A series of Ti-Al-Sn-Zr-Mo-Si-Nd alloys with various content of Al were solution treated in α+β phase field and air-cooled. The precipitation of a2 phase in cooling was investigated by transmission electron microsco...A series of Ti-Al-Sn-Zr-Mo-Si-Nd alloys with various content of Al were solution treated in α+β phase field and air-cooled. The precipitation of a2 phase in cooling was investigated by transmission electron microscopic analysis The precipitation characteristic of α2 phase was discussed. The precipitation of α2 phase would proceed by the nucleation and growth of α2 phase dependent on the diffusion of Al atoms. And a comparison on the difference of precipitation of α2 phase was carried out under the conditions of air-cooling and quenching in water. The investigation showed that the air-cooling and even quenching could supply enough time for the precipitation and growth of α2 phase when Al content reached a certain value even though far away from the stoichiometric composition of Ti3Al.展开更多
The precipitation characteristics of the α2 ordered phase in Ti-AI-Sn-Zr-Mo-Si-Nd alloys with various content of Al, under different aging conditions, were investigated. The distribution and size of the α2 ordered p...The precipitation characteristics of the α2 ordered phase in Ti-AI-Sn-Zr-Mo-Si-Nd alloys with various content of Al, under different aging conditions, were investigated. The distribution and size of the α2 ordered phase changed with temperature and Al content. The dislocations were the only places where the α2 ordered phase could precipitate at higher temperature near the critical transformation temperature for each alloy experimented. With the addition of Al content, the critical transformation temperature of α2 ordered phase increased. When the aging temperature was relatively low (650℃), the precedent precipitation of α2 ordered phase took place in primary a phase at the early stage of aging, in the duplex microstructure (the primary a with the transformed (3) of the alloys with lower Al content. But after certain aging time (50 h), the size of α2 particles was almost equal in both the primary a and the transformed β. And no obvious growth of α2 particles could be observed after 50 h.展开更多
文摘A series of Ti-Al-Sn-Zr-Mo-Si-Nd alloys with various content of Al were solution treated in α+β phase field and air-cooled. The precipitation of a2 phase in cooling was investigated by transmission electron microscopic analysis The precipitation characteristic of α2 phase was discussed. The precipitation of α2 phase would proceed by the nucleation and growth of α2 phase dependent on the diffusion of Al atoms. And a comparison on the difference of precipitation of α2 phase was carried out under the conditions of air-cooling and quenching in water. The investigation showed that the air-cooling and even quenching could supply enough time for the precipitation and growth of α2 phase when Al content reached a certain value even though far away from the stoichiometric composition of Ti3Al.
文摘The precipitation characteristics of the α2 ordered phase in Ti-AI-Sn-Zr-Mo-Si-Nd alloys with various content of Al, under different aging conditions, were investigated. The distribution and size of the α2 ordered phase changed with temperature and Al content. The dislocations were the only places where the α2 ordered phase could precipitate at higher temperature near the critical transformation temperature for each alloy experimented. With the addition of Al content, the critical transformation temperature of α2 ordered phase increased. When the aging temperature was relatively low (650℃), the precedent precipitation of α2 ordered phase took place in primary a phase at the early stage of aging, in the duplex microstructure (the primary a with the transformed (3) of the alloys with lower Al content. But after certain aging time (50 h), the size of α2 particles was almost equal in both the primary a and the transformed β. And no obvious growth of α2 particles could be observed after 50 h.
