Magnetron-sputter deposition was used to produce Ti-48Al-8Cr-2Ag coating on a cast alloy substrate with the same composition. Hot corrosion was carried out in molten (Na,K)2SO4 and Na2SO4+NaCl at 900 ℃. The sputtered...Magnetron-sputter deposition was used to produce Ti-48Al-8Cr-2Ag coating on a cast alloy substrate with the same composition. Hot corrosion was carried out in molten (Na,K)2SO4 and Na2SO4+NaCl at 900 ℃. The sputtered nanocrystalline coating shows much better hot-corrosion resistance in molten (Na,K)2SO4 as a result of the formation of a continuous and compact Al2O3 scale. The nanocrystallization of TiAlCrAg alloy prolongs the incubation of breakaway corrosion and improves the hot-corrosion resistance of TiAlCrAg alloy in molten Na2SO4+NaCl. The relevant corrosion mechanism was discussed.展开更多
The main factors limiting the mass production of TiAl-based components are the high reactivity of TiAl-based alloys with the crucible or mould at high temperature.In this work,various crucibles (e.g.CaO,Y2O3 ceramic c...The main factors limiting the mass production of TiAl-based components are the high reactivity of TiAl-based alloys with the crucible or mould at high temperature.In this work,various crucibles (e.g.CaO,Y2O3 ceramic crucibles and water-cooled copper crucible) were used to fabricate the Ti-47Al-2Cr-2Nb alloy in a vacuum induction furnace.The effects of crucible materials and melting parameters on the microstructure and mechanical properties of the alloy were analyzed by means of microstructure observation,chemical analysis,tensile test and fracture surface observation.The possibilities of melting TiAl alloys in crucibles made of CaO and Y2O3 refractory materials were also discussed.展开更多
A method combining theoretical analysis with experiment is adopted and the flowing process of Ti-48A1-2Cr-2Nb alloy melt poured in a permanent mould during the centrifugal casting process has been analyzed. A mathemat...A method combining theoretical analysis with experiment is adopted and the flowing process of Ti-48A1-2Cr-2Nb alloy melt poured in a permanent mould during the centrifugal casting process has been analyzed. A mathematical model of the filling process is established and the forming mechanism of internal gaseous defect is summarized. The results of calculation show that the melt fills the mould with varying cross-section area and inclined angle. The filling speed of the cross-section is a function of filling time. The cross-section area is directly proportional to the filling speed and the inclined angle is inversely proportional to the filling speed at a given rotating speed of the platform. Both of them changes more obvious near the mould entrance. The gaseous defect can be formed in several ways and the centrifugal field has an important influence on the formation of the defect. In addition, the filling process in centrifugal field has been verified by wax experiments and the theoretical analysis are consistent with experimental results.展开更多
基金Project(59971052) supported by the National Natural Science Foundation of China
文摘Magnetron-sputter deposition was used to produce Ti-48Al-8Cr-2Ag coating on a cast alloy substrate with the same composition. Hot corrosion was carried out in molten (Na,K)2SO4 and Na2SO4+NaCl at 900 ℃. The sputtered nanocrystalline coating shows much better hot-corrosion resistance in molten (Na,K)2SO4 as a result of the formation of a continuous and compact Al2O3 scale. The nanocrystallization of TiAlCrAg alloy prolongs the incubation of breakaway corrosion and improves the hot-corrosion resistance of TiAlCrAg alloy in molten Na2SO4+NaCl. The relevant corrosion mechanism was discussed.
文摘The main factors limiting the mass production of TiAl-based components are the high reactivity of TiAl-based alloys with the crucible or mould at high temperature.In this work,various crucibles (e.g.CaO,Y2O3 ceramic crucibles and water-cooled copper crucible) were used to fabricate the Ti-47Al-2Cr-2Nb alloy in a vacuum induction furnace.The effects of crucible materials and melting parameters on the microstructure and mechanical properties of the alloy were analyzed by means of microstructure observation,chemical analysis,tensile test and fracture surface observation.The possibilities of melting TiAl alloys in crucibles made of CaO and Y2O3 refractory materials were also discussed.
文摘A method combining theoretical analysis with experiment is adopted and the flowing process of Ti-48A1-2Cr-2Nb alloy melt poured in a permanent mould during the centrifugal casting process has been analyzed. A mathematical model of the filling process is established and the forming mechanism of internal gaseous defect is summarized. The results of calculation show that the melt fills the mould with varying cross-section area and inclined angle. The filling speed of the cross-section is a function of filling time. The cross-section area is directly proportional to the filling speed and the inclined angle is inversely proportional to the filling speed at a given rotating speed of the platform. Both of them changes more obvious near the mould entrance. The gaseous defect can be formed in several ways and the centrifugal field has an important influence on the formation of the defect. In addition, the filling process in centrifugal field has been verified by wax experiments and the theoretical analysis are consistent with experimental results.