The effect of sputtered Ti-50Al-10Cr and Ti-50A1-20Cr coatings on both isothermal and cyclic oxidation resistance at 800-900℃ and hot corrosion resistance at 850℃ of Ti-24Al-14Nb-3V was investigated. Results indicat...The effect of sputtered Ti-50Al-10Cr and Ti-50A1-20Cr coatings on both isothermal and cyclic oxidation resistance at 800-900℃ and hot corrosion resistance at 850℃ of Ti-24Al-14Nb-3V was investigated. Results indicated that Ti-24Al-14Nb-3V alloys exhibited poor oxidation resistance due to the formation of Al2O3+TiO2+AlNbO4 mixed scales in air at 800-900℃ and poor hot corrosion resistance due to the spoliation of scales formed in Na2SO4+K2SO4 melts at 850℃. Both Ti-50Al-10Cr and Ti-50Al-20Cr coatings remarkably improved the oxidation and hot corrosion resistance of Ti-24Al-14Nb-3V alloy.展开更多
文摘The effect of sputtered Ti-50Al-10Cr and Ti-50A1-20Cr coatings on both isothermal and cyclic oxidation resistance at 800-900℃ and hot corrosion resistance at 850℃ of Ti-24Al-14Nb-3V was investigated. Results indicated that Ti-24Al-14Nb-3V alloys exhibited poor oxidation resistance due to the formation of Al2O3+TiO2+AlNbO4 mixed scales in air at 800-900℃ and poor hot corrosion resistance due to the spoliation of scales formed in Na2SO4+K2SO4 melts at 850℃. Both Ti-50Al-10Cr and Ti-50Al-20Cr coatings remarkably improved the oxidation and hot corrosion resistance of Ti-24Al-14Nb-3V alloy.