Pitting corrosion behavior and corrosion protection performance of cold sprayed double layered noble barrier coating on magnesium-based alloy in chloride containing solutions

Nitrogen processed, cold sprayed commercially pure(CP)-Al coatings on Mg-based alloys mostly lack acceptable hardness, wear resistance and most importantly are highly susceptible to localized corrosion in chloride containing solutions. In this research, commercially pure α-Ti top coating having good pitting potential(~1293 mV_(SCE)), high microhardness(HV_(0.025): 263.03) and low wear rate was applied on a CP-Al coated Mg-based alloy using high pressure cold spray technology. Potentiodynamic polarization(PDP) curves indicated that the probability of transition from metastable pits to the stable pits for cold spayed(CS) Al coating is considerably higher compared to that with the CS Ti top coating(for Ti/Al/Mg system). In addition, CS Ti top coating was in the passivation region in most pH ranges even after 48 h immersion in 3.5 wt% NaCl solution. The stored energy in the CS Ti top coating(as a passive metal) was presumed to be responsible for the easy passivation. Immersion tests indicated no obvious pits formation on the intact CS Ti top coating surface and revealed effective corrosion protection performance of the CS double layered noble barrier coatings on Mg alloys in 3.5 wt% NaCl solution even after 264 h.

Effects of surface roughness of substrate on properties of Ti/TiN/Zr/ZrN multilayer coatings

Ti/TiN/Zr/ZrN multilayer coatings were deposited on Cr_17Ni_2 steel substrates with different surface roughnesses by vacuum cathodic arc deposition method. Microstructure, micro-hardness, adhesion strength and cross-sectional morphology of the obtained multilayer coatings were investigated. The results show that the Vickers hardness of Ti/TiN/Zr/ZrN multilayer coating, with a film thickness of 11.37 μm, is 29.36 GPa. The erosion and salt spray resistance performance of Cr_17Ni_2 steel substrates can be evidently improved by Ti/TiN/Zr/ZrN multilayer coating. The surface roughness of Cr_17Ni_2 steel substrates plays an important role in determining the mechanical and erosion performances of Ti/TiN/Zr/ZrN multilayer coatings. Overall, a low value of the surface roughness of substrates corresponds to an improved performance of erosion and salt spray resistance of multilayer coatings. The optimized performance of Ti/TiN/Zr/ZrN multilayer coatings can be achieved provided that the surface roughness of Cr_17Ni_2 steel substrates is lower than 0.4μm.

High temperature oxidation behavior of Ti(Al,Si)_3 diffusion coating on γ-TiAl by cold spray

A Ti(Al,Si)3 diffusion coating was prepared on γ-TiAl alloy by cold sprayed Al?20Si alloy coating, followed by a heat-treatment. The isothermal and cyclic oxidation tests were conducted at 900 °C for 1000 h and 120 cycles to check the oxidation resistance of the coating. The microstructure and phase transformation of the coating before and after the oxidation were studied by SEM, XRD and EPMA. The results indicate that the diffusion coating shows good oxidation resistance. The mass gain of the diffusion coating is only a quarter of that of bare alloy. After oxidation, the diffusion coating is degraded into three layers: an inner TiAl2 layer, a two-phase intermediate layer composed of a Ti(Al,Si)3 matrix and Si-rich precipitates, and a porous layer because of the inter-diffusion between the coating and substrate.

Coating titanium on carbon steel by in-situ electrochemical reduction of solid TiO_2 layer

Ti coating on A3 steel was successfully prepared by direct electrochemical reduction of high-velocity oxy-fuel （HVOF） thermally sprayed and room-temperature dip-coating titanium dioxide coating on A3 steel in molten CaCl2 at 850 ℃. The interfacial microstructure and mutual diffusion between coating and steel substrate were investigated using scanning electron microscopy （SEM） and energy dispersive X-ray （EDX） spectroscopy. The results show that the precursory TiO2 coating prepared by HVOF has closer contact and better adhesion with the A3 steel substrate. After electrolysis, all of the electro-generated Ti coatings show intact contact with the substrates, regardless of the original contact situation between TiO2 layer and the steel substrate in the precursors. The inter-diffusion between the iron substrate and the reduced titanium takes place at the interface. The results demonstrate the possibility of the surface electrochemical metallurgy （SECM） is a promising surface engineering and additive manufacturing method.

Ti含量对氩弧熔覆CoCrFeNiCuTi_(x)高熵合金涂层组织及性能的影响

采用氩弧熔覆技术在Q235钢基体表面制备了CoCrFeNiCuTi_(x)(x表示摩尔比值,x=0、0.3、0.5、0.8和1)高熵合金涂层,研究了Ti含量对CoCrFeNiCuTi_(x)高熵合金微观结构和力学性能的影响。结果表明,不同Ti含量的CoCrFeNiCuTi_(x)高熵合金均为FCC单相固溶体。CoCrFeNiCu合金的微观组织为柱状晶结构。随着Ti的加入,微观组织中开始出现析出相,且Ti含量越高,析出相越多。同时Ti的加入明显提高了合金的显微硬度,当Ti的摩尔比为1时,涂层的截面显微硬度值达到最高值439.54 HV0.1。Ti对CoCrFeNiCuTi_(x)高熵合金的耐磨性具有显著影响,CoCrFeNiCuTi合金表现出最好的耐磨性。随着Ti含量的升高,合金的磨损机理由黏着磨损转化成黏着磨损与氧化磨损并存。

TiC-Fe coatings prepared by flame spray synthesis process

A new process, flame spray synthesis (FSS), has been developed for producing ceramic containing composite coatings. By combining self propagation high temperature synthesis (SHS) and flame spraying, the cermet based material was synthesized and deposited simultaneously. TiC Fe coatings were deposited from commercial ferrotitanium, iron and graphite powders by the flame spraying synthesis process. Microstructure analyses revealed that TiC was synthesized during spraying, and that submicron and round TiC particles were dispersed within an iron matrix. Flame spray synthesized coatings were composed of alternate soft and hard layers, whose hardness were 3.0～6.0 GPa and 11～13 GPa, respectively.

Salt spray corrosion test of micro-plasma oxidation ceramic coatings on Ti alloy

Ceramic coatings were prepared on Ti-6Al-4V alloy in NaAlO2 solution by micro-plasma oxidation （MPO）. The salt spray tests of the coated samples and the substrates were carded out in a salt spray test machine. The phase composition and surface morphology of the coatings were investigated by XRD and SEAM. Severe corrosion occurred on the substrate surface, while there were no obvious corrosion phenomena on the coated samples. The coatings were composed of Al2TiO5 and a little α-Al2O3 and mille TiO2, and the salt spray test did not change the composition of the coatings. The weight loss rate of the coatings decreased with increasing MPO time because of the increase in density and thickness of the coatings. The surface morphology of the coatings was influenced by salt spray corrosion test. Among the coated samples, the coating prepared for 2 h has the best corrosion resistance under salt spray test.

Properties of hydrophobic carbon-PTFE composite coating with high corrosion resistance by facile preparation on pure Ti

Composite coatings consisting of carbon and polytetrafluoroethylene(PTFE) were prepared on Ti alloy substrate by a simple two-step process of hydrothermal and impregnation. The morphology, composition, hydrophobic and corrosion properties of the composite coatings were characterized by scanning electron microscopy(SEM), Fourier transform infrared spectroscopy(FTIR), water contact angle method, X-ray photoelectron spectroscopy(XPS) and electrochemical technique, respectively. The effect of PTFE content on the corrosion properties of the composite coatings was studied. It is found that the composite coating film exhibits a full coverage with uniformly distributed PTFE when 0.1 mol/L of glucose is used as carbon source and 20 wt.% PTFE suspension as impregnating solution. The coating with 20 wt.% PTFE has a good bonding strength with Ti plate and exhibits excellent hydrophobic property with a water contact angle of 142.3° as well as superior corrosion resistance with corrosion current density as low as 0.0045 μA/cm^2. With regard to its excellent hydrophobicity and corrosion resistance, the carbon-PTFE composite coating may find potential application in automobiles and metal corrosion industries.

Pulsed DC plasma enhanced chemical vapor deposited TiN/Ti(C,N) multilayer coatings

TiN single coatings and TiN/Ti(C,N) multilayer coatings deposited on Cr12MoV substrate have been completed by pulsed DC plasma enhanced chemical vapor deposition(PCVD) process. The SEM, XRD and microvicker’s hardness as well as the indentation test were used to study the microstructure and mechanical properties of TiN/Ti(C,N) multilayer coatings. The results show that TiN/Ti(C,N) coatings are fine and have free column structure, and carbon atoms take the place of some nitrogen atoms in Ti(C,N) coatings when lower flow ratio of CH 4 is used. The microvicker’s hardness and interfacial adhesion between TiN/Ti(C,N) coatings and Cr12MoV substrate increases more obviously than that of TiN single hard coatings due to the more dense and free column structure when process is optimized.

Structural characteristics and high-temperature tribological behaviors of laser cladded NiCoCrAlY−B_(4)C composite coatings on Ti6Al4V alloy

In order to improve the hardness and tribological performance of Ti6Al4V alloy,NiCoCrAlY-B_(4)C composite coatings with B_(4)C of 5%,10%and 15%(mass fraction)were fabricated on its surface by laser cladding(LC).The morphologies,chemical compositions and phases of obtained coatings were analyzed using scanning electronic microscope(SEM),energy dispersive spectrometer(EDS),and X-ray diffraction(XRD),respectively.The effects of B_(4)C mass fraction on the coefficient of friction(COF)and wear rate of NiCoCrAlY-B_(4)C coatings were investigated using a ball-on-disc wear tester.The results show that the NiCoCrAlY-B_(4)C coatings with different B_(4)C mass fractions are mainly composed of NiTi,NiTi_(2),α-Ti,CoO,AlB_(2),TiC,TiB and TiB_(2)phases.The COFs and wear rates of NiCoCrAlY-B_(4)C coatings decrease with the increase of B_(4)C content,which are contributed to the improvement of coating hardness by the B_(4)C addition.The wear mechanisms of NiCoCrAlY-B_(4)C coatings are changed from adhesive wear and oxidation wear to fatigue wear with the increase of B_(4)C content.

Microstructures and properties of PVD TiAlN coating deposited on cermets with different Ti(C,N)grain size

In the present work,TiAlN coatings were deposited on Ti(C,N)-based cermet substrates by physical vapor deposition method.Emphasis was focused on the influence of grain size of cermet substrates on the microstructure,growth behavior,mechanical properties,adhesion strength and wear behavior of the coatings.The results show that finer Ti(C,N)grain size leads to higher nucleation density and lower growth rate of coatings,indicating the crystallite size of the TiAlN coatings decreases with decreasing Ti(C,N)grain size.Nanoindentation tests show that the coatings deposited on cermets of the finest grain size exhibit the highest hardness(H),elastic modulus(E),H/E and H3/E2 of 34.5 GPa,433.2 GPa,0.080 and 0.22,respectively.The adhesion strength between coating and substrate is also enhanced with decreasing Ti(C,N)grain size by scratch test,which corresponds to the grain size and H/E and H3/E2 of the coating.Besides,the lower surface roughness and better mechanical properties of the coating deposited on finer grained cermet contribute to the better wear resistance of the coating.

Multifunctional hopeite nanocoating on Ti64 substrates by pulsed laser deposition and radio frequency magnetron sputtering for orthopedic implant applications:A comparative study

Functionalized implants demonstrate an upgraded approach in orthopedic implants,aiming to achieve long term success through improved bio integration.Bioceramic coatings with multifunctionality have arisen as an effective substitute for conventional coatings,owing to their combination of various properties that are essential for bio-implants,such as osteointegration and antibacterial character.In the present study,thin hopeite coatings were produced by Pulsed laser deposition(PLD)and radio frequency magnetron sputtering(RFMS)on Ti64 substrates.The obtained hopeite coatings were annealed at 500°C in ambient air and studied in terms of surface morphology,phase composition,surface roughness,adhesion strength,antibacterial efficacy,apatite forming ability,and surface wettability by scanning electron microscope(SEM),X-ray diffraction(XRD),atomic force microscope(AFM),tensometer,fluorescence-activated cell sorting(FACS),simulated body fluid(SBF)immersion test and contact angle goniometer,respectively.Furthermore,based on promising results obtained in the present work it can be summarized that the new generation multifunctional hopeite coating synthesized by two alternative new process routes of PLD and RFMS on Ti64 substrates,provides effective alternatives to conventional coatings,largely attributed to strong osteointegration and antibacterial character of deposited hopeite coating ensuring the overall stability of metallic orthopedic implants.

Effect of N-ion implantation and diamond-like carbon coating on fretting wear behaviors of Ti6Al7Nb in artificial saliva

The tribology behaviors of Ti6Al7Nb,its alloy with N-ion implantation,and its alloy with diamond-like carbon(DLC)coating were investigated in artificial saliva.Fretting wear tests of untreated,N-ion implanted and DLC coated Ti6Al7Nb alloys plate against a Si3N4ball were carried out on a reciprocating sliding fretting wear test rig.Based on the analysis of X-ray diffraction,Raman spectroscopy,3-D profiler,SEM morphologies and frictional kinetics behavior analysis,the damage behavior of surface modification layer was discussed in detail.The results indicated that the fretting wear behavior of Ti6Al7Nb alloy with N-ion implantation was increased with the dose increase of the implanted nitrogen ions.Moreover,the DLC-coated Ti6Al7Nb alloy with low ion implantation could improve the fretting wear behavior greatly.In addition,the Ti6Al7Nb with DLC coating had better ncorrosion resistance due to the special compact structure.All results suggested that the Ti6Al7Nb with DLC coating had better wear resistance than that with N-ion implantation in artificial saliva.

Zr-Ti-B-N刀具涂层在600℃恒温过程的演变研究

评估Zr-Ti-B-N刀具涂层在600℃下的耐热能力,研究不同热处理时间对涂层结构和性能的影响规律。采用高功率脉冲磁控溅射和脉冲直流磁控溅射复合技术制备Zr-Ti-B-N涂层,利用高温马弗炉对涂层进行热处理,借助纳米压痕仪、高温摩擦磨损试验机测试热处理后Zr-Ti-B-N涂层的力学性能、摩擦学性能。采用X射线衍射仪(XRD)和扫描电子显微镜(SEM)对热处理前后Zr-Ti-B-N涂层的微观结构进行表征,在高温环境下,不同热处理时间对涂层的力学性能、摩擦学性能和微观结构有显著影响。结果证明,在600℃的大气环境下,经1h热处理后,涂层的综合性能稳定,涂层硬度为23.7GPa,临界载荷为31.7N;经2h热处理后,晶粒尺寸逐渐增大,柱状晶结构变得明显,涂层硬度开始下降;经3h热处理后,涂层表面出现明显的氧化膜,晶粒尺寸增大了27.0%,摩擦系数降到最低,为0.66,临界载荷未发生明显变化。

Influence of Si Content on Properties of Ti1-xSixN Coatings

To investigate the evolution of microstructure and wear behavior of TiSiN coatings with the variation of Si in targets and lays the foundation for its controllable mass production, Ti1-xSixN composite coatings were deposited onto Si(100) and cemented carbide substrates using TiSi targets with different Si content by cathodic arc ion plating. The influences of Si on the microstructure and mechanical properties were studied. Nano-amorphous composite structure appeared in the Ti1-xSixN coatings when Si content in TiSi target was higher than 5 at%. However, further increase of Si content in TiSi target exhibited a negligible effect on the microstructure of Ti1-xSixN coatings. Hardness and deformation resistance were correlated to the content of Si in TiSi targets. Maximum hardness was obtained as the Si content in target increased up to 20 at%. Friction coefficient and wear rate significantly decreased with addition of Si in TiN coating, and then dually increased with the increase of Si content in targets.

INFLUENCE OF PHASE COMPOSITION ON PITTING CORROSION RESISTANCE OF SPUTTERED COATING OF 1Cr18Ni9Ti STAINLESS STEEL

A series of single bcc,bcc plus fcc duplex and single fcc microcrystalline coatings of 1Cr18Ni9Ti stainless steel were prepared by using sputtering technique.The resistance against pitting corrosion was studied by measurements of pitting corrosion potentials and electrochemical noise during initiation of corrosion pits.The results show that the sputtered coatings with single bcc phase or single fcc structure are more resistant to pitting corrosion than those with bcc plus fcc duplex phase structure.

Improvement on the Oxidation Resistance of a Ti_3Al Based Alloy by Cr1-xAl_xN (0≤x≤0.47) Coatings

Cr1-xAlxN coatings have been deposited on a Ti3Al based alloy by reactive sputtering method. The results of the isothermal oxidation test at 800-900℃ showed that Cr1-xAlxN coatings could remarkably reduce the oxidation rate of the alloy owing to the formation of Al2O3＋Cr2O3 mixture oxide scale on the surface of the coatings. No spallation of the coatings or oxide scales took place during the cyclic oxidation at 800℃. Ti was observed to diffuse into the coatings, the diffusion distance of which was very short, and the diffusion ability of it was proportional to the AI content in the coatings. Compared to Ti, Nb can diffuse much more easily through the whole coatings and oxide scales.

Microstructural and tribological behavior of TiAlN/MoS_2-Ti coatings

A TIA1N/MoS2-Ti coating was developed to improve the tribological characteristics of a single TiAlN coating. The MoS2-Ti layer was deposited by a DC magnetron sputtering system on the hard TiAIN coated SKD-11 steel substrate. The titanium content in the MoS2-Ti layer was 11.3 at.% determined by EPMA. The surface morphology was observed by FE-SEM. The TiAlN layer exhibited excellent adhesion and hardness. However, the deposition of an MoS2-Zi layer on the TRAIN led to a significant improvement in tribological properties without affecting the adhesion to the substrate. The MoS2-Ti layer significantly decreased the friction coefficient of the TiAIN coating, and the drop was 48% after MoS2-Ti deposition. Also, the MoS2-Ti layer remarkably decreased the wear rate of the TtA1N coating.

Microstructure evolution and mechanical properties of Ti-B-N coatings deposited by plasma-enhanced chemical vapor deposition

Ternary Ti-B-N coatings were synthesized on AISI 304 and Si wafer by plasma-enhanced chemical vapor deposition (PECVD) technique using a gaseous mixture of TiCl4,BCl3,H2,N2,and Ar.By virtue of X-ray diffraction analysis,X-ray photoelectron spectroscopy,scanning electron microscope,and high-resolution transmission electron microscope,the influences of B content on the microstructure and properties of Ti B N coatings were investigated systematically.The results indicated that the microstructure and mechanical properties of Ti-B-N coatings largely depend on the transformation from FCC-TiN phase to HCP-TiB2 phase.With increasing B content and decreasing N content in the coatings,the coating microstructure evolves gradually from FCC-TiN/a-BN to HCP-TiB2 /a-BN via FCC-TiN+HCP-TiB2/a-BN.The highest microhardness of about 34 GPa is achieved,which corresponds to the nanocomposite Ti-63%B-N (mole fraction) coating consisting of the HCP-TiB2 nano-crystallites and amorphous BN phase.The lowest friction-coefficient was observed for the nanocomposite Ti-41%B-N (mole fraction) coating consisting of the FCC-TiN nanocrystallites and amorphous BN

Reactive synthesis Ti （CN） -based metal ceramic coating by electric-spark deposition

Electric-spark deposition （ESD） was adopted for depositing a Ti（ CN） -based ceramic coating on the TC4 titanium alloy substrate using a laboratory-developed electric-spark deposition system, a nitrogen-sealed atmosphere and graphite electrode. The surface morphology, microstructure, interfacial behavior between the coatings and substrate, phase and element composition of the coatings were investigated by scanning electron microscope （ SEM ） , X-ray diffraction （ XRD ） , X-ray photoelectron spectroscopy （ XPS ） and Auger electron spectroscopy （ AES ） . Microhardness profile was measured with a Vickers microhardness tester. The results show that metallurgical bond between the coating and substrate is realized and the phase of coatings are made up of Ti（ CN ） spherocrystal and dendritic crystal, TiV and C. Ti（ CN） ceramic particles, which is in-situ synthesized by the reaction among titanium from the substrate, carbon from the graphite electrode and nitrogen from the shielding nitrogen gas, is about 600 mn and distributes dispersively among the coatings. Microharduess profile falls off with the coatings thickness increasing and the highest microhardness values of the superficial coating could be up to 1 496HV, which is six times more than that of the substrate.