The corrosion resistance and antibacterial properties of Ti−3Cu alloy prepared by selective laser melting were evaluated using electrochemical experiments and a variety of antibacterial characterization.It is found th...The corrosion resistance and antibacterial properties of Ti−3Cu alloy prepared by selective laser melting were evaluated using electrochemical experiments and a variety of antibacterial characterization.It is found that the charge transfer resistance of Ti−3Cu alloy was 4.89×10^(5)Ω∙cm^(2),which was doubled the data obtained by CP-Ti alloy.The antibacterial rates of Ti−3Cu alloy against S.mutans and P.gingivalis were 45.0%and 54.5%.And the antibacterial rates increased with the prolongation of cultivation time,reaching up to 62.8%and 68.6%,respectively.The in-situ nano Ti_(2)Cu precipitates were homogeneously distributed in the matrix of the Ti−3Cu alloy,which was the key reason of increasing the corrosion resistance.Additionally,the microscale electric fields between theα-Ti matrix and the Ti_(2)Cu was responsible for the enhancement of the antibacterial properties.展开更多
Aluminum alloys are widely used in industry due to their light weight.These alloys are generally exposed to abrasive wear,which diminishes their effective lifespan.The wear resistance of these alloys is enhanced by ad...Aluminum alloys are widely used in industry due to their light weight.These alloys are generally exposed to abrasive wear,which diminishes their effective lifespan.The wear resistance of these alloys is enhanced by adding various reinforcements,however,this enhancement comes at the cost of reduced fracture toughness.This paradox of increased wear resistance versus decreased fracture toughness in aluminum alloys can be resolved by using functionally graded materials (FGMs).This study focuses on the abrasive wear behavior of functional graded aluminum matrix composites reinforced with Al_(3)Ti particles.The wear properties of the composites were investigated by considering the characteristics of the composite such as matrix type and various composite zones,as well as the wear parameters such as abrasive particle diameter,load,sliding speed and distance.Taguchi method was used in the abrasive wear tests in order to get more reliable results in a timeefficient manner.Experiment recipes were created based on the L_(27)(3^(6)) orthogonal series.As a result of the study,it is observed that the wear resistance of the composites increases with an increase in Al_(3)Ti reinforcement content and hardness of the matrix.In addition,the size of abrasive particles and the applied load are significant factors affecting abrasive wear.展开更多
光电化学(PEC)分解水是一种清洁可持续的获取氢燃料的方法,其中产氧半反应(OER)是制约整个水分解过程效率的关键步骤.因此,光阳极的性能是决定太阳能到氢能转化效率的关键因素.在各种水氧化光阳极材料中,赤铁矿(α-Fe_(2)O_(3))因具有...光电化学(PEC)分解水是一种清洁可持续的获取氢燃料的方法,其中产氧半反应(OER)是制约整个水分解过程效率的关键步骤.因此,光阳极的性能是决定太阳能到氢能转化效率的关键因素.在各种水氧化光阳极材料中,赤铁矿(α-Fe_(2)O_(3))因具有良好的化学稳定性、合适的带隙(~2.1 eV)、无毒、储量丰富等优点而成为最有前途的光阳极材料之一.然而,α-Fe_(2)O_(3)丰富的受体表面态和缓慢的水氧化动力学导致光生电荷复合严重,限制了其在光电化学中的实际应用.因此,有必要对α-Fe_(2)O_(3)进行表面工程设计以提高水氧化效率.本文提出了一种新方法,以金属有机框架(Ti-MOFs)为模板,在Ti-Fe_(2)O_(3)表面煅烧合成TiO_(2)层,然后将富活性位点的ZIF-67加载在TiO_(2)/Ti-Fe_(2)O_(3)上作为助催化剂,制备出具有较好光电化学性能的ZIF-67/TiO_(2)/Ti-Fe_(2)O_(3)复合光阳极.X射线衍射、高分辨透射电镜、X射线光电子能谱和拉曼光谱等表征结果证实成功合成了ZIF-67/TiO_(2)/Ti-Fe_(2)O_(3).同时,氮气等温吸附脱附曲线和表面接触角测试结果表明,MOFs衍生的TiO_(2)为介孔材料.采用表面光伏技术、光致发光光谱、飞秒-瞬态吸收光谱和电化学阻抗谱分析,研究了光生电荷的分离和复合行为.结果表明,MOFs衍生的TiO_(2)不仅可以作为钝化层有效抑制了表面复合,还作为Ti-Fe_(2)O_(3)的电子阻挡层,显著减少了电子向表面的流失,从而大大提高了Ti-Fe_(2)O_(3)表面和体相的电荷分离效率.进一步的累积电荷量测试、电化学阻抗谱和Bode图分析显示,负载MOFs衍生TiO_(2)后,可以明显促进光生空穴向电解质的注入,其多孔结构也可以增加反应接触面积,这有利于光生电荷在固液界面传输.此外,理论计算结果表明,Ti-Fe_(2)O_(3)水氧化速控步骤的能垒(ΔG=3.38 eV)明显高于TiO_(2)(ΔG=1.67 eV),说明OER更容易在TiO_(2)/Ti-Fe_(2)O_(3)表面发生,这与其光电流密度结果一致.为进一步提高反应活性和加快水氧化动力学,负载助催化剂ZIF-67后,ZIF-67/TiO_(2)/Ti-Fe_(2)O_(3)复合光阳极实现了较好的光电化学性能,其在1.23 V vs.RHE时光电流密度高达4.04 mA cm^(‒2),是Ti-Fe_(2)O_(3)的9.3倍,并且复合光阳极的入射光子电流转换效率和空穴注入效率分别达到93%(390 nm)和91%.综上所述,本研究通过MOFs衍生的TiO_(2)和ZIF-67助催化剂改性α-Fe_(2)O_(3)光阳极,显著提升了其光电化学水氧化性能.其中,MOFs衍生TiO_(2)不仅优化了电荷分离,还促进了光生空穴的注入,从而显著提高其光电化学水氧化性能.本研究为构筑高性能的有机-无机杂化光阳极提供了新思路.展开更多
Magnesium(Mg)stands out in temporary biomaterial applications due to its biocompatibility,biodegradability,and low Young’s modulus.However,controlling its corrosion through next-generation polymer-based functional co...Magnesium(Mg)stands out in temporary biomaterial applications due to its biocompatibility,biodegradability,and low Young’s modulus.However,controlling its corrosion through next-generation polymer-based functional coatings is crucial due to the rapid degradation behavior of Mg.In this study,the function of 2D lamellar Ti_(3)C_(2)T_(x)(MXene)in Hydroxyapatite(HA)and Halloysite nanotube(HNT)hybrid coatings in biodegradable poly-(lactic acid)(PLA)was investigated.The morphological and structural characterizations of the coatings on Mg were revealed through HRTEM,XPS,SEM-EDX,XRD,FTIR,and contact angle analyses/tests.Electrochemical in vitro corrosion tests(OCP,PDS,and EIS-Nyquist)were conducted for evaluate corrosion resistance under simulated body fluid(SBF)conditions.The bioactivity of the coatings in SBF have been revealed in accordance with the ISO 23,317 standard.Finally,antibacterial disk diffusion tests were conducted to investigate the functional effect of MXene in coatings.It has been determined that the presence of MXene in the coating increased not only surface wettability(131°,85°,77°,and 74°for uncoated,pH,PHH,and PHH/MXene coatings,respectively)but also increased corrosion resistance(1857.850,42.357,1.593,and 0.085×10^(-6),A/cm^(2) for uncoated,pH,PHH,and PHH/MXene coatings,respectively).It has been proven that the in vitro bioactivity of PLA-HA coatings is further enhanced by adding HNT and MXene,along with SEM morphologies after SBF.Finally,2D lamellar MXene-filled coating exhibits antibacterial behavior against both E.coli and S.aureus bacteria.展开更多
基金financially supported by the National Natural Science Foundation of China(No.51404302)the Natural Science Foundation of Hunan Province,China(Nos.2020JJ4732,2022JJ30897)the Natural Science Foundation of Changsha City,China(No.kq2202430).
文摘The corrosion resistance and antibacterial properties of Ti−3Cu alloy prepared by selective laser melting were evaluated using electrochemical experiments and a variety of antibacterial characterization.It is found that the charge transfer resistance of Ti−3Cu alloy was 4.89×10^(5)Ω∙cm^(2),which was doubled the data obtained by CP-Ti alloy.The antibacterial rates of Ti−3Cu alloy against S.mutans and P.gingivalis were 45.0%and 54.5%.And the antibacterial rates increased with the prolongation of cultivation time,reaching up to 62.8%and 68.6%,respectively.The in-situ nano Ti_(2)Cu precipitates were homogeneously distributed in the matrix of the Ti−3Cu alloy,which was the key reason of increasing the corrosion resistance.Additionally,the microscale electric fields between theα-Ti matrix and the Ti_(2)Cu was responsible for the enhancement of the antibacterial properties.
基金financially supported by the Scientific Research Project Coordinatorship (BAP) of Yildiz Technical University (YTU) (Project No: FYL-2021-3825)。
文摘Aluminum alloys are widely used in industry due to their light weight.These alloys are generally exposed to abrasive wear,which diminishes their effective lifespan.The wear resistance of these alloys is enhanced by adding various reinforcements,however,this enhancement comes at the cost of reduced fracture toughness.This paradox of increased wear resistance versus decreased fracture toughness in aluminum alloys can be resolved by using functionally graded materials (FGMs).This study focuses on the abrasive wear behavior of functional graded aluminum matrix composites reinforced with Al_(3)Ti particles.The wear properties of the composites were investigated by considering the characteristics of the composite such as matrix type and various composite zones,as well as the wear parameters such as abrasive particle diameter,load,sliding speed and distance.Taguchi method was used in the abrasive wear tests in order to get more reliable results in a timeefficient manner.Experiment recipes were created based on the L_(27)(3^(6)) orthogonal series.As a result of the study,it is observed that the wear resistance of the composites increases with an increase in Al_(3)Ti reinforcement content and hardness of the matrix.In addition,the size of abrasive particles and the applied load are significant factors affecting abrasive wear.
文摘光电化学(PEC)分解水是一种清洁可持续的获取氢燃料的方法,其中产氧半反应(OER)是制约整个水分解过程效率的关键步骤.因此,光阳极的性能是决定太阳能到氢能转化效率的关键因素.在各种水氧化光阳极材料中,赤铁矿(α-Fe_(2)O_(3))因具有良好的化学稳定性、合适的带隙(~2.1 eV)、无毒、储量丰富等优点而成为最有前途的光阳极材料之一.然而,α-Fe_(2)O_(3)丰富的受体表面态和缓慢的水氧化动力学导致光生电荷复合严重,限制了其在光电化学中的实际应用.因此,有必要对α-Fe_(2)O_(3)进行表面工程设计以提高水氧化效率.本文提出了一种新方法,以金属有机框架(Ti-MOFs)为模板,在Ti-Fe_(2)O_(3)表面煅烧合成TiO_(2)层,然后将富活性位点的ZIF-67加载在TiO_(2)/Ti-Fe_(2)O_(3)上作为助催化剂,制备出具有较好光电化学性能的ZIF-67/TiO_(2)/Ti-Fe_(2)O_(3)复合光阳极.X射线衍射、高分辨透射电镜、X射线光电子能谱和拉曼光谱等表征结果证实成功合成了ZIF-67/TiO_(2)/Ti-Fe_(2)O_(3).同时,氮气等温吸附脱附曲线和表面接触角测试结果表明,MOFs衍生的TiO_(2)为介孔材料.采用表面光伏技术、光致发光光谱、飞秒-瞬态吸收光谱和电化学阻抗谱分析,研究了光生电荷的分离和复合行为.结果表明,MOFs衍生的TiO_(2)不仅可以作为钝化层有效抑制了表面复合,还作为Ti-Fe_(2)O_(3)的电子阻挡层,显著减少了电子向表面的流失,从而大大提高了Ti-Fe_(2)O_(3)表面和体相的电荷分离效率.进一步的累积电荷量测试、电化学阻抗谱和Bode图分析显示,负载MOFs衍生TiO_(2)后,可以明显促进光生空穴向电解质的注入,其多孔结构也可以增加反应接触面积,这有利于光生电荷在固液界面传输.此外,理论计算结果表明,Ti-Fe_(2)O_(3)水氧化速控步骤的能垒(ΔG=3.38 eV)明显高于TiO_(2)(ΔG=1.67 eV),说明OER更容易在TiO_(2)/Ti-Fe_(2)O_(3)表面发生,这与其光电流密度结果一致.为进一步提高反应活性和加快水氧化动力学,负载助催化剂ZIF-67后,ZIF-67/TiO_(2)/Ti-Fe_(2)O_(3)复合光阳极实现了较好的光电化学性能,其在1.23 V vs.RHE时光电流密度高达4.04 mA cm^(‒2),是Ti-Fe_(2)O_(3)的9.3倍,并且复合光阳极的入射光子电流转换效率和空穴注入效率分别达到93%(390 nm)和91%.综上所述,本研究通过MOFs衍生的TiO_(2)和ZIF-67助催化剂改性α-Fe_(2)O_(3)光阳极,显著提升了其光电化学水氧化性能.其中,MOFs衍生TiO_(2)不仅优化了电荷分离,还促进了光生空穴的注入,从而显著提高其光电化学水氧化性能.本研究为构筑高性能的有机-无机杂化光阳极提供了新思路.
文摘Magnesium(Mg)stands out in temporary biomaterial applications due to its biocompatibility,biodegradability,and low Young’s modulus.However,controlling its corrosion through next-generation polymer-based functional coatings is crucial due to the rapid degradation behavior of Mg.In this study,the function of 2D lamellar Ti_(3)C_(2)T_(x)(MXene)in Hydroxyapatite(HA)and Halloysite nanotube(HNT)hybrid coatings in biodegradable poly-(lactic acid)(PLA)was investigated.The morphological and structural characterizations of the coatings on Mg were revealed through HRTEM,XPS,SEM-EDX,XRD,FTIR,and contact angle analyses/tests.Electrochemical in vitro corrosion tests(OCP,PDS,and EIS-Nyquist)were conducted for evaluate corrosion resistance under simulated body fluid(SBF)conditions.The bioactivity of the coatings in SBF have been revealed in accordance with the ISO 23,317 standard.Finally,antibacterial disk diffusion tests were conducted to investigate the functional effect of MXene in coatings.It has been determined that the presence of MXene in the coating increased not only surface wettability(131°,85°,77°,and 74°for uncoated,pH,PHH,and PHH/MXene coatings,respectively)but also increased corrosion resistance(1857.850,42.357,1.593,and 0.085×10^(-6),A/cm^(2) for uncoated,pH,PHH,and PHH/MXene coatings,respectively).It has been proven that the in vitro bioactivity of PLA-HA coatings is further enhanced by adding HNT and MXene,along with SEM morphologies after SBF.Finally,2D lamellar MXene-filled coating exhibits antibacterial behavior against both E.coli and S.aureus bacteria.