Corrosion resistance and antibacterial properties of Ti−3Cu alloy prepared by selective laser melting

The corrosion resistance and antibacterial properties of Ti−3Cu alloy prepared by selective laser melting were evaluated using electrochemical experiments and a variety of antibacterial characterization.It is found that the charge transfer resistance of Ti−3Cu alloy was 4.89×10^(5)Ω∙cm^(2),which was doubled the data obtained by CP-Ti alloy.The antibacterial rates of Ti−3Cu alloy against S.mutans and P.gingivalis were 45.0%and 54.5%.And the antibacterial rates increased with the prolongation of cultivation time,reaching up to 62.8%and 68.6%,respectively.The in-situ nano Ti_(2)Cu precipitates were homogeneously distributed in the matrix of the Ti−3Cu alloy,which was the key reason of increasing the corrosion resistance.Additionally,the microscale electric fields between theα-Ti matrix and the Ti_(2)Cu was responsible for the enhancement of the antibacterial properties.

High performance micromachining of sapphire by laser induced plasma assisted ablation(LIPAA)using GHz burst mode femtosecond pulses

GHz burst-mode femtosecond(fs)laser,which emits a series of pulse trains with extremely short intervals of several hundred picoseconds,provides distinct characteristics in materials processing as compared with the conventional irradiation scheme of fs laser(single-pulse mode).In this paper,we take advantage of the moderate pulse interval of 205 ps(4.88 GHz)in the burst pulse for high-quality and high-efficiency micromachining of single crystalline sapphire by laser induced plasma assisted ablation(LIPAA).Specifically,the preceding pulses in the burst generate plasma by ablation of copper placed behind the sapphire substrate,which interacts with the subsequent pulses to induce ablation at the rear surface of sapphire substrates.As a result,not only the ablation quality but also the ablation efficiency and the fabrication resolution are greatly improved compared to the other schemes including single-pulse mode fs laser direct ablation,single-pulse mode fs-LIPAA,and nanosecond-LIPAA.

Laser processing effects on Ti−45Nb alloy surface,corrosive and biocompatible properties

The Ti−45Nb(wt.%)alloy properties were investigated in relation to its potential biomedical use.Laser surface modification was utilized to improve its performance in biological systems.As a result of the laser treatment,(Ti,Nb)O scale was formed and various morphological features appeared on the alloy surface.The electrochemical behavior of Ti−45Nb alloy in simulated body conditions was evaluated and showed that the alloy was highly resistant to corrosion deterioration regardless of additional laser surface modification treatment.Nevertheless,the improved corrosion resistance after laser treatment was evident(the corrosion current density of the alloy before laser irradiation was 2.84×10^(−8)A/cm^(2),while that after laser treatment with 5 mJ was 0.65×10^(−8)A/cm^(2))and ascribed to the rapid formation of a complex and passivating bi-modal surface oxide layer.Alloy cytotoxicity and effects of the Ti−45Nb alloy laser surface modification on the MRC-5 cell viability,morphology,and proliferation were also investigated.The Ti−45Nb alloy showed no cytotoxic effect.Moreover,cells showed improved viability and adherence to the alloy surface after the laser irradiation treatment.The highest average cell viability of 115.37%was attained for the alloy laser-irradiated with 15 mJ.Results showed that the laser surface modification can be successfully utilized to significantly improve alloy performance in a biological environment.

Ionization behavior and dynamics of picosecond laser filamentation in sapphire

Currently,laser-induced structural modifications in optical materials have been an active field of research.In this paper,we reported structural modifications in the bulk of sapphire due to picosecond(ps)laser filamentation and analyzed the ionization dynamics of the filamentation.Numerical simulations uncovered that the high-intensity ps laser pulses generate plasma through multi-photon and avalanche ionizations that leads to the creation of two distinct types of structural changes in the material.The experimental bulk modifications consist of a void like structures surrounded by cracks which are followed by a submicrometer filamentary track.By increasing laser energy,the length of the damage and filamentary track appeared to increase.In addition,the transverse diameter of the damage zone increased due to the electron plasma produced by avalanche ionizations,but no increase in the filamentary zone diameter was observed with increasing laser energy.

A High-Pulse-Energy High-Beam-Quality Tunable Ti:Sapphire Laser Using a Prism-Dispersion Cavity

A high-pulse-energy high-beam-quality tunable Ti：sapphire laser pumped by a frequency-doubled Nd：YAG laser is demonstrated. Using a fused-silica prism as the dispersion element, a tuning range of 740-855 nm is obtained. At an incident pump energy of 774mJ, the maximum output energy of 104mJ at 790nm with a pulse width of 100μs is achieved at a repetition rate of 5 Hz. To the best of our knowledge, it is the highest pulse energy at 790 nm with pulse width of hundred micro-seconds for an all-solid-state laser. The linewidth of output is 0.5 nm, and the beam quality factor M2 is 1.16. The high-pulse-energy high-beam-quality tunable Ti：sapphire laser in the range of 740-855 nm can be used to establish a more accurate and consistent absolute scale of second-order optical-nonlinear coefficients for KBe2BO3F2 measured in a wider wavelength range and to assess Miller＇s rule quantitatively.

Operation of Kerr-lens mode-locked Ti:sapphire laser in the non-soliton regime

A Kerr-lens mode-locked Ti：sapphire laser operating in a non-soliton regime is demonstrated. Dispersive wave generation is observed as a result of third order dispersion in the vicinity of zero dispersion. The characteristics of the Ti：sapphire l^ser operating in a positive dispersion regime are presented, where the oscillator directly generates pulses with duration continuously tunable from 0.37 ps to 2.11 ps, and 36 fs pulses are achieved atter extracavity compression. The oscillation is numerically simulated with an extended nonlinear Schr6dinger equation, and the simulation results are in good agreement with the experimental results.

An all-solid-state high power quasi-continuous-wave tunable dual-wavelength Ti：sapphire laser system using birefringence filter

This paper describes a tunable dual-wavelength Ti：sapphire laser system with quasi-continuous-wave and high-power outputs. In the design of the laser, it adopts a frequency-doubled Nd：YAG laser as the pumping source, and the birefringence filter as the tuning element. Tunable dual-wavelength outputs with one wavelength range from 700 nm to 756.5 nm, another from 830 nm to 900mn have been demonstrated. With a pump power of 23 W at 532 nm, a repetition rate of 7 kHz and a pulse width of 47.6 ns, an output power of 5.1 W at 744.8 nm and 860.9 nm with a pulse width of 13.2 ns and a line width of 3 nm has been obtained, it indicates an optical-to-optical conversion efficiency of 22.2%.

Microstructural evolution and mechanical properties of duplex-phase Ti6242 alloy treated by laser shock peening

The effects of laser shock peening(LSP)on the microstructural evolution and mechanical properties of the Ti6242 alloy,including the residual stress,surface roughness,Vickers microhardness,tensile mechanical response,and high-cycle fatigue properties,were studied.The results showed that the LSP induced residual compressive stresses on the surface and near surface of the material.The maximum surface residual compressive stress was−661 MPa,and the compressive-stress-affected depth was greater than 1000μm.The roughness and Vickers micro-hardness increased with the number of shocks,and the maximum hardness-affected depth was about 700μm after three LSP treatments.LSP enhanced the fraction of low-angle grain boundaries,changed the grain preferred orientations,and notably increased the pole density ofαphase on the near surface from 2.41 to 3.46.The surface hardness values of the LSP samples increased with the increase of the number of shocks due to work hardening,while the LSP had a limited effect on the tensile properties.The high-cycle fatigue life of the LSP-treated sample was significantly enhanced by more than 20%compared with that of the untreated sample,which was caused by the suppression of the initiation and propagation of fatigue cracks.

High performance laser induced plasma assisted ablation by GHz burst mode femtosecond pulses

High performance laser micromachining based on the combination of GHz burst mode femtosecond pulses irradiation and laser induced plasma assisted ablation can open a new avenue for high-quality and high-efficiency micromachining of single crystalline sapphire.

Effect of energy density on microstructure and mechanical properties of Ta−33Ti alloy prepared via laser powder bed fusion

The influence of laser process parameters on the densification,phase composition,microstructure,and mechanical properties of Ta−33wt.%Ti alloy prepared via laser powder bed fusion(LPBF)was investigated.The results show that fully dense and homogeneous Ta−Ti parts can be obtained from LPBF with appropriate energy input.The cellular and dendritic structures were formed due to constitutional undercooling.Transmission electron microscopy(TEM)analysis showed that the lamellarα″phase within the cellular structures preferred to concentrate at the cellular boundaries owing to the elemental micro-segregation in the solidification front.The samples fabricated under the energy density of 166.7 J/mm^(3) had a favorable ultimate tensile strength of 806 MPa and an excellent Young’s modulus of 36.7 GPa.

激光高速应变对双态组织近α型Ti-6Al-3Nb-2Zr-1Mo合金组织与性能的影响

利用激光冲击强化使Ti-6Al-3Nb-2Zr-1Mo(Ti80)合金表面产生严重塑性变形,借助SEM、TEM和XRD等方法深入研究了表面严重塑性变形对Ti80合金显微组织、力学性能以及耐腐蚀性能的影响。结果表明:激光冲击强化使Ti80合金表面产生无相变的严重塑性变形层,表层晶粒内部产生大量位错胞、位错墙、位错缠结等晶体缺陷。此外,通过位错间的相互作用,表面粗大晶粒细化至纳米级。晶粒细化和晶粒内高密度位错严重阻碍了位错的运动,从而增加了样品的硬度和强度。与原始试样相比,LSP处理试样的表面显微硬度提高了16.5%,产生了386.4 MPa的高幅残余压应力,在不牺牲延展性的前提下提高了强度。电化学和静态浸泡实验结果表明,LSP处理后试样的自腐蚀电位增加了77.7 mV vs.SCE,腐蚀电流密度和腐蚀速率分别降低了1.358μA·cm^(-2)、0.08 mm·year^(-1),点蚀和晶间腐蚀现象减弱。这是由于LSP处理后样品晶粒得到细化,增强了表面结构的稳定性并提供了更多钝化膜的形核位点,从而提高了Ti80合金的耐腐蚀性能。

Tunable Supercontinuum Generated in a Yb^3＋-Doped Microstructure Fiber Pumped by Ti：Sapphire Femtosecond Laser

We experimentally demonstrate that a tunable supercontinuum（SC） can be generated in a Yb3＋-doped microstructure fiber by the concept of wavelength conversion with a Ti：sapphire femtosecond（fs） laser as the pump.Experimental results show that an emission light around 1040 nm in an anomalous dispersion region is first generated and amplified by fs pulses in the normal dispersion region. Then, SC spectra from 1100 to 1380 nm and 630 to 840 nm can be achieved by combined effects of higher-order soliton fission and Raman soliton self-frequency shift in the anomalous dispersion region and self-phase modulation, dispersive wave, and four-wave mixing in the normal dispersion region. It is also demonstrated that the 20 nm change of pump results in a 280 nm broadband shift of soliton and the further red-shift of soliton is limited by OH-absorption at 1380 nm.

Diode-pumped Kerr-lens mode-locked Ti: sapphire laser with broad wavelength tunability

We report a direct blue-diode-pumped wavelength tunable Kerr-lens mode-locked Ti: sapphire laser.Central wavelength tunability as broad as 89 nm(736-825 nm) is achieved by adjusting the insertion of the prism.Pulses as short as 17 fs are generated at a central wavelength of 736 nm with an average output power of 31 mW.The maximum output power is 46.8 mW at a central wavelength of 797 nm with a pulse duration of 46 fs.

A 100-TW Ti:Sapphire Laser System at a Repetition Rate of 0.1 Hz

We demonstrate a 100-TW-class femtosecond Ti:sapphire laser running at a repetition rate of 0.1Hz based on a 20TW/10 Hz laser facility (XL-Ⅱ).Pumping the new stage amplifier with a 25J green Nd:glass laser,we successfully improve the laser energy to 3.4J with duration of 29 fs,corresponding to a peak power of 11 7 TW.

Synthesis of Y_2O_3 particle enhanced Ni/TiC composite on TC4 Ti alloy by laser cladding

A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.

LASER LIFT-OFF OF GaN THIN FILMS FROM SAPPHIRE SUBSTRATES

Gallium Nitride film was successfully separated from sapphire substrate by laser radiation. The absorption of the 248 nm radiation by the GaN at the interface results in rapid thermal decomposition of interfacial layer, yielding metallic Ga and N2 gas. The substrate can be easily removed by heating above the Ga melting point (29°C). X-ray diffraction, atomic force microscopy and photoluminescence of GaN before and after lift-off process have been performed, which demonstrated that the separation and transfer process do not alter the structural quality of the GaN films. And further discussions on the threshold energy and crack-free strategies of laser lift-off process have also been presented.

Laser machining of transparent brittle materials: from machining strategies to applications

Transparent brittle materials such as glass and sapphire are widely concerned and applied in consumer electronics, optoelectronic devices, etc. due to their excellent physical and chemical stability and good transparency. Growing research attention has been paid to developing novel methods for high-precision and high-quality machining of transparent brittle materials in the past few decades. Among the various techniques, laser machining has been proved to be an effective and flexible way to process all kinds of transparent brittle materials. In this review, a series of laser machining methods, e.g. laser full cutting, laser scribing, laser stealth dicing, laser filament, laser induced backside dry etching (LIBDE), and laser induced backside wet etching (LIBWE) are summarized. Additionally, applications of these techniques in micromachining, drilling and cutting, and patterning are introduced in detail. Current challenges and future prospects in this field are also discussed.

Surface modification of TC4 Ti alloy by laser cladding with TiC+Ti powders

Laser surface cladding was applied on a TC4 Ti alloy to improve its surface properties. Mixed TiC and Ti powders with a TiC-to-Ti mass ratio of 1：3 were put onto the TC4 Ti alloy and subsequently treated by laser beam. The microstructure and composition modifications in the surfaee layer were carefully investigated by using SEM, EDX and XRD. Due to melting, liquid state mixing followed by rapid solidification and cooling, a layer with graded microstructures and compositions formed. The TiC powders were completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The inter-dendritic areas were filled with fine a＇ phase lamellae enrich in A1. Mainly due to the reduced TiC volume fraction with increasing depth, the hardness decreases with increasing depth in the laser clad layer with a maximum value of HV1400, about 4.5 times of the initial one.

Microstructure and mechanical property of additively manufactured NiTi alloys:A comparison between selective laser melting and directed energy deposition

NiTi shape memory alloy(SMA)with nominal composition of Ni 50.8 at%and Ti 49.2 at%was additively manufactured(AM)by selective laser melting(SLM)and laser directed energy deposition(DED)for a comparison study,with emphasis on its phase composition,microstructure,mechanical property and deformation mechanism.The results show that the yield strength and ductility obtained by SLM are 100 MPa and 8%,respectively,which are remarkably different from DED result with 700 MPa and 2%.The load path of SLM sample presents shape memory effect,corresponding to martensite phase detected by XRD;while the load path of DED presents pseudo-elasticity with austenite phase.In SLM sample,fine grain and hole provide a uniform deformation during tensile test,resulting in a better elongation.Furthermore,the nonequilibrium solidification was studied by a temperature field simulation to understand the difference of the two 3D printing methods.Both temperature gradient G and growth rate R determine the microstructure and phase in the SLM sample and DED sample,which leads to similar grain morphologies because of similar G/R.While higher G×R of SLM leads to a finer grain size in SLM sample,providing enough driving force for martensite transition and subsequently changing texture compared to DED sample.

Microstructure and wear behavior of laser cladding Ni-based alloy composite coating reinforced by Ti(C,N) particulates

In this paper, Ni-based alloy composite coating reinforced by Ti （C, N） particles was fabricated on the mild steel through laser cladding technology. The microstrncture of laser cladding layer was analyzed by means of optical microscopy （OM）, X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The wear resistance test of the coating was evaluated using an M-2000 tester. The results showed that the Ni-based composite coating had an ability of rapid solidification to form dendritic crystals microstructure consisting of Ti （ C, N） particulates uniformly distributed in the matrix. It was found that some Ti（ C,N） particles are similar to be round in shape, and the others are irregular. Laser cladding layer reinforced by Ti（ C, N） particulates was found to possess good wear resistance property.