This study employs advanced electrochemical and surface characterization techniques to investigate the impact of electrochemical hydrogen charging on the corrosion behavior and surface film of the Ti-6Al-4V alloy.The ...This study employs advanced electrochemical and surface characterization techniques to investigate the impact of electrochemical hydrogen charging on the corrosion behavior and surface film of the Ti-6Al-4V alloy.The findings revealed the formation ofγ-TiH andδ-TiH_(2) hydrides in the alloy after hydrogen charging.Prolonging hydrogen charging resulted in more significant degradation of the alloy microstructure,leading to deteriorated protectiveness of the surface film.This trend was further confirmed by the electrochemical measurements,which showed that the corrosion resistance of the alloy progressively worsened as the hydrogen charging time was increased.Consequently,this work provides valuable insights into the mechanisms underlying the corrosion of Ti-6Al-4V alloy under hydrogen charging conditions.展开更多
To overcome the disadvantages of inhomogeneous microstructures and poor mechanical properties of additively manufactured Ti-6Al-4V alloys,a novel technique of hybrid deposition and synchronous micro-rolling is propose...To overcome the disadvantages of inhomogeneous microstructures and poor mechanical properties of additively manufactured Ti-6Al-4V alloys,a novel technique of hybrid deposition and synchronous micro-rolling is proposed.The micro-rolling leads to equiaxed prior β grains,thin discontinuous intergranular α,and equiaxed primary α,in contrast to the coarse columnar prior β grains without the application of micro-rolling.The recrystallization by micro-rolling results in discontinuous intergranular α via the mechanism of strain and interface-induced grain boundary migration.The evolution of α globularization,driven by a solute concentration gradient,starts from the sub-boundary until the formation of equiaxed primary α.Simultaneous strengthening and toughening are achieved,which means an increase in yield strength,ultimate tensile strength,fracture elongation,and work hardening rate.The formation of α recrystallization leads to more fine grain boundaries to strengthen the yield strength,and the improvement of ductility is due to the better-coordinated deformation ability of discontinuous intergranular α and equiaxed primary α.As a result,the fracture mode in micro-rolling changes from intergranular type to transgranular type.展开更多
基金Supported by National Natural Science Foundation of China(Grant Nos.52001142,52005228,51801218,51911530211,51905110)Young Scientists Sponsorship Program by CAST(Grant No.2022QNRC001).
文摘This study employs advanced electrochemical and surface characterization techniques to investigate the impact of electrochemical hydrogen charging on the corrosion behavior and surface film of the Ti-6Al-4V alloy.The findings revealed the formation ofγ-TiH andδ-TiH_(2) hydrides in the alloy after hydrogen charging.Prolonging hydrogen charging resulted in more significant degradation of the alloy microstructure,leading to deteriorated protectiveness of the surface film.This trend was further confirmed by the electrochemical measurements,which showed that the corrosion resistance of the alloy progressively worsened as the hydrogen charging time was increased.Consequently,this work provides valuable insights into the mechanisms underlying the corrosion of Ti-6Al-4V alloy under hydrogen charging conditions.
基金the support of the National Natural Science Foundation of China (No.51971099)the Analytical and Testing Center, HUST。
文摘To overcome the disadvantages of inhomogeneous microstructures and poor mechanical properties of additively manufactured Ti-6Al-4V alloys,a novel technique of hybrid deposition and synchronous micro-rolling is proposed.The micro-rolling leads to equiaxed prior β grains,thin discontinuous intergranular α,and equiaxed primary α,in contrast to the coarse columnar prior β grains without the application of micro-rolling.The recrystallization by micro-rolling results in discontinuous intergranular α via the mechanism of strain and interface-induced grain boundary migration.The evolution of α globularization,driven by a solute concentration gradient,starts from the sub-boundary until the formation of equiaxed primary α.Simultaneous strengthening and toughening are achieved,which means an increase in yield strength,ultimate tensile strength,fracture elongation,and work hardening rate.The formation of α recrystallization leads to more fine grain boundaries to strengthen the yield strength,and the improvement of ductility is due to the better-coordinated deformation ability of discontinuous intergranular α and equiaxed primary α.As a result,the fracture mode in micro-rolling changes from intergranular type to transgranular type.
基金supported by the National Natural Science Foundation of China(No.51674187)the International Joint Research Center for Value-added Metallurgy and Processing of Non-ferrous Metals,China(No.2019SD0010)the Key Industry Chain(Group)-Industrial Field in Shaanxi Province,China(No.2019ZDLGY05-03)。