The true stress-sWain relationships of Ti-5A1-2Sn-2Zr-4Mo-4Cr(TC17) alloy with a wide range of strain rates were investigated by tmiaxial quasi-static and dynamic compression tests, respectively. Quasi- static compr...The true stress-sWain relationships of Ti-5A1-2Sn-2Zr-4Mo-4Cr(TC17) alloy with a wide range of strain rates were investigated by tmiaxial quasi-static and dynamic compression tests, respectively. Quasi- static compression tests were carried out with Instron 8874 test machine, while dynamic compression tests were performed with the split Hopkinson pressure bar (SHPB) which was installed with heating device and synchro- assembly system. The dynamic mechanical behaviors tests of TC17 were carded out from room temperature to 800 ℃ at intervals of 200 ℃ and at high sWain rates (5 500-1 9200 s-l). The stress-strain curves considering temperature-sWain rate coupling actions were obtained. The Johnson-Cook constitutive model was developed through data fitting of the stress-sWain curves. The material constants in the developed constitutive model can be determined using isothermal and adiabatic stress-strain curves at different strain rates. The Johnson-Cook constitutive model provided satisfied prediction of the plastic flow stress for TC17 alloy.展开更多
The characteristics of fatigue crack initiation in Ti-5AI-4Sn-2Zr1Mo-O.7Nd-O.25Si alloy wereStudied. Two modes Of fatigue crack initiation were found. The Nd-rich phase particles displaybetter resistance to fatigue cr...The characteristics of fatigue crack initiation in Ti-5AI-4Sn-2Zr1Mo-O.7Nd-O.25Si alloy wereStudied. Two modes Of fatigue crack initiation were found. The Nd-rich phase particles displaybetter resistance to fatigue crack initiation than the matrix at lower stress.展开更多
In the as-cast Ti-55 alloy, the intragranular rare earth-rich phase particles are about 1. 0~14 μm in diameter, elliptical, and rich in Nd, Sn, and O. The contents of Nd and Sn on the grain boundaries are higher th...In the as-cast Ti-55 alloy, the intragranular rare earth-rich phase particles are about 1. 0~14 μm in diameter, elliptical, and rich in Nd, Sn, and O. The contents of Nd and Sn on the grain boundaries are higher than those at other sites. The intragranular phases grow preferably at the region on the grain boundaries, which causes the formation of the elliptical morphology of the intragranular phases.展开更多
基金Project(51275416)supported by the National Natural Science Foundation of ChinaProject(KP201513)supported by the Fund of the State Key Laboratory of Solidification Processing in NWPU,China
基金Funded by the National Basic Research Program of China(No.2009CB724401)the Major Science and Technology Program of High-end CNC Machine Tools and Basic Manufacturing Equipment(No.2012ZX04003-041)
文摘The true stress-sWain relationships of Ti-5A1-2Sn-2Zr-4Mo-4Cr(TC17) alloy with a wide range of strain rates were investigated by tmiaxial quasi-static and dynamic compression tests, respectively. Quasi- static compression tests were carried out with Instron 8874 test machine, while dynamic compression tests were performed with the split Hopkinson pressure bar (SHPB) which was installed with heating device and synchro- assembly system. The dynamic mechanical behaviors tests of TC17 were carded out from room temperature to 800 ℃ at intervals of 200 ℃ and at high sWain rates (5 500-1 9200 s-l). The stress-strain curves considering temperature-sWain rate coupling actions were obtained. The Johnson-Cook constitutive model was developed through data fitting of the stress-sWain curves. The material constants in the developed constitutive model can be determined using isothermal and adiabatic stress-strain curves at different strain rates. The Johnson-Cook constitutive model provided satisfied prediction of the plastic flow stress for TC17 alloy.
文摘The characteristics of fatigue crack initiation in Ti-5AI-4Sn-2Zr1Mo-O.7Nd-O.25Si alloy wereStudied. Two modes Of fatigue crack initiation were found. The Nd-rich phase particles displaybetter resistance to fatigue crack initiation than the matrix at lower stress.
基金the financial supports from the National Natural Science Foundation of China (Nos. 52001163, 52075237)the Primary Research and Development Plan of Jiangsu Province, China (No. BE2019119)
文摘In the as-cast Ti-55 alloy, the intragranular rare earth-rich phase particles are about 1. 0~14 μm in diameter, elliptical, and rich in Nd, Sn, and O. The contents of Nd and Sn on the grain boundaries are higher than those at other sites. The intragranular phases grow preferably at the region on the grain boundaries, which causes the formation of the elliptical morphology of the intragranular phases.