The dynamic recrystallization（DRX） behavior of Ti-6Al-2Zr-1Mo-1V alloy was investigated at deformation temperature of 1000-1100 °C and strain rate of 10-3-1.0 s-1 by using compression test.The results show that...The dynamic recrystallization（DRX） behavior of Ti-6Al-2Zr-1Mo-1V alloy was investigated at deformation temperature of 1000-1100 °C and strain rate of 10-3-1.0 s-1 by using compression test.The results show that discontinuous dynamic recrystallization（DDRX） is the predominant recrystallization mechanism at temperature higher than 1050 °C and strain rate lower than 0.01 s-1.Meanwhile,continuous dynamic recrystallization is the main mechanism observed at temperature below 1050 °C and strain rate above 0.01 s-1,mixed with a few DDRX grains.In addition,decreasing strain rate and increasing deformation temperature are found to facilitate the progress of DRX and refinement of grains in the Ti alloy in β forging process.展开更多
The isothermal compression tests were carried out in the Thermecmastor-Z thermo-simulator at temperatures of 800, 850, 900, 950, 1000 and 1050 ℃ and the strain rates of 0.01, 0.1, 1 and 10 s-1. The influence of defor...The isothermal compression tests were carried out in the Thermecmastor-Z thermo-simulator at temperatures of 800, 850, 900, 950, 1000 and 1050 ℃ and the strain rates of 0.01, 0.1, 1 and 10 s-1. The influence of deformation temperature and strain rate on the flow stress of Ti-6Al-2Zr-IMo-IV alloy was studied. Based on the experimental data sets, the high temperature deformation behavior of Ti-6A1-2Zr-IMo-IV alloy was presented using the intelligent method of artificial neural network （ANN）. The results indicate that the predicted flow stress values by ANN model is quite consistent with the experimental results, which implies that the artificial neural network is an effective tool for studying the hot deformation behavior of the present alloy. In addition, the development of graphical user interface is implemented using Visual Basic programming language.展开更多
The true stress-strain curves of Ti-6Al-2Zr-1Mo-1V alloy were achieved by a series of isothermal compression tests with height reduction of 60% under the deformation temperatures of 1073-1323 K and the strain rates of...The true stress-strain curves of Ti-6Al-2Zr-1Mo-1V alloy were achieved by a series of isothermal compression tests with height reduction of 60% under the deformation temperatures of 1073-1323 K and the strain rates of 0.01-10s 1.The critical conditions for the onset of DRX were attained when the value of d /d,where strain hardening rate d /d,reached the minimum which corresponds to an inflection of θ versus σ curve.Thus,two important potential parameters,critical strain and critical stress,were identified,and expressed as εc/εp=0.37-0.60,σc/σp=0.81-0.91.Furthermore,by the regression analysis for conventional hyperbolic sine equation,the main material parameters such as α,β,n,and DRX activation energy,Q,were calculated.In addition,the evolution of Q with strain rate and temperature was revealed as a 3D response surface.展开更多
The initiation sites and influencing factors of cavity nucleation were investigated for a Ti-6Al-2Zr-1Mo-1V alloy with lamellar starting structure,using the isothermal hot compression test.All samples were deformed to...The initiation sites and influencing factors of cavity nucleation were investigated for a Ti-6Al-2Zr-1Mo-1V alloy with lamellar starting structure,using the isothermal hot compression test.All samples were deformed to a true strain of 0.70 in the temperature range of 750-950°C and strain rate range of 0.001-10 s-1.The corresponding microstructures were observed by means of the metallurgical microscopy and scanning electron microscopy(SEM).It was found that all cavities occurred at the bulge regions of the compression specimens.Most of cavities nucleated along prior beta boundaries oriented 45°to the compression axis,while others nucleated at the interfaces of lamellar alpha colonies.Cavity nucleation was inhibited with increasing the volume fraction of beta phase and the volume fraction spheroidized of lamellar alpha phase.展开更多
基金Project (2007CB613803) supported by the National Basic Research Program of ChinaProject (2010GQC0170) supported by the Natural Science Foundation of Jiangxi Province,ChinaProject (GJJ11159) supported by the Educational Committee of Jiangxi Province,China
文摘The dynamic recrystallization（DRX） behavior of Ti-6Al-2Zr-1Mo-1V alloy was investigated at deformation temperature of 1000-1100 °C and strain rate of 10-3-1.0 s-1 by using compression test.The results show that discontinuous dynamic recrystallization（DDRX） is the predominant recrystallization mechanism at temperature higher than 1050 °C and strain rate lower than 0.01 s-1.Meanwhile,continuous dynamic recrystallization is the main mechanism observed at temperature below 1050 °C and strain rate above 0.01 s-1,mixed with a few DDRX grains.In addition,decreasing strain rate and increasing deformation temperature are found to facilitate the progress of DRX and refinement of grains in the Ti alloy in β forging process.
基金Project (2007CB613807) supported by the National Basic Research Program of ChinaProject (35-TP-2009) supported by the Fund of the State Key Laboratory of Solidification Processing in NWPU,ChinaProject (51075333) supported by the National Natural Science Foundation of China
文摘The isothermal compression tests were carried out in the Thermecmastor-Z thermo-simulator at temperatures of 800, 850, 900, 950, 1000 and 1050 ℃ and the strain rates of 0.01, 0.1, 1 and 10 s-1. The influence of deformation temperature and strain rate on the flow stress of Ti-6Al-2Zr-IMo-IV alloy was studied. Based on the experimental data sets, the high temperature deformation behavior of Ti-6A1-2Zr-IMo-IV alloy was presented using the intelligent method of artificial neural network （ANN）. The results indicate that the predicted flow stress values by ANN model is quite consistent with the experimental results, which implies that the artificial neural network is an effective tool for studying the hot deformation behavior of the present alloy. In addition, the development of graphical user interface is implemented using Visual Basic programming language.
基金Project(2012ZX04010081)supported by the National Key Technologies R&D Program of ChinaProject(cstc2009aa3012-1)supported by the Science and Technology Committee of Chongqing,ChinaProject(CDJZR12130045)supported by the Fundamental Research Funds for the Central Universities,China
文摘The true stress-strain curves of Ti-6Al-2Zr-1Mo-1V alloy were achieved by a series of isothermal compression tests with height reduction of 60% under the deformation temperatures of 1073-1323 K and the strain rates of 0.01-10s 1.The critical conditions for the onset of DRX were attained when the value of d /d,where strain hardening rate d /d,reached the minimum which corresponds to an inflection of θ versus σ curve.Thus,two important potential parameters,critical strain and critical stress,were identified,and expressed as εc/εp=0.37-0.60,σc/σp=0.81-0.91.Furthermore,by the regression analysis for conventional hyperbolic sine equation,the main material parameters such as α,β,n,and DRX activation energy,Q,were calculated.In addition,the evolution of Q with strain rate and temperature was revealed as a 3D response surface.
基金Project(2009ZE56014)supported by the Aeronautical Science Foundation of ChinaProject(gf200901008)supported by the Open Fund of National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology,Nanchang Hangkong University,China
文摘The initiation sites and influencing factors of cavity nucleation were investigated for a Ti-6Al-2Zr-1Mo-1V alloy with lamellar starting structure,using the isothermal hot compression test.All samples were deformed to a true strain of 0.70 in the temperature range of 750-950°C and strain rate range of 0.001-10 s-1.The corresponding microstructures were observed by means of the metallurgical microscopy and scanning electron microscopy(SEM).It was found that all cavities occurred at the bulge regions of the compression specimens.Most of cavities nucleated along prior beta boundaries oriented 45°to the compression axis,while others nucleated at the interfaces of lamellar alpha colonies.Cavity nucleation was inhibited with increasing the volume fraction of beta phase and the volume fraction spheroidized of lamellar alpha phase.