The bonding interface characteristic and shear strength of diffusion bonded Ti-17 titanium alloy at different bonding time were investigated. The results show that the average size of voids decreases while the amount ...The bonding interface characteristic and shear strength of diffusion bonded Ti-17 titanium alloy at different bonding time were investigated. The results show that the average size of voids decreases while the amount of voids decreases after increasing to the maximum value with the increasing bonding time. The irregular void with a scraggly edge tends to an ellipse void with smooth surface and then changes to a tiny void with round shape. The grains across bonding interface occur at bonding time of 60 min. The shear strength of bond increases with increasing bonding time, and the highest shear strength of bond is 887.4 MPa at 60 min. The contribution of plastic deformation on the void closure and the increase of shear strength is significant even though the action time of plastic deformation is short.展开更多
Ultrasonic rolling is an advanced non-cutting surface strengthening method that combines traditional rolling with ultrasonic vibration.In this research,the experiment of orthogonal end milling-ultrasonic rolling compo...Ultrasonic rolling is an advanced non-cutting surface strengthening method that combines traditional rolling with ultrasonic vibration.In this research,the experiment of orthogonal end milling-ultrasonic rolling composite process has been carried out.The surface integrity refactoring changes and its mechanism of Ti-17 titanium alloy during the milling-ultrasonic rolling composite process has been studied and analyzed by the test and analysis of the surface geometric characteristics,residual stress,microhardness and microstructure before and after ultrasonic rolling.The residual stress and microhardness gradient distribution were characterized by cosine decay function and exponential decay function.All indicators of surface integrity were significantly improved after ultrasonic rolling.The study demonstrates that the reduction effect of the surface roughness by ultrasonic rolling process is inversely proportional to the initial surface roughness value.The ultrasonic rolling can only change the distribution form of the surface topography when the initial surface roughness is small.In addition,the improvement effect of ultrasonic rolling on surface compressive residual stress and microhardness decreased with the increase of initial milled surface roughness and surface compressive residual stress due to the factors such as energy absorption efficiency and mechanical properties changes of surface materials.A better ultrasonic rolled surface can be obtained by controlling the roughness and residual compressive stress of the initial milling surface to a small level.展开更多
The mechanical properties of Ti-23Al-17Nb (mole fraction,%) laser beam welding alloy joint at room temperature are comparable to that of the base materials.However,the strength and ductility of the as-welded joint det...The mechanical properties of Ti-23Al-17Nb (mole fraction,%) laser beam welding alloy joint at room temperature are comparable to that of the base materials.However,the strength and ductility of the as-welded joint deteriorate seriously after high temperature circulation.The effect of post-welded heat treatment on the microstructure and mechanical properties of the joint was investigated.The heat treatment was taken at 980 ℃ for 1.5 h,then furnace cooling and air cooling were performed separately.The results indicate that proper post-welded heat treatment improves the ductility of the joint at high temperature.展开更多
基金Project(51275416)supported by the National Natural Science Foundation of China
文摘The bonding interface characteristic and shear strength of diffusion bonded Ti-17 titanium alloy at different bonding time were investigated. The results show that the average size of voids decreases while the amount of voids decreases after increasing to the maximum value with the increasing bonding time. The irregular void with a scraggly edge tends to an ellipse void with smooth surface and then changes to a tiny void with round shape. The grains across bonding interface occur at bonding time of 60 min. The shear strength of bond increases with increasing bonding time, and the highest shear strength of bond is 887.4 MPa at 60 min. The contribution of plastic deformation on the void closure and the increase of shear strength is significant even though the action time of plastic deformation is short.
基金supported by the National Natural Science Foundation of China(Grant Nos.51875472,91860206,51905440,and 92160301)the National Science and Technology Major Project(Grant No.2017-VII-0001-0094)the Key Research and Development Program of Shaanxi Province(Grant No.2021ZDLGY10-06).
文摘Ultrasonic rolling is an advanced non-cutting surface strengthening method that combines traditional rolling with ultrasonic vibration.In this research,the experiment of orthogonal end milling-ultrasonic rolling composite process has been carried out.The surface integrity refactoring changes and its mechanism of Ti-17 titanium alloy during the milling-ultrasonic rolling composite process has been studied and analyzed by the test and analysis of the surface geometric characteristics,residual stress,microhardness and microstructure before and after ultrasonic rolling.The residual stress and microhardness gradient distribution were characterized by cosine decay function and exponential decay function.All indicators of surface integrity were significantly improved after ultrasonic rolling.The study demonstrates that the reduction effect of the surface roughness by ultrasonic rolling process is inversely proportional to the initial surface roughness value.The ultrasonic rolling can only change the distribution form of the surface topography when the initial surface roughness is small.In addition,the improvement effect of ultrasonic rolling on surface compressive residual stress and microhardness decreased with the increase of initial milled surface roughness and surface compressive residual stress due to the factors such as energy absorption efficiency and mechanical properties changes of surface materials.A better ultrasonic rolled surface can be obtained by controlling the roughness and residual compressive stress of the initial milling surface to a small level.
文摘The mechanical properties of Ti-23Al-17Nb (mole fraction,%) laser beam welding alloy joint at room temperature are comparable to that of the base materials.However,the strength and ductility of the as-welded joint deteriorate seriously after high temperature circulation.The effect of post-welded heat treatment on the microstructure and mechanical properties of the joint was investigated.The heat treatment was taken at 980 ℃ for 1.5 h,then furnace cooling and air cooling were performed separately.The results indicate that proper post-welded heat treatment improves the ductility of the joint at high temperature.