Microstructure and phase transformation behaviors of the film annealed at different temperatures were studied by X-ray diffractometry (XRD), transmission electron microscopy and differential scanning calorimeter (...Microstructure and phase transformation behaviors of the film annealed at different temperatures were studied by X-ray diffractometry (XRD), transmission electron microscopy and differential scanning calorimeter (DSC). Also tensile tests were examined. For increasing annealed temperature, multiple phase transformations, transformations via a B19-phase or direct martensite/austenite transformtion are observed. The TiNiPd thin film annealed at 750℃ had relatively uniform martensite/austenite transformtion and shape memory effect. Martensite/austenite transformtion was also found in strain-temperature curves. Subsequent annealing at 450℃ had minor effect on transformation temperatures of Ti-Ni-Pd thin films but resulted in more uniform transformation and improved shape memory effect.展开更多
Different fragments of a hot-rolled and homogenized Cu–Zn–Al shape memory alloy(SMA) were subjected to thermal cycling by means of a differential scanning calorimetric(DSC) device. During thermal cycling, heatin...Different fragments of a hot-rolled and homogenized Cu–Zn–Al shape memory alloy(SMA) were subjected to thermal cycling by means of a differential scanning calorimetric(DSC) device. During thermal cycling, heating was performed at the same constant rate of increasing temperature while cooling was carried out at different rates of decreasing temperature. For each cooling rate, the temperature decreased in the same thermal interval. During each cooling stage, an exothermic peak(maximum) was observed on the DSC thermogram. This peak was associated with forward martensitic transformation. The DSC thermograms were analyzed with PROTEUS software: the critical martensitic transformation start(Ms) and finish(Mf) temperatures were determined by means of integral and tangent methods, and the dissipated heat was evaluated by the area between the corresponding maximum plot and a sigmoid baseline. The effects of the increase in cooling rate, assessed from a calorimetric viewpoint, consisted in the augmentation of the exothermic peak and the delay of direct martensitic transformation. The latter had the tendency to move to lower critical transformation temperatures. The martensite plates changed in morphology by becoming more oriented and by an augmenting in surface relief, which corresponded with the increase in cooling rate as observed by scanning electron microscopy(SEM) and atomic force microscopy(AFM).展开更多
基金supported by Science&Technology Commission of Shanghai Municipality(STCSM),China(No.02DJ14042)the Key Project of Chinese Ministry of Education(No.0307).
文摘Microstructure and phase transformation behaviors of the film annealed at different temperatures were studied by X-ray diffractometry (XRD), transmission electron microscopy and differential scanning calorimeter (DSC). Also tensile tests were examined. For increasing annealed temperature, multiple phase transformations, transformations via a B19-phase or direct martensite/austenite transformtion are observed. The TiNiPd thin film annealed at 750℃ had relatively uniform martensite/austenite transformtion and shape memory effect. Martensite/austenite transformtion was also found in strain-temperature curves. Subsequent annealing at 450℃ had minor effect on transformation temperatures of Ti-Ni-Pd thin films but resulted in more uniform transformation and improved shape memory effect.
基金supported by the project PN-II-ID-PCE-2012-4-0033,contract 13/2013
文摘Different fragments of a hot-rolled and homogenized Cu–Zn–Al shape memory alloy(SMA) were subjected to thermal cycling by means of a differential scanning calorimetric(DSC) device. During thermal cycling, heating was performed at the same constant rate of increasing temperature while cooling was carried out at different rates of decreasing temperature. For each cooling rate, the temperature decreased in the same thermal interval. During each cooling stage, an exothermic peak(maximum) was observed on the DSC thermogram. This peak was associated with forward martensitic transformation. The DSC thermograms were analyzed with PROTEUS software: the critical martensitic transformation start(Ms) and finish(Mf) temperatures were determined by means of integral and tangent methods, and the dissipated heat was evaluated by the area between the corresponding maximum plot and a sigmoid baseline. The effects of the increase in cooling rate, assessed from a calorimetric viewpoint, consisted in the augmentation of the exothermic peak and the delay of direct martensitic transformation. The latter had the tendency to move to lower critical transformation temperatures. The martensite plates changed in morphology by becoming more oriented and by an augmenting in surface relief, which corresponded with the increase in cooling rate as observed by scanning electron microscopy(SEM) and atomic force microscopy(AFM).