The Ti-35V-15Cr-0.05C (wt% is a new nonburning titanium alloy. The test for alloy combustibility was carried out by using CO2 laser. A 430 watt and 6mm diameter laser spot impinges directly on the sample within normal...The Ti-35V-15Cr-0.05C (wt% is a new nonburning titanium alloy. The test for alloy combustibility was carried out by using CO2 laser. A 430 watt and 6mm diameter laser spot impinges directly on the sample within normal atmospheric pressure and temperature. The results show that the ignition time of the nonburning titanium alloy is the longest in the eight examined titanium alloys, and is 3.5 times that of TC4 alloy. The ignition tempeerature of the nonburning alloy is 2991° C, and is higher than that of TC4 alloy by 1976°C. On the condition of high tempeerature and rich oxygen,the surface of alloy forms a melting layer which plays roles of oxygen insulation, heat insulation and burning products insulation. This is the mechanism of combustion resistance.展开更多
The effect of heat treatment and thermal exposure on the microstructure and mechanical properties of non burning β titanium alloy Ti 25V 15Cr 2Al 0.2C (mass fraction, %) was investigated. It is found that the amount ...The effect of heat treatment and thermal exposure on the microstructure and mechanical properties of non burning β titanium alloy Ti 25V 15Cr 2Al 0.2C (mass fraction, %) was investigated. It is found that the amount of α precipitation in samples after solution treatment followed by air cooling increases with increasing solution temperature. After solution treatment, the alloy was subjected to two different heat treatments to stabilize the material. The results show that the single ageing treatment(700 ℃, 4 h, AC) leads to a large amount of α precipitation, while the triplex treatment(850 ℃, 2 h, FC+700 ℃, 6 h, FC+540 ℃, 6 h, AC) significantly suppresses the formation of α precipitates. It is more important that after long term exposure at 540 ℃(the expected application temperature) samples heat treated by the triplex treatment have markedly higher ductility than those given the single aging treatment. The intermetallic compound TiCr 2 is observed in samples after long term exposure, which further degrades the ductility of the alloy.展开更多
文摘The Ti-35V-15Cr-0.05C (wt% is a new nonburning titanium alloy. The test for alloy combustibility was carried out by using CO2 laser. A 430 watt and 6mm diameter laser spot impinges directly on the sample within normal atmospheric pressure and temperature. The results show that the ignition time of the nonburning titanium alloy is the longest in the eight examined titanium alloys, and is 3.5 times that of TC4 alloy. The ignition tempeerature of the nonburning alloy is 2991° C, and is higher than that of TC4 alloy by 1976°C. On the condition of high tempeerature and rich oxygen,the surface of alloy forms a melting layer which plays roles of oxygen insulation, heat insulation and burning products insulation. This is the mechanism of combustion resistance.
文摘The effect of heat treatment and thermal exposure on the microstructure and mechanical properties of non burning β titanium alloy Ti 25V 15Cr 2Al 0.2C (mass fraction, %) was investigated. It is found that the amount of α precipitation in samples after solution treatment followed by air cooling increases with increasing solution temperature. After solution treatment, the alloy was subjected to two different heat treatments to stabilize the material. The results show that the single ageing treatment(700 ℃, 4 h, AC) leads to a large amount of α precipitation, while the triplex treatment(850 ℃, 2 h, FC+700 ℃, 6 h, FC+540 ℃, 6 h, AC) significantly suppresses the formation of α precipitates. It is more important that after long term exposure at 540 ℃(the expected application temperature) samples heat treated by the triplex treatment have markedly higher ductility than those given the single aging treatment. The intermetallic compound TiCr 2 is observed in samples after long term exposure, which further degrades the ductility of the alloy.