因此,急需一种高效、洁净、经济的方法处理含苯胺废水.电化学氧化法比较新颖,相比传统废水处理方法,它具有高效、简单、清洁等优点,因此被应用于很多废水处理当中,但过多的能耗限制了其进一步广泛应用.阳极作为电化学氧化技术的核心部件,直接影响到电化学氧化反应性能.因此开发出一种高效、经济的阳极材料很有必要.此外,对苯胺降解条件的优化也同样重要.关于苯胺电化学氧化,已有的研究包括Pt电极、PbO_2电极和石墨电极等阳极材料.比较而言,Ti/Sb-SnO_2电极具有制备工艺简单,析氧过电位较高,材料廉价和电催化性能较强等优点.然而,它的稳定性仍有待提高.因此本文制备了一种高稳定性的Ti/TiO_xH_y/Sb-SnO_2电极,并用于处理苯胺废水.较为系统地研究了电流密度、苯胺初始浓度、pH、NaCl投加量及反应器类型对苯胺电催化氧化性能的影响,同时采用扫描电镜(SEM)、X射线衍射(XRD)和电化学测试对该电极进行了表征,并应用紫外-可见光谱、化学需氧量、电流效率及能耗对不同参数进行评定和优化.SEM及XRD结果表明,Ti/TiO_xH_y/Sb-SnO_2电极涂层覆盖比较完全、紧实,未出现裂缝的发生,因而有利于提高电极稳定性.循环伏安测试结果表明,此电极具备较高的析氧过电位(2.0 V vs Ag/AgCl)及电化学孔隙度(76.31%),因此有利于电极催化性能的提高.苯胺电化学氧化实验结果发现,该反应符合准一级动力学模型,且高电流密度、酸性环境、适当NaCl投加量(0.2 wt%)更有利于苯胺的降解.另外,Ti/TiO_xH_y/Sb-SnO_2电极在三维反应器中对苯胺的处理效果要远远好于在二维反应器中.可以看出,Ti/TiO_xH_y/Sb-SnO_2电极具有较好的处理苯胺性能,可为苯胺废水处理的应用提供了一定的理论指导.展开更多
基金Project supported by the Institute of Environmental Engineering,Peking University and China Postdoctoral Science Foundation(No.2005037032)
文摘Ti/Sb-SnO2 anodes were prepared by thermal decomposition to examine the influence of the amount of Sb dopant on the structure and electrocatalytic capability of the electrodes in the oxidation of 4-chlorophenol. The physicochemical properties of the Sb-SnO2 coating were markedly influenced by different amounts of Sb dopant. The electrodes, which contained 5% Sb dopant in the coating, presented a much more homogenous surface and much smaller mud-cracks, compared with Ti/Sb-SnO2 electrodes containing 10% or 15% Sb dopant, which exibited larger mud cracks and pores on the surface. However, the main microstructure remained unchanged with the addition of the Sb dopant. No new crystal phase was observed by X-ray diffraction （XRD）. The electrochemical oxidation of 4-chlorophenol on the Ti/SnO2 electrode with 5% Sb dopant was inclined to electrochemical combustion; while for those containing more Sb dopant, intermediate species were accumulated. The electrodes with 5% Sb dopant showed the highest efficiency in the bulk electrolysis of 4-chlorophenol at a current density of 20 mA/cm^2 for 180 min; and the removal rates of 4-chlorophenol and COD were 51.0% and 48.9%, respectively.
基金National Natural Science Foundation of China with Grant No.21905304Natural Science Foundation of Shandong Province(No.ZR2019BEM031)the Fundamental Research Funds for the Central Universities(Nos.18CX02158A and 19CX05001A).
文摘Ti3C2Tx,a novel two-dimensional layer material,is widely used as electrode materials of supercapacitor due to its good metal conductivity,redox reaction active surface,and so on.However,there are many challenges to be addressed which impede Ti3C2Tx obtaining the ideal specific capacitance,such as restacking,re-crushing,and oxidation of titanium.Recently,many advances have been proposed to enhance capacitance performance of Ti3C2Tx.In this review,recent strategies for improving specific capacitance are summarized and compared,for example,film formation,surface modification,and composite method.Furthermore,in order to comprehend the mechanism of those efforts,this review analyzes the energy storage performance in different electrolytes and influencing factors.This review is expected to predict redouble research direction of Ti3C2Tx materials in supercapacitors.
基金the Fund of the Natural Science of Guangxi (0731015)
文摘Praseodymium was selected as a promoter for SnO2/Ti electrode to improve the electrocatalytic performance by electrodeposition in pharmaceutical wastewater treatment; the micrograph and the structure were characterized by SEM and XRD. Mixture uniform design was used in the optimization of the electrolytic conditions; mathematical model was established according to the rate of wiping COD off, which revealed the relationship between the current intensity, time of electrolysis, the amount of doped Pr, and the ratio of area （SnOJTi：Al）. On the basis of the analysis of the empirical model, the optimized parameters had been obtained; the rate of wiping COD off was up to 94.9%, it decreased from 392 to 20 mg/L. Experimental results showed that the electrocatalytic performance of the electrode doped with Pr was superior for the treatment of pharmaceutical wastewater.
基金Thanks to the financial support from the Science and technology project of Shaanxi Province(2017ZDXM-GY-041).
文摘Regulation of the electronic structure and interface property becomes a major strategy in the preparation of electrocatalyst.This paper reports the synthesis of cerium(Ce)and sodium dodecyl benzene sulfonate(SDBS)comodified Ti/PbO_(2)electrodes(Ti/PbO2CeSDBS).Ce and SDBS could greatly change the electronic structure and interface property of PbO2.Ti/PbO_(2)CeSDBS exhibited excellent electrocatalytic activity and stability in Rhodamine B(RhB)electrocatalytic oxidation reaction.The improved electrocatalytic activity associates with the synergistic effect of electronic and interface factors.In the electrochemical degradation of RhB,the removal efficiencies of RhB and COD are about 0.880 and 0.694 respectively after the electrolysis of 220 min with Ti/PbO_(2)Ce4SDBS40,which are higher than the contrast Ti/PbO_(2)electrodes.In the meantime,the accelerated lifetime of Ti/PbO_(2)Ce4SDBS40 is more than 6.2 times than that of Ti/PbO_(2).
文摘The degradation of ethinylestradiol (EE, an orally bio-active estrogen) in an aqueous-methanolic solution using a Ti/TiO2 thin-film electrode and UV radiation (a photoelectrocatalytic system) was evaluated. Hence, HPLC/UV analysis shows that EE (at 0.34 mmol) is totally consumed after 30 minutes of exposure to the photoelectrocatalytic system in the presence of Na2SO4 (0.1 mol·L-1) and with an applied bias potential of +1.0 V versus the Ag/AgCl reference electrode. Moreover, monitoring by direct infusion electrospray ionization mass spectrometry (ESI-MS) and SPME-GC/ MS (solid phase microextraction coupled with gas chromatography-mass spectrometry) reveals that apparently no degradation products are formed under these conditions. Hence, this study demonstrates that the photoelectrocatalytic system can be efficiently used to promote the complete degradation (and likely mineralization) of this hormone under these conditions.
基金supported by the National Natural Science Foundation of China(21507104)the Fundamental Research Funds for the Central Universities of China
文摘苯胺是一种重要的化工原料,广泛应用于印染、制药、造纸、橡胶等领域.随着化工行业的迅速发展,苯胺的需求量越来越大.然而,苯胺毒性高,大量使用势必造成水体中苯胺浓度的升高,给人类健康及生态环境造成危害.因此,急需一种高效、洁净、经济的方法处理含苯胺废水.电化学氧化法比较新颖,相比传统废水处理方法,它具有高效、简单、清洁等优点,因此被应用于很多废水处理当中,但过多的能耗限制了其进一步广泛应用.阳极作为电化学氧化技术的核心部件,直接影响到电化学氧化反应性能.因此开发出一种高效、经济的阳极材料很有必要.此外,对苯胺降解条件的优化也同样重要.关于苯胺电化学氧化,已有的研究包括Pt电极、PbO_2电极和石墨电极等阳极材料.比较而言,Ti/Sb-SnO_2电极具有制备工艺简单,析氧过电位较高,材料廉价和电催化性能较强等优点.然而,它的稳定性仍有待提高.因此本文制备了一种高稳定性的Ti/TiO_xH_y/Sb-SnO_2电极,并用于处理苯胺废水.较为系统地研究了电流密度、苯胺初始浓度、pH、NaCl投加量及反应器类型对苯胺电催化氧化性能的影响,同时采用扫描电镜(SEM)、X射线衍射(XRD)和电化学测试对该电极进行了表征,并应用紫外-可见光谱、化学需氧量、电流效率及能耗对不同参数进行评定和优化.SEM及XRD结果表明,Ti/TiO_xH_y/Sb-SnO_2电极涂层覆盖比较完全、紧实,未出现裂缝的发生,因而有利于提高电极稳定性.循环伏安测试结果表明,此电极具备较高的析氧过电位(2.0 V vs Ag/AgCl)及电化学孔隙度(76.31%),因此有利于电极催化性能的提高.苯胺电化学氧化实验结果发现,该反应符合准一级动力学模型,且高电流密度、酸性环境、适当NaCl投加量(0.2 wt%)更有利于苯胺的降解.另外,Ti/TiO_xH_y/Sb-SnO_2电极在三维反应器中对苯胺的处理效果要远远好于在二维反应器中.可以看出,Ti/TiO_xH_y/Sb-SnO_2电极具有较好的处理苯胺性能,可为苯胺废水处理的应用提供了一定的理论指导.
文摘采用电沉积法镀制Ti/Sb-SnO2/β-PbO2电极,研究电沉积时间、镀液温度、pH值、NaF浓度,以及电流密度等因素对电极催化活性和稳定性的影响规律.结果表明,当电沉积时间为1 h,镀液温度为60℃,镀液pH值为1,NaF浓度为0.04 mol.L-1,组合电流密度为600/400 A.m-2(梯度电流密度)时,电极性能最佳,对苯酚降解率达91.4%,强化寿命为23 h.