Long-lasting phosphor Y2O2S ： Eu^3＋ , Mg^2＋ , Ti^4＋ was synthesized by a flux method and their luminescence properties were investigated. The result indicates that the unit cell parameter c is linearly increased w...Long-lasting phosphor Y2O2S ： Eu^3＋ , Mg^2＋ , Ti^4＋ was synthesized by a flux method and their luminescence properties were investigated. The result indicates that the unit cell parameter c is linearly increased with the increase of Eu2O3 content in Y2O2S： Eu^3＋ （0.01 ≤ x ≤0.10）. On the other hand, the change of unit cell parameter a is not linear dependence. In the Y2O2S： Eu^3 ＋ crystal structure, Eu^3＋ ions only replaced Y^3 ＋ ions＇ places in which it posited center position of c axis. With the increase of Eu2O3 content, the position of the strongest emission peak changed from 540 nm （5D1→^ 7F2 transition） to 626 nm （^5Do→^7TF2 transition）, and the maximum intensity was obtained when x = 0.09 in Y2O2S： Eu^3＋ （0.01 ≤x ≤0.10）. This is due to the environment of trivalent europium in the crystal structure of Y2O2S. Doping with Mg^2＋ or Ti^4＋. ions alone cannot get the good long-lasting afterglow effect, whereas co-doping with Mg^2 ＋ and Ti^4 ＋ ions and excited with 365 nm ultraviolet light, a strong thermoluminesence peak appeared, red and orange long-lasting phosphorescence （LLP） was also observed and the phosphorescence lasted nearly 3 h in the light perception of the dark-adapted human eye （0.32 mcd·m^-2）. Thus the LLP mechanism was analyzed.展开更多
文摘Long-lasting phosphor Y2O2S ： Eu^3＋ , Mg^2＋ , Ti^4＋ was synthesized by a flux method and their luminescence properties were investigated. The result indicates that the unit cell parameter c is linearly increased with the increase of Eu2O3 content in Y2O2S： Eu^3＋ （0.01 ≤ x ≤0.10）. On the other hand, the change of unit cell parameter a is not linear dependence. In the Y2O2S： Eu^3 ＋ crystal structure, Eu^3＋ ions only replaced Y^3 ＋ ions＇ places in which it posited center position of c axis. With the increase of Eu2O3 content, the position of the strongest emission peak changed from 540 nm （5D1→^ 7F2 transition） to 626 nm （^5Do→^7TF2 transition）, and the maximum intensity was obtained when x = 0.09 in Y2O2S： Eu^3＋ （0.01 ≤x ≤0.10）. This is due to the environment of trivalent europium in the crystal structure of Y2O2S. Doping with Mg^2＋ or Ti^4＋. ions alone cannot get the good long-lasting afterglow effect, whereas co-doping with Mg^2 ＋ and Ti^4 ＋ ions and excited with 365 nm ultraviolet light, a strong thermoluminesence peak appeared, red and orange long-lasting phosphorescence （LLP） was also observed and the phosphorescence lasted nearly 3 h in the light perception of the dark-adapted human eye （0.32 mcd·m^-2）. Thus the LLP mechanism was analyzed.